• Bulletin of the Korean Chemical Society
• /
• v.24 no.3
• /
• pp.274-278
• /
• 2003

New banana-shaped achiral compounds, 1,3-phenylene bis [4-{4-(alkenyloxy) phenyliminomethyl}benzoate]s were synthesized by varying the length of alkenyl group; their ferroelectric properties are described. The smectic mesophases, including a switchable chiral smectic C $(Sm\;C^*)$ phase, were characterized by differential scanning calorimetry, polarizing optical microscopy and triangular wave method. The presence of vinyl groups at the terminals of linear side wings in the banana-shaped achiral molecules containing Schiff's base mesogen induced a decrease in melting temperature and formation of the switchable $(Sm\;C^*)$ phase in the melt. The smectic phases having the octenyloxy group such as $(CH_2)_6CH=CH_2$ showed ferroelctric switching, and their values of spontaneous polarization on reversal of an applied electric field were 120 nC/cm² (X=H) and 225 nC/ cm² (X=F), respectively. We could obtain ferroelectric phases by controlling the number of carbon atom in alkenyloxy chain of a bent-core molecule.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1181-1182
• /
• 2006

Y-type barium ferrite $(Ba_2Zn_2Fe_{12}O_{22})$ was prepared by the glass-ceramic method. Glasses with composition of $0.1ZnO{\cdot}0.9(0.3Fe_2O_3{\cdot}0.5BaO{\cdot}0.2B_2O_3)$ were prepared, and the precipitation behavior of Y-type ferrite from the glass matrix was investigated by heating glass specimens at various temperature. $\alpha-BaFe_2O_4$ which is a precursor of M-type ferrite $(BaFe_{12}O_{19})$ was precipitated at about 813 K and an unknown compound, phase X, was precipitated at about 850 K. M-type ferrite and Y-type ferrite started to form at about 923 K and 1103 K, respectively. The formation of Y-type ferrite was int erpreted as the result of the reaction of M-type ferrite with a melt of phase X.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.2
• /
• pp.334-338
• /
• 2009

Trifunctional epoxy resin triglycidyl paraaminophenol (TGPAP)/$CaCO_3$ nanocomposites were prepared using the melt blending method. The effects of nano-$CaCO_3$ content on the thermal behaviors, such as cure behavior, glass transition temperature ($T_g$), thermal stability, and the coefficient of thermal extension (CTE), were investigated by several techniques. Differential scanning calorimetry (DSC) results indicated that the cure reaction of the TGPAP epoxy resin was accelerated with the addition of nano-$CaCO_3$. When the nano-$CaCO_3$ content was increased, the $T_g$ of the TGPAP/$CaCO_3$ nanocomposites did not obviously change, whereas the crosslinking density was linearly increased. The nanocomposites showed a higher thermal stability than that of the neat epoxy resin. This result could be attributed to the increased surface contact area between the nano-$CaCO_3$ particles and the epoxy matrix, as well as the high crosslinking density in the TGPAP/$CaCO_3$ nanocomposites. The CTE of the nanocomposites in the rubbery region was significantly decreased as the nano-$CaCO_3$ content was increased.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.613-617
• /
• 2013

The effects of nano size kenaf cellulose fiber on mechanical property of polypropylene (PP) composite were investigated. The addition of nano-kenaf in place of natural kenaf showed higher tensile strength, flexural strength, impact strength, and heat deflection temperature compared to the natural kenaf filled PP composite, while it shows lower melt flow index, elongation%, and flexural modulus. These seemed to be due to the increased surface area of nano-kenaf fiber contacting PP matrix and reduced impurities such as volatile extractives on the fiber surface.

• Journal of Electrochemical Science and Technology
• /
• v.2 no.3
• /
• pp.168-173
• /
• 2011

The availability, low toxicity, and high degree of technological development make silicon the most likely material to be used in solar cells, the cost of solar cells depends entirely on cost of high purity silicon production. The present work was conducted to electrodeposite of silicon from $K_2SiF_6$, an inexpensive raw material prepared from fluorosilicic acid ($H_2SiF_6$) produced in Iraqi Fertilizer plants, and using inexpensive graphite material as cathode electrode. The preparation of potassium fluorosilicate was performed at ($60^{\circ}C$) in a three necks flask provided with a stirrer, while the electro deposition was performed at $750^{\circ}C$ in a three-electrodes configuration with melt containing in graphite pot. High purity potassium fluorosilicate (99.25%) was obtained at temperature ($60^{\circ}C$), molar ratio-KCl/$H_2SiF_6$(1.4) and agitation (600 rpm). Spongy compact deposits were obtained for silicon with purity not less than (99.97%) at cathode potential (-0.8 V vs. Pt), $K_2SiF_6$ concentration (14% mole percent) with grain size (130 ${\mu}m$) and level of impurities (Cu, Fe and Ni) less than (0.02%).

