• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.807-811
• /
• 2000

CeO$_2$ and SrBi$_2$Ta$_2$O$_{9}$ (SBT) thin films for MFISFET (Metal-ferroelectric-insulator-semiconductor-field effect transistor) were deposited by r.f. sputtering and pulsed laser ablation method, respectively. The effects of sputtering gas ratio(Ar:O$_2$) during deposition for CeO$_2$ films were investigated. The CeO$_2$ thin films deposited on Si(100) substrate at $600^{\circ}C$ exhibited (200) preferred orientation. The preferred orientation, Brain size and surface roughness of films decreased with increasing oxygen to argon gas ratio. The films deposited under the condition of Ar:O$_2$= 1 : 1 showed the best C- V characteristics. The leakage current of films showed the order of 10$^{-7}$ ~10$^{-8}$ A at 100kV/cm. The SBT thin films on CeO$_2$/Si substrate showed dense microstructure of polycrystalline phase. From the C-V characteristics of MFIS structure with SBT film annealed at 80$0^{\circ}C$, the memory window width was 0.9V at 5V The leakage current density of Pt/SBT/CeO$_2$/Si structure annealed at 80$0^{\circ}C$ was 4$\times$10$^{-7}$ /$\textrm{cm}^2$ at 5V.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.569-574
• /
• 2012

Large single grain $Gd_{1.5}Ba_2Cu_3O_{7-y}$ (Gd1.5) bulk superconductors were fabricated by a top-seeded melt growth (TSMG) process using an $NdBa_2Cu_3O_{7-y}$ seed. The seeded Gd1.5 powder compacts with a diameter of 50 mm were subjected to the heating cycles of a TSMG process. After the TSMG process, the diameter of the single grain Gd1.5 compact was reduced to 43 mm owing to the volume contraction during the heat treatment. The superconducting transition temperature ($T_c$) of the top surface of the single grain Gd1.5 sample was as high as 93.5 K. The critical current densities ($J_cs$) at 77 K and 1T and 1.5 T were in ranges of 25,200-43,900 $A/cm^2$ and 10,000-23,000 $A/cm^2$, respectively. The maximum attractive force at 77 K of the sample field-cooled using an Nd-B-Fe permanent magnet (surface magnetic field of 0. 527 T) was 108.3 N; the maximum repulsive force of the zero field-cooled sample was 262 N. The magnetic flux density of the sample field-cooled at 77 K was 0.311T, which is approximately 85% of the applied magnetic field of 0.375 T. Microstructure investigation showed that many $Gd_2BaCuO_5$ (Gd211) particles of a few ${\mu}m$ in size, which are flux pinning sites of Gd123, were trapped within the $GdBa_2Cu_3O_{7-y}$ (Gd123) grain; unreacted $Ba_3Cu_5O_8$ liquid and Gd211 particles were present near the edge regions of the single grain Gd1.5 bulk compact.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1129-1136
• /
• 1999

TIN films were prepared on Si(100) substrate by ICP-CVD(inductive1y coupled plasma enhanced chemical vapor deposition) using TEMAT(tetrakis ethylmethamido titanium : Ti$[\textrm{N}\textrm{(CH)}_{3}\textrm{C}_{2}\textrm{H}_{5}]_{4}$) precursor at various deposition conditions. Phase, microstructure, and the electrical properties of TIN films were characterized by x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), high resolution transmission electron microscopy (HRTEM) and electrical measurements. Polycrystalline TiN films with B1 structure were grown at temperatures over $200^{\circ}C$. Preferentially oriented along TiN(111) films were obtained at temperatures over $300^{\circ}C$ with the flow rates of 10, 5, and 5 sccm for TEMAT, $\textrm{N}_{2}$ and Ar gas. The TiN/Si(100) interface was flat and no chemical reaction between TIN and $\textrm{SiO}_2$ was found. The resistivity, carrier concentration and the carrier mobility for the TiN sample prepared at $500^{\circ}C$ are 21 $\mu\Omega$cm, 9.5$\times\textrm{10}^{18}\textrm{cm}^{-3}$ and $462.6\textrm{cm}^{2}$/Vs, respectively.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.493-498
• /
• 1998

