• Journal of Ceramic Processing Research
• /
• 제20권4호
• /
• pp.363-371
• /
• 2019

In this study, physical properties of normal concrete, magnetite concrete, EAF concrete, and EAF concrete with added iron powder were evaluated and a feasibility of radiation shielding is also evaluated through irradiation tests against X-rays and gamma-rays. While the unit weight of EAF concrete (3.21 t/㎥) appeared lower than that of magnetite concrete (3.50 t/㎥), the results in compressive strength of EAF concrete were greater than those in magnetite and normal concrete. While the radiation transmission rate of normal concrete reaches 26.0% in the X-ray irradiation test, only 6.0% and 9.0% of transmission rate were observed in magnetite concrete and linear relationship with unit volume weight and radiation shielding. In the gamma-ray irradiation test, the performance of EAF and magnetite concretes appeared to be similar. Through the results on the excellent physical properties and radiation shielding performance a potential applicability of EAF concrete to radiation shielding was verified.

• Advances in environmental research
• /
• 제4권2호
• /
• pp.119-133
• /
• 2015

Water pollution means that the physical, chemical and biological properties of water are changing. In this study, adsorption was chosen as the treatment method because it is an eco-friendly and low cost approach. Magnetite is a magnetic material that can synthesize chemical precipitation. Magnetite was used for the removal of copper in artificial water samples. For this purpose, metal removal from water dependent on the pH, initial concentration of metal, amount of adsorbent and effect of sorption time were investigated. Magnetite was characterized using XRD, SEM and particle size distribution. The copper ions were determined by atomic absorption spectrometry. The adsorption of copper on the magnetite was studied in a batch process, with different aqueous solutions of Cu (II) at concentrations ranging from 10 to $50mg\;l^{-1}$. Optimum conditions for using magnetite were found to be concentration of $10mg\;L^{-1}$, pH: 4.5, contact time: 40 min. Optimum adsorbent was found to be 0.3 gr. Furthermore, adsorption isotherm data were analyzed using the Langmuir and Freundlich equations. The adsorption data fitted well with the Freundlich ($r^2=0.9701$) and Langmuir isotherm ($r^2=0.9711$) equations. Kinetic and equilibrium aspects of the adsorption process were studied. The time-dependent Cu (II) adsorption data were described well by a pseudo-second-order kinetic model.

• 암석학회지
• /
• 제7권2호
• /
• pp.98-110
• /
• 1998

홍천자철광상은 경기변성암복합체의 동북부에 위치하는 흑움노대상편마암내에 렌즈상으로 협재되어 있다. 자철광체는 모암인 석영-장석질대상편마암과는 광물함량에 있어 점이적이다. 자철광체는 자철광석과 자철석대상편마암으로 이루어져 있으며 이들은 자철석의 함량의 차이에 따라 구분되어진다. 이들 암석의 주 구성광물은 자철석, 석영, 사장석과 녹니석이며 각섬석류, 흑운모, 백운모, 인회석, 능철석, 안케라이트, 모나자이트, 돌로마이트 및 방해석 등이 부성분 광물로 산출된다. 각섬석류는 자철광석인 경우 보통각섬석, 리치테라이트(richterite), Mg-아페소나이트(arfvedsonite), Mg-리베카이트(riebekite), 그리고 자철석대상편마암의 경우 보통각섬석에 해당되는 화학조성을 나타내고 있어 이들이 모암의 화학조성과 변성작용시 글로코페인(glaucophane) Na(M4)Al3VI=CaMg 및 리치테라이트 Na(M4)Na(A)=Ca 치환에 의하여 주로 조절되어졌음을 나타낸다. 흑운모는 주로 자철석 대상편마암에 함유되며 앤나이트(annite)의 화학조성을 갖는다. 녹니석은 자철광석의 경우 피크노녹니석(pycnochlorite)에서 다이아반타이트(diabantite)에 이르는, 그리고 자철석대상편마암의 경우 피크노녹니석의 화학조성을 보여 준다. 함탄산염광물은 후기에 도입된 열수용액에 의해 2차로 생성된 것이며 Fe, Mg 및 Mn의 함량비에 따라 능철석, 안케라이트 및 능망간질돌로마이트 등으로 구분된다.

