• 한국재료학회지
• /
• 제10권7호
• /
• pp.499-504
• /
• 2000

최근에 고온용 항공기 구조 재료로 Ti, Zr, V, Nb 및 Ta 등의 천이금속을 첨가한 Al 합금계 제조와 특성에 관한 연구가 되어져 왔다. 본 연구에서는 Al-Nb합금에 Zr을 첨가하여 상형성거동을 연구하였다. Al-1.3at.%(Nb+Zr) 합금에서 Nb와 Zr의 원자비를 1:3, 1:1 및 3:1로 하여 기계적합금화하였다. 기계적합금화하는 동안 Al-Nb-Zr의 형태변화와 미세구조를 SEM, XRD 및 TEM으로 관찰하였다. X-선 회절 시험에 의하여 $Nb_2Al$ 과 $Al_3Zr_4$가 생성됨을 확인하였다. $500^{\circ}C$에서 1시간동안의 진공열처리에 의하여 $Al_3Zr$, $Al_3Zr_4$ 등의 금속간화합물을 형성하였다. 30시간동안 기계적 합금화한 분말을 열처리하여 TEM으로 관찰한 결과 100nm 이하의 금속간화합물 입자들을 관찰하였다.

• Current Applied Physics
• /
• 제18권12호
• /
• pp.1523-1527
• /
• 2018

The thermal stability, magnetic and magnetocaloric properties of $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) melts-pun ribbons were studied. The relatively high reduced glass transition temperature ($T_{x1}/T_m$ > 0.60) and low melting point ($T_m$) resulted in excellent glass forming ability (GFA). The Curie temperatures ($T_C$) of melt-spun amorphous ribbons $Gd_{55}Co_{35}M_{10}$ for M = Si, Zr and Nb were 166, 148 and 173 K, respectively. For a magnetic field change of 2 T, the values of maximum magnetic entropy change $(-{\Delta}S_M)^{max}$ for $Gd_{55}Co_{35}Si_{10}$, $Gd_{55}Co_{35}Zr_{10}$ and $Gd_{55}Co_{35}Nb_{10}$ were found to be 2.86, 4.28 and $4.05J\;kg^{-1}K^{-1}$, while the refrigeration capacity (RC) values were 154, 274 and $174J\;kg^{-1}$, respectively. The $RC_{FWHM}$ values of amorphous alloys $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) are comparable to or larger than that of $LaFe_{11.6}Si_{1.4}$ crystalline alloy. Large values of $(-{\Delta}S_M)^{max}$ and RC along with good thermal stability make $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) amorphous alloys be potential materials for magnetic cooling operating in a wide temperature range from 150 to 175 K, e.g., as part of a gas liquefaction process.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2007년도 The 1st International Symposium on Advanced Magnetic Materials
• /
• pp.150.1-150.1
• /
• 2007

• Journal of Magnetics
• /
• 제21권2호
• /
• pp.192-196
• /
• 2016

The Fe-Si-B-Nb-Cu alloys containing Ca and Al were rapidly solidified to thin ribbons by melt-spinning. The ribbons were ball-milled to make powders, and then mixed with 1 wt.% water glass and 1.5 wt.% lubricant. The mixed powders were burn-off, and then compacted to form toroidal-shaped cores, which were heat treated to crystallize the nano-grain structure and to remove residual stress of material. The characteristics of the powder cores were analyzed using a differential scanning calorimetry (DSC) and a B-H meter. The microstructures were observed using transmission electron microscope (TEM). The optimized soft magnetic properties (${\mu}_i$ and $P_{cv}$) of the powder cores were obtained from the Ca and Al containing alloys after annealing at $530^{\circ}C$ for 1 h. The core loss of Fe-Si-B-Nb-Cu-based powder cores was reduced by the addition of Ca element, and the initial permeability increased due to the addition of Al element.

• 한국수소및신에너지학회논문집
• /
• 제18권2호
• /
• pp.182-188
• /
• 2007

[ $Zr_{50}-Ni_{27}-Nb_{18}-Co_5$ ] amorphous alloys ribbon was prepared by a single-roller melt-spinning technique. In order to improve the hydrogen kinetics Pd-coating were carried out on each side of the amorphous ribbon. Pd prevents oxidation of Zr and catalyses the dissociation of molecular hydrogen to atomic hydrogen. In this work, the hydrogen embrittlement and surface properties on Zr-based amorphous alloys were investigated. The Zr-based amorphous alloys were characterized by X-ray diffractometry(XRD) and differential scanning calorimetry(DSC). The morphology of surface and roughness was observed by using scanning electron microscopy(SEM) and atomic force microscopy (AFM). A lattice parameter of both Pd and Zr-based amorphous alloy was increased after hydrogen permeation at 473 K. After hydrogen permeation at 473 K, some cracks were observed on the surface of Pd, which was the cause for the hydrogen embrittlement. The crystallization temperature of Zr-based amorphous alloy was decreased due to the permeated hydrogen.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.942-943
• /
• 2006

