• Journal of the Korean Ceramic Society
• /
• v.34 no.9
• /
• pp.921-926
• /
• 1997

Two NbCx-C1-x/Y2O3/Ti sputter-coated Al2O3 substrates (L 5.5 cm$\times$W 0.5 cm) were diffusion bonded together using hot press method at 95$0^{\circ}C$ for 3 hours under 1 MPa of applied pressure. 4 points bending tests were used to evaluate the mechanical performance of these precracked laminate beams. Two types of mechanical responses were observed: crack penetration through the interface for x=0.75, 1 and crack deflection into an interface for x=0.25, 0.5. The Al2O3/NbCx-C1-x/Y2O3/Ti system suggested here has been proves to be effective for the thermokinetical stability and tailorability of the interfaces of Al2O3/Ti composites at 95$0^{\circ}C$.

• Journal of the Mineralogical Society of Korea
• /
• v.15 no.3
• /
• pp.161-169
• /
• 2002

high pressure and temperature conditions. However, those results are not consistent with one another, and phase boundary between ilmenite and perovskite phases determined only from the quenching method may be not so reliable at all. Therefore, in-situ high pressure-temperature (hP-T) X-ray diffraction measurements were performed up to 19 GPa and $700^{\circ}C$ in a large volume press apparatus using synchrotron radiation. Experimental results show that perovskite phase is stable at pressures above 16 GPa, and transforms back to $LiNbO_3$phase near 15 CPa at room temperature, and that the perovskite-ilmenite transition is back and forth near 15 CPa at $500^{\circ}C$. LiNbO$_3$phase transforms to ilmenite at 13 CPa and $300^{\circ}C$ and at 10.8 CPa and $400^{\circ}C$, respectively. These data indicate that $LiNbO_3$phase may have a stability region in the hP-T phase diagram and that the perovskite-ilmenite phase boundary would be quite different from that previously reported.

• Nuclear Engineering and Technology
• /
• v.4 no.3
• /
• pp.203-213
• /
• 1972

The precipitation sequence of Inconel 718 alloy, aged at $760^{\circ}C$ for times up to 200 hr, has been studied by means of electron microscopy and X-ray diffraction methods. The dominant hardening phase was identified as the metastable, body-centered tetragonal $Ni_3Nb$ Phase in the morphology of platelets. The other phases identified in the aging sequence were (Nb, Ti)C and the stable acicular phase of orthorhombic $Ni_3Nb.$ The observations were made on the interaction of dislocations with the precipitates in the underaged condition. The shearing of the precipitates and the planar defects, e.g., stacking faults on i1101 planes of the intermetallic phase, were observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.439-442
• /
• 2004

The effects of sintering additives on the low-temperature sintering and microwave dielectric properties of $Mg_4Nb_2O_9$ dielectric ceramics were studied. When $3{\sim}20wt%$ of $0.242Bi_2O_3-0.758V_2O_5$ was added, the sintering temperature decreased from $1100{\sim}1300^{\circ}C$ to $950^{\circ}C$ and high density was obtained. When $Mg_4Nb_2O_9$ was sintered at $950^{\circ}C$ with 10wt% of sintering additive, the microwave dielectric properties of $Q{\times}f_0\;=\;80.035GHz,\;\epsilon_r\;=\;13.3\;and\;\tau_f\;=\;-12.9\;ppm/^{\circ}C$ were obtained.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.48-55
• /
• 1997

The steel for automotive exhaust system needs a good corrosion resistance at the atmosphere of high temperature NaCl. Effect of the alloying elements Me, Ti, Nb on the NaCl induced hot corrosion behavior was investigated at the temperatures between 55$0^{\circ}C$ and 75$0^{\circ}C$ for 18Cr ferritic stainless steels. The weight loss by corrosion has increased linearly with corrosion cycle time, and the corrosion rate has accelerated at higher temperature. The alloying of Mo significantly improved corrosion resistance of the steel and the effect was more pronounced at higher temperature. The addition of alloying elements Ti, Nb have also shown improved corrosion resistance by formation of Ti(C,N) or Nb(C, N) precipitates.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.1
• /
• pp.58-63
• /
• 2004

The oxidation behavior of Ti-Nb alloys was studied in dry atmosphere. After vacuum arc melting and hot rolling treatment, Ti-Nb alloys were oxidized at $450^{\circ}C$∼$750^{\circ}C$. The oxidation behaviors between matrix and oxide scale were analyzed by SEM, XPS and XRD. Ti-Nb alloys had higher oxidation resistance than pure Ti at $750^{\circ}C$. XPS analysis of oxide film revealed that $TiO_2$ oxide was formed on the top of surface. The weight gains during the oxidation increase rapidly at temperature above $600^{\circ}C$ which obey the parabolic law.

