• Transactions on Electrical and Electronic Materials
• /
• v.17 no.3
• /
• pp.155-158
• /
• 2016

The effect of microsilica content modified with silicone-modified epoxy on electrical and mechanical properties of cycloaliphatic epoxy/microsilica system was investigated. The cycloaliphatic epoxy resin was diglycidyl 1,2-cyclohexanedicarboxylate and curing agent was an anhydride. Surface of microsilica was modified with silicone-modified epoxy. Electrical breakdown strength, the most important property for electrical insulation materials was tested. Tensile and flexural tests were also performed using universal testing machine (UTM). The microcomposite with 60 wt% microsilica shows maximum values in electrical breakdown strength.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.11
• /
• pp.1840-1847
• /
• 2016

The surface of nanosilica and microsilica was modified in order to develop a high voltage insulation material for outdoor application. The modified silicas were well dispersed in an aliphatic cyclic epoxy resin. Dielectric properties were studied for 8 kinds of specimens: 1 kind of neat epoxy, 3 kinds of epoxy/microsilica composites, and 4 kinds of epoxy/microsilica/nanosilica composites. Complex dielectric constants were measured in the range of 10-2~1.2 Hz at room temperature.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.62 no.5
• /
• pp.649-656
• /
• 2013

A conventional epoxy-microsilica composite (EMC) and an epoxy-microsilica-nanosilicate composite (EMNC) were prepared in order to apply them to mold-type transformers, current transformers (CT) and potential transformers (PT). Nanosilicate was exfoliated in a epoxy resin using our electric field dispersion process and AC insulation breakdown strength at $30{\sim}150^{\circ}C$, glass transition temperature and viscoelasticity were studied. AC insulation breakdown strength of EMNC was higher than that of EMC and that value of EMNC was far higher at high temperature. Glass transition temperature and viscoelasticity property of EMNC was higher than those of EMC at high temperature. These results was due to the even dispersion of nanosilicates among the nanosilicas, which could be observed using transmission electron microscopy (TEM). That is, the nanosilicates interrupt the electron transfer and restrict the mobility of the epoxy chains.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.4
• /
• pp.203-206
• /
• 2017

The effect of the content of microsilica and nanosilica continuously modified with hydroxy silane and epoxy-modified silicone in cycloaliphatic epoxy/microsilica/nanosilica composites (EMNCs) on the mechanical and water repellent properties was evaluated. Surface-modified micro- and nanosilica was well-mixed with a cycloaliphatic epoxy resin in the presence of polyester-modified polydimethylsiloxane (PEM-PDMS) as a dispersing agent using an ultrasonicator. Tensile and flexural tests were carried out using a universal testing machine (UTM). The water repellent property was evaluated by contact angle measurements of water on the composite surface. Tensile strength of the composite could be enhanced by 32.2% up to 91.4 MPa, and the flexural strength was raised to 122.0 MPa, which is 38.8% higher than that of neat epoxy. The contact angle of water on the composite was as high as $104.1^{\circ}$.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.6
• /
• pp.301-304
• /
• 2012

Epoxy/microsilica (65 phr)/nanosilica (0~5 phr) composites (EMNC) were prepared in order to develop a high-voltage insulation material, where phr means parts per hundred relative to the epoxy oligomer. Tensile and flexural tests of the composites were carried out, and the AC electrical breakdown strength was measured, after which all the data were estimated by Weibull statistical analysis. As the nanosilica content increased, the tensile strength increased, and the highest value was 117.7 MPa in the EMNC system with 3 phr nanosilica, which was ca. 10% higher than that of the system without nanosilica. The value then decreased after 3 phr. The flexural strength and AC electrical breakdown strength showed the same tendencies as the tensile strength. The highest value of the flexural strength was 184.6 MPa in the EMNC system with 3 phr of nanosilica, which was ca. 15% higher than that of the system without nanosilica. The strongest value of the AC electrical breakdown strength was 79.0 kV/0.5 mm in the EMNC system with 3 phr of nanosilica, which was ca. 34% higher than that of the system without nanosilica.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1296-1302
• /
• 1999

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.11
• /
• pp.886-894
• /
• 2012

