• 한국도로학회논문집
• /
• 제19권2호
• /
• pp.67-74
• /
• 2017

PURPOSES : The objective of this study is to ascertain the curing period of cementless cold central plant recycled asphalt base-layer, using mechanical analyses and specimen quality tests on the field. METHODS : Cold central plant recycled asphalt base-layer mixture was produced in the plant from reclaimed asphalt, natural aggregate, filler for the cold mix, and the modified emulsion AP using asphalt mix design and plant mix design. In order to examine the applicability of the curing period during the field test, the international standards for the possibility of core extraction and the degree of compaction and LFWD deflection were analyzed. Moreover, Marshall stability test, porosity test, and indirect tensile strength test were performed on the specimens of asphalt mix and plant mix design. RESULTS : The plant production process and compaction method of cementless cold central plant recycled asphalt base-layer were established, and the applicability of the optical moisture content for producing the mixture was verified through the field test. In addition, it was determined that the core extraction method of the conventional international curing standard was insufficient to ensure performance, and the LFWD test demonstrated that the deflection converges after a two-day curing. However, the back-calculation analysis reveals that a three-day curing is satisfactory, resulting in a general level of performance of dense asphalt base-layer. Moreover, from the result of the specimen quality test of the asphalt mix design and plant mix design according to the curing period, it was determined that the qualities satisfied both domestic and international standards, after a two-day curing. However, it was determined that the strength and stiffness after three-day curing are higher than those after a two-day curing by approximately 3.5 % and 20 %, respectively. CONCLUSIONS:A three-day curing period is proposed for the cementless cold central plant recycled asphalt base-layer; this curing period can be demonstrated to retain the modulus of asphalt-base layer in the field and ensure stable quality characteristics.

• 한국산학기술학회논문지
• /
• 제12권7호
• /
• pp.3296-3301
• /
• 2011

배수성포장은 다양한 장점을 가지고 있어 점차 보편화되고 있는데, 주요 효과로는 수막현상 최소화, 빗물에 의한 미끄럼저항값을 일정하게 유지하고, 차량과 포장체 사이에서 발생하는 소음을 저감시켜준다. 도로소음 및 수막현상 감소효과에 대한 많은 연구가 수행되었다. 본 연구의 목적은 배수성 포장 표층의 역학적 특성(강도 및 탄성계수)을 평가하는 것이다. 시험에 사용된 시편은 선회다짐기를 이용하여 제작하였다. 배수성포장의 상부표층 및 하부표층용 시편을 실험에 이용하였다. 마샬안정도시험(KS F 2377), 자유단공진주시험(KS F 2730), 일축압축시험(KS F 2314), 슈미트햄머시험 등을 수행하였다. 일축압축강도 및 슈미트햄머를 이용한 강도값을 비교 분석하였다.

• 대한토목학회논문집
• /
• 제38권4호
• /
• pp.611-619
• /
• 2018

현무암 석분슬러지는 석재가공 과정에서 필연적으로 발생하는 산업부산물이다. 최근 건축 및 조경분야에서 천연자재에 대한 수요가 증가하고 있어 석분슬러지 발생량도 증가하고 있다. 현무암 석분슬러지는 현재 발생량의 대부분이 단순 매립과 복토용으로 처리되고 있어 활용성 제고를 위한 노력이 필요하다. 이에 본 연구에서는 제주지역의 강우특성을 고려해 현무암 석분슬러지를 시멘트와 섞어 아스팔트혼합물의 채움재로 활용하기 위한 검토를 수행하였다. 검토결과 현무암 석분슬러지는 KS F 3501에서 요구하는 품질기준을 만족하였다. 마샬 배합설계를 실시하여 개질재생아스팔트혼합물(순환골재 27%)과 일반아스팔트혼합물에 대한 최적 아스팔트 함량(OAC)을 결정하였다. 두 종의 아스팔트혼합물에 채움재의 혼합비(3 수준) 및 현무암 석분슬러지와 시멘트의 구성비(3 수준)를 변화시켜 마샬안정도 시험으로 현무암 석분슬러지의 활용 범위를 파악하였다. 채움재의 혼합비와 구성비가 안정적인 활용성을 보이는 아스팔트혼합물들에 대한 공용성을 평가한 결과 두 종의 아스팔트혼합물 모두 국토교통부(2015)의 품질기준을 만족하였다. 따라서 현무암 석분슬러지는 아스팔트혼합물의 채움재로 활용이 가능한 것으로 판단된다.

