The dependency of the rate of $CO_2$ reforming of methane on the catalyst loading and the reactor size was examined at a fixed temperature of $750\;^{\circ}C$ and a fixed GHSV of 18000 mL(STP)/$g_{cat}.h$. The conversion of methane in $CO_2$reforming decreased with increase in the reactor size. The catalyst was severely deactivated with increase in the catalyst amount. The amount of carbonaceous species combustible below $550\;^{\circ}C$, determined by TPO experiments with the used catalyst samples increased with increase in the catalyst amount, which was again confirmed by XRD and TEM experiments. The increase of the carbonaceous species combustible below $550\;^{\circ}C$ may be due to the suppression of the reverse Boudouard reaction, since the $CO_2$ reforming of methane, a highly endothermic reaction, resulted in lowering the reaction temperature.

• 한국진공학회지
• /
• 제22권6호
• /
• pp.277-284
• /
• 2013

아세틸렌과 수소기체를 원료기체로 하고 육불화황을 첨가기체로 하여 열화학 기상 증착하에서 탄소코일을 합성하였다. 이 때 산화실리콘 기판위의 니켈막을 탄소코일 성장의 촉매로 사용하였다. 성장된 탄소코일의 생성밀도, 형상, 기하구조 등을 수소 플라즈마 전처리의 유무에 따라 조사하였다. 상대적으로 짧은 시간(1분)의 수소 플라즈마 전처리는 탄소 마이크로 코일을 우세하게 성장시켰다. 긴 시간(30분)동안의 수소플라즈마 전처리는 탄소마이크로 성장 축을 따라 수많은 탄소 나노코일이 들어붙어 있는 특이한 구조를 보였다. 이 특이한 구조는 매우 작은 니켈 촉매의 알갱이를 효과적으로 지지할 수 있는 촉매 지지대로서의 역할을 할 수 있을 것으로 예견되었다.

• 신재생에너지
• /
• 제6권4호
• /
• pp.30-40
• /
• 2010

Syngas from gasification of coal can be converted to SNG(Synthesis Natural Gas) through gas cleaning, water gas shift, $CO_2$ removal, and methanation. One of the key technologies involved in the production of SNG is the methanation process. In the methanation process, carbon oxide is converted into methane by reaction with hydrogen. Major factors of methanation are hydrogen-carbon oxide ratio, reaction temperature and space velocity. In order to understand the catalytic behavior, temperature programmed surface reaction (TPSR) experiments and reaction in a fixed bed reactor of carbon monoxide have been performed using two commercial catalyst with different Ni contents (Catalyst A, B). In case of catalyst A, CO conversion was over 99% at the temperature range of $350{\sim}420^{\circ}C$ and CO conversions and $CH_4$ selectivity were lower at the space condition over 3000 1/h. In case of catalyst B, CO conversion was 100% at the temperature over $370^{\circ}C$ and CO conversions and $CH_4$ selectivity were lower at the space condition over 4700 1/h. Also, conditions to satisfy $CH_4$ productivity over 500 ml/h.g-cat were over 2000 1/h of space velocity in case of catalyst A and over 2300 1/h of space velocity in case of catalyst B.

