• Journal of Powder Materials
• /
• v.8 no.1
• /
• pp.55-60
• /
• 2001

Mechanical alloying technique was applied to prepare hard magnetic $Sm_2Fe_{17}N_x$ compound powders. Staring from pure Fe and Sm powders, the formation process of hard magnetic $Sm_2Fe_{17}N_x$ phase by mechanical alloying and subsequent solid state reaction was studied. As milled powders were found to consist of Sm-Fe amorphous and $\alpha$-Fe phases in all compositions of $Sm_xFe_{100-x}$(x = 11, 13, 15, 17). The effects of starting composition on the formation of $Sm_2Fe_{17}$ intermetallic compound was investigated by heat treatment of mechanically-alloyed powders. When Sm content was 15 at.％, heat-treated powders consisted of nearly $Sm_2Fe_{17}$ single phase. For preparation of hard magnetic $Sm_2Fe_{17}N_x$ powders, additional nitriding treatment was performed under $N_2$ gas flow at 45$0^{\circ}C$. The increase in the coercivity and remanence was proportional to the nitrogen content which increased drastically at first and then increased gradually as the nitriding time was extended to 3 hours.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.687-689
• /
• 1995

Our team works on mixture of hard magnetic materials. As hard magnetic material we used mixture of powders: melt-spun ribbon Nd-Fe-B, ferrite and Alnico. Their different mixtures are basic material for dielectromagnets under our investigation. Main disadvantage of dielectromagnets with Nd-Fe-B alloy powder as a component is a low corrosion resistance. Protection against corrosion is covering dielectromagnets with metallic or organic coating film. The coating film protects dielectromagnets from free particles on the surface and low resistance for mechanical stresses too. The surface of dielectromagnets prepared from mixture of powders if formed by metallic particles - powder of Nd-Fe-B and Alnico, particles of oxide - powder of ferrite and particles of resin - bonding materials. Team work on technology of laying the metallic coating on dielectromagnets prepared from mixture of mentioned powders. Papers show the results of initial investigation on metallic coating technology. It shows influence of type and used technology of the metallic coating film on magnetic properties of dielectromagnets.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.74-80
• /
• 2020

Synthesis of composite powders for the Fe₂O₃-Zn system by mechanical alloying (MA) has been investigated at room temperature. Optimal milling and heat treatment conditions to obtain soft magnetic composite with fine microstructure were investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that α-Fe/ZnO composite powders in which ZnO is dispersed in α-Fe matrix can be obtained by MA of Fe₂O₃ with Zn for 4 hours. The change in magnetization and coercivity also reflects the details of the solid-state reduction process of hematite by pure metal of Zn during MA. Densification of the MA powders was performed in a spark plasma sintering (SPS) machine at 900 ~ 1,000 ℃ under 60 MPa. Shrinkage change after SPS of sample MA'ed for 5 hrs was significant above 300 ℃ and gradually increased with increasing temperature up to 800 ℃. X-ray diffraction results show that the average grain size of α-Fe in the α-Fe/ZnO composite sintered at 900 ℃ is in the range of 110 nm.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.24-29
• /
• 2005

Nano Fe-6.5wt%Si powders have been synthesized by mechano-chemical process (MCP) for an application of soft magnetic core. Owing to hard and brittle characteristics of Fe-6.5Si nano powders having large surface area, it is very difficult to reach high density more than 70% of theoretical density (~7.4 g/$cm_3$) by cold compaction. To overcome such problem a magnetic pulsed compaction (MPC), which is one of dynamic compaction techniques, was applied. The green density was achieved about 78% (~5.8 g/$cm_3$) by MPC at room temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.124-127
• /
• 1997

The magnetic properties of calcined Sr-ferrites, related to the iron oxides, produced from three different process in steel plants, have been investigated. The powder f.characteristics of iron oxides are much affected on the magnetic properties of calcined Sr-ferrite Powders. It was possible to improve the magnetic property of calcined Sr-ferrites with the iron oxide powders of small size and narrow size distribution. The maximum magnetic properties of calcined Sr-ferrites, showing 69 emu/g of saturation magnetization and 4020 Oe of intrinsic coercivity, are achieved at the following conditions; the iron oxides from the chemirite process(EP), mole ratio of 5.8, and calcination condition of 120$0^{\circ}C$/1hr.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.120-121
• /
• 2006

