• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.829-834
• /
• 2002

Recently, research and development for a number of repairing material like an epoxy-based material and polymer-cementitious material as well as anti-washout underwater concrete have been carried out. But, the study on tile materials for the concrete structure exposed to a wetted condition is at a standstill and there are not any suitable reference data at a repairing work for the concrete structure at a splash as well as a structure under severe moisture condition. In this study, the material, called as “ceramic metal”, with an excellent mobility and plasticity as well as with a high bond strength and durability of freezing-thawing resistant properties under any environmental conditions was developed. And, the experimental evaluations for the utility wert widely performed.

• Journal of the Korean Ceramic Society
• /
• v.27 no.6
• /
• pp.755-762
• /
• 1990

The tungsten paste was printed on the surface of 92% alumina sheet which was made by type casting process. The printed tungsten was bonded on the Al2O3 by co-firing in reducing atmosphere. During the co-firing, the binder burn-out was easier in wet H2 atmosphere than in dry H2, which affected sintered density. In practically, the use of wet H2 above 100$0^{\circ}C$ was beneficial for density of alumina and bond strength. This phenomena occured more distinctly when atmosphere varied from dry H2 to wet H2 than varied dew point in wet H2. In wet H2, the improvement in bonding strength can be attributed to good glass migration into the metal layer due to inhibition of the tungsten particle growth, with increase of alumina density, at the temperatrue higher than 100$0^{\circ}C$.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.3
• /
• pp.260-272
• /
• 2001

All-ceramic restorations have had a more limited life expectancy than metal ceramic restorations because of their low strength. Their relatively lower strength and resistance to fracture have restricted the use of all-ceramic crowns to anterior applications where occlusal loads are lower. But there has been increasing interest in all-ceramic restorations because patients are primarily concerned with improved esthetics. Many efforts have been made to in prove the mechanical properties of dental ceramics. This study was designed to elucidate the influence of the luting agent on the strength of the Empress 2 crown (staining technique) cemented on human teeth. Seventy extracted human permanent molar teeth were chosen. Teeth were prepared for Empress 2 crowns with milling machine on a surveyor. A dental bur was placed in the mandrel that was positioned so that the long axis of the bur was perpendicular to the surveyor base. Dimensions of the Empress 2 crown preparation were $6^{\circ}$ taper on each side, $1.5{\pm}0.1mm$ shoulder margin, and 4mm crown height. The luting cements used in this study were as follow: 1. Uncemented 2. Zinc phosphate cements (Confi-Dental) 3. Conventional glass ionomer cement : Fuji 1 (GC) 4. Resin-modified glass ionomer cements : Fuji plus (GC) 5. Adhesive cements : Panavia F (Kuralay), Variolink II (Vivadent), Choice (Bisco). Fracture test using Instron. The crowns were loaded in compressive force to evaluate the effect of these cements on the breaking strength of these all-ceramic crowns. A steel ball with a diameter of 4mm was placed on the occlusal surface and load was applied to the steel ball by a cylindrical bolt with a crosshead speed of 0.5mm per minute until fracture occurred. The fractured surface was examined using Scanning Electron Microscopic Image (SEM) to discover the correlation between fracture strength and bonding capacity. Within the limitation of this in vitro study design, the results were as follows : 1. fomentations significantly increased the fracture resistance of Empress ceramic crowns compared to control. Uncemented (206.9 N): ZPC (812.9 N): Fuji 1 (879.5 N): Fuji Plus (937.7 N): Choice (1105.4 N): Variolink II (1221.1 N): Panavia F (1445.2 N). 2. Resin luting agent, treated by a silane bond enhancing agents, yielded a significant increase in fracture resistance. In some of the Panavia F group, a fracture extended into dentin. 3. According to SEM images of fractured Empress crowns, the stronger the bond at both interfaces(crown and die), the more fracture strength was acquired.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.7
• /
• pp.4357-4363
• /
• 2015

This study is to compare the differences of bonding strength based on the Degassing temperatures and various opaque materials for Ni-Cr alloy specimen which does not contain beryllium(Be). Numerous comparison tests have been performed to measure the bonding strength by experimenting 3-point flexural rigidity tests in order to find out ways of stabilization and enhancement of bonding strength between metal and porcelain. AVOVA, surface component observation experiment by SAM/EDS, and Tukey's HSAD posteriori tests results are as follows: First, The bonding strength in all groups has exceeded the minimum (25MPa) of ISO9693 bonding strength regulation for dental mental-porcelain specimen. Second, The bonding strength of Group V1 was $32.37{\pm}1.91MPa$, $38.25{\pm}1.38MPa$ in Group V2, $46.43{\pm}2.14MPa$ in Group V3 and $47.21{\pm}1.72MPa$ Group V4. The difference has been statistically meaningful. Tukey's HSAD posteriori tests results have shown that the bonding strength in Group V4 was higher than that of Group V1. Third, the bonding strength between metal and porcelain without degassing process was higher than that of with degassing process, and the bonding strength of powder opaque was higher than that of paste opaque. Fourth, Group V4 has ranked the highest on the comparison table of metal and porcelain bonding strength.