• 자원리싸이클링
• /
• 제2권2호
• /
• pp.9-15
• /
• 1993

본 연구에서는 광양제철소 전로 dust를 사용하여 자력산별 및 심강(분급) 실험을 통해서 산화철(magnetite)를 분리.회수하였다. 그리고 분리.회수한 산화철(magnetite)과 SrCO$_{#}$를 고상방응시켜 Sr-ferrite를 제조하고 그 자기적 특성은 조사하였으며, 이를 통하여 다음과 같은 결론을 얻었다. 1. 광양제철소 제동전로 Ep dust는 대부분 ${\alpha}$-Fe와 magnetite, wustite 등의 철산화물 상태로 존재하며 자력산별과 심강(분급)실험을 행한 결과 magnetite가 주된 구성물질인 산물을 얻을 수 있었다. 2. 전로 dust 정제를 통하여 얻어진 magnetite와 SrCO$_{4}$를 혼합한 후 하소를 행한 결과 magnetite의 산화배소과정 없이도 Sr-ferrite 생성이 가능함을 확인 하였으며, Sr-ferrite 생성 반응은 다음과 같다. I. $SrCO_3$ $+Fe_3$O$_4$+1/2(1-X)$O_2 $longrightarrow$\alpha$ $-Fe _2$$O_3$ $+SrFeO _3$\ulcorner+$CO_2$ II. $5.5\alpha$ $-Fe_2$$O_3$ $+SrFeO_3$\ulcornerlongrightarrowSrFe\ulcornerO\ulcorner+1/2(1/2-X)$O_2$ 3. 1150$^{\circ}C$에서 1시간동안 하소한 후 1250$^{\circ}C$에서 2시간 동안 산결하여 Br=3.75GK, $_{1}$Hc=1.7KOe, (B.H)$_{max}$=2.64 MGOe인 Sr-ferrite 이방성 영구자석을 제조하였다.

• 한국재료학회지
• /
• 제20권6호
• /
• pp.301-306
• /
• 2010

The chemical formula of magnetite ($Fe_3O_4$) is $FeO{\cdot}Fe_2O_3$, t magnetite being composed of divalent ferrous ion and trivalent ferric ion. In this study, the influence of the coexistence of ferrous and ferric ion on the formation of iron oxide was investigated. The effect of the co-precipitation parameters (equivalent ratio and reaction temperature) on the formation of iron oxide was investigated using ferric sulfate, ferrous sulfate and ammonia. The equivalent ratio was varied from 0.1 to 3.0 and the reaction temperature was varied from 25 to 75. The concentration of the three starting solutions was 0.01mole. Jarosite was formed when equivalent ratios were 0.1-0.25 and jarosite, goethite, magnetite were formed when equivalent ratios were 0.25-0.6. Single-phase magnetite was formed when the equivalent ratio was above 0.65. The crystallite size and median particle size of the magnetite decreased when the equivalent ratio was increased from 0.65 to 3.0. However, the crystallite size and median particle size of the magnetite increased when the reaction temperature was increased from $25^{\circ}C$ to $75^{\circ}C$. When ferric and ferrous sulfates were used together, the synthetic conditions to get single phase magnetite became simpler than when ferrous sulfate was used alone because of the co-existence of $Fe^{2+}$ and $Fe^{3+}$ in the solution.

• 자원리싸이클링
• /
• 제9권5호
• /
• pp.28-32
• /
• 2000

본 연구에서는 자성일성분용 흑색 토너의 자성체인 마그네타이트의 새로운 제조방법에 대해 연구를 하였다. 기존의 습식법과는 달리 건식법이라 할 수 있는 분무배소법을 이용하여 마그네타이트를 제조하였다. 이때 제조조건을 달리하며 제조된 마그네타이트분말의 특성을 수입제인 TMB 125와 비교하였다. 질소 분위기하에서 염화제일철과 염화제이철 수용액의 혼합비를 7:3~3:7까지 변화시켜 가면서 제조했을 때 100% 마그네타이트 상을 관찰 할 수 있었고, 염화제일철의 농도가 그보다 크면 FeO의양이 많아지고, 염화제이철의 농도가 크면 $\Gamma-Fe_2O_3$의 양이 많아졌다. 두 염화철의 혼합비가 5:5일때, 분무배소법에 의해 제조된 마그네타이트의 보자력은 110~130Oe, 포화자화는 80~85emu/gdldlT다. 입자의 형태는 불규칙한 구형에 가깝고 입자의 평균크기는 $0.3~0.5\mu\textrm{m}$로 토너용 자성재료로서 매우 적합한 특성을 나타냈다.