• 청정기술
• /
• 제21권3호
• /
• pp.184-190
• /
• 2015

대부분의 LNT 촉매는 낮은 온도 영역에서의 NO_x 산화를 위하여 Pt와 같은 귀금속류를 사용하는 것은 경제적인 부담을 가지고 있다. 따라서, 본 연구는 이러한 문제를 해결하기 위하여 시도되었다. 즉, Pt, Pd, Rh 등과 같은 귀금속류(platinum group metal, PGM)를 사용하지 않는 LNT (lean NO_x trap)용 DeNO_x 촉매를 개발하기 위해 시도하였다. 이를 위해서 예비실험을 통해 Pt등 귀금속류등의 PGM (platinum group metal)을 사용하지 않는 Al/Co/Ni 혼합 금속 산화물을 선정하였다. 궁극적으로는, 선정된 촉매의 소성온도에 따른 물리화학적 특성 변화가 NO_x 전환율에 미치는 영향을 살펴보고자 하였다. 이들의 물리화학적인 성질을 평가하기 위해 XRD, EDS, SEM, BET 분석을 실시하였다. 이러한 평가를 실시한 결과, 모든 소성온도에서 혼합금속 산화물은 Co₂AlO₄ 및 NiAl₂O₄의 스피넬 구조가 혼재되어 있는 것으로 나타났고, NO_x 기체들의 산화-환원 반응이 이루어지기에는 충분한 기공부피와 기공크기를 갖고 있음을 알 수 있었다. 그러나 NH₃-TPD 분석 결과에서는 소성온도가 700 ℃ 이하를 유지해야 하는 것으로 판단되었다. 더욱이 ramp test를 통해서는 NO 및 NO_x 전환율을 동시에 만족할 수 있는 시료는 소성온도는 500 ℃에서 처리된 경우임을 알 수 있었다. 이러한 결과 등을 바탕으로, Al/Co/Ni=1.0/2.5/0.3 혼합 금속 산화물의 최적 소성온도는 500 ℃임을 알 수 있었다.

• 한국세라믹학회지
• /
• 제51권4호
• /
• pp.367-373
• /
• 2014

In this study, the reducing agent hydrazine and precipitator NaOH were used with $NiCl_2$ as a starting material in order to compound Ni-based material with spherical nano characteristics; resulting material was used as an anode for SOFC. Synthetic temperature, pH, and solvent amounts were experimentally optimized and the synthesis conditions were confirmed. Also, a 0 ~ 0.15 mole ratio of metal(Co, Fe) was alloyed in order to increase the catalyst activation performance of Ni and finally, spherical nano $Ni_{(1-x)}-M_{(x=0{\sim}0.15)}$(M = Co, Fe) alloy materials were compounded. In order to evaluate the catalyst activation for hydrocarbon fuel, fuel gas(10%/$CH_4$+10%/Air) was added and the responding gas was analyzed with GC(Gas Chromatography). Catalyst activation improvement was confirmed from the 3% hydrogen selectivity and 2.4% methane conversion rate in $Ni_{0.95}-Co_{0.05}$ alloy; those values were 4.4% and 19%, respectively, in $Ni_{0.95}-Fe_{0.05}$ alloy.

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1162-1166
• /
• 2001

석유화학 공정 중 Styrene(SM) 공정에서 발생되는 산화철 폐촉매는 산업 폐기물로서 전량 매립되고 있는데, 이를 출발 원료로 사용하여 NiZn-페라이트를 합성하였고 그 자기적 특성을 조사하였다. 산화철 폐축매 펠렛을 분쇄한 후 NiO 및 ZnO를 혼합하여 90$0^{\circ}C$에서 하소하고 123$0^{\circ}C$에서 5시간 소결하여 스핀넬형 페라이트 소결체를 얻었다. N $i_{x}$ Z $n_{1-x}$F $e_2$ $O_4$(x=0.36, 0.50, 0.66)조성에 대하여 초투자율을 측정하였고, S-parameter를 측정하여 반사 감쇄량을 계산하였다. 산화철 폐촉매를 이용하여 X-band 주파수 영역에서 높은 전자파 흡수능을 갖는 전파흡수체를 제조할 수 있음을 확인하였다.다.

• 한국재료학회지
• /
• 제31권9호
• /
• pp.525-531
• /
• 2021

Carbon-encapsulated Ni catalysts are synthesized by an electrical explosion of wires (EEW) method and applied for CO₂ methanation. We find that the presence of carbon shell on Ni nanoparticles as catalyst can positively affect CO₂ methanation reaction. Ni@5C that is produced under 5 % CH₄ partial pressure in Ar gas has highest conversions of 68 % at 350 ℃ and 70 % at 400 ℃, which are 73 and 75 % of the thermodynamic equilibrium conversion, respectively. The catalyst of Ni@10C with thicker carbon layer shows much reduced activity. The EEW-produced Ni catalysts with low specific surface area outperform Ni catalysts with high surface area synthesized by solution-based precipitation methods. Our finding in this study shows the possibility of utilizing carbon-encapsulated metal catalysts for heterogeneous catalysis reaction including CO₂ methanation. Furthermore, EEW, which is a highly promising method for massive production of metal nanoparticles, can be applied for various catalysis system, requiring scaled-up synthesis of catalysts.