• The Journal of the Korean dental association
• /
• v.58 no.7
• /
• pp.435-442
• /
• 2020

Porcelain is the first ceramic material to be introduced into dentistry. Porcelain jacket crown was introduced by Dr. Charles H Land in 1886, which was an excellent aesthetic dental restoration but has not been widely used due to high firing shrinkage and low tensile strength. Then metal-ceramic system, which combines the esthetic properties of ceramics and the mechanical properties of metals, was introduced and nowadays it is still used in dental clinical field. However, the metal-ceramic system has shown some problems, such as increased lightness by reflection of light at opaque layer, shadow beneath the gingival line due to the block-out of light by metal coping, exposure of metal in margin part, bond failure between metal and porcelain, oxidation of metal coping during firing the porcelain, etc. Recently, along with the advance of fabrication methods of dental ceramics, the all-ceramic restorations with high esthetic and mechanical properties has increased and gradually replaced metal-ceramic restorations. Especially, CAD/CAM technology has opened a new era in fabricating the dental ceramic restorations. This overview will take a look at the past, present and future possibility of the dental ceramic materials.

• Journal of dental hygiene science
• /
• v.9 no.4
• /
• pp.405-412
• /
• 2009

The purpose of this study investigated the effect of Au coating on adhesion between porcelain matrix and metal substructure interface. Titanium, Ni-Cr alloy and Co-Cr alloy are well known as proper metal for the dental restorations. The success of a porcelain fused to metal (PFM) restoration depends upon the quality of the porcelain-metal bond. However, adhesion between dental alloys and porcelain is related to diffusion of oxygen during ceramic firing. The excessive oxidized layers make hard adhesion between dental alloy and ceramic. Ni-Cr and Co-Cr specimens were divided into test and a control group and Titanium specimens were divided into three test groups and a control group. Each group had 20 specimens. The adhesion characteristics of porcelain and metal with Au coating layer and without Au coating layer were observed with scanning electron microscopy(SEM). The adhesion was evaluated by a biaxial flexure test and volume fraction of adherent porcelain was determined by SEM/EDS analysis. Result of this study suggest that Au coating layer is effective barrier to diffuse oxide layer completely protect non-precious alloys from oxidation during the porcelain firing. The SEM photomicrographs of cross-section specimens showed a smooth interface between Au coating layer and metals and porcelain which suggested proper chemical bonding, and no gap, porosity were observed. The mode of failure was mainly adhesive for Ti tested specimens, but mixed failures with adhesive and cohesive were observed in Ni-Cr and Co-Cr specimens. The adhesion between non-precious metals and porcelain would not be improved by Au coating agent. However, It is suggested that the continuous study is required further investigation and development.

• The Journal of Korean Academy of Prosthodontics
• /
• v.36 no.6
• /
• pp.888-899
• /
• 1998

In-Ceram system is one of contemporary esthetic all ceramic restorations and has relatively high flexural strength. The purpose of this study was to evaluate the marginal fidelity according to type of resin cement and measuring position, and to evaluate fracture strength according to type of resin cement. In this study, twenty seven In-Ceram crowns were fabricated on the metal master die of prepared maxillary right central incisor and devided into three groups. All specimens were cemented with Panavia 21 (group PV), Super-bond (group SB) and Lute-it (group LI) on the metal master die. After cementation, specimens were measured marginal gap between the margin of the In-Ceram crown and the finishing line of metal master die by using a stereomicroscope (SZ-ST, Olympus, Japan). Marginal gaps were recorded at the labial, lingual, mesial and distal measuring points on the metal master die. For the mesurement of fracture strength, lingual surfaces of cemented specimens were loaded at a distance of 1mm from incisal edge by using the Autograph S-2000 (Shimadzu, Japan). The results of marginal fidelity and fracture strength were statistically analyzed with the SPSS version 8.0 programs. The results of this study were as follows: 1. In comparison of marginal fidelity according to the measuring points, there was no significant difference. 2. The marginal fidelity according to the type of resin cement was decreased in order of group $LI\;(63.75{\mu}m),\;SB\;(77.78{\mu}m),\;PV\;(86.53{\mu}m)$, and there was significant difference between group LI and PV (p<0.05). 3. The fracture strength according to the type of resin cement was showed descending order of group $LI\;(60.00kg/cm^2),\;SB\;(56.80kg/cm^2),\;PV\;(56.11kg/m^2)$, but there was no significant difference.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.53.2-53.2
• /
• 2011

