• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.41 no.3
• /
• pp.229-235
• /
• 2015

Skin aging is the phenomena finally expressed on the skin surface and related to the changes in the microstructure of the skin texture. Which is resulted in wrinkle formation and uneven tone of skin and so on. In this study, the synergy effect of Cedrol and a collagen-derived peptide in type III collagen synthesis was evaluated by in vitro test. The physiological skin state of 22 female volunteers was measured after using the cosmetics for 4 weeks. Results showed that Cedrol and a collagen-derived peptide had the excellent synergy effect in type III collagen synthesis. The cosmetics improved skin microrelief, star configurations, skin gloss, skin tone, hydration and elasticity except skin lightening. In conclusion, this study proved that Cedrol and collagen-derived peptide had the synergy effect of type III collagen synthesis in the cell level and cosmetics with those was improved skin aging in human volunteer test.

• Journal of the Korean Chemical Society
• /
• v.41 no.11
• /
• pp.594-599
• /
• 1997

Lithium nickel oxide ($Li_{2x}Ni_{1-x}O$) thin films have been prepared by the RF sputtering of lithiated nickel oxide target, where the film microstructure was controlled by the sputtering atmosphere $(Ar/O_2)$ and the substrate temperature ($T_s=50/230^{\circ}C$). From the transmission electron microscopic analysis, it is found that the most porous film with the grain size of $∼80\AA$ could be fabricated under the sputtering atmosphere of $P(O_2)=8{\times}10^2$ mbar with the $$T_s$=50^{\circ}C.$ In the optical and electrochemical studies, the$Li_{2x}Ni_{1-x}O$ films exhibit a significant electrochromic property in association with the lithium insertion/deinsertion process. The amount of charge insertion ($Q_i$) and the optical density (OD) variation depend on the crystallinity of the film as well as its thickness, and for the $Li_{2x}Ni_{1-x}O$ film (170 nm thickness) prepared under $O_2$ atmosphere and $T_s=50^{\circ}C$, the OD could be increased up to ∼1.3 by the charge insertion with $Q_i=30\;mC/cm^2.$

• Restorative Dentistry and Endodontics
• /
• v.22 no.2
• /
• pp.505-518
• /
• 1997

The objective of this investigation was to compare the effects of water storage on the aspect of hardness and diametral tensile strengths of four hybrid glass ionomer cements(two compomers and two resin-reinforced glass ionomers) with a resin composite material. One composite resin(Degufill Ultra), two compomers(Dyract, Compoglass Cavifil), and two resin-reinforced glass ionomers(Fuji Duet, Vitremer) were used in this study. Cylindrical specimens were prepared and stored at $36{\pm}1^{\circ}C$ in distilled water for 10 minutes after set, and then tested on an Instron testing machine(No.4467) at 1.0 mm/min displacement rate. Vicker's hardness and diametral tensile strengths as time elapsed were measured after aging in water for 10 minutes, 1 hour, 3 hours, 1 day, 3 days, 5 days and 7 days at $36{\pm}1^{\circ}C$. During the test of diametral tensile strength, stress-strain curves were obtained, from which the compressive modulus were calculated and compared. The structure of four set glass ionomer cement mass was observed on SEM(Hitachi, S-2300) after being etched with 9.6% hydrofluoric acid for 1 minute. The results were as follows; 1. The hardness of the experimental group(compomer and the resin reinforced glass ionomer cement) did not exceed the value of control group(Degufill Ultra). 2. Vicker's hardness of the Fuji Duet tended to increase succeedingly, Dyract was decreased after 3 hours in water, and Vitremer was the lowest. 3. The control group(Degufill Ultra) presented progressively on increased diametral tensile strength with time, Fuji Duet were decreased after 3 days, Compoglass Cavifil and Vitremer were decreased after 5 days in water storage. 4. Compressive modulus of the control group(Degufill Ultra) and Dyract were increased sharply timely, Fuji Duet and Vitremer were increased smoothly by lapse of time in water. Fuji Duet were stronger than Vitremer. On the other hand, Vitremer exhibited the lowest toughness. 5. The microstructure of compomer was similar with that of the composite resin(Degufill Ultra), and the fillers in resin-reinforced glass ionomer cements were noticed. It can be concluded that mechanical properties of hybrid glass ionomer cements is weaker than composite resin, and that the compomers or the resin-reinforced glass ionomers can not substitute the composite resins. A plenty of considerations should be done on the application of them to the area under the loading and high wear has a little adverse effect on the mechanical properties on the water storage for 7 days. The further research should be needed to confirm the advantage of the compomer.

