• Korean Journal of Materials Research
• /
• v.10 no.10
• /
• pp.715-720
• /
• 2000

By the mechanical alloying method. Ni-WC composite materials were prepared to improve the deformation-resistance for creep and sintering of Ni-anode at the operating temperature of $650^{\circ}C$. Mechanically alloyed powder w was initially fabricated by ball milling for 80hr, and then amorphization was occurred by the destruction of ordered crystals based on XRD analysis. In order to investigate the electrochemical performance and sheet characteristics of Ni-WC anode, tape casting process was adopted. Finally, the obtained sheet thickness of Ni- we after sintering at $1180^{\circ}C$ for 60 minutes in $H_2$ atmosphere was O.9mm and the average pore size was $3~5{\mu\textrm{m}}$ with porosities of 55%. The second phase was not observed in Ni- W matrix while W particles were finely and uniformly distributed in Ni matrix. This fine and uniform distributed W particles in Ni matrix are expected to enhance the mechanical properties of Ni anode through the dispersion and solid solution hardening mechanisms.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.31-36
• /
• 2003

In this study, nano-sized NiCuZn-ferrites for the multi-layered chip inductor application were prepared by a coprecipitation method and its electromagnetic properties were analyzed. Also, the property of low temperature sintering were studied with the initial heat treatment of powder.$(Ni_{0.4-x}Cu_xZn_{0.60})_{1+w}(Fe_2O_4)_{1-w}$ (x=0.2, w=0.03) were calcined at $300^{circ}C~750^{circ}C.$ The sintered NiCuZn-ferrites at $900^{\circ}C$ showed good apparent density $4.90g/cm^3,$ and magnetic properties of initial permeability 164 and quality factor 72. As the calcination temperature increase, the grain size of NiCuZn-ferrite increased with irregular grain distribution and its magnetic properties were deteriorated.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.79-84
• /
• 1994

The mechanism of activated sintering of tungsten powder was discussed in terms of diffusion and segregation of activator atoms at W grain boundaries. Shrinkage behaviours of W-0.2wt.% Ni, W-0.2wt.% Cu or pure W powder compacts during sintering at low temperatures of 900~ $1200^{\circ}C$ were investigated. It was found that the Cu additive inhibits sintering process causing lower densification than pure W compact while remarkable shrinkage occurred in the Ni added W powder. Such contrary effect was explained by comparing self diffusion processes along Ni or Cu segregated W boundaries in which Ni segregants enhance but Cu atoms retard the migration of W atoms at W boundaries.

• Journal of Surface Science and Engineering
• /
• v.38 no.1
• /
• pp.1-6
• /
• 2005

Ni-15at.% W coatings with film thicknesses of 20-40 ㎛ were electroplated on a steel substrate, and their oxidation behavior was investigated at 700 and 800℃ in air. For comparison, a pure Ni coating and a bulk Ni were also oxidized. The Ni-15at.%W coating displayed the worst oxidation resistance, due to the formation of less-protective NiO, Fe₂O₃, NiFe₂O₄ and NiWO₄. The corrosion behavior Ni-15at.%W coatings electroplated on a steel substrate was similarly investigated at 700 and 800℃ in the Ar-l%SO₂ atmosphere. For comparison, the uncoated steel substrate was also corrosion-tested in the Ar-l %SO₂ atmosphere. Severe scale spallation and the internal corrosion of the steel that occurred in the uncoated substrate were not observed in the coated specimen. However, it seemed that the Ni-15at.%W coating cannot be a potential candidate as a sulfidation-resistant coating, due to the formation of less-protective NiO, NiS, WO₃ and NiWO₄.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.201-201
• /
• 2011

크롬대체도금으로 개발 추진되고 있는 전기Ni-W합금도금피막은 경질크롬 도금피막보다도 고온에서 경도 및 내 산성이 우수하고, 유리성형용 금형으로 사용되고 있다. 최근 일본에서는 지금까지의 무전해Ni-W-P합금피막에 비해서 텅스텐, 인의 함유율이 높고, 질산 이외의 염산, 황산의 산성 환경과 암모니아, 수산화나트륨 등의 알칼리성 환경에서도 부식이나 변색이 생기지 않는 무전해Ni-W-P합금도금기술을 크롬도금을 대체하는 도금으로서 개발하고 있다.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1995.11a
• /
• pp.31-31
• /
• 1995

