Synthesis of Nano-sized NiCuZn-ferrites for Chip Inductor and Properties with Calcination Temperature

In this study, nano-sized NiCuZn-ferrites for the multi-layered chip inductor application were prepared by a coprecipitation method and its electromagnetic properties were analyzed. Also, the property of low temperature sintering were studied with the initial heat treatment of powder.$(Ni_{0.4-x}Cu_xZn_{0.60})_{1+w}(Fe_2O_4)_{1-w}$ (x=0.2, w=0.03) were calcined at $300^{circ}C~750^{circ}C.$ The sintered NiCuZn-ferrites at $900^{\circ}C$ showed good apparent density $4.90g/cm^3,$ and magnetic properties of initial permeability 164 and quality factor 72. As the calcination temperature increase, the grain size of NiCuZn-ferrite increased with irregular grain distribution and its magnetic properties were deteriorated.

칩인덕터용 NiCuZn-ferrites 나노 분말합성 및 하소 온도에 따른 특성 변화

본 연구에서는 칩 인덕터용 코어 소재로 사용되는 NiCuZn-ferrite를 공침법을 이용하여 나노크기의 초미세 분말로 합성하고, 합성된 NiCuZn-ferrite의 하소 온도에 따른 저온소결 특성 및 전자기적 특성에 관하여 고찰하였다. 조성은 (N $i_{0.4-X}$C $u_{x}$Z $n_{0.6}$)$_{1+w}$(F $e_2$ $O_4$)$_{1-w}$에서 x 값을 0.2, w 값은 0.03으로 고정하였고, 하소는 30$0^{\circ}C$에서 7$50^{\circ}C$의 온도범위에서 진행하였다. 하소 후 90$0^{\circ}C$에서 소결한 시편의 특성을 측정한 결과, 공침법으로 합성한 NiCuZn-ferrite는 90$0^{\circ}C$의 저온에서 소결밀도 4.90g/㎤, 초기투자율 164, Q-factor 72임을 확인하였다. 또한, NiCuZn-ferrite의 미세구조는 하소온도가 증가함에 따라 입자가 커지고 불균일한 상태가 되며, 초기투자율 등의 ferrites의 전자기적 특성이 저하되었다.되었다.