• Food Science and Preservation
• /
• v.21 no.5
• /
• pp.652-660
• /
• 2014

To maintain the microbiological safety of Prunus mume fruit before it is processed, it was treated with a combination of 0.5% citric acid and 0.1% Tween 20, and stored at $4{\pm}1^{\circ}C$ for seven days. The combined treatment reduced total aerobic bacteria, yeast, and mold populations in the fruit by 2.20 and 1.70 log CFU/g, respectively, compared to those in the control. Organic acid contents and the Hunter $L^*$, $a^*$, and $b^*$ values were not affected by the treatment during the storage. In addition, the dried Prunus mume fruit prepared with 40% red algae extract (RAE) or maltodextrin (MD) treatment and hot-air drying were compared with respect to the fruit's physicochemical properties such as color, total phenolic and flavonoid content, and microstructure. The hot-air dried samples had undesirable color changes and inferior textures. The RAE-treated samples had a higher total phenolic content (225.15 mg gallic acid equivalent (GAE)/100 g) and total flavonoid content (49.25 mg quercetin equivalent (QE)/100 g) than the other treatments. The treatment of Prunus mume fruit with RAE can provide better-dried products than can MD treatment or hot-air drying. These results suggest that the combined treatment with citric acid and Tween 20 can be effective in preserving the microbiological safety of Prunus mume fruit, and its dehydration using RAE is an efficient drying method.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.807-811
• /
• 2000

CeO$_2$ and SrBi$_2$Ta$_2$O$_{9}$ (SBT) thin films for MFISFET (Metal-ferroelectric-insulator-semiconductor-field effect transistor) were deposited by r.f. sputtering and pulsed laser ablation method, respectively. The effects of sputtering gas ratio(Ar:O$_2$) during deposition for CeO$_2$ films were investigated. The CeO$_2$ thin films deposited on Si(100) substrate at $600^{\circ}C$ exhibited (200) preferred orientation. The preferred orientation, Brain size and surface roughness of films decreased with increasing oxygen to argon gas ratio. The films deposited under the condition of Ar:O$_2$= 1 : 1 showed the best C- V characteristics. The leakage current of films showed the order of 10$^{-7}$ ~10$^{-8}$ A at 100kV/cm. The SBT thin films on CeO$_2$/Si substrate showed dense microstructure of polycrystalline phase. From the C-V characteristics of MFIS structure with SBT film annealed at 80$0^{\circ}C$, the memory window width was 0.9V at 5V The leakage current density of Pt/SBT/CeO$_2$/Si structure annealed at 80$0^{\circ}C$ was 4$\times$10$^{-7}$ /$\textrm{cm}^2$ at 5V.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.845-852
• /
• 2000

Mesoporous ${\gamma}-Al_2O_3$ has been prepared by selective leaching of silica from calcined domestic kaolinite. From XRD and TG-DTA data, it was found that the microstructure of a spinel phase, consisting of ${\gamma}-Al_2O_3$ containing a small mount of amorphous silica, was obtained by calcining kaolinite samples at around $1000^{\circ}C$ for 24h. Porous ${\gamma}-Al_2O_3$ was prepared by selectively dissolving the amorphous silica in KOH solutions of 1~4M at temperatures of $25~90^{\circ}C$ for leaching time of 0.5~4h. In the case of the ${\gamma}-Al_2O_3$ obtained upon KOH treatment of 4M at $90^{\circ}C$ for 1h, it showed a very narrow unimodal pore size distribution, and also formed much mesopore at a diameter of around $40~80{\AA}$. The specific surface area was $250\textrm{m}^2/g$ and the total pore volume was $0.654\textrm{cm}^3/g$.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.1018-1024
• /
• 1999

The effects of operating temperature and stress on degradation of components in high temperature steam generator were investigated. Several 2.25CrlMo tubes which had operated over 20 years and an unused 9CrlMoVNb tube were tested. For the former samples, the amount of $\textrm{M}_{6}\textrm{C}$ carbide and its size are increased with the aging or operating time. The precipitation behavior of carbides ($\textrm{M}_{2}\textrm{O}$, $\textrm{M}_{6}\textrm{C}$) is changed with the operating temperature of the tubes. However, unused 9CrlMoVNb samples show a different carbide precipitation process due to high chromium, vanadium, and niobium contents. The amount of Cr-rich $\textrm{M}_{23}\textrm{C}_{6}$ carbide is significantly increased with aging time, but that of $\textrm{M}_{6}\textrm{C}$ type carbide is rarely changed with aging time at elevated temperatures.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.569-574
• /
• 2012