• 분석과학
• /
• 제24권4호
• /
• pp.298-303
• /
• 2011

셀레늄은 인체의 필수영양소로써 환경에서 또한 많은 관심을 가지고 있는 원소이다. 셀레늄은 자연수에서 주로 +4가의 selenite ($SeO_3^{-2}$)와 +6가의 selenate ($SeO_4^{2-}$)로 용해되어 있는데, 이들의 독성 및 화학적 성질은 매우 다르다. 따라서 자연수에서 셀레늄의 거동을 이해하기 위해서는 이들 두 화학종을 분리하는 것이 필요하다. 기존에 알려진 알루미나 충전 컬럼과 이온크로마토그래피를 이용한 selenite와 selenate의 분리방법들은 silicate 때문에 자연수에 직접 적용하기가 곤란하였다. 따라서 마그네타이트가 용액의 pH에 따라 selenite와 selenate를 흡착하는 정도가 다르므로 마그네타이트가 충전된 컬럼을 이용하여 이들의 분리를 수행한 결과, 성공적으로 분리할 수 있었다. 아울러 자연수에 존재하는 다른 음이온들 중에서 silicate는 selenite의 흡착을 방해하므로 silicate의 농도를 고려하여 충분한 양의 마그네타이트를 사용하여야만 한다.

• 폴리머
• /
• 제27권1호
• /
• pp.40-45
• /
• 2003

본 연구에서는 $Fe_3O_4$ (magnetite)의 함량 변화와 온도 변화가 NBR/$Fe_3O_4$ 혼합물의 전기걱도도 ($\sigma$)에 미치는 영향을 조사하였다. 최소 최적 혼합비 (percolation threshold, $P_c$) 개념이 본 연구에서 제조한 전도성 입자가 충전된 복합체에 적용되며, 혼합물내 $Fe_3O_4$의 농도가 22%를 초과할 때 $\sigma$가 급격히 증가함을 확인하였다. $\sigma$의 온도 의존성은 $P_c$ 또는 그 이하에서 열적으로 활성화되며, 마그네이트가 NBR 고무의 강화 및 전도성 충전제로서의 역할을 할 수 있음을 조사하였으며, 충전제 함량이 30 phr인 복합체는 실온에서 고전압을 걸어줄 경우 전류는 전압제곱에 비례한 것으로 나타났다. 또한, 50 pk의 마그네이트가 충전된 복합체가 최적의 물리적 가교점으로 인하여 가장 우수한 인장강도와 파단시 신장율을 보였으며 모듈러스가 마그네이트의 강화효과 및 혼합물의 토오크 곡선으로부터 얻은 점도와 관련이 있음을 확인하였다.

• 한국환경과학회지
• /
• 제31권2호
• /
• pp.141-148
• /
• 2022

In this study, the inhibition of ammonia on anaerobic digestion of butyric acid was evaluated and the potential alleviating effects of such ammonia inhibition by the addition of magnetite particles were investigated. Independent anaerobic batch tests fed with butyric acid as a sole organic source were conducted in twenty 60-mL glass bottles with 10 different treatment conditions, comprising ammonia: 0.5, 2.0, 4.0, 6.0, and 7.0 g total ammonia nitrogen (TAN)/L and magnetite particles: 0 mM and 20 mM. The increase in ammonia concentration did not cause significant inhibition on methane yield; however, a significant inhibition on lag time and specific methane production rate was observed. The IC₅₀ in the control treatments (without magnetite addition) was estimated as 6.2654 g TAN/L. A similar inhibition trend was observed in magnetite-added treatments; however, the inhibition effect by ammonia was significantly alleviated in lag time and specific methane production rate when compared to those in the control treatments. The lag time was shortened by 1.6-46.3%, specific methane production rate was improved by 6.0-69.0%. In the magnetite-added treatments, IC₅₀ was estimated as 8.5361 g TAN/L. This study successfully demonstrated the potential of magnetite particles as an enhancer in anaerobic digestion of butyric acid under conditions of ammonia stress.

• 한국환경보건학회지
• /
• 제17권1호
• /
• pp.67-73
• /
• 1991

In this study are investigated to the optimal coagulation conditions and magnetite which was used as coagulation-aids. To accomplish this study, analysis of water quality, removing tubidity and SS from wastewater were measured with jar-tester. The results were obtained that waste water requires 10g magnetite, 100mg aluminum sulfate, and pH valuse was 6~9.