• Journal of Korea Foundry Society
• /
• v.38 no.4
• /
• pp.75-81
• /
• 2018

This study examined the effect of the CaMgSn ternary phase on the aging response of the Mg-Sn-Zn alloy. The results revealed that the CaMgSn ternary phase formed in rod-like or needle-like shapes in Mg-3Zn-0.3Ca-xSn (x=1.5, 3, and 5 wt%) alloys and its size decreased as the Sn content increased from 1.5 wt% to 5 wt%. The Mg-3Zn-0.3Ca-5Sn alloy with a relatively fine CaMgSn phase was subjected to solution heat treatment and an aging process. Both the Mg-5Sn-3Zn-0.3Ca and Mg-5Sn-3Zn (base alloy) alloys had similar peak hardness values throughout all aging temperatures but the time-to-peak hardness in the Mg-5Sn-3Zn-0.3Ca alloy was 24-36 hours-earlier than that in the base alloy. Precipitates in the Mg-5Sn-3Zn-0.3Ca alloy were more refined than those in the Mg-5Sn-3Zn alloy and were mostly formed on basal planes. The $Mg_2Sn$ phase formed in either plate-like or rod-like shapes in the Mg-5Sn-3Zn alloy, whereas block-shaped $Mg_2Sn$ particles also formed in the Mg-5Sn-3Zn-0.3Ca alloy.

• Journal of Korea Foundry Society
• /
• v.37 no.1
• /
• pp.14-20
• /
• 2017

The microstructure, electrical conductivity and hardness variation of an AZ91-5wt%Sn Mg alloy sample during a solid-solution and aging heat treatment were instigated by optical microscopy, scanning electron microscopy, X-ray diffraction and by Rockwell hardness techniques in this study. The XRD result shows that the main phases in the as-casted alloy are ${\alpha}$-Mg, $Mg_{17}Al_{12}$ and $Mg_2Sn$. From the SEM images of the AZ91-5wt%Sn Mg alloy after the solution treatment, the $Mg_{17}Al_{12}$ phases in the alloy were found to have dissolved into the matrix with an increase in the holding time during the solution treatment, but $Mg_2Sn$ phases were clearly observable. The highest peak hardness of the AZ91-5wt%Sn Mg alloy is 82HRE at an aging temperature of $200^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.35 no.2
• /
• pp.36-43
• /
• 2015

In this study, the influences of aluminum and tin additions (individual and combined) on corrosion behavior of magnesium alloy have been determined. The studied alloys were fabricated by permanent mold casting method to measure the corrosion properties, a potentiodynamic test, hydrogen evolution test and immersion test were carried out in a 3.5% NaCl solution at pH 7.2. From the results of microstructure analysis, the Mg-9Al-1Zn alloy was found to be composed of ${\alpha}$-Mg and rod-like $Mg_{17}Al_{12}$ phase and the Mg-5Sn-5Al-1Zn alloy was found to be composed of ${\alpha}$-Mg, rod-like $Mg_{17}Al_{12}$ and $Mg_2Sn$ phases. In the case of the Mg-9Sn-1Zn alloy, the microstructure was composed of ${\alpha}$-Mg and eutectic $Mg_2Sn$ phase. With Sn addition (individual and combined), the corrosion resistance of the Mg alloys improved.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.5
• /
• pp.229-238
• /
• 2015

The effects of Sn addition and solution treatment on corrosion behavior were studied in AZ91 magnesium casting alloy. The addition of 5%Sn contributed to the introduction of $Mg_2Sn$ phase, to the reduction in dendritic cell size and to the increase in the amount of secondary phases. After the solution treatment, trace amount of $Al_8Mn_5$ particles were observed in the ${\alpha}$-(Mg) matrix for the AZ91 alloy, while $Mg_2Sn$ phase with high thermal stability was additionally found in the AZ91-5%Sn alloy. Before the solution treatment, the AZ91-5%Sn alloy had better corrosion resistance than the Sn-free alloy, which is caused by the enhanced barrier effect of the (${\beta}+Mg_2Sn$) phases formed more continuously along the dendritic cell boundaries. It is interesting to note that after the solution treatment, the corrosion rate of both alloys became increased, but the Sn-added alloy showed higher corrosion rate than the Sn-free alloy. The microstructural examination on the corroded surfaces revealed that the remaining $Mg_2Sn$ particles in the solution-treated AZ91-5%Sn alloy play a role in accelerating corrosion by galvanic coupling with the ${\alpha}$-(Mg) matrix.

• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.5
• /
• pp.255-261
• /
• 2022

In this work, the strain-amplitude independent and strain-amplitude dependent damping capacities of Mg-5%Sn alloy have been investigated as a function of its age-hardening response. The hardness increased with an increase in aging time, reached a peak value after 48 h, and then it gradually decreased. The damping capacities of the Mg-5%Sn alloy exhibited a decreasing tendency in the order of solution-treated, under-aged, peakaged, and over-aged states in the strain-amplitude dependent region, whereas they increased continuously with aging time in the strain-amplitude independent region. The microstructural examination during aging revealed that the lower concentration of Sn solutes in the α-(Mg) matrix and the lower density of the Mg₂Sn precipitate particles may well be the crucial factors for better damping values in the strain-amplitude independent and strain-amplitude dependent regions, respectively.

• Journal of Korea Foundry Society
• /
• v.37 no.3
• /
• pp.63-70
• /
• 2017

In the present study, effects of an addition of Sn on the microstructure and corrosion behavior were investigated in Mg-4%Zn-(0-3)%Sn casting alloys. With an increase in the Sn content, the ${\alpha}-(Mg)$ dendritic cell size was reduced, whereas the total amount of precipitates increased due to the formation of the $Mg_2Sn$ phase. It was found in immersion and electrochemical corrosion tests that the addition of Sn has a detrimental effect on the corrosion resistance of the Mg-4%Zn alloy. Microstructural examinations of the corrosion product and the corroded surface indicated that an accelerated micro-galvanic effect by the $Mg_2Sn-phase$ particles and a less protective corrosion product on the surface were responsible for the increased corrosion rate at a higher Sn content.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.4
• /
• pp.185-190
• /
• 2014

The influences of small amount of Sn addition on microstructure and creep resistance of AZ91-0.4%Ca alloy have been investigated. The microstructure of the AZ91-0.4%Ca alloy was characterized by ${\alpha}$-(Mg) dendrite cells surrounded by eutectic ${\beta}(Mg_{17}Al_{12})$ and $Al_2Ca$ phases. The 0.5%Sn addition resulted in the formation of rod-shaped CaMgSn particles with the extinction of $Al_2Ca$. The Sn-containing alloy exhibited better creep resistance below $175^{\circ}C$, but the tendency was reversed above $200^{\circ}C$. The reason was discussed in relation to the change in thermal stability of ${\beta}$ phase in response to the Sn addition.

• Journal of Korea Foundry Society
• /
• v.36 no.6
• /
• pp.215-221
• /
• 2016

In a recent study, the microstructures and mechanical properties of AM80-xSn magnesium alloys with semi solid casting and hot extrusion process were investigated. With increasing Sn content, the amount of ${\beta}$(Mg2Sn) phase increased, while the ${\alpha}-Mg$ dendritic size decreased. The hardness was increased by the Mg2Sn as the Sn content increased. With increasing Sn content, permanent mold cast and semi solid cast AM80 Mg alloy showed less reduction of hardness and also of extruded AM80 Mg alloy after annealing. In the case of the mechanical properties, the extruded semi solid casting AM80 Mg alloy showed higher tensile strength and yield strength with increasing Sn content compared to the extruded permanent mold cast AM80 Mg alloy at room temperature.

• Transactions of Materials Processing
• /
• v.21 no.5
• /
• pp.324-329
• /
• 2012

Mg-(9-x)Sn-xAl-1Zn (x=1, 2, 3 and 4 wt.%) alloys were subjected to indirect extrusion, and the microstructure and mechanical properties of the as-extruded Mg-Sn-Al-Zn (TAZ) alloys were investigated. The TAZ 811 alloy exhibited a finer grain structure than the TAZ 541 alloy due to a larger number of Mg2Sn particles, which pinned the grain boundaries and prevented growth of recrystallized grains. The TAZ alloys showed an unusual yield asymmetry behavior. The tension-compression yield asymmetry increased with decreasing average grain size. The TAZ 811 alloy with a small grain size exhibited a larger yield asymmetry than that of the TAZ 541 alloy having a relatively large grain size, which is mainly attributed to the low Al content and large number of second phase particles in the TAZ 811 alloy.

• Journal of Korea Foundry Society
• /
• v.32 no.6
• /
• pp.289-295
• /
• 2012

Mg-Al-Sn-Si system alloy, as a promising cheap heat-resistant Mg alloy for automobile engine part, has been investigated. Refinement of microstructure and precipitation of thermally stable secondary phases are important goal for the design of heat-resistant Mg alloy. In this study, the effect of Ce on the microstructure and room temperature mechanical properties of Mg-Al-Sn-Si alloy was investigated. High thermally stable $Mg_2Si$ phases in Mg-Al-Sn-Si alloy is very useful intermetallic compound. However, the $Mg_2Si$ phases often result in poor mechanical properties due to the coarse chinese type $Mg_2Si$ phases. The experimental specimens were fabricated by fluxless melting under $CO_2+SF_6$ atmosphere and poured into the permanent pre-heated at $200^{\circ}C$. It was told that Ce addition can modify $Mg_2Si$ phases and refine microstructure and improve the tensile strength, yield strength and elongation.