• 한국염색가공학회:학술대회논문집
• /
• 한국염색가공학회 2008년도 제38차 학술발표대회
• /
• pp.31-33
• /
• 2008

The study related that Red Phosphorus is surface coated by Al(OH)$_3$ using the proportion 1:1, 1:3, 1:5 respectively, and then take the coated red phosphorus as the core material, at the same time, use Melamine-Formaldehyde resin as the capsule materials for microcapsule processing. According to the TG analysis, the coated red phosphorus with the proportion 1:3 has the tiptop temperature of thermal decomposition, it reaches 376.20^{\circ}C$$. The same to the ratio of burning incomplete carbon it reaches 26.5%. The lowest moisture absorption ratio of the red phosphorus that used coated red phosphorus for microcapsule processing can reach 0.5% with the condition that thermal decomposition temperature decline 3.6%.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권5호
• /
• pp.671-677
• /
• 1999

This study has been performed to investigate REW(relative electrode wear) in condition of vari-ous pulse-on duration using the copper and graphite electrode with change of the electrode size on the heat treated STD11 which is extensively used for metallic molding steel with the EDM. The results obtained are as follows; a) Graphite has much benefits than copper electrode when rapid machining is done without electrode wear, b) Neative REW result from the electrode that is very liable attach to decomposition carbide c)Increasing of machining time cause to increase wear length of the copper electrode and decrease wear length of the graphite electorde d)The more pulse-on duration copper electrode has the less REW. e) The edge portion of the electorde wears remarkably at the beginning of machining,.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2010년도 제34회 춘계학술대회논문집
• /
• pp.113-122
• /
• 2010

고체추진기관의 연소 환경에서 복잡한 형상을 갖는 내열 복합재료의 온도, 밀도분포 및 삭마두께를 예측할 수 있는 방법을 개발하였다. 복합재료의 내부 열반응은 Arrhenius 모델을 이용하였으며, 표면 삭마반응은 Zvyagin 이론을 사용하였다. 표면 삭마에 의한 경계조건 및 격자 이동은 상용해석 코드에서 활용되는 Rezoning-remeshing 기법을 사용하였다. 형상이 복잡한 부품으로 이루어진 2차원 축대칭 노즐 조립체에 적용된 방법은 향후 3차원 FEM 열구조 해석에 활용을 목표로 발전될 것이다.

• 한국환경과학회지
• /
• 제11권7호
• /
• pp.743-748
• /
• 2002

UV photolysis process is little known in parts of air pollution treatment, so there are not many applications in field. Therefore we have to do more experiment and study application possibility for treatment of VOCs(Volatile organic compounds). To solve these problems, we have been studying for simultaneous application of this technology. It has shown that concentration of TCE and B.T.X., diameter of reactor and wavelength of lamp have effected on decomposition efficiency. Analysis of TCE and B.T.X. concentration was carried out by GC-FID. A cylinderical reactor consisting of a quartz tube and a centrally located lamp(${\psi}25mm$) was used. The length and diameter of reactor were 1800mm, 75mm. It has shown that the generated ozone concentration goes up 250ppm when using 64watt ozone lamp. When using Photolysis process only, the rates of fractional conversion of each material are TCE 79%, Benzene 65%, Toluene 68%, Xylene 76%. This phenomenon can be rationalized in terms of the different bond energy that indicates how easily VOCs species can be decomposed.

• 한국정보통신학회:학술대회논문집
• /
• 한국정보통신학회 2021년도 춘계학술대회
• /
• pp.567-568
• /
• 2021

본 논문에서는 UV-A와 UV-C를 포함하는 복합 파장의 LED 모듈을 적용한 캐빈 필터를 설계 및 제작하고 성능를 시험하였다. 제작한 캐빈 필터의 세균 및 공팜이 살균 시험에서 살균 능력을 확인하였고 유기화합물 분해 시험에서는 특수 챔버를 제작하여 유기물 분해 능력을 검증하였다. 광촉매로 콜케이트를 사용하는 것이 매탈매쉬를 사용하는 것보다 우수한 성능을 확인하였다. 본 연구를 통해서 제작한 캐빈 필터의 살균 및 공기 정화 능력을 실제와 유사한 환경 시험을 통해서 확인하였다.

• 전기학회논문지
• /
• 제66권11호
• /
• pp.1651-1656
• /
• 2017

This paper deals with the thermal and mechanical properties of ceramic coating material for bus bars. A ceramic coated samples were prepared for the mechanical properties test. There are two types of samples. One is a square shape and the other is a busbar shape. Each sample was deteriorated for 30 days to compare the thermal and mechanical properties with the non-degraded samples. Two thermal properties tests are TGA and flammability tests, and four mechanical properties tests are drop impact test, cross cut, tensile test, and bend test. The ceramic coating material was never damaged by impact and did not separate from aluminum in the cross cut test. In the tensile test, the breakage of the insulating material did not occur until aluminum fractured, and the breakage of the insulating material did not occur until the maximum load in the bending test. The decomposition temperature (melting point) of the ceramic coating material was higher than that of other epoxy insulators. This ceramic coating material is nonflammable and it has excellent fire stability.