CdTe films were deposited by close spaced sublimation with various substrate temperatures, cell areas, and thicknesses of CdTe and ITO layers and their effects on the CdS/CdTe solar cells were investigated. The resistivity of CdTe layers employed in this study was 3$\times$ $10^{4}$$\Omega$cm For constant substrate temperature the optimum substrate ternperature for CdTe deposition was $600^{\circ}C$. To obtain larger grain size and more compact microstructure, CdTe film was initially deposited at 62$0^{\circ}C$, and then deposited at 54$0^{\circ}C$. The CdTe film was annealed at 62$0^{\circ}C$ and $600^{\circ}C$ sequentially to maintain the CdTe film quality. The photovoitaic cell efficiency improved by the "two-wave" process. For constant substrate temperature, the optimum thickness for CdTe was 5-6$\mu m$. Above 6$\mu m$ CdTe thickness, the bulk resistance of CdTe film degraded the cell performance. As the cell area increased the $V_{oc}$ remained almost constant, while $J_{sc}$ and FF strongly decreased because of the increase of lateral resistance of the ITO layer. The optimum thickness of the ITa layer in this study was 300~450nm. In this experiment we obtained the efficiency of 9.4% in the O.5cm' cells. The series resistance of the cell should be further reduced to increase the fill factor and improve the efficiency.

• Journal of Conservation Science
• /
• v.27 no.1
• /
• pp.1-11
• /
• 2011

For the silver artifacts in the Koryo Dynasty excavated from Neungnae-ri Ganghwa island, the metallographic section analysis and hardness and chemical analysis were conducted. After making samples in the similar ratio of the composition concentration, the changes of the microstructure were checked according to the working method and temperature. The results show that those silver artifacts are Au-Cu alloys with 2 to 6 % of Cu. From the results it is judged that Cu was artificially alloyed with them to keep the proper hardness and identified that they were gilded by the amalgamation process seeing that mercury was included at the guilt layer. Also the porous texture on the surface of them could be formed at over $400^{\circ}C$, therefore, it is assumed the hot working or heat treatment at over $400^{\circ}C$ were performed. In silver artifacts made by the relief and repousse, they have the similar composition analysis to other 7 artifacts but the hardness is lower than pure silver. Consequently from differences in the hardness, it can be inferred that the low hardness of silver artifacts is concerned with manufacturing techniques.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.6
• /
• pp.254-257
• /
• 2007

TiN coating on tool steel has been widely used for the improvement of durability of tools. In this work, radical nitriding(RN) is carried out on SKD61 at $450^{\circ}C$ for 5 hours in the ammonia gas pressure $2.7{\times}10^3\;Pa$. The TiN coating is carried out by arc ion plating(AIP) with the process parameters: arc power 150 A, bias voltage -50V, coating time 40 minutes and nitrogen gas pressure $4{\times}10^3\;Pa$. Hardness, elastic modulus, friction coefficient and adhesion of TiN coating on substrates of both TiN/SKD61 and TiN/RN SKD61 coatings are investigated comparatively. The primary crystalline faces of TiN surface are(200) and(111) for TiN/SKD61 and TiN/RN SKD61 respectively. In addition to the primary phase, Fe phase exists in TiN/SKD61 coating, but not in TIN/RN SKD61. The hardness of TiN/RN SKD61 is about 700 Hv, 250 Hv(56%) higher than that of TiN/SKD61 at the near interface of TiN and substrates. At the TiN surface, hardness of TiN/RN SKD61 is 2,149 Hv, 71 Hv(3%) higher than that of TiN/SKD61. The elastic modulus of TiN coating is improved to 26.7 GPa(6%) by radical nitriding. The adhesion is improved by the RN coating showing no spalling. buckling and chipping on the scratch test track which are shown on the non-RN TiN/SKD61.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.1
• /
• pp.53-57
• /
• 2010

