• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.839-840
• /
• 2006

Sintering behavior of the Fe-0.8Mn-0.5C powder system was studied on the specimens with a density of ${\sim}7.0g/cc$ sintered at $1120^{\circ}C$ for 30 min in a gas mixture of $7%H_2/93%N_2$ with the inlet dew point of $-60^{\circ}C$. During the atmosphere monitoring ($CO/CO_2$-content and dew point) was showed, that carbothermical reduction occurs in two different temperature ranges; three peaks of dew point profile also can be distinguished during sintering cycle as well. Following sintering the Mn-content distribution and microstructures around the Mn-source were micro-analytical evaluated; the results showed that manganese travels through porous iron matrix up to ${\sim}60{\mu}m$.

• 한국수소및신에너지학회논문집
• /
• 제18권3호
• /
• pp.250-255
• /
• 2007

Hydrogen storage properties of $Ti_{0.32}Cr_{0.43-X}V_{0.25}M_X$($0{\leq}X{\leq}0.1$, M=Fe, Mn, Si) have been investigated. With varing of Mn content, the lattice parameter of the alloy was unchanged and similar to that of $Ti_{0.32}Cr_{0.43}V_{0.25}$ alloy. With increase of Fe, Si content, the lattice parameters of the BCC phases decreased. When the Fe content was 8 at%, the desorption plateau pressure increased to several atmospheres without decrease of the effective hydrogen storage capacity of the alloy. When the Mn content was 8 at%, the effective hydrogen storage capacity showed approximately 2.5 wt% without change in the desorption plateau pressure. With increase of Si content, hysteresis increased and hydrogen storage capacity decreased rapidly. A study was also made on how desorption temperature affected the usable hydrogen of the $Ti_{0.32}Cr_{0.35}V_{0.25}Mn_{0.08}$ alloy. The temperature was varied from 293 to 413 K, and the pressure from 5 to 0.002 MPa. The usable hydrogen of the alloy was 2.7 wt% when absorbed and desorbed at 293 K and 373 K., respectively. The heat of hydride formation of the alloy was approximately -35.5 kJ/mol $H_2$.

• 한국환경보건학회지
• /
• 제12권1호
• /
• pp.69-78
• /
• 1986

In order to determine the content levels of trace metals in cow's milk, 79 market milk samples were collected from markets in major cities of Korea from July to August, 1985 and analyzed for content levels of Cu, Fe, Zn, Mn, Pb, Cd. The Results were as follows Cu, average 43.5 $\mu$g/l range 14 ~ 172.7 $\mu$g/l Fe, average 398.4 $\mu$g/l range 35 ~ 1,873 $\mu$g/l Zn, average 2.917 mg/l range 1.233 ~ 7.46 mg/l Mn, average 26.74 $\mu$g/l range 7.6 ~ 102 $\mu$g/l Pb, average 33.9 $\mu$g/l range N.D. ~ 105 $\mu$g/l Cd, average 1.73 $\mu$g/l range N.D. ~ 5.4 $\mu$g/l

• Current Research on Agriculture and Life Sciences
• /
• 제11권
• /
• pp.111-120
• /
• 1993

폐광산(廢鑛山) 주변(周邊)의 토양(土壤) 및 식물체(植物體)에 존재(存在)하는 중금속(重金屬)과 그들의 토양(土壤)에서의 존재형태(存在形態)에 따른 분포(分布)를 조사(調査)하였다. 토양(土壤) 중(中) 중금속(重金屬) 함량(含量)은 Mn을 제외(除外)하고 A토양(土壤)에서 제일 많았고, Mn은 B토양(土壤)에서 함량(含量)이 제일 높았다. 존재형태(存在形態)에 따른 각 중금속(重金屬)의 함량(含量)은 각 원소별(元素別)로 차이가 있었는데, 즉 Cd와 As는 유기태(有機態), Cu와 Pb 및 Mn은 Carbonate태(態), Fe와 Zn은 잔사태(殘渣態)가 다른 형태(形態)보다 더 높게 나타났다. 참억새와 골풀은 각각 75%와 15% 정도(程度)로 서식(棲息)하고 있었으며, 이는 이들 식물(植物)들이 중금속(重金屬)에 대해 내성(耐性)을 가지고 있음을 보여주었다. 참억새와 골풀에 분포(分布)되어 있는 중금속(重金屬)은 Mn을 제외하고 줄기보다는 뿌리에 더 많이 함유(含有)되어 있었다. 참억새의 경우 Zn은 줄기와 뿌리에 비슷하게 분포(分布)하는 것으로 나타났다. 주변(周邊) 용수(用水)의 분석(分析) 결과(結果) 침출수(浸出水)에서 중금속(重金屬) 함량(含量)이 높게 나타났으며, Fe와 Mn 및 Zn이 많이 검출(檢出)되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.959-962
• /
• 2001

