• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1855-1857
• /
• 1999

$Mn_{1-x}Fe_{2+x}O_4$, $Mg_{1-x}Fe_{2+x}O_4$ (x=0.0, 0.025, 0.1, 0.2) for negative temperature coefficient (NTC) thermistor were prepared by calcining at $800^{\circ}C$ and sintering from 1100 to $1250^{\circ}C$ with $50^{\circ}C$ intervals. The best linear property was obtained in the Mn-based sample sintered at $1200^{\circ}C$ with x=0.0 composition. Temperature coefficient of resistance, $\alpha$, was -3.0 %/$^{\circ}C$ in the Mg-based sample at $25^{\circ}C$. Thermistor parameter, B, was in the range of 2500 [K] $\sim$7400 [K]. The results show the possibility that Mn-Ni-Co based thermistor could be substituted by the composition used in this study.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.107.2-107
• /
• 2003

• Proceedings of the KIEE Conference
• /
• 1990.07a
• /
• pp.227-230
• /
• 1990

The addition of titanium has come to produce an increase in the conductivity of ${\alpha}-Fe_2O_3$ and has been shown NTC ( negative temperature coefficient ) characteristics. Titanium enters the ${\alpha}-Fe_2O_3$ lattice substitutionally as $Ti^{4+}$,thus producing an $Fe^{2+}$ and maintaining the average charge per cation at three. Thus the $Fe^{2+}$ acts as a donor center with respect to the surrounding $Fe^{3+}$ ions. The sintering temperature, compacting pressure and sintering tire have an effect on the electrical properties. C-V and other properties have been measured on polycrystalline samples of ${\alpha}-Fe_2O_3$ containing small deviations from stoichiometry and small amounts of added Titanium. This measurment was made in the course of an investigation of the NTC mechanism in oxides whose cations have a partially filled d-level. C-V and frequency properties have been applied to the measurement of the trap barrier properties at the grain boundary. The double Schottky barrier at the grain boundary is the major cause of the NTC mechanism in NTC thermistor of ${\alpha}-Fe_2O_3$ containing N-type impurity.

• The Magazine of the IEIE
• /
• v.21 no.8
• /
• pp.19-29
• /
• 1994

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.63-69
• /
• 2013

Negative-temperature coefficient (NTC) thermistors based on nickel manganite spinel ($NiMn_2O_4$) are widely used for many applications, such as sensors and temperature compensators, due to their good thermistor characteristics and stabilities. However, to achieve thermistors with a high NTC B constant, which is an important figure of merit pertaining to the degree of temperature sensitivity, the activation energy should be high such that high resistivity at ambient temperatures results. To obtain a high B constant and low resistivity, Al and Si modified spinel structured $Ni_{0.6}Si_{0.2}Al_{0.6}Mn_{1.6}O_4$ hybrid thick films with the conducting metal oxide of $LaNiO_3$ were fabricated on a glass substrate by aerosol deposition at room temperature (RT). The NTC-$LaNiO_3$ hybrid thick films showed resistivity as low as < $100k{\Omega}\;cm$ at $90^{\circ}C$, which is one or two orders of magnitude lower than that of the monolithic NTC films, while retaining a high B constant of $NiMn_2O_4$ of over 5500 K when 20 wt% $LaNiO_3$ was added without a post-thermal treatment. These phenomena are explained by the percolation threshold mechanism.

• Korean Journal of Materials Research
• /
• v.21 no.5
• /
• pp.277-282
• /
• 2011

Negative temperature coefficient (NTC) materials have been widely studied for industrial applications, such as sensors and temperature compensation devices. NTC thermistor thick films of $Ni_{1+x}Mn_{2-x}O_{4+{\delta}}$ (x = 0.05, 0, -0.05) were fabricated on a glass substrate using the aerosol deposition method at room temperature. Resistance verse temperature (R-T) characteristics of the as-deposited films showed that the B constant ranged from 3900 to 4200 K between $25^{\circ}C$ and $85^{\circ}C$ without heat treatment. When the film was annealed at $600^{\circ}C$ 1h, the resistivity of the film gradually decreased due to crystallization and grain growth. The resistivity and the activation energy of films annealed at $600^{\circ}C$ for 1 h were 5.203, 5.95, and 4.772 $K{\Omega}{\cdot}cm$ and 351, 326, and 299 meV for $Ni_{0.95}Mn_{2.05}O_{4+{\delta}}$, $NiMn_2O_4$, and $Ni_{1.05}Mn_{1.95}O_{4+{\delta}}$, respectively. The annealing process induced insulating $Mn_2O_3$ in the Ni deficient $Ni_{0.95}Mn_{2.05}O_{4+{\delta}}$ composition resulting in large resistivity and activation energy. Meanwhile, excess Ni in $Ni_{1.05}Mn_{1.95}O_{4+{\delta}}$ suppressed the abnormal grain growth and changed $Mn^{3+}$ to $Mn^{4+}$, giving lower resistivity and activation energy.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.391-396
• /
• 2001

In order to estimate thermal cracking in mass concrete and to decide the removal time of the forms outside the concrete structures in wintertime, temperature measurement is indispensible. Until now, the measurement system employs thermocouple type. In this paper, we introduce economical and accurate NTC(Negative Temperature Coefficient) ceramic type measurement system. In principle, NTC ceramic type sensor is very sensitive in the range -20~15$0^{\circ}C$. In this range, the signal change is so large that the sensor needs less amplification than thermocouple. Therefore, not only the sensor itself is inexpensive but also the system is too. In this experiments the temperature of the NTC system are identical to those of thermocouple. In conclusion, inexpensive NTC thermistor system is very adequate to the temperature measurement during concrete curing.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.5
• /
• pp.225-229
• /
• 2015

This study was performed to investigate crystal structure of cubic spinel-type monophase oxide composed of the Mn-Co-Ni ternary system. Starting material was prepared by mixing Mn, Co, Ni oxides then evaporation to dryness. The XRD patterns were analyzed by in-situ XRD as increasing temperature from room temperature to $1400^{\circ}C$ in air atmosphere. The cubic spinel phase was existed in a temperature range from $900^{\circ}C$. However, separation of NiO phase was detected from $1300^{\circ}C$, which was the origin of deterioration in the crytallinity. The surface morphology of the manufactured NTC thermistors were analyzed by FE-SEM for comparison of good and bad samples.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.6
• /
• pp.337-341
• /
• 2016

In this study, $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ (x=0~0.25) specimens were prepared by using a conventional mixed oxide method. All specimens were sintered in air at $1,200^{\circ}C$ for 12 h and cooled at a rate of $2^{\circ}C/min$ to $800^{\circ}C$, subsequently quenching to room temperature. We investigated the structural and electrical properties of $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ specimens with variation of CuO amount for the application of NTC thermistors. As results of X-ray diffraction patterns, all specimens showed the formation of a complete solid solution with cubic spinel phase. The relationship between ln ${\rho}$ and the reciprocal of absolute temperature(1/T) for the NTC thermistors was shown linearity, which exhibited the typical NTC thermistor properties. With increasing the amount of CuO, resistivity at room temperature, B-value, and temperature coefficient resistance decreased.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.168-171
• /
• 2000

VO$_2$ceramics exhibiting a negative temperature coefficient (NTC) of resistivity have been widely used as temperature dependence resistors. The NTC effect similar to $VO_2$ceramics was observed when a low-thermal-expansion ceramic matrix was loaded near the percolation threshold with conductive metal particles. The resistivity in a composite made from silica glass and 20 vol% Ag filler suddenly decreased from $10^{-7}$ to $10^3\;\Omega$cm at about $300^{\circ}C$.