• 한국재료학회지
• /
• 제29권10호
• /
• pp.603-608
• /
• 2019

Plastic waste is becoming a problem in various countries because of the difficulty of natural decomposition. One type is PET plastic(Polyethylene Terephthalate), which is often used as a bottle for soft drink packaging, and LDPE(Low Density Polyethylene), which is also widely used as a food or beverage packaging material. The use of these two types of plastic continuously, without good recycling, will have a negative impact on the environment. Building material waste is also becoming a serious environmental problem. This study aims to provide a solution to the problem of the above plastic waste and building material waste by making them into a mixture to be used as bricks. Research is carried out by mixing both materials, namely plastic heated at a temperature of $180-220^{\circ}C$ and building material waste that had been crushed and sized to 30-40 mesh with homogeneous stirring. The ratios of PET and LDPE plastic to building material waste are 9 : 1, 8 : 2, 7 : 3, 6 : 4 and 5 : 5. After heating and printing, density, water absorption and compressive strength tests are carried out. Addition of PET and LDPE plastic can increase compressive strength, and reduce water absorption, porosity and density. A maximum compressive strength of 10.5 MPa is obtained at the ratio of 6 : 4.

• Elastomers and Composites
• /
• 제36권1호
• /
• pp.52-60
• /
• 2001

발포체의 물성은 발포체의 밀도, 사용된 폴리머의 기계적 물성과 열린 셀(open cell) 함량, 셀 크기, 셀 크기 분포, 셀 형태, 격벽의 두께 등을 포함하는 셀 구조에 의존하며 이러한 발포체의 밀도는 사용된 폴리머의 종류와 가교제의 농도, 발포제의 농도 그리고 가공 기술 및가공 조건 같은 다양한 원료물질과 가교조건에 영향을 받는다. Ethylene vinyl acetate coplymer (EVA) 발포체는 가교 발포체로서 가교속도와 발포제의 분해속도에 의해 발포특성에 영향을 받으며 이에 따라 발포체 물성에도 영향을 미친다. 본 연구에서는 가공 온도인 $155^{\circ}C$에서의 시간에 따른 발포제의 분해 속도 차이와 이에 따른 발포특성과 발포체의 물성에 대한 영향을 평가하였다. 발포제 분해 속도가 보다 느린 경우, 발포제 분해속도가 빠른 경우와 비교하여 낮은 밀도를 보여주었으며, 우수한 충격흡수성을 나타내었고 발포체의 셀 크기는 보다 균일하였다.

• 대한기계학회논문집A
• /
• 제36권10호
• /
• pp.1109-1114
• /
• 2012

제품 생산 시 발생하는 제작 공차, 항복강도와 탄성계수 등 재료 물성치의 불확실성, 온도와 습도 같이 시스템에 작용하는 환경인자 등은 시스템의 성능에 영향을 미친다. 강건 최적설계는 이러한 인자들이 시스템에 미치는 영향을 최소화하면서 성능을 개선하는 설계기법으로 최근 많은 연구가 이루어지고 있다. 하지만 기존의 강건 최적설계 기법은 여러 인자들의 분포를 고려해야 하기 때문에 막대한 계산비용이 드는 문제가 있다. 본 논문에서는 이러한 문제점을 개선하기 위하여 곱분해 기법을 이용한 강건 최적설계를 제안한다. 제안된 기법을 이용하여 설계영역을 크리깅 메타모델로 근사하고 곱분해 기법을 적용하여 평균과 분산을 효율적이고 정확하게 계산하여 강건 최적설계를 수행한다. 제안된 방법을 수학예제와 공학예제에 적용하여 유용성을 검증한다.

• 공업화학
• /
• 제8권6호
• /
• pp.1029-1033
• /
• 1997

본 연구에서는 $Na_2B_4O_7{\cdot}10H_2O$의 열분해 반응계를 이용하여 축열식 열교환기에 적용하기 위한 반응속도의 비등온 해석에 대한 기초연구를 수행하였다. $Na_2B_4O_7{\cdot}10H_2O/Na_2B_4O_7{\cdot}5H_2O$ 계에서 반응의 평형온도가 373K 이하의 저온 온도범위에서 화학축열재로 적합하였으며, 열효율이 일정하여 장시간 사용할 수 있었다. 계 내의 반응 개시온도는 가열속도 증가에 따라 저온 영역에서 고온영역으로 이동하였으며, 수증기 분압의 변화가 있어도 저하되지 않았다. 열분해 탈수반응에 의한 반응속도식의 차수는 0.67차로서 반응의 비등온 해석에 의하여 화학축열재로 사용할 수 있었다.