• 한국도로학회논문집
• /
• 제20권1호
• /
• pp.47-58
• /
• 2018

PURPOSES : The purpose of this study is to evaluate the mechanical properties of a cold-recycling asphalt mixture used as a base layer and to determine the optimum emulsified-asphalt content for ensuring the mixture's performance. METHODS : The physical properties (storage stability, mixability, and workability) of three types of asphalt emulsion (CMS-1h, CSS-1h, and CSS-1hp) were evaluated using the rotational viscosity test. Asphalt emulsion residues, prepared according to the ASTM D 7497-09 standard, were evaluated for their rheological properties, including the $G*/sin{\delta}$and the dynamic shear modulus (${\mid}G*{\mid}$). In addition, the Marshall stability, indirect tensile strength, and tensile-strength ratio (TSR) were evaluated for the cold-recycling asphalt mixtures fabricated according to the type and contents of the emulsified asphalt. RESULTS : The CSS-1hp was found to be superior to the other two types in terms of storage stability, mixability, and workability, and its $G*/sin{\delta}$ value at high temperatures was higher than that of the other two types. From the dynamic shear modulus test, the CSS-1hp was also found to be superior to the other two types, with respect to low-temperature cracking and rutting resistance. The mixture test indicated that the indirect tensile strength and TSR increased with the increasing emulsified-asphalt content. However, the mixtures with one-percent emulsified-asphalt content did not meet the national specification in terms of the aggregate coverage (over 50%) and the indirect tensile strength (more than 0.4 MPa). CONCLUSIONS : The emulsified-asphalt performance varied greatly, depending on the type of base material and modifying additives; therefore, it is considered that this will have a great effect on the performance of the cold-recycling asphalt pavement. As the emulsified-asphalt content increased, the strength change was significant. Therefore, it is desirable to apply the strength properties as a factor for determining the optimum emulsified-asphalt content in the mix design. The 1% emulsified-asphalt content did not satisfy the strength and aggregate coverage criteria suggested by national standards. Therefore, the minimum emulsified-asphalt content should be specified to secure the performance.

• 한국지반환경공학회 논문집
• /
• 제3권2호
• /
• pp.35-47
• /
• 2002

대구 지역의 경우 최근의 지하철 1호선 공사 완공과 함께 2~4호선 공사와 더불어 많은 양의 토사와 암석들을 발생기킬 것으로 생각되지만, 발생되는 암석류는 주로 기계적 강도가 낮고 팽창, 수축에 대한 내성이 작아서 쉽게 분쇄되는 단점을 갖는 퇴적암이 대부분이므로 자원 공학적 측면에서 활용가치에 어려움이 있는 것으로 생각된다. 하지만, 천연자원이 부족한 우리나라의 경우 지반자원을 이용한다는 것은 자원의 활용이라는 측면에서 매우 중요하다. 이에 본 연구에서는 대구지역에 다량으로 매장되어 있는 퇴적암을 파쇄한 후 골재로서의 타당성여부를 도로공사 현장에 많이 사용되어지고 있는 화강암 골재와 비교 검토하였다. 결과적으로 각각의 시료가 원암석의 역학적 특성에서는 양호한 결과를 나타내었으나, 골재의 안정성 시험에서는 블랙셰일이 12.9%, 레드셰일이 37.5%로 KS규준에 미달하였다. 콘크리트 동결-융해 시험결과 세 암석이 큰차이를 보이지 않았으나, 레드셰일이 상대적으로 약하게 나타났다. 아스팔트 동결융해 시험에서는 50cycle에서의 안정도값은 레드셰일이 표층과 기층에서 각각 484~561kg, 336~375kg으로 낮은 결과가 나타났다. 이를 통해 셰일의 골재로서 타당성 여부는 추후에 더 연구되어져야 한다.