Ti metal has superior mechanical properties along with biocompatibility, but it still has the problem of bio-inertness thus forming weaker bond in bone/implant interface and long term clinical performance as orthopaedic and dental devices are restricted for stress shielding effect. On the other hand, despite the excellent biodegradable behavior as being an integral constituent of the natural bone, the mechanical properties of ${\beta}$-tricalcium phosphate $(Ca_3(PO_4)_2;\;{\beta}-TCP)$ ceramics are not reliable enough for post operative load bearing application in human hard tissue defect site. One reasonable approach would be to mediate the features of the two by making a composite. In this study, ${\beta}$-TCP/Ti ceramic-metal composites were fabricated by spark plasma sintering in inert atmosphere to inhibit the formation of $TiO_2$. Composites of 30 vol%, 50 vol% and 70 vol% ${\beta}$-TCP with Ti were fabricated. Detailed microstructural and phase characteristics were investigated by FE-SEM, EDS and XRD. Material properties like relative density, hardness, compressive strength, elastic modulus etc. were characterized. Cell viability and biocompatibility were investigated using the MTT assay and by examining cell proliferation behavior.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.2
• /
• pp.112-118
• /
• 2012

Purpose: The purpose of this study was to evaluate the difference in shear bonding strength between resin cements to dental materials when a universal primer (Monobond plus) was applied in place of a conventional primer. Materials and methods: Four groups of testing materials: gold alloy (Argedent Euro, n = 16), non precious metal (T-4, n = 20), zirconia (Cercon, n = 20) and glass ceramic (IPS e.max press, n = 20), were fabricated into discs, which were embedded in an acrylic resin matrix. The gold alloy specimens were airborne-particle abraded, 8 of the specimens were coated with Metal primer II, while the remaining 8 specimens were coated with Monobond plus. The non precious and zirconia specimen were airborne-particle abraded then, the control group received Alloy primer coating, while the other was coated with Monobond plus. Glass ceramic specimens were etched. 10 specimens were coated with Monobond-S and the remaining specimens were coated using Monobond plus. On top of the surface, Multilink N was polymerized in a disc shape. All of the specimens were thermal cycled before the shear bonding strength was measured. Statistical analysis was done with Two sample $t$-test or Mann-Whitney U test (${\alpha}$=.05). Results: There were no significant differences in bonding strength depending on the type of primer used in the gold alloy and glass ceramic groups ($P$>.05), however, the bonding strengths of resin cements to non precious metal and zirconia groups, were significantly higher when the alloy primer was used ($P$<.05). Conclusion: Within the limitations of this study, improvement of universal primers which can be applied to all types of restorations is recommended to precious metals and zirconia ceramics. But, the bond strengths of non precious metals and zirconia ceramics were significantly lower when compared to a 10-MDP primer. More research is needed to apply universal primers to all types of restorations.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.5
• /
• pp.656-673
• /
• 2003

Statement of problem : Long-term exposure of dental porcelain to saliva during temporary cementation of a porcelain-fused to metal (PFM) restoration could affect mechanical strength of dental porcelain if the restoration is refired. Purpose : This work was performed to verify the effect of water on the mechanical strength in aged dental porcelain. Material and method : 63 specimens(Vintage Metalbond opaque and opal powder) were distributed to three experimental groups ; non-water immersed control, immersed and pedried, and immersed and non-predired groups. The changes in flexural strength and fracture toughness after specimen refiring related to Fourier Transform Infrared (FT-IR) spectroscopy. Results : 1. The FT-IR reflectances assigned to molecular bonds of $H_2O$ were noted as significantly different between the first-fired group and three refired groups and between two water-immersed groups and control group after refiring(p<0.05). They were also significantly different between predried group and non-predried group after refiring(p<0.05) 2. For opal specimens, FT-IR absorbances for hydrogen bond of $H_2O$ and silanols were significantly higher in non-predried group than in predreid group(p<0.05). 3 Predried opal group showed the highest mean flexural strength(p<0.05). Non-predried group indicated higher mean flexural strength than control group(p<0.05). 4. The mean fracture toughness for predired group was higher than non-predried group(p<0.05). 5. The difference of leucite crystal size is noted between control group and water-immersed, predried group in scanning electron microscopic study(${\times}10000$).