Large single grain $Gd_{1.5}Ba_2Cu_3O_{7-y}$ (Gd1.5) bulk superconductors were fabricated by a top-seeded melt growth (TSMG) process using an $NdBa_2Cu_3O_{7-y}$ seed. The seeded Gd1.5 powder compacts with a diameter of 50 mm were subjected to the heating cycles of a TSMG process. After the TSMG process, the diameter of the single grain Gd1.5 compact was reduced to 43 mm owing to the volume contraction during the heat treatment. The superconducting transition temperature ($T_c$) of the top surface of the single grain Gd1.5 sample was as high as 93.5 K. The critical current densities ($J_cs$) at 77 K and 1T and 1.5 T were in ranges of 25,200-43,900 $A/cm^2$ and 10,000-23,000 $A/cm^2$, respectively. The maximum attractive force at 77 K of the sample field-cooled using an Nd-B-Fe permanent magnet (surface magnetic field of 0. 527 T) was 108.3 N; the maximum repulsive force of the zero field-cooled sample was 262 N. The magnetic flux density of the sample field-cooled at 77 K was 0.311T, which is approximately 85% of the applied magnetic field of 0.375 T. Microstructure investigation showed that many $Gd_2BaCuO_5$ (Gd211) particles of a few ${\mu}m$ in size, which are flux pinning sites of Gd123, were trapped within the $GdBa_2Cu_3O_{7-y}$ (Gd123) grain; unreacted $Ba_3Cu_5O_8$ liquid and Gd211 particles were present near the edge regions of the single grain Gd1.5 bulk compact.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.562-567
• /
• 2013

A 90 wt% Mg-10 wt% $NbF_5$ sample was prepared by mechanical milling under $H_2$ (reactive mechanical grinding). Its hydriding and dehydriding properties were then examined. Activation of the 90 wt% Mg-10 wt% $NbF_5$ sample was not required. At n=1, the sample absorbed 3.11 wt% H for 2.5 min, 3.55 wt% H for 5 min, 3.86 wt% H for 10 min, and 4.23 wt% H for 30 min at 593K under 12 bar $H_2$. At n=1, the sample desorbed 0.17 wt% H for 5 min, 0.74 wt% H for 10 min, 2.03 wt% H for 30 min, and 2.81 wt% H for 60 min at 593K under 1.0 bar $H_2$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ after reactive mechanical grinding showed Mg, ${\beta}-MgH_2$ and small amounts of ${\gamma}-MgH_2$, $NbH_2$, $MgF_2$ and $NbF_3$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ dehydrided at n=3 revealed Mg, ${\beta}-MgH_2$, a small amount of MgO and very small amounts of $MgH_2$ and $NbH_2$. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial hydriding rate and a larger quantity of hydrogen absorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$, which were reported to have quite high hydriding rates and/or dehydriding rates. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial dehydriding rate (after an incubation period) and a larger quantity of hydrogen desorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.210-219
• /
• 2000

The magnetoresistance characteristics of FeN/Co/Cu/Co and FeN/Co/Cu/Co/Cu/Co/FeN multilayers using ferromagnetic iron-nitrides (FeN) has been studied. The microstructure of FeN film is the mixed ${\alpha}$-Fe and $\varepsilon$-Fe$_3$N phase on the condition that the flow rate of N$_2$ gas is over 0.4 sccm. The magnetoresistance effect is observed because of shape magnetic anisotropy induced by needle-shaped $\varepsilon$-Fe$_3$N phase. This magnetoresistance effect changes, because the degree that the shape magnetic anisotropy adheres to the adjacent Co pinned layer is varied according to the flow rate of N$_2$ gas and the thickness of FeN film. The best magnetoresistance effect is obtained on the condition that the thickness of Co free layer is 70 ${\AA}$ and the maximum MR ratio(%) value of 3.2% shows in the FeN(250 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/FeN(250 ${\AA}$) mutilayer film which is fabricated at the N, gas flow rate of 0.5 sccm and the FeN film thickness of 250 ${\AA}$. Four steps are observed in the magnetoresistance curve owing to this difference of coercive force, because respective magnetic layers in the multilayer possess different coercive forces. These effects observed in these mutilayer films can be expected to application to the memory device the same MRAM as can carry out simultaneously four signals.