• 한국도로학회논문집
• /
• 제4권1호
• /
• pp.135-147
• /
• 2002

폼드 아스팔트 공법은 가열 아스팔트 혼합물공법과 비교했을 때 골재와 아스팔트 가열에 필요한 다량의 에너지 소모가 없으며 가열로 인한 이산화탄소가 발생하지 않기 때문에 환경적으로 안정한 공법으로 평가되고 있다. 특히, 아스팔트 재활용 측면에서는 전체 혼합물량의 60$\sim$70% 까지 많은량의 폐 아스팔트를 사용할 수 있기 때문에 폐 아스팔트 재활용에 매우 효과적인 방법이다. 그러나, 폼드 아스팔트 공법은 항상 일정한 양질의 혼합물을 얻기가 어렵고 중(重)교통의 도로에 적용하기에는 문제점이 있다. 본 연구는 골재와 폐 아스팔트를 $100^{\circ}C$ 미만으로 가열하는 새로운 방식인 반 가열공법을 사용했을 때 얻어지는 반 가열 재생 폼드 아스팔트 혼합물의 성능과 반 가열 방식의 타당성에 대한 연구결과이다. 반 가열 방식으로 제조된 재생 폼드 흔합물을 실내에서 코팅율, 크리프시험, 회복탄성시험, 간접인장강도 및 마샬 안정도시험을 실시한 결과 혼합물의 현저한 개선 효과를 나타내었다.

• 한국도로학회논문집
• /
• 제7권3호
• /
• pp.71-78
• /
• 2005

본 연구는 판유리 등의 생산 기초 원료인 소다회 $(Na_2CO_3)$ 생산 과정에서 발생되는 산업 부산물인 부산석회를 아스팔트 혼합물의 채움재로서 재활용 가능성을 검토하여 부산석회의 실질적인 활용 방안을 제시하고자 한다. 이를 위하여 부산석회를 기존의 석회석분 채움재에서 중량 대비 25%, 50%, 75%, 100%로 대체하여 제조한 아스팔트 혼합물에 대해 간접인장강도 시험, 회복탄성계수 시험, 수분 민감성 시험, 반복하중 간접인장 시험, 휠트래킹 시험을 실시하여 부산석회의 채움재 활용 가능성을 파악하였다. 또한 기존 석회석분 채움재를 사용한 아스팔트 혼합물과 소석회 (Hydrated Lime)를 사용한 아스팔트 혼합물의 공학적 특성을 비교 분석하여 부산석회를 재활용한 아스팔트 혼합물의 성능 증진 효과를 평가하고 본 기술의 실용화 가능성을 판단하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권1호
• /
• pp.119-127
• /
• 2014

본 연구에서는 유황폴리머에멀젼 (SPE)을 반강성 포장용 주입재의 아크릴레이트 대체재로서 활용가능성과 성능향상재료 (PVA섬유)에 대한 역학적 성능과 내구성능을 평가하였다. 평가결과, 반강성 포장재의 충전률은 섬유의 혼입률이 증가함에 따라 충전률이 저하되었지만, 모든 배합조건에서 평균 92~94%로 측정되어 목표 성능인 90%를 만족하였다. 반강성 포장재의 마샬안정도 값은 최대 25.4kN으로 측정되어 반강성 포장재의 국내 기준인 5.0 kN 보다 약 4.7배 우수한 것으로 나타났다. 반강성 포장재의 동적안정도 평가결과, 휠 트래킹시험에 따른 변형저항성은 SPE를 대체한 배합조건이 보다 우수하였고, 모든 배합조건에서 45분 이후에는 변형량이 일정한 값에 수렴되어 동적안정도가 31,500회/mm로 동일한 결과를 나타내었다. 파단변형률은 최대 0.53% 정도로 나타나 아스팔트 포장재보다 우수한 강성으로 나타났다. 마모저항성 및 충격저항성 검토결과 모든 배합조건에서 손실률이 9.8~6.0%로 나타나 우수한 내마모성을 나타내었으며, 섬유를 0.3% 혼입한 경우 혼입하지 않은 Plain에 비하여 2.82배의 내충격성 향상을 나타내었다. 역학적성능 및 내구성능 등을 모두 고려하여 볼 때, 이 연구 범위에서는 SPE 대체율 30%가 적정 수준이고, 혼입률 0.3% 범위에서 PVA 섬유를 적용하면 우수한 인성을 갖는 반강성 포장재 제조가 가능 할 것으로 판단된다.