Magnetic properties of nanostructured materials are affected by the microstructures such as grain size (or particle size), internal strain and crystal structure. Thus, it is necessary to study the synthesis of nanostructured materials to make significant improvements in their magnetic properties. In this study, nanostructured Fe-20at.%Co and Fe-50at.%Co alloy powders were prepared by hydrogen reduction from the two oxide powder mixtures, $Fe_2O_3$ and $Co_3O_4$. Furthermore, the effect of microstructure on the magnetic properties of hydrogen reduced Fe-Co alloy powders was examined using XRD, SEM, TEM, and VSM.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.740-744
• /
• 1995

For the fabrication of a multi-pole anisotropic Sr-ferrite magnet by powder injection molding, it is important to control effectively the alignment of magnetic powders during the injection molding process. The effect of the fluidity of powder/binder mixture on the powder alignment was studied with changing the particle sizes and the volume fraction of Sr-ferrite magnetic powders. The critical volume fraction of Sr-ferrite powders increases from 58 vol.% to 64 vol.% as the mean powder size increases from $0.8\;\mu\textrm{m}$ to $1.2\;\mu\textrm{m}$. A Sr-ferrite powder alignment greater than 80 % is achieved at the conditions of an apparent viscosity lower than 1000 poise at $1600\;sec^{-1}$ shear rate, an applied magnetic field higher than 4 kOe, and a powder volume fraction 8 vol.% lower than the critical fraction. The powder alignment obtained during the injection molding process is not much affected by the subsequent processes of debinding and sintering, showing the magnetic properties of 3.8 kG of remanent flux density and 3.37 kOe of intrinsic coercivity.

• Journal of Magnetics
• /
• v.5 no.4
• /
• pp.111-115
• /
• 2000

Ultrafine $Co_{0.9}Mn_{0.1}Fe_2O_4$ powders have been fabricated by a sol-gel method. Structural and magnetic properties of the powders were investigated by x-ray diffractometry, transmission electron microscopy (TEM), Mossbauer spectroscopy, and vibrating sample magnetometry (VSM). Co-Mn ferrite powders that were fired at and above 773 K contained only a single spinel phase and behaved ferrimagnetically. Powders fired at 673 and 723 K had a spinel structure and were mixed paramagnetic and ferrimagnetic in nature. The magnetic behavior of Co-Mn ferrite powders fired at and above 873 K showed that an increase of the firing temperature yielded a decrease in the coercivity and an increase in the saturation magnetization. The maximum saturation magnetization and coercivity of Co-Mn ferrite powders were 66.7 emu/g and 1523 Oe, respectively, Mossbauer spectra of the powder fired at 923 K were taken at various temperatures ranging from 13 to 850 K. The iron ions.at both A (tetrahedral) and B (octahedral) sites were found to be in ferric high-spin states. The Nel temperature $T_N$ was found to be 850 $\pm$ 2 K. Debye temperatures far A and B sites were found to be $\Theta_A = 757 \pm$5K and $Theta_B = 282 \pm$5 K, respectively.

• Journal of the Korean Ceramic Society
• /
• v.28 no.2
• /
• pp.146-152
• /
• 1991

Ultra fine and homogeneous (Ni0.4Zn0.6)Fe2O4 ferrite powders were prepared by direct-wet, Hydrothermal and coprecipitation methods. In case that specific surface areas of Ni-Zn ferrite powders were over 220㎡/g, 100㎡/g, 30㎡/g individually direct-wet, hydrothermal and coprecipitation methods. The Ni-Zn ferrite magnetic fluids of which Solvents were benzene or kerosene was prepared by making cation surfactant adsorbed on the surface of the (Ni0.4Zn0.6)Fe2O4. The results that measured dispersion and viscosity by making cation surfactant adsorbed were as follows. 1. The adsorption amount of Oleric acid be proportioned the specific surface area of powders. 2. The maximum amount of Oleric acid was 36wt% of dried powders which has 220㎡/g of specific surface area. 3. The stability of fluid by direct-wet synthesis emthod in benzene or kerosene solvent excellent.

• Journal of Powder Materials
• /
• v.26 no.6
• /
• pp.