Objectives: Nanomaterials have been used in various fields. As use of nanoproducts is increasing, workers dealing with nanomaterials are also gradually increasing. Exposure assessments for nanomaterials have been carried out for protection of worker's health in workplace. Exposure studies were mainly focused on manufacturing processes, but these studies on after-treatment processes such as refinement, weighing, and packing were insufficient. So, we investigated exposure characteristics of particles during after-treatment processes of $Al_2O_3$ fibers and Ni powders. Methods: Mass-production of Ni powder process was carried out in enclosed capture-type canopy hood. In a developing stage, $Al_2O_3$ was handled with a local ventilation unit. Exposure characteristics of particles were investigated for $Al_2O_3$ fiber and Ni powder processes during the periods of 10:00 to 16:00, 20 May 2014 and 13:00 to 16:00, 21 May 2014, respectively. Three real-time aerosol instruments were utilized in exposure assessment. A scanning mobility particle sizer(SMPS, nanoscan, model 3910, TSI) and an optical particle counter(OPC, portable aerosol spectrometer, model 1.109, Grimm) were used to determine the particle size distribution in the size range of 10-420 nm and $0.25-32{\mu}m$, respectively. In addition, a nanoparticle aerosol monitor(NAM, model 9000, TSI) was used to measure lung-deposited nanoparticle surface area. Membrane filters(isopore membrane filter, pore size of 100 nm) were also used for air sampling for the FE-SEM(model S-5000H, Hitachi) analysis using a personal sampling pump(model GilAir Plus by 2.5 L/min, Gilian). Conclusions: For Ni powder after-treatment process, only 27% increase in particle concentration was found during the process. However, for $Al_2O_3$ fiber after-treatment process, significant exposure(1.56-3.34 times) was observed during the process.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.2
• /
• pp.71-79
• /
• 2021

In this study, we have successfully fabricated the Sn-Ni paste and evaluated the bonding properties for high-temperature endurable EV (Electric Vehicle) power module applications. From evaluating of the micro-structural changes in the TLPS (Transient Liquid Phase Sintering) joints with Sn and Ni contents in the Sn-Ni pastes, a lack of Ni powders and Ni particle agglomerations by Ni surplus were observed in the Sn-20Ni and Sn-50Ni joints (in wt.%), respectively. In contrast, relatively dense microstructures are observed in the Sn-30Ni and Sn-40Ni TLPS joints. From differential scanning calorimetry (DSC) thermal analysis results of the fabricated Sn-Ni paste and TLPS bonded joints, we confirmed that the complete reactions of Sn with Ni to form Ni-Sn intermetallic compounds (IMCs) at bonding temperatures occurred, and there is no remaining Sn in the joints after TLPS bonding. In addition, the interfacial reactions and IMC phase changes of the Sn-30Ni joints under various bonding temperatures were reported, and their mechanical shear strength were investigated. The TLPS bonded joints were mainly composed of residual Ni particles and Ni₃Sn₄ intermetallic phase. The average shear strength tended to increase with increasing bonding temperature. Our results indicated a high shear strength value of approximately 30 MPa at a bonding temperature of 270 ℃ and a bonding time of 30 min.

• Journal of Powder Materials
• /
• v.20 no.4
• /
• pp.264-268
• /
• 2013

Nickel-based superalloy IN 713C powders have been consolidated by hot isostatic pressing (HIPing). The microstructure and mechanical properties of the superalloys were investigated at the HIPing temperature ranging from $1030^{\circ}C$ to $1230^{\circ}C$. When the IN 713C powder was heated above ${\gamma}^{\prime}$ solvus temperature (about $1180^{\circ}C$), the microstructure was composed of the austenitic FCC matrix phase ${\gamma}$ plus a variety of secondary phases, such as ${\gamma}^{\prime}$ precipitates in ${\gamma}$ matrix and MC carbides at grain boundaries. The yield and tensile strengths of HIPed specimens at room temperature were decreased while the elongation and reduction of area were increased as the processing temperature increased. At $700^{\circ}C$, the strength was similar regardless of HIPing temperature; however, the ductility was drastically increased with increasing the temperature. It is considered that these properties compared to those of cast products are originated from the homogeneity of microstructure obtained from a PM process.

• Journal of the Korean Ceramic Society
• /
• v.50 no.3
• /
• pp.195-200
• /
• 2013

Here, we report preparation of cyan ceramic nano-pigment for inkjet printing and the Ni substitutional effects on the cyan color. $MgAl_2O_4$ was selected as the crystalline host network for the synthesis of nickel-based cyan ceramic nano-pigments. Various compositions of $Ni_xMg_{1-x}Al_2O_4$ ($0{\leq}x{\leq}1$) powders were prepared using the polymerized complex method. The powder was then preheated at $400^{\circ}C$ for 5 h and finally calcined at $1000^{\circ}C$ for 5 h. XRD patterns of $Ni_xMg_{1-x}Al_2O_4$ showed a single phase of the spinel structure in all the compositions. The particle sizes ranged from 20 to 50 nm in TEM observations. The characteristics of the color tones of $Ni_xMg_{1-x}Al_2O_4$ were analyzed by UV-Visible spectroscopy and CIE $L^*a^*b^*$ measurement. CIE $L^*a^*b^*$ measurement results indicate that the pigment color changes from light cyan to deep cyan due to the decrease of the $a^*$ and $b^*$ values with an increase of an Ni substitutional amount. In addition, the thermal stability and the binding nature of $Ni_xMg_{1-x}Al_2O_4$ are also discussed using TG-DSC and FT-IR results respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.5
• /
• pp.401-409
• /
• 2013

Numerical analysis on RF (Radio-Frequency) thermal plasma treatment of micro-sized Ni metal was carried out to understand the synthesis mechanism of nano-sized Ni powder by RF thermal plasma. For this purpose, the behaviors of Ni metal particles injected into RF plasma torch were investigated according to their diameters ($1{\sim}100{\mu}m$), RF input power (6 ~ 12 kW) and the flow rates of carrier gases (2 and 5 slpm). From the numerical results, it is predicted firstly that the velocities of carrier gases need to be minimized because the strong injection of carrier gas can cool down the central column of RF thermal plasma significantly, which is used as a main path for RF thermal plasma treatment of micro-sized Ni metal. In addition, the residence time of the injected particles in the high temperature region of RF thermal plasma is found to be also reduced in proportion to the flow rate of the carrier gas In spite of these effects of carrier gas velocities, however, calculation results show that a Ni metal particle even with the diameter of $100{\mu}m$ can be completely evaporated at relatively low power level of 10 kW during its flight of RF thermal plasma torch (< 10 ms) due to the relatively low melting point and high thermal conductivity. Based on these observations, nano-sized Ni metal powders are expected to be produced efficiently by a simple treatment of micro-sized Ni metal using RF thermal plasmas.

• Korean Journal of Crystallography
• /
• v.14 no.1
• /
• pp.1-6
• /
• 2003

NiZn-ferrites were synthesized from the waste catalysts. which were by product of styrene monomer process and buried underground as an industrial wastes, and their magnetic properties were investigated. Nickel oxide and zinc oxide powders were mixed with finely ground waste catalysts, and spinel type ferrite was obtained by calcination at 900℃ and sintering at 1325℃ for 5 hours. The initial permeabilities were measured and reflection losses were calculated from S-parameters for the composition of Ni/sub x/Zn/sub 1-x/Fe₂O₄(x=0.36, 0.50, 0.66) and (Ni/sub 0.5/Zn/sub 0.5)/sub 1-y/Fe/sub 2+y/O₄(y=-0.02, 0, 0.02).

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1162-1166
• /
• 2001

NiZn-ferrite was synthesized from waste catalysts, which were produced from styrene monomer process and buried underground as an industrial wastes, and its magnetic properties were investigated. Nickel oxide and zinc oxide powders were mixed with finely ground waste catalysts, and spinel type ferrite was obtained by calcination at 900$\^{C}$ and sintering at 1230$\^{C}$ for 5 hours. The intial permeability was measured and reflection loss was calculated from S-parameters for the composition of Ni$\_$x/Zn$\_$1-x/Fe$_2$O$_4$(x=0.36, 0.50, 0.66). NiZn-ferrite synthesized from waste iron oxide catalyst showed a feasibility for the use as electromagnetic wave absorber in X-band.

• Resources Recycling
• /
• v.22 no.3
• /
• pp.43-49
• /
• 2013

A study on the recovery of lithium and leaching behavior of NCM powder by hydrogen reduction for NCM system Li-ion battery scraps was investigated. The reductive rate was about 93% at $800^{\circ}C$ by hydrogen treatment. The lithium carbonate with 99% purity was manufactured by using $CO_2$ gas and washing method with water for NCM powder after hydrogen reduction. As a result of comparing the powders before and after the hydrogen reduction treatment for acid leaching behavior we obtained 32% enhanced leaching rate of cobalt, 45% enhanced leaching rate of nickel and the 90% leaching effect for manganese by hydrogen reduction at 2M $H_2SO_4$ concentration condition.

• Resources Recycling
• /
• v.4 no.1
• /
• pp.52-59
• /
• 1995

Treating bulk superalloy scrap with molten zinc has been studled to facililate recycling and recovery- of cobalt.Superalloys investigated were the cobalt-base Mar-M-509 and X45 and the nickel-base Rene 80. Charges withZnlscrap ratlos of 1.5-6.5 were heated to 750-9002 far 1-7.5 hours in a nitrogen atmosphere. The moltenzinc dissolved superalloy scrap and zinc was removed by vacuum distillation at 850-Wk for 4-6 hours. Ithas been concluded that the optimum conditions of decomposition for Mar-M-509 and Rene 80 \"ere dissolutiontemperature of about 850k, Znlscrap ratlo of about 5, and dissalution time of about 5.5 hours. The zinc-treatedsuperalloy prouducts were friable and reacted rapidly with acid solutions. Leaching 9mm pieces of unalloyedMar-M-509 or Rene 80 with 5 times the stolchlometric amount oi 6N HCI at 90t ior 3 hours dissolved about1.5-7.270, while leachmg of the minus 20-mesh products dissolved about 89.0-93.0%.ved about 89.0-93.0%.

• Resources Recycling
• /
• v.28 no.1
• /
• pp.23-31
• /
• 2019

Cementation is one of economical and efficient recycling method precipitating the metal ion in solution by adding another active metal. In this study for optimizing cadmium recovery efficiency, it was performed as a function of the effect of pH, temperature, particle size, and input amount of zinc in 0.1 M $CdSO_4$ solution and Ni-Cd battery leaching solutions, respectively. The particle size of zinc and temperature were key factors for Cd cementation and it was confirmed that the input amount of 2.6 of Zn/Cd ratio using granular-type zinc was optimal condition for selective Cd recovery efficiency at $25^{\circ}C$.