• 한국도로학회논문집
• /
• 제4권3호
• /
• pp.43-49
• /
• 2002

국내 아스팔트 포장은 중차량 교통량의 증가와 겨울철 및 여름철의 온도차이가 크게나는 환경조건하에서 공용되고 있다. 이러한 요인으로 인하여 포장 조기파손의 대부분인 소성변형의 문제점이 심각하며, 이에 대한 개선책으로 개질 아스팔트의 적용에 대한 연구들이 활발하게 진행되고 있다. 그러나, 대부분의 개질 아스팔트의 사용이 표층을 절삭하고 택코팅후 시공되고 있으며, 신설도로의 포장이 아닌 유지보수에서 많이 사용되고 있다. 본 연구는 부산지방국토관리청 산하의 신설국도의 도로포장현장에 개질 아스팔트 혼합물이 적용된 기층 위에 표층용 개질 아스팔트인 SBS PMA 혼합물과 PSMA 혼합물에 대하여 2차로로 200m를 시험 시공하였으며. 나머지 구간은 일반밀입도 아스팔트 혼합물로 시공하였으며, 시공에 사용된 재료에 대한 실내시험을 통한 공용성 및 장기 공용성 평가를 실시하고자 하였다. 실내 실험은 마샬안정도시험, 강도시험과 휠트랙킹 시험을 하여 분석하였으며, 현장의 시험 시공시 온도관리 및 평탄성에 대한 평가를 기초로 향후 장기 공용성 평가와 LCC 분석을 실시하여 가장 경제적인 개질 아스팔트를 평가하여 설계에 반영하고자 한다.

• 대한토목학회논문집
• /
• 제36권6호
• /
• pp.1101-1107
• /
• 2016

폐아스팔트 콘크리트(RAP)의 발생이 증가함에 따라 이를 자원으로 재활용 할 수 있는 재생 아스팔트 콘크리트에 대한 관심이 높아지고 있다. 폐아스팔트 콘크리트를 아스팔트 콘크리트용 순환골재로 사용할 경우 품질저하로 인해 사용량을 제한하거나 재생첨가제를 사용하도록 하고 있다. 본 연구에서는 공정상의 편리성을 위해 재생첨가제가 포함된 중온 재생 아스팔트 바인더(WMRA)를 사용하여 RAP의 사용비율을 50% 까지 증가시킬 수 있는 재생 아스팔트 콘크리트의 실내 공용성능 평가를 수행하였다. 마샬안정도 실험 결과 RAP 30% 사용시에는 WMRA 바인더와 스트레이트 아스팔트 바인더 사용시 큰 차이가 없었으나 RAP 혼합비율이 50%로 늘어날 경우 WMRA 바인더 사용시 흐름값 34.7 (1/10 mm)로 기준을 만족시킬 수 있는 것으로 나타났다. 간접인장강도 실험의 터프니스 계산 결과 RAP 사용비율 50% 일 때 WMRA 바인더 사용시 스트레이트 아스팔트 바인더 사용시에 비해 55% 높은 값을 나타내어 균열저항성이 향상된 것을 알 수 있었다. 또한 반복직접인장실험을 통해 직접적인 균열저항성 비교 결과 WMRA 재생 아스팔트 콘크리트의 피로균열 저항성이 263% 증가하는 것으로 나타나 WMRA 바인더가 RAP 사용비율을 50%까지 높일 수 있어 RAP의 재활용에 효과적인 것으로 나타났다.