• 한국세라믹학회지
• /
• 제32권3호
• /
• pp.313-320
• /
• 1995

We investigated the preferred orientation, electrical and magnetic properties of the Mn-Zn ferrite thin films deposited on SiO2/Si(100) by ion beam sputtering. The Cu-added Mn-Zn ferrite thin films had a preferred orientation of (111) with a weak orientation, (311). While the Zn-added one had a strong (111) preferred orientation. The saturation magnetization of the Cu- or Zn-doped Mn-Zn ferrite films increased with increasing substrate temperature (Ts) due to the increase of grain size and the enhancement of crystallinity. For the same reason the coercivity of Cu- or Zn-doped Mn-Zn ferrite films deposited at low Ts increased with increasing Ts, but those of the films deposited at high Ts slightly decreased not only because the defect density of the films decreases but because more grains have multi-domains with increasing Ts. The resistivity of Cu- or Zn-added Mn-Zn ferrite thin fims measured by complex impedance method decreased with increasing Ts due to the ehhancement of crystallinity as well as due to the increase of grain size.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2006년도 춘계종합학술대회
• /
• pp.898-901
• /
• 2006

본 논문에서는 저손실 Mn-Zn 페라이트의 제조공정과 첨가제가 코어의 자기적 특성에 미치는 영향을 조사하였다. 통신부품재료로 Mn-Zn 페라이트 개발에는 필요한 높은 포화자속밀도 및 투자율을 가진 고주파 특성이 양호하고 자기손실도 적은 재료의 필요하다. 따라서, Mn-Zn 페라이트의 고주파 자기 특성의 개선을 위해서는 결정입자의 소경화와 입자계층의 고저항화에 따른 와전류 손실의 억제 및 미세 구조의 균일화에 따른 히스테리시스 손실의 저감이 중요하다. 본 논문에서는 고성능, 저손실의 자심재료를 위해 Mn-Zn Ferrite에 $V_2O_5$와 $CaCo_3$를 첨가하였다. 조성은 MnO : ZnO : $Fe_2O_3$ = 21 : 10 : 69 mol%로 하였다. 이 시료를 $1250^{\circ}C$에서 3시간 소결하였다. 측정은 0.1MHz에서 초투자율을 측정하였으며, 전력손실은 50mT에서 100kHz 및 온도를 변화시켜 측정하였다.

• 한국전기전자재료학회논문지
• /
• 제19권9호
• /
• pp.883-887
• /
• 2006

In order to attain high-rate deposition of Mn-Zn ferrite thin film for soft magnetic underlayer in perpendicular magnetic recording media, a reactive sputtering using powder-metal targets under the mixture gas of Ar and $O_{2}$ was performed. It was succeeded that Mn-Zn ferrite films with (111) crystal orientation were deposited on Pt(111) underlayer without any annealing process. The film revealed 3.4 kG of 4 ${\pi}Ms$, 70 Oe of coercivity. The deposition rate of the new method was 16 times as high as that of the conventional method using ferrite target.

• 자원리싸이클링
• /
• 제9권6호
• /
• pp.31-35
• /
• 2000

Mn-Zn ferrite 폐기물을 시멘트와 혼합한 복합전파흡수체를 제작하여 재료정수 및 반사감쇠량을 조사하였다. 지지재로 사용한 시멘트는 실리콘 고무의 재료정수와 비교하여 높은 복소유전율($\varepsilon$=$_{r}$': 7.6, $\varepsilon_{r}$ ": 0.6)을 나타내었고, Mn-Zn ferrite 폐기물과 시멘트의 혼합무게비(F/C)가 증가함에 따라 복소유전율은 감소하였고, 복소투자율은 증가하였다. 최대반사감쇠량을 나타내는 주파수는 F/C가 1에서 3으로 증가함에 따라 2.7 GHz에서1.3 GHz로 감소하였고, 정합두께는 8.7 mm에서 12.7 mm로 증가하는 경향이 나타났다. 모든 시편에서 최대반사감쇠량은 -40 dB 이상으로 Mn-Zn ferrite 폐기물을 전파흡수체로 활용이 가능하다.

• 한국세라믹학회지
• /
• 제38권6호
• /
• pp.506-508
• /
• 2001

The ferrite plating with applying power ultrasound waves of 19.5 kHz and 600W enabled us to encapsulate entirely MnZn ferrite cores for transformers with Ni$\sub$x/Zn$\sub$y/Fe$\sub$3-x-y/O$_4$coating. Supplying a NH$_4$OH solution during the plating broke the limit of the solubility of Ni ions to ferrite-plated films. The electrical resistivity of the NiZn ferrite coating increased with increasing the Ni and Zn content, reaching 2.3${\times}$10$\^$5/Ωcm at the composition of Ni$\sub$0.24/Zn$\sub$0.30/Fe$\sub$2.46/O$_4$. The saturation magnetization was 540 emu/㎤. As a result, the MnZn ferrite cores were successfully encapsulated with the NiZn ferrite coatings for an insulation layer.