• Korean Journal of Materials Research
• /
• v.9 no.5
• /
• pp.452-459
• /
• 1999

To develop advanced cladding materials, the effect of Nb addition on the microstructure and corrosion characteristics of Zr-0.8Sn-xNb alloys was investigated. As the Nb content increased, the grain size decreased and the volume fraction of precipitates increased. It was observed from the corrosion test at $360^{\circ}C$ that the corrosion resistance increased with decreasing Nb content. The best corrosion resistance was obtained in Zr-0.8Sn-0.2Nb alloy with high volume fraction of tetra-$ZrO_2$in the oxide. Therefore, it is suggested that Nb in theZr-0.85Sn-xNb system should be added within the solubility limit of Nb from the viewpoint of alloy design.

• Korean Journal of Materials Research
• /
• v.14 no.3
• /
• pp.211-217
• /
• 2004

The oxidation behaviors of Ti-10Ta-10Nb alloy and Ti-6Al-4V alloy were studied in dry air atmosphere. Specimens were melted in consumable vacuum arc furnace and homogenized at $1050^{\circ}C$ for 24 h. Hot rolling was performed at $1000^{\circ}C$. Specimens of the alloys were oxidized as the temperature range $400~650^{\circ}C$ for 30 min. The oxidation behavior of the alloys was analysed by optical microscope, SEM/EDX, XRD, XPS and TGA. Immersion test was performed in 1% Lactic acid. In the microscope observation, oxide layer of Ti-10Ta-10Nb alloy was denser and thinner than Ti-6Al-4V's. The weight gains during the oxidation rapidly increased at the temperature above $600^{\circ}C$ in Ti-6Al-4V's alloy and$ 700^{\circ}C$ in Ti-10Ta-10Nb alloy. According to XRD results, oxide layers were composed of mostly $TiO_2$(rutile) phase. It was analysed that the passive film of the Ti alloys consisted of $TiO_2$ through X-ray photoelectron spectroscopy(XPS) analysis.

• Journal of the Korean Ceramic Society
• /
• v.35 no.2
• /
• pp.123-128
• /
• 1998

Multilayer ceramic capacitors(MLCC) were prepared by laminating the layer of composition with dif-ferent Curie temperature to improve temperature coefficient in the Pb(Mg1/3Nb2/3)O3-PbTiO3 binary system. Green sheet was formed by tape casting using Pb(Mg1/3Nb2/3)O3-PbTiO3 and PbTiO3 synthesized with solid state reaction of PBO. Nb2O5 MgO and TiO2. Green sheet with electrode of 70Ag-30Pd was laminated under 300 kg/cm2 at 70$^{\circ}C$ and sintered at 1100$^{\circ}C$ for 2hr. Curie temperatues for MLCC with 10 layers of pure PMN and 0.9PMN-0.1PT were lowered to -22$^{\circ}C$ and 36$^{\circ}C$ respectively. MLCC with 7 layers of PMN and 3 layers of 0.9PMN-0.1PT showed nearly zero temperature coefficient of capacitance in the range of -20∼30$^{\circ}C$ and sum of dissipation factor of each layer.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.995-1001
• /
• 1998

As a basic study for cathode materials of {{{{ { {LiMn }_{2 }O }_{4 } }}-based lithium-ion secondary batteries Li({{{{ { { { {Mn }_{1-$\delta$ }Nb }_{$\delta$} )}_{2 }O }_{4 } }} ($\delta$=0.05, 0.1, 0.2) materials which Nb is substituted for Mn were synthesized by the solid state reaction at 80$0^{\circ}C$ and 110$0^{\circ}C$ respectively. The second phase {{{{ { LiNbO}_{3 } }} appeared above $\delta$=0.1 As the result of im-pedance analysis as the amount of substituted Nb increased the resistivity of grain boundary increased greatly. Compared to undoped-{{{{ { {LiMn }_{2 }O }_{4 } }} the electrical conductivity of Li({{{{ { { { {Mn }_{1-$\delta$ }Nb }_{$\delta$} )}_{2 }O }_{4 } }} decreased slightly but is charging capacity and potential plateau increased.