In order to develop electrical insulation materials, epoxy-nanosilica-microsilica mixture composites (ENMC) was synthesized, and mechanical properties such as their tensile and flexural strength, and AC insulation breakdown strength were investigated. Properties of mechanical strength and AC insulation breakdown strength are analyzed as scale and shape parameter with respect to weibull plot. Their tensile and flexural strength, AC insulation breakdown strength were compared original epoxy or EMC to ENMC. The 4 phr nano-silica addition and the 65 wt% micron-silica mixture composite (ENMC) was found to have the highest tensile and flexural strength. In the tensile strength was improved 29%, and flexural strength was improved 60.9% higher than those of the original epoxy. In the insulation breakdown strength, ENMC_4 phr was improved 17% and ENMC_5 phr was improved 15.8% higher than those of the EMC.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.11
• /
• pp.895-901
• /
• 2012

In order to application for high voltage heavy electric equipments, epoxy/microsilica 60 wt%/nano layered silicate composites (EMNC_60) and epoxy/microsilica 65 wt%/nano layered silicate composites (EMNC_65) respectively was synthesized by our electric field dispersion method and the result was obtained completely dispersion state. Thermal properties such as glass transition temperature (Tg) and thermal expansion coefficient, and DMA characteristics were studied, and mechanical properties such as tensile and flexural tests were performed. AC electrical insulation strength was also tested. The study on thermal property, EMNC_65 was better than EMNC_60 and mechanical, electrical properties much improved EMNC_60 compared with EMNC_65.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.9
• /
• pp.1181-1188
• /
• 2018

In order to develop new insulating materials for GIS Spacer using environmentally friendly insulating gas, three kinds of dispersed liquid nano composites of solid epoxy /nano layered silicate filled material were prepared. And the epoxy/nano/micro silica composite was prepared by mixing epoxy/nano 3 phr dispersion/4 kinds of filler contents(40,50,60, 70wt%). The electrical insulation breakdown strengths of the nano and nano/micro mixed composites were evaluated by using 8 kinds of samples including the original epoxy. The mechanical tensile strength of the epoxy / nano / micro silica composite were evaluated, also. The TEM was measured to evaluate the internal structure of nano/micro composites. As a result, it was confirmed that the layered silicate nano particles was exfoliated through the process of inserting epoxy resin between silicate layers and the layers. In addition, dispersion of nano / micro silica resulted in improvement of electrical insulation breakdown strength with increase of filling amount of dense tissue with nanoparticles inserted between microparticles. In addition, the tensile strength showed a similar tendency, and as the content of microsilica filler increased, the mechanical improvement was further increased.

• Advances in concrete construction
• /
• v.6 no.2
• /
• pp.123-143
• /
• 2018

Self compacting concrete (SCC) has good flowability, passability and segregation resistance because of voluminous cementitious material & high coarse aggregate to fine aggregate ratio, and high free water availability. But these factors make it highly susceptible to shrinkage. Fibers are known to reduce shrinkage in concrete mixes. Until now for conserving cement, only pozzolanic materials are admixed in concrete to yield a SCC. Hence, this study compares the use of wollastonite micro fiber (WMF), a cheap pozzolanic easily processed raw mineral fiber, and flyash in yielding economical SCC for rigid pavement. Microsilica was used as a complimentary material with both admixtures. Since WMF has large surface area ($827m^2/kg$), is acicular in nature; therefore its use in yielding SCC was dubious. Binary and ternary mixes were constituted for WMF and flyash, respectively. Paste mixes were tested for compatibility with superplasticizer and trials were performed on a normal concrete mix of flexural strength 4.5 MPa to yield SCC. Flexural strength test and restrained shrinkage test were performed on those mixes, which qualified self compacting criteria. Results revealed that WMF admixed pastes have high water demand, and comparable setting times to flyash mixes. Workability tests showed that 20% WMF with microsilica (5-7.5%) is efficient enough in achieving SCC and higher flexural strength than normal concrete at 90 days. Also, stress rate due to shrinkage was lesser and time duration for final strain was higher in WMF admixed SCC which encourages its use in yielding a SCC than pozzolanic materials.