• Journal of electromagnetic engineering and science
• /
• 제5권4호
• /
• pp.161-165
• /
• 2005

We prepared Mn-Zn ferrite Electromagnetic(EM) wave absorbers. The Mn-Zn ferrite EM wave absorbers were coated with Sr ferrite powders and $Al(OH)_3$ powders. The coated Mn-Zn ferrite EM wave absorbers show improved absorption compared with non-coated Mn-Zn EM wave absorbers.

• 한국세라믹학회지
• /
• 제36권11호
• /
• pp.1143-1149
• /
• 1999

• 한국세라믹학회지
• /
• 제36권11호
• /
• pp.1150-1155
• /
• 1999

• 한국전자파학회논문지
• /
• 제19권2호
• /
• pp.244-249
• /
• 2008

본 논문에서는 Sendust와 Mn-Zn ferrite를 이용하여 2.4 GHz ISM 대역 PCB 노이즈 제거용 전파흡수체를 설계 및 제작하였다. Sendust와 Mn-Zn ferrite를 바인더인 CPE와 혼합하여 조성비별 전파흡수체 샘플을 제작하였고, 이를 분석한 결과 최적의 조성비가 Sendust : Mn-Zn ferrite : CPE=70:5:20 wt.%임을 확인하였다. 전파흡수체 샘플로부터 계산되어진 재료 정수를 이용하여 두께에 따른 흡수능의 변화를 시뮬레이션 하였으며, 시뮬레이션 결과를 토대로 전파흡수체를 실제작하여 전파 흡수능을 비교, 분석하였다. 그 결과, 시뮬레이션 결과와 실측정 결과는 잘 일치하였으며, 중심 주파수 2.4 GHz에서 흡수능 5.4 dB, 1.4$\sim$4.1 GHz 대역에서 3 dB 이상의 흡수능을 보였으며, 이때 두께는 0.85 mm이었다.

• 한국결정성장학회지
• /
• 제33권6호
• /
• pp.294-302
• /
• 2023

Ni-Mn-Zn ferrite, Ni_0.5-xMn_xZn_0.5Fe₂O₄(0 ≤ x ≤ 0.5)를 sol-gel 법으로 합성하여 Mn 치환량 x에 따른 결정 구조와 미세구조, 자기적 특성, 고주파 특성, 그리고 전자기파 흡수 특성을 연구하였다. Mn의 함량이 증가함에 따라 보자력 (H_C)에 큰 변화 없이 포화자화값(M_S)이 연속적으로 감소하는 것을 확인하였다. Ni-Mn-Zn ferrite-epoxy(10 wt%) 복합체에 대하여 0.1~18 GHz 주파수 범위에서 고주파 복소 유전율(ε', ε'') 및 복소 투자율(µ', µ'') spectra를 측정하고 전송선 이론을 통하여 전자기파 흡수 특성을 평가하였다. 각 시료는 1.5~2.5 GHz 및 6~11 GHz 범위에서 최소 반사손실 RL_min < -40 dB를 만족하는 1, 2차 강한 전자기파 흡수 영역이 존재하였고, Mn이 치환됨에 따라 RL_min 주파수는 저주파 방향으로 이동하였다. 또한 Ni-Zn ferrite(x = 0) 시료에 대하여 자기장(H)을 100 Oe에서 최대 400 Oe까지 단계적으로 인가한 상태로 ε', ε'', µ', µ'' spectra를 얻고 전자기파 흡수 특성을 평가하였다. 인가자장의 증가에 따라 시료의 강자성 공명 주파수가 증가하기 때문에 µ', µ'' spectra도 고주파 방향으로 단계적으로 이동해갔으며 최대 전자기파 흡수 주파수도 이에 대응하여 이동하였다. 이는 Ni-Mn-Zn ferrite에서 전자기파의 흡수는 자기적 손실에 의존하기 때문이며 Mn의 치환이나 인가자장에 의해 µ', µ'' spectra를 조절하면 전자기파 흡수 주파수도 조절할 수 있음을 보여준다. Ni-Zn ferrite-epoxy는 2.8~11.6 GHz에서 RL < -10 dB를 만족하는 광대역 전자기파 흡수 특성을 보였다.