The influence of CaO addition on the crystallization temperature, crystal types, and microstructure of L-A-S ($Li_2O-Al_2O_3-SiO_2$) glass-ceramics system fabricated from a coal bottom ash, produced at thermal power plant, was studied. The glass transition and crystallization temperatures were shifted to the higher temperature position with increasing CaO content in a non-isothermal analysis using a DTA. The major crystalline phases of L-A-S glass-ceramics system produced were identified as ${\beta}$-spodumene ($LiAlSi_2O_6$) and eucryptite ($LiAlSiO_4$). The glass-ceramics showed a bulk and surface crystallization behavior at a time. With increasing CaO content, the ${\beta}$-spodumene peak in XRD increased and some CaO-related phases were formed. The surface crystal grown from the exterior to the center in glass-ceramics showed various shapes by amount of CaO added. Some cracks were generated at the glass-ceramics containing CaO above 9 wt% due to the mismatch of thermal expansion coefficients between a ${\beta}$-spodumene and CaO-related crystal phases.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.1
• /
• pp.15-20
• /
• 2014

In this research, the geopolymer was fabricated using municipal solid waste incineration ash (denoted as MSWIA) slag and alkali activator, NaOH and its properties were analyzed. Particularly, the effects of NaOH molarity, particle size of MSWIA, and liquid/solids ratio on the compressive strength of geopolymers were investigated. The compressive strength of geopolymers fabricated increased with finer grain size of MSWIA, and optimum value of the liquid/solids ratio was identified as 0.13. As the molarity of the NaOH increased, the compressive strength of geopolymers was increased. Even more the 20 M of NaOH, but the strength was not increased. The calcium aluminum silicate and calcium aluminum silicate hydrate zeolites were generated in the geopolymer fabricated with more than 20 M of NaOH, with some unreacted silica and unknown crystals remained. The highest compressive strength, 163 MPa, of geopolymer was appeared at conditions of curing temperature $70^{\circ}C$, and 20 M of NaOH, indicating that the high concentration of NaOH accelerates the geopolymer reaction and dense microstructure. The high-strength geopolymer fabricated in the present study is expected to contribute significantly to develop the field of cement alternative substances and to improve the recycling rate of MSWIA slag.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.449-456
• /
• 2002

Recently, the application of high strength and high performance concrete has been gradually increased as an important construction material for high rise and huge scaled construction. However, high performance concrete has undesirable characteristics of spalling subjected to high temperature due to its dense microstructure content. A spalling by fire brings surface failure and falling off concrete member. It is considered that spalling by fire should be taken into account for the safety of the concrete structure under fire. Therefore, in this paper, tests are carried out using high performance concrete containing polypropylene(PP) fiber in order to improve the fire resistance performance. PP fiber contents and member sizes are varied. According to experimental results, as for the influence of PP fiber contents, all the test specimens without PP fiber show entire failure in W/C of 35％, while they show nearly sound shape except some kinds of surface fracture in W/C of 55％. When PP fiber is contained more than 0.07％, favorable prevention effects of spatting by fire are obtained. As for the effects of test specimens size, it tends to increase the possibilities of spatting by fire as test specimens become larger. And spatting by fire at the edge of test specimens occurs more frequently than at the surface of test specimens. Residual compressive and tensile strength shows 45∼65 ％ of its original strength at W/C of 35％, and 30∼40％ at W/C of 55 ％.

• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.265-272
• /
• 2011

Even though concrete is the most important material for building structures, its intrinsic gray color degrades urban esthetics. In order to improve this problem, coloring methods of mixing pigment in concrete batch and painting the surface of concrete surface have been tried. However, applications of the coloring methods in construction field are difficult due to high cost and low durability. Recently, acid stain agent is emerging as a new coloring method for concrete. It is able to apply a remarkably thin colored layer on a concrete surface from chemical reaction between acid and alkaline solutions. This study has examined the changes and variations of the surface layer of mortar specimen from chemical reaction of acid stained agents. The colors were changed into natural irregular stains according to aging. After the staining, no shape change was found from visible inspections. Microstructure of the colored surface applied with acid stained agent was much rougher than that of original mortar. When the colored layer was compared to original surface, crystals of hydrate such as $Ca(OH)_2$ and C-S-H gel were observed. Surface hardness was same or slightly higher in the colored layer. The value of pH was reduced by approximately 10%, weight contents of elements such as Ca, Si, and Al were low. In the chemical composition of the colored layer, the non-cement based elements of Mn, Cr, and Cu increased. Also, Fe and alkali elements of K and Na increased.