• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1999년도 추계학술발표강연 및 논문개요집
• /
• pp.32-32
• /
• 1999

• 한국표면공학회지
• /
• 제20권3호
• /
• pp.95-105
• /
• 1987

For the purpose of improving the hot corrosion resistance of Ni-base superalloy, Inconel 600, aluminide and chromium-aluminide coatings by pack cementation process were studied. The morphology of these coatings is dependent on the type of process employed. And their overall composition depends on the composition of the base alloy and on the nature of the cement. Therefore the different aluminide and chromium-aluminide coatings obtained on a superalloy do not possess the same resistance to oxidation and hot corrosion. The mechanisms governing the formation of the coatings and the composition of the coating were varied by pack composition and temperature, and cyclic hot corrosion resistance of the auluminide coating formed by one-step process was inferior to that of the coating formed by two-step process. and Cr-Al composite coating showed good resistance for cyclic hot corrosion.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.511-512
• /
• 2006

Tungsten coatings with different interlayers onto the oxygen-free copper substrates were fabricated by atmosphere plasma spraying. The effects of different interlayers of NiCrAl, NiAl and W/Cu on bonding strength were studied. SEM, EDS and XRD were used to investigate the photographs and compositions of these coatings. The tungsten coatings with different initial particle sizes resulted in different microstructures. Oxidation was not detected in the tungsten coating, but in the interlayer, it was found by both XRD and EDS. The tungsten coating deposited directly onto the copper substrate presented higher bonding strength than those with different interlayers.

• 한국재료학회지
• /
• 제31권8호
• /
• pp.439-444
• /
• 2021

The oxidation resistance of the diffusion aluminide bond coat (BC) is compromised largely by interdiffusion (ID) effects on coated turbine blades of aeroengines. The present study is designed to understand the influence of ID on βNiAl coatings or BC. In this regard, nickel substrate and CMSX-4 superalloy are deposited. In total, four sets of BCs are developed, i.e. pure βNiAl (on Ni substrate), simple βNiAl (on CMSX-4 substrate), Zr-βNiAl (on CMSX-4 substrate) and Pt-βNiAl (on CMSX-4 substrate). The main aim of this study is to understand the interdiffusion of Al, Zr and Pt during preparation and oxidation. In addition, the beneficial effects of both Zr and platinum are assessed. Pure βNiAl and simple βNiAl show Ni-out-diffusion, whereas for platinum inward diffusion to the substrate is noticed under vacuum treatment. Interestingly, Zr-βNiAl shows the least ID in all BCs and exhibit stability under both vacuum and oxidation treatments. However, its spallation resistance is slightly lower than that of Pt-βNiAl BC. All BCs show similar oxide growth trends, except for Zr-βNiAl, which exhibits two-stage oxidations, i.e. transient and steady-state. Moreover, it is suggested that the localized spallation in all BCs is caused by βNiAl - γ'-Ni₃Al transformation.

• 한국세라믹학회지
• /
• 제53권1호
• /
• pp.81-86
• /
• 2016

The effect of substrate rotation speed on the phase forming behavior and microstructural variation of 8 wt% yttria ($Y_2O_3$) stabilized $ZrO_2$ (8YSZ) coatings as a thermal barrier coating has been investigated. 8YSZ coatings with $100{\sim}200{\mu}m$ thickness were deposited by electron beam-physical vapor deposition onto a super alloy (Ni-Cr-Co-Al) substrate with a bond coating (NiCo-CrAlY). The width of the columnar grains of the 8YSZ coatings increased with increasing substrate rotation speed from 1 to 30 rpm at a substrate temperature range of $900{\sim}950^{\circ}C$. In spite of the different growth behaviors of coatings with different substrate rotation speeds, the phases of each coating were not changed remarkably. Even after post heat treatments with various conditions of the coated specimens fabricated at 20 rpm, only a change of color was noticeable, without any remarkable change in the phase or microstructure.