To meet the demands for use in extremely abrasive and corrosive environments, a new material was developed. The VeKo25Cr distinguishes itself through specifically selected amounts of carbon and carbide forming elements such as Cr, Mo, V, W and Nb. The alloy is based on a Fe matrix. The strength after heat treatment and the wear and corrosion properties are compared to those of other materials. VeKo25Cr can be combined with easy-to-process materials such that the difficult handling is minimized to those places on the piece most subjected to operational wear.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.788-789
• /
• 2006

Microstructure and soft magnetic properties of bulk amorphous and/or nanocrystalline $Fe_{73.5}Cu_1Nb_3Si_{13.5}B_9$ alloys prepared by consolidation at 5.5GPa were investigated. The relative density of the bulk sample 1 (from amorphous powders) was 98.5% and the grain sizes were about 10.6nm. While the relative density and grain sizes of bulk sample 2 (from nanocrystalline powders) are 98% and 20.1nm, respectively. Particularly, the bulk samples exhibited a good combined magnetic property: for Sample1, $M_s=125emu/g$ and $H_c=1.5Oe;$ for Sample2, $M_s=129emu/g$ and $H_c=3.3Oe$. The success of synthesizing the nanocrystalline Fe-based bulk alloys will be encouraging for the future development of bulk nanocrystalline soft magnetic alloys.

• 대한치과기공학회지
• /
• 제28권2호
• /
• pp.321-329
• /
• 2006

The popularity of Ni-Cr-Mo based metal alloys for metal-ceramic crown have increased recently because of low price, superior yield strength and rigidity. the use of these alloys give them the potential advantage of thinner copping with the required rigidity for long span bridges. The purpose of this study was to assess the microstructures and mechanical properties of Ni-Cr-Mo-(Si,Al,Nb,Zr,Ti.Cu,Mm) based Alloys not containing beryllium(Be) related toxic effects. The abtained results indicated that as-cast these specimen alloys showed compositional and microstructural differences, and mechanical properties values of Ni69Cr20Mo5Si2Al4 alloy among these specimen alloys was found to be superior to those of commercial Ni-Cr based alloy using in market place today.

• 한국자기학회지
• /
• 제25권3호
• /
• pp.67-73
• /
• 2015

본 연구는 철기(Fe based) $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ 나노결정 합금의 분말코어(powder core)의 연자기적 특성 향상을 위한 기초연구로서, 절연 코팅제의 첨가량 및 분말입도에 따른 투자율, 코어손실 및 DC 바이어스 특성을 주로 조사하였다. 우선 합금조성을 PFC 장치를 이용하여 비정질 합금리본을 제조한 후, 열처리, 미분쇄 및 분급하여 얻어진 합금분말에 절연 코팅제(PEI)의 첨가량을 0.5, 1.0, 2.0, 2.5 wt%로 변화시켜 $16ton/cm^2$으로 압축성형 및 결정화 열처리하여 제조한 토로이달 나노결정 분말코어($OD12.7mm{\times}ID7.62mm{\times}H4.75mm$)는 절연 코팅제 함량이 증가할수록 투자율은 감소하였지만, 코어손실 및 DC 바이어스 특성은 향상됨을 확인하였다. 이러한 이유는 합금분말 절연 코팅제 첨가량이 증가할수록 비정질 합금분말 입자가 적어져 분말코어의 성형밀도가 낮아지기 때문으로 추정되었으며, 절연 코팅제의 함량은 1 wt%가 가장 적합한 것으로 판단되었다. 또한 절연 코팅제 함량을 1 wt%로 고정하고, 합금분말의 입도에 따라 제조한 분말코어의 경우, 실효투자율 및 코어손실은 입도가 클수록 우수하였지만, DC 바이어스 특성은 인가자장이 증가함에 따라 더욱 나빠짐을 확인하였다. 그 이유는 합금분말 표면의 코팅층 두께 차이에 의한 절연효과, 잔류기공 혹은 분말코어의 성형밀도 차이 등에 기인하는 것으로 추정되었다.

• 한국주조공학회지
• /
• 제34권2호
• /
• pp.49-53
• /
• 2014

In commercial Zr-Nb-Cu-Ni-Al amorphous alloys, expensive element, Zr, was substituted to Sn which was cheaper one, and then, glass forming ability, compressive strength and hardness of them were estimated. Even though the Sn was added up to 1.5%, resulting phase was not changed to the crystalline form. It was confirmed by X-ray diffraction and thermal analyses. In the X-ray profiles, there were no peaks for crystalline phases and typical halo pattern for amorphous phase was appeared at the diffraction angle of $35^{\circ}{\sim}45^{\circ}$. Thermal analyses also showed that the Sn modified alloys were corresponded to the amorphous standards where ${\delta}T$(= Tx - Tg) and Trg(= Tg/Tm) affecting to the amorphous forming ability were more than 50K and 0.60 respectively. Compressive strengths were 1.77 GPa, 1.63 GPa, 1.65 GPa and 1.77 GPa for 0%Sn, 0.5%Sn, 1.0%Sn and 1.5%Sn respectively. Hardnesses of the Sn modified alloys were decreased from 752 Hv to 702 Hv in 1.0%Sn and recovered to 746 Hv in 1.5%Sn.