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.2
• /
• pp.19-25
• /
• 2013

Extrusion is one of the most important operations in the polymer-processing industry. Balancing the distribution of flow through a die to achieve a uniform velocity distribution is the primary objective and one of the most difficult tasks of extrusion die design. If the manifold in a coat-hanger die is not properly designed, the exit velocity distribution may be not uniform; this can affect the thickness across the width of the die. Yet, no procedure is known to optimize the coat hanger die with respect to an even velocity profile at the exit. While optimizing the exit velocity distribution, the constraint optimization used in this work with allowable pressure drop in the die; according to this constraint we can control the pressure in the die. The computational approach incorporates three-dimensional finite element simulations software STAR-CCM+. These simulations are used with numerical optimization to design polymer coat hanger dies with pressure drop, uniform velocity and temperature variation across the die exit.

• Journal of Magnetics
• /
• v.22 no.1
• /
• pp.60-64
• /
• 2017

Mischmetal of Bayan Obo ore was utilized to prepare the high performance $(Pr_{7.34}Nd_{21.86})_{1-x}MM_xFe_{68.7}Al_{0.1}Cu_{0.12}Co_{0.88}B$ ribbons using melt-spinning method. Phase composition and magnetic properties were investigated at room temperature. The ribbons mainly consist of $R_2Fe_{14}B$ phase in isotropic nanostructure. Both coercivity and maximum energy product decrease with the increase of MM content. The magnetic parameters of the ribbons with MM = 20 % in mass are $B_r=7.38kGs$, $H_{cj}=13.66kOe$, $(BH)_{max}=11.81MGOe$. Henkel plots were applied to demonstrate the exchange coupling interaction between grains.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.6
• /
• pp.561-565
• /
• 2007

Because of a good wear resistance and a stable contact resistance, Ag-CdO is widely used as electrical contact material. But, the Cd-oxide mainly exists as a coarse particle and adversely affected to environment. As a reason, $Ag-SnO_2$ alloy has been developed. The Sn-oxide maintains stable and fine particle even at high temperature. In order to investigate the effect of Misch metal (Mm) additional that affects the formation of the oxide and the formation of fine matrix Ag, we studied the microstructures and properties of Ag-Sn-In(-Mm) material fabricated by rapid solidification process. The experimental procedure were melting using high frequency induction, melt spinning, and internal oxidation. The Mm addition makes Ag matrix more fine than no Mm addition. The reason is that the addition of Misch metal decreased a latent heat of fusion of alloy, as a result the rapid solidification effect of alloy is increased. The maximum hardness shows at 0.3 wt%Mm. after that the hardness is decreased until 0.4 wt% Mm, but still larger than no Mm addition alloy. At 0.5 wt% Mm alloy, the precipitation of Misch metal causes a decrease of hardness than no Mm addition alloy.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.1
• /
• pp.20-23
• /
• 2011

Amorphous Ti-(50-x)Ni-xCu (at%) (x = 20, 25, 27, 30) alloy ribbons were prepared by melt spinning. Subsequently, the crystallization behavior of the alloy ribbons was investigated by X-ray diffraction and differential scanning calorimetry. ${\Delta}T$ (the temperature gap between $T_g$ and $T_x$) increased from 33 K to 47 K and the wavenumber ($Q_p$) decreased from 29.44 $nm^{-1}$ to 29.29 $nm^{-1}$ with increasing Cu content from 20 at% to 30 at%. The activation energy for crystallization decreased from 188.5 kJ/mol to 170.6 kJ/mol with increasing Cu content from 20 at% to 25 at%; afterwards, the activation energy remained near constant. Crystallization occurred in two-stage: amorphous-B2-$TiCu_2$ in Ti-Ni-Cu alloys with Cu content less than 25 at%, while it occurred in three-stage; amorphous-B2-TiCu-$TiCu_2$ in Ti-Ni-Cu alloys with Cu content more than 27 at%.