• 한국재료학회지
• /
• 제27권2호
• /
• pp.63-68
• /
• 2017

A black nickel oxide powder, one of the commercial nickel oxide ores, was reduced by hydrogen gas in a batch-type fluidized-bed reactor in a temperature range of 350 to $500^{\circ}C$ and in a residence time range of 5 to 120 min. The hydrogen reduction behavior of the black nickel oxide was found to be somewhat different from that of green nickel oxide ore. For the black nickel oxide, the maximum temperature (below which nickel oxide particles can be reduced without any agglomeration) was significantly lower than that observed for the green nickel oxide. In addition, the best curve fittings of the Avrami model were obtained at higher values of the overall rate constant "k" and at lower values of the exponent "m", compared to those values for the green nickel oxide. It may be inferred from these results that the hydrogen reduction rate of the black nickel oxide is faster than that of the green nickel oxide in the early stages, but the situation reverses in the later stages. For the black nickel oxide ore, in spite of the low temperature sintering, it was possible to achieve a high degree fluidized-bed reduction at lower temperatures and at lower gas consumption rates than was possible for the green nickel oxide. In this regard, the use of black nickel oxide is expected to yield a benefit if its ore price is sufficiently lower than that of the green nickel oxide.

• 한국결정성장학회지
• /
• 제13권3호
• /
• pp.117-121
• /
• 2003

염화 니켈과 마그네슘 스테아린산 혼합 분말로부터 수소환원 공정에 의하여 니켈 분말을 제조하고 반응온도 및 마그네슘스테아린산의 첨가에 따른 분말의 특성을 검토하였다. 마그네슘 스테아린산을 함유한 경우 과도한 입자 성장의 억제로 인하여 입경 감소 효과가 있었다. 마그네슘 스테아린산의 함유량이 증가함에 따라 이에 따른 액상량의 증가로 인하여 입경 감소와 입자들간의 응집 정도에도 영향을 주었다.

• 한국분말재료학회지
• /
• 제26권4호
• /
• pp.340-344
• /
• 2019

Due to the rapid development of electricity, electronics, information communication, and biotechnology in recent years, studies are actively being conducted on nanopowders as it is required not only for high strengthening but also for high-function powder with electric, magnetic, and optical properties. Nonetheless, studies on nickel nanopowders are rare. In this study of the synthesis of nickel nanoparticles from $LiNiO_2$ (LNO), which is a cathode active material, we have synthesized the nanosized nickel powder by the liquid reduction process of $NiSO_4$ obtained through the leaching and purification of LNO. Moreover, we have studied the reduction reaction rate according to the temperature change of liquid phase reduction and the change of particle size as a function of NaOH addition amount using hydrazine monohydrate ($N_2H_4{\cdot}H_2O$) and NaOH.

• Elastomers and Composites
• /
• 제50권3호
• /
• pp.217-222
• /
• 2015

Carbon-nickel nanocomposites were prepared by the reaction of fullerene ($C_{60}$) and nickel hydroxide in an electric furnace at $700^{\circ}C$ for 2 h. The hybrid carbon-nickel nanocomposites were characterized by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy. The kinetics and catalytic activity of the carbon-nickel nanocomposites in the reduction of 4-nitrophenol were confirmed by UV-vis spectroscopy.

• Elastomers and Composites
• /
• 제55권3호
• /
• pp.191-198
• /
• 2020

Nickel oxide (NiO) nanoparticles were synthesized by a reaction of nickel nitrate hexahydrate (Ni(NO₃)₂·6H₂O) and sodium hydroxide (NaOH). The synthesized NiO nanoparticles were examined with X-ray diffraction, scanning electron microscopy, Raman spectroscopy, and ultraviolet-visible (UV-vis) spectroscopy. The NiO nanoparticles were used as the catalyst for the reduction of o- and m-nitroaniline to phenylenediamine. The reduction rate of m-nitroaniline was faster than that of o-nitroaniline. The reduction rate for both o- and m-nitroaniline increased as the reaction temperature increased. The rate of reduction for nitroaniline followed a pseudo first-order reaction rate law.

• 대한화학회지
• /
• 제38권5호
• /
• pp.397-403
• /
• 1994

질산니켈과 아연을 에탄올 용매하에서 환류반응시켜 얻은 활성화시킨 촉매는 히드라진 존재하에서 방향족 니트로화합물을 주로 아족시 화합물로 환원시켜 주었다. 그러나 질산니켈 대신 염화니켈을 사용하여 얻은 촉매는 같은 조건하에서 단지 방향족 아민만을 얻을 수 있었다. 활성화시키지 않고, 방향족 니트로화합물, 염화니켈이나 질산니켈, 아연 그리고 히드라진 혼합물을 환류반응 시킬 때는 낮은 수율의 아조, 아족시와 아민 화합물을 얻을 수 있었다.

• 한국결정성장학회지
• /
• 제6권3호
• /
• pp.415-423
• /
• 1996

황산니켈염 수용액에서 가압수소환원법을 이용하여 알루미나 분말상에 니켈 코팅층을 형성하기 위하여 실험조건(수소분압, 반응온도, $PdCl_{2}$ 첨가량, 알루미나의 종류 및 입도)을 변화시키면서 니켈이온의 환원속도 및 석출상태를 조사하였다. 환원온도 $165^{\circ}C$, 수소분압 300 psi, 코팅촉매제 $PdCl_{2}\;2\;mg/\ell$를 첨가한 조건에서 균질한 니켈코팅층을 얻을 수 있었다.

• 대한화학회지
• /
• 제68권1호
• /
• pp.12-14
• /
• 2024

• 자원리싸이클링
• /
• 제27권5호
• /
• pp.23-29
• /
• 2018

일반적으로 탄산니켈을 제조하기 위한 원료로 $NiSO_4$ 및 $NiCl_2$가 사용되었다. 제조된 탄산니켈의 경우 표면 및 내부에 있어 $Na_2SO_4$ 및 NaCl이 생성되어 탄산니켈의 순도를 감소시키는 원인이 되고 있으며, 이러한 불순물의 제거정도에 따라 고순도 탄산니켈을 제조할 수 있다. 본 연구에서는 니켈MHP 용매추출 공정으로 제조된 $NiCl_2$를 이용하여 탄산니켈제조 연구를 진행하였다. 실험은 니켈염과 탄산염 당량비에 따른 제조, 탄산니켈 수세에 따른 탄산니켈 내 Na 및 Cl 감소 및 수세용수의 온도에 따른 Na 및 Cl의 감소에 대한 조건을 실험하여 고순도 탄산니켈을 제조할 수 있었다.

• 한국재료학회지
• /
• 제12권10호
• /
• pp.803-808
• /
• 2002

Nickel powders were prepared from nickel chloride solution by wet reduction process, and the size control of the particles was investigated with reactant concentration, dispersant agent, and the addition of ethanol as an organic solvent in NiCl$_2$ aqueous solution. The size of the particle decreased with the increase of nickel chloride concentration. Their average particle size were 1.9$\mu\textrm{m}$, 1.6$\mu\textrm{m}$ and $1.5\mu\textrm{m}$ with 0.5M, 0.8M and 1.0M of nickel chloride concentration respectively. The spherical particle was easily controlled by the addition of ethanol as an organic solvent. Especially, in 30 vol% of ethanol, the average particle size and specific surface area were about 0.2$\mu\textrm{m}$ and 8.98m$^2$/g, respectively.