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.56-56
• /
• 2001

Ni-W alloy deposit is one of the best alternatives to hard chromium plating because of its good mechanical properties (high hardness, high strength, and good wear resistance). Ni-W alloy is deposited from weakly acidic or alkaline electrolytic bath with nickel sulfate, sodium tungstate or APT, and some kinds of organic hydroxy-acid complex and ammonia salts. W content of the deposit can be changed from 0 to 5Owt% and the coating with high W content is more attracted. But, meanwhile, the deposited layers are always found high internal stress, which cause them to become brittle and to bond insufficiently with the substrate. On the second hand, as the W content is incresed, the current efficiency reduced, which results in large quantities of hydrogen evolution and then produces bubbles on surface and pitting appearance In this paper, the influence of some additives on Ni-W alloy electroplating was investigated by means of compositional analysis and SEM. The initial results showed that 2-butyne-1,4-diol was the best brightener for Ni-W plating process. It could brighten and level deposit, but decreased the cathodic current efficiency. Its optimum concentration range is from O.lgjL to 0.5gjL. Besides, three kinds of additives including 2-butyne-1,4-diol were examined with Dagguchi method.

• 한국전기화학회:학술대회논문집
• /
• 2003.04a
• /
• pp.41-41
• /
• 2003

• Korean Journal of Materials Research
• /
• v.28 no.2
• /
• pp.108-112
• /
• 2018

The present study demonstrates the effect of raw powder on the pore structure of porous W-Ni prepared by freeze drying of camphene-based slurries and sintering process. The reduction behavior of $WO_3$ and $WO_3-NiO$ powders is analyzed by a temperature programmed reduction method in Ar-10% H2 atmosphere. After heat treatment in hydrogen atmosphere, $WO_3-NiO$ powder mixture is completely converted to metallic W without any reaction phases. Camphene slurries with oxide powders are frozen at $-30^{\circ}C$, and pores in the frozen specimens are generated by sublimation of the camphene during drying in air. The green bodies are hydrogen-reduced at $800^{\circ}C$ and sintered at $1000^{\circ}C$ for 1 h. The sintered samples show large and aligned parallel pores to the camphene growth direction, and small pores in the internal wall of large pores. The strut between large pores, prepared from pure $WO_3$ powder, consists of very fine particles with partially necking between the particles. In contrast, the strut densification is clearly observed in the Ni-added W sample due to the enhanced mass transport in activation sintering.

• Journal of Surface Science and Engineering
• /
• v.26 no.2
• /
• pp.87-107
• /
• 1993

The grain size of the final products of WC-Co and WC-Ni composite powders is dependent on the size of the starting material and the conditions employed for the reduction and carburization. APT-Co and -Ni com-plex salts were prepared by the substitution reaction between ammonium ions in APT and the metal ions in Co(NO3)2 and Ni(NO3)2 solutions of different concentrations(0.1 to 0.7M) at $50^{\circ}C$ and the grain sizes of the com-plex salts was $0.54~0.76\mu\textrm{m}$. The complex which calcined the complex salts at $700^{\circ}$~80$0^{\circ}C$ for 60min. were 0.2~0.5$\mu\textrm{m}$. W-Co($5.92^{\circ}C$) and -Ni(6.95%) powders which reduced the complex oxides with H2d atmo-sphere(flow rate;600cc/min.) at $700^{\circ}$~$800^{\circ}C$ for 60min. were $0.5~0.6\mu\textrm{m}$. The mean grain sizes of WC-Co and WC-Ni composite powders which carburized both complex metals of W-Co and W-Ni at $800^{\circ}C$ for 60min. were $0.5~0.6\mu\textrm{m}$, and take place the coarsening of the grain above $800^{\circ}C$ and the optmium ratio of C3H8 and H2 was 0.2 for the control of the free carbon. The effect of Co contents on the particle sizes decreased from 0.4 to $0.25\mu\textrm{m}$ with increasing the content from 2.0 to 7.6w%. The activation energies on the reductions of oxides and the formations of carbides were as follows ; W-Co : Q = 8.7 kcal/mole, W-Ni : Q = 8.1 kcal/mole, WC-Co pow-der : Q = 17.8 kcal/mole, WC-Ni powder : Q = 16.6 kcal/mole.