• 대한금속재료학회지
• /
• 제50권1호
• /
• pp.28-33
• /
• 2012

Ball-milled Ni-Al powder compacts have been synthesized by the heat of molten cast iron and have been coated on cast iron. The effects of the ball-milling time on the microstructure of the intermetallic coatings have been investigated. The experimental results showed that the ball-milled Ni-Al powder compacts were completely reacted and were successfully coated on the cast iron without re-melting the substrate. Densification of the coating layers was enhanced by increasing the ball-milling time. This might be attributed to the fact that the heat released during the intermetallic reaction was dispersed over a prolonged reaction time by the ball-milling of the elemental powders.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.726-731
• /
• 2002

Reaction synthesis is a process to form ceramics, intermetallics and their composites from elemental powder mixture. Application of this process to a surface modification techniques has a possibilities to enable the process at a lower temperature or for a shorter time, although synthesized materials are likely to include voids and unreacted elements. This paper intend to examine the effect of Si addition to the mixture of Al and Ni on the densification of synthesized Ni-Al intermetallic compounds and to evaluate the surface properties of obtained coatings. By the Si addition, exothermic reaction temperature to form Ni-Al intermetallic was lowered to be below the melting point of Al. Si soluted $Al_3$Ni$_2$, $Al_3$Ni and $Al_{6}$Ni$_3$Si were mainly formed in the coating layer when powder mixture was heated to 973K for 300s. Besides, densification was enhanced by increasing hot press pressure, Si additions and heating rate. When the composition of eutectic Al-Si reaches 78%, void ratio of sintered compact reduced to 0.4%. It is caused by higher flowability of Al-Si liquid phase generated and its infiltration into the void. Since the hardness of NiAl(Si) compound (about 600HV) formed in the coating layer is higher than that of Ni-Al compound (about 400HV), coating layer with high density and superior wear property is obtained by hot press using reaction synthesis from Al-Ni-Si powder mixture.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2009년도 제33회 추계학술대회논문집
• /
• pp.421-425
• /
• 2009

재생냉각형 액체로켓 연소기 챔버에서 열차폐 코팅이 미치는 열/구조적인 영향에 대하여 유한요소 해석을 통하여 고찰하였다. 열차폐 코팅은 현재 개발하고 있는 연소기에 사용되는 NiCrAlY-$ZrO_2$과 향후 적용할 가능성이 있는 Ni-Cr 두 종류를 적용하였다. 열/구조해석 결과 NiCrAlY-$ZrO_2$ 코팅이 Ni-Cr 코팅에 비하여 열차폐에 의한 온도감소 효과가 크게 나타났다. 결과적으로 냉각채널의 온도와 변형 또한 NiCrAlY-$ZrO_2$ 코팅을 적용하였을 때 Ni-Cr 코팅보다 감소하였다. 외측구조물의 구조안정성에 있어서 Ni-Cr 코팅이 미치는 영향은 없었으나, NiCrAlY-$ZrO_2$ 코팅은 외측구조물의 유효응력을 감소시켜 챔버의 구조안정성을 증가시켰다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.116-116
• /
• 2013

(Ni-22Cr-10Al-1Y)와 ($ZrO_2-25CeO_2-2.5Y_2O_3$)로 구성되는 금속/세라믹 복합코팅을 대기용사(ASP; air plasma spay)으로 철 기판위에 1:3, 2:2, 3:1의 무게비로 혼합하여 제조하였다. 용사된 코팅은 금속이영지역과 세라믹잉여지역으로 구별되고, 용사중에 NiCrAlY중의 Al이 선택적으로 산화되어 Al2O3가 계면에 존재하였다. 복합코팅은 $NaCl-Na_2SO_4$ 용융염에서 $800{\sim}900^{\circ}C$, 50시간 동안 부식실험을 실시하였다. 부식생성물은 NiO, $Cr_2O_3$, ${\alpha}-Al_2O_3$가 생성되는데, 부식이 진행되면서 용해되었다. 용융염 부식이 진행되는 동안에 Cr, Al이 외방확산하였고, Na, Cl, S는 내부로 확산되었다. 시간 및 온도뿐만 아니라 금속의 양이 증가할수록 코팅의 내식성은 저하되었다.

• Journal of Welding and Joining
• /
• 제18권3호
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool