• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.841-845
• /
• 2001

The steam generator tubes of power plant damaged by sliding wear due to flow-induced motion of foreign object. Amount of wear have been predicted by Achard's wear equation until now. However, there are large error and low reliability, because this equation regards wear coefficient(k) as constant. The sliding wears tests have been performed at room temperature to examine parameters of wear (wear distance, contact stress). The steam generator tube material for wear test is used Inconel 600 and foreign object material is used 304 austenite stainless steel. The sliding wear tests show that the amount of wear is not linearly proportional to the wear distance(for 374 austenite stainless steel). According to experimental result, wear coefficient is not constant k but function k(s) of wear distance. The newly modified wear predictive equation V=k(s)F have small error and high reliability.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.14 no.3
• /
• pp.38-46
• /
• 2005

The destructive method is reliable and widely used for the estimation of material degradation but it have time-consuming and a great difficulty in preparing specimens from in-service industrial facilities. Therefore, the estimation of degraded structural materials used at high temperature by nondestructive evaluation such as electric resistance method, replica method, Barkhausen noise method, electro-chemical method and ultrasonic method are strongly desired. In this study, various nondestructive evaluation(NDE) parameters of the Barkhausen noise method, such as MPA(Maximum Peak Amplitude), RMS, IABNS(Internal Area of Barkhausen Noise on Signal) and average amplitude of frequency spectrum are investigated and correlated with thermal damage level of 2.25cr-1.0Mo steel using wavelet analysis. Those parameters tend to increase while thermal degradation proceeds. It also turns out that the wavelet technique can help to reduce experimental false call in data analysis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.621-624
• /
• 1999

Metalization technology of the fine patterns by electroless plating is required in place of electrodeposition as high-density printed boards(PCR) become indispensable with the miniaturization of electronic components. Electroless nickel plating is a suitable diffusion barrier between conductor meta1s, such as Al and Cu and solder is essetional in electronic packaging in order to sustain a long period of service. Moreover, Electroless nickel has particular characteristics including non-magnetic property, amorphous structure. wear resistance, corrosion protection and thermal stability In this study fundamental aspects of electroless nickel deposition were studied with effort of complexeing agents of different kinds. Then the property of electroless deposit are controlled by the composition of the deposition solution the deposition condition such as temperature and pH value and so on. the characteristics of the deposits has been carried out.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.05a
• /
• pp.295-298
• /
• 2012

Repair and strengthening is necessary to extend the service life of existing buildings. Polymer-modified cement mortar (PCM) has been extensively used as a high performance material particularly for finishing and repairing works in concrete building because of itsexcellent adhesion, waterproofing, resistance to chemical attack, and workability. As PCM contains organic polymer, it is necessary to clarify its properties at high temperature under fire, on which sufficient data are not available. This paper evaluated the burn-up characteristics of polymer-modified cement mortar with cone calorimeter test, non-combustibility test and flammability test with experimental parameters such as the types of polymer, unit-polymer content, polymer-cement ratio and thickness of the specimen.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.3
• /
• pp.127-134
• /
• 2010

Components in thermal power plants are subjected to service conditions under which creep damages take place causing material exhaustion. Comprehensive creep damage investigations have been performed on a 0.5Cr0.5Mo0.25V pipe bend which had been taken out of service after 117,603h and 501 start-ups because of severe cracks. The propagation of creep damage in a long term exposed pipe bend has been analysed by the replication, Indentation and hardness tests. Also, Calculation of creep lifetime has been investigated in order to verify actual lifetime of a damaged pipe bend. By measuring diametrical expansion, Accumulated creep strain and creep strain rate were calculated. Calculated results of creep lifetime on the Larson-Miller Parameter method are good agreement with actual service-exposed hour.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.11 no.1
• /
• pp.74-78
• /
• 2015

Nuclear power plant steam generator that is one of the main component has several thousands of thin tubes. And the steam generator tube is subject to damage because of the severe operation conditions such as the high temperature and pressure. Therefore periodic inspections are conducted to ensure the integrity of steam generator component. Hanul unit 3 also has been inspected in accordance with in-service inspection program and is scheduled to be replaced for exceeding the plugging rate which was recommended by manufacturer. During the steam generator replacement activity, we found several clustered porosity on inner surface of main feed water pipe. Additionally crack-like indications were found at weld interface between base material and weld of main feed water pipe. This paper describes the field experience and visual testing results for inner surface of main feed water pipes. The destructive test result had shown that these indications were porosities which were caused by manufacturing process not by operation service.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.489-496
• /
• 2010

The power generation and chemical industry have been subjected to further material degradation with long term operations and need to predict the remaining service life of components, such as reformer tube and steam turbine rotor, that have operated at elevated temperatures. As a non-destructive technique, replication method with reliable metallurgical life and microstructural soundness assessment has been recognized with strongly useful method until now. Developments of this method have variously accomplished by new quantitative approach, such as carbide analysis, with A-parameter and grain deformation method. An overview of replication, some new techniques for material degradation and life assessment were introduced in this paper. Also, on-site applications and its reasonableness were described. As a result of having analyzed microstructure by replication method, carbide approach was quantitatively useful to life assessment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.10
• /
• pp.812-816
• /
• 2011

An optical lens is usually produced in the manner of high temperature compression molding with tungsten carbide alloy molding cores, it is necessary to develop and study technology for super-precision processing of molding cores and coating the core surface. As main methods used in surface improvement technologies using thin film, DLC present high hardness, chemical stability, and outstanding durability of abrasion to be extensively applied in various industrial fields. In this study, the effect of DLC coating of a thin film by means of the FVAS (filtered vacuum arc source) analyzed the characteristics of thin film. Surface roughness before and after DLC coating was measured and the result showed that the surface roughness was improved after coating as compared to before coating. In conclusion, it was observed that DLC coating of the ultra hard alloy core surface for molding had an effect on improving the surface roughness and shape of the core surface. It is considered that this will have an effect on improving abrasion resistance and the service life of the core surface.

• Korean Journal of Veterinary Service
• /
• v.38 no.3
• /
• pp.195-198
• /
• 2015

Mannheimia haemolytica is an opportunistic bacterium that is widely recognized among the bovine respiratory disease (BRD) complex in cattle. Five Hanwoo with a history of fever, anorexia and dyspnea were died within 2 days in a the middle of summer. Four cattle were pregnant. The cattle house were located in mountainous area but the window for air ventilation was open only one side. In addition, the fecal material for fermentation was located indoor. Air ceiling fan did not work. The indoor temperature was $40^{\circ}C$. After working on air fan, the indoor temperature was still $36^{\circ}C$. On necropsy, there was fibrinous pleuritis with a rich yellowish pleural fluids in the thorax. The cross-section of the lung showed lobar fibrinonecrotic pneumonia with expanded interlobular septa by edema and fibrin. Microscopically, parenchymal necrosis with dense layer of inflammatory cells were observed surrounding interlobular septum. Fibrin and inflammatory cells were filled in the alveoli. Bacteriological cultures of pulmonary tissue showed growth of M. haemolytica. This pneumonia case in Hanwoo suggests that environmental stressors such as high temperature, insufficient air ventilation, and pregnancy be the cause of mannheimoisis. Control of environmental stressor, such as temperature indoor is necessary to prevent BRD caused by M. haemolytica.

• Journal of Energy Engineering
• /
• v.8 no.4
• /
• pp.605-611
• /
• 1999

Conventional methods for assessing remaining life of critical high temperature components in fossil power plants rely on nondestructive inspection practices and accompanying life analysis based on fracture mechanics By using these conventional methods. It has been difficult to perform uninterrupted in-service inspection for life prediction. Thus, efforts have been made for developing on-line remaining life monitoring systems employing information on the shape of structures, operating variables and material properties. In thus study, a software for on-line life monitoring system which performs real-time life evaluation of a high temperature system headers was developed. The software is capable of evaluating creep and fatigue life usage from the real-time stress data calculated by using temperatures/stress transfer Green functions derived in advance for the specific headers. The major benefits of the developed software life in determining future operating schedule, inspection interval, and replacement plan by monitoring real-time life usage based on prior operating history.