• 한국환경과학회지
• /
• 제28권1호
• /
• pp.65-73
• /
• 2019

The catalytic activity of Ni-0.2%YSZ (Yttria-Stabilized Zirconia) with different promoters was evaluated for $CO_2$ methanation. The catalysts were weighed for mixing and they were dried at $110^{\circ}C$ for molding into disks. The concentration of $CO_2$ and $CH_4$ for conducting of $CO_2$ methanation were analyzed by gas chromatography and the physical characteristics of the disk-type catalyst formed were analyzed by X-ray diffraction, scanning electron microscope and energy dispersive x-ray spectrometer. The addition of $CeO_2$ as a promoter for Ni-0.2%YSZ (denoted as Ni-5%Ce-0.2%YSZ) resulted in the highest $CO_2$ methanation. It also showed catalytic activity at a low temperature($200^{\circ}C$). Following this, $ZrO_2$, $SiO_2$, $Al_2O_3$ and $TiO_2$ were added to Ni-5%Ce-0.2%YSZ to compare the $CO_2$ methanation, and the highest efficiency was found for. Ni-1%Ti-5%Ce-0.2%YSZ Then, the concentration of Ti was increased to 10% and the catalytic activity was estimated using seven different types of commercial $TiO_2$. In conclusion, ST-01 $TiO_2$ showed the highest efficiency for $CO_2$ methanation.

• 공업화학
• /
• 제32권4호
• /
• pp.478-482
• /
• 2021

고정층 상압 유통식 반응기를 사용하여 Ln(1)-Ni(5)/SBA-15 (Ln = Dy, Eu, Pr, Tb) 촉매상에서 메탄의 부분 산화 반응을 수행하여 수소의 수율을 조사하였다. X-ray photoelectron spectroscopy (XPS) 분석으로 Ni(5)/SBA-15 촉매에 1 wt%의 Eu를 첨가함으로써 Eu(1)-Ni(5)/SBA-15의 O1s와 Si2p의 핵심 전자 수준의 화학적 이동이 있었으며, O1s, Ni2p_3/2, Si2p의 원자의 비가 1.284, 1.298, 1.058로 증가하였다. 촉매 표면상에 O^-, O^2-의 산소와 Eu³⁺, Ni⁰, Ni²⁺, Si⁴⁺의 이온이 존재함을 알 수 있었다. Eu(1)-Ni(5)/SBA-15 촉매상에서 수소의 수율은 57.2%이었으며, Ln(1)-Ni(5)/SBA-15 (Ln = Dy, Pr, Tb)보다 우수한 수소 수율을 보여주었고 25 h의 반응에서 안정된 촉매 활성을 유지하였다. Eu를 Ni(5)/SBA-15에 1wt%를 첨가함으로서 금속과 담체 간에 강한 상호 작용에 의한 SMSI 효과로 산소 빈자리를 만들고 촉매 표면상에 Ni⁰, N²⁺의 나노입자의 분산을 증가시켜 촉매 활성을 유지시켰다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.263-263
• /
• 2010

High temperature annealing is required to synthesize graphene using CVD. When thin metal catalyst is used for the synthesis, the high temperature pre-annealing makes the thin catalyst highly agglomerated. We investigated the agglomeration effect on the shape of the synthesized graphene. It is found that high temperature annealing makes randomly distributed many hole or blister on metal catalyst, and the synthesized graphene features floral pattern around the hole. The floral patterns of graphene turned out to be multi-layers and higher D peaks in raman spectrum.