In this study, the piezoelectric and dielectric properties and Temperature stability of resonant frequency with MnO$_2$doped 0.36Pb(Sc$_{1}$2/Nb$_{1}$2/)O$_3$- 0.25Pb(Ni$_{1}$3/Nb$_{2}$3/)O$_3$-0.39PbTiO$_3$(hereafter PSNNT) were investigated. The tetagonality of crystal structure was developed with increasing MnO$_2$additive content. With increasing MnO$_2$additive content, the electromechanical coupling factor and quality factor were increased. Electromechanical coupling k$_{p}$ and quality factor Q$_{m}$ at MnO$_2$doped with 2.0mol% were showed highest value of 55.6% and 252. In the case of specimen for MnO$_2$doped with 2mol%, temperature dependance of resonant frequency had a good properties.ies.

• 한국주조공학회지
• /
• 제31권1호
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• 한국주조공학회지
• /
• 제9권1호
• /
• pp.80-88
• /
• 1989

SGCI(Spheroidal Graphite Cast Iron), CVGCI(CV Graphite Cast Iron) and FGCI(Flake Graphite Cast Iron) having different contents of Mn($0.25%{\sim}0.85%$) and Ni($0.3%{\sim}1.2%$) were produced, respectively. The thermal expansion and thermal conductivity of the cast iron were investigated in the temperature range of $50^{\circ}C{\sim}300^{\circ}C$. As the graphite nodularity of the cast iron increases, thermal expansion coefficient increases, thermal conductivity and electrical conductivity to thermal conductivity ratio decrease. The thermal expansion coefficient of the cast iron increases with increasing Mn content and decreases with increasing Ni content. The thermal conductivity of the cast iron decreases with increasing Mn and Ni contents.

• 한국분말재료학회지
• /
• 제25권4호
• /
• pp.302-308
• /
• 2018

A lean alloy is defined as a low alloy steel that minimizes the content of the alloying elements, while maintaining the characteristics of the sintered alloy. The purpose of this study is to determine the change in microstructure and mechanical properties due to the addition of silicon or tin in Fe-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P alloys. Silicon- or tin-added F-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P master alloys were compacted at 700 MPa and subsequently sintered under a $H_2-N_2$ atmosphere at $1120^{\circ}C$. The sintered density of three alloy systems decreases under the same compacting pressure due to dimensional expansion with increasing Si content. As the diffusion rate in the Fe-P-Mo system is higher than that in the Fe-P-Mn system, the decrease in the sintered density is the largest in the Fe-P-Mn system. The sintered density of Sn added alloys does not change with the increasing Sn content due to the effect of non-dimensional changes. However, the effect of Si addition on the transverse rupture strengthening enhancement is stronger than that of Sn addition in these lean alloys.

• 동력기계공학회지
• /
• 제11권1호
• /
• pp.115-120
• /
• 2007

The effect of grain size on the damping capacity of Fe-26Mn-2Al alloy studied in this paper has been investigated after changing the microstructure by cold rolling and changing grain size. Micro structures in Fe-26Mn-2Al at room temperature consist of a large quantity of austenite and a small quantity of ${\varepsilon}\;and\;{\alpha}'$ martensite. And ${\varepsilon}\;and\;{\alpha}'$ martensite was increased by increasing the degree of cold rolling. The content of deformation induced martensite was increased with increasing the degree of cold rolling. Damping capacity was linearly increased with increasing ${\varepsilon}$ martensite content, which suggests that stacking faults and ${\varepsilon}$ martensite variant boundaries are the principle damping sources. With increasing the grain size in Fe-26Mn-2Al alloy, the damping capacity was increased due to increasing the volume fraction of ${\varepsilon}$ martensite by decrement in stability of austenite phase. With decreasing the grain size, the content of deformation induced martensite was decreased and the damping capacity was decreased.

• 한국식품영양과학회지
• /
• 제22권5호
• /
• pp.592-595
• /
• 1993

인삼의 재배년근별, 국내산지별 및 국가별 무기물의 분포를 조사하기 위하여 시험한 결과 Mn은 2년근에 비하여 5년근에서 4배 가까운 증가추세를 나타내었다. 재배산지별로 볼때 P은 각 지역별로 큰 차이를 나타내지 않았다. 한편 각국 인삼별로는 중국 천칠삼에서 N의 함량이 적제 나타났으며 P은 한국산 정상홍삼에서 가장 높게 나타났다.