Effects of the Substitution of Mischmetal for PrNd on the Microstructures and Magnetic Properties of Rapidly Quenched (MM)PrNd-Fe-B Nanocrystalline Magnets  

Zhao, Zeng-ru (School of Science, Inner Mongolia University of Science & Technology)
Wang, Xin (School of Science, Inner Mongolia University of Science & Technology)
Zhang, Xue-feng (School of Science, Inner Mongolia University of Science & Technology)
Ma, Qiang (School of Science, Inner Mongolia University of Science & Technology)
Liu, Yan-li (School of Science, Inner Mongolia University of Science & Technology)
Li, Yong-feng (School of Science, Inner Mongolia University of Science & Technology)
Liu, Fei (School of Science, Inner Mongolia University of Science & Technology)
Wang, Gao-feng (Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science & Technology)
Publication Information
Abstract
Mischmetal of Bayan Obo ore was utilized to prepare the high performance $(Pr_{7.34}Nd_{21.86})_{1-x}MM_xFe_{68.7}Al_{0.1}Cu_{0.12}Co_{0.88}B$ ribbons using melt-spinning method. Phase composition and magnetic properties were investigated at room temperature. The ribbons mainly consist of $R_2Fe_{14}B$ phase in isotropic nanostructure. Both coercivity and maximum energy product decrease with the increase of MM content. The magnetic parameters of the ribbons with MM = 20 % in mass are $B_r=7.38kGs$, $H_{cj}=13.66kOe$, $(BH)_{max}=11.81MGOe$. Henkel plots were applied to demonstrate the exchange coupling interaction between grains.
Keywords
permanent magnets; mischmetal; $R_2Fe_{14}B$; magnetic properties;
Citations & Related Records
Times Cited By KSCI : 1  (Citation Analysis)
연도 인용수 순위
1 K. M. Kim, H. W. Kwon, J. G. Lee, and J. H. Yu, J. Magn. 20, 21 (2015).   DOI
2 S. Sugimoto, N. Koike, D. Book, T. Kagotani, M. Okada, K. Inomata, and M. Homma, J. Alloys Compd. 330, 892 (2012).
3 Z. B. Li, B. G. Shen, M. Zhang, F. X. Hu, and J. R. Sun, J. Alloys Compd. 628, 325 (2015).   DOI
4 A. Alam, M. Khan, R. W. McCallum, and D. D. Johnson, Appl. Phys. Lett. 102, 042402 (2013).   DOI
5 X. F. Zhang, J. T. Lan, Z. B. Li, Y. L. Liu, L. L. Zhang, Y. F. Li, and Q. Zhao, Chin. Phys. B 25, 057502 (2016).   DOI
6 M. Hussain, J. Liu, L. Z. Zhao, X. C. Zhong, G. Q. Zhang, and Z. W. Liu, J. Magn. Magn. Mater. 399, 26 (2016).   DOI
7 J. Y. Jin, Y. J. Zhang, T. Y. Ma, and M. Yan, IEEE Trans. Magn. 18, 9464 (2015).
8 M. Hussain, L. Z. Zhao, C. Zhang, D. L. Jiao, X. C. Zhong, and Z. W. Liu, Physica B 483, 69 (2016).   DOI
9 J. J. Croat, J. F. Herbst, R. W. Lee, and F. E. Pinkerton, J. Appl. Phys. 55, 2078 (1984).   DOI
10 M. Sagawa, S. Fujimura, N. Togawa, H. Yamamoto, and Y. Matsuura, J. Appl. Phys. 55, 2083 (1984).   DOI
11 J. Y. Jin, Y. J. Zhang, G. H. Bai, Z. Y. Qian, C. Wu, T. Y. Ma, B. G. Shen, and M. Yan, Scientific Reports 6, 30194 (2016).   DOI
12 Q. A. La, C. H. Groot, F. R. Boer, and K. H. J. Buschow, J. Alloys Compd. 256, 82 (1997).   DOI
13 A. K. Pathak, M. Khan, K. A. Gschneidner Jr., R. W. McCallum, L. Zhou, K. W. Sun, K. W. Dennis, C. Zhou, F. E. Pinkerton, M. J. Kramer, and V. K. Pecharsky, J. Adv. Mater. 27, 2663 (2015).   DOI
14 M. G. Zhu, W. Li, J. D. Wang, L. Y. Zheng, Y. F. Li, K. Zhang, H. B. Feng, and T. Liu, IEEE Trans. Magn. 50, 1000104 (2014).
15 E. Niu, Z. A. Chen, G. A. Chen, Y. G. Zhao, J. Zhang, X. L. Rao, B. P. Hu, and Z. X. Wang, J. Appl. Phys. 115, 113912 (2014).   DOI
16 Z. B. Li, M. Zhang, B. G. Shen, F. X. Hu, and J. R. Sun, Mater. Lett. 172, 102 (2016).   DOI
17 X. C. Wang, M. G. Zhu, W. Li, L. Y. Zheng, Z. H. Gou, X. Du, and A. Du, Physica B. 476, 150 (2015).   DOI
18 M. Zhang, Z. B. Li, B. G. Shen, F. X. Hu, and J. R. Sun, J. Alloys Compd. 651, 144 (2015).   DOI
19 X. B. Liu, Z. Altounian, M. D. Huang, Q. M. Zhang, and J. P. Liu, J. Alloys Compd. 549, 366 (2013).   DOI
20 Y. X. Qiang, Y. Ming, and L.W. Qiang, J. Rare Earths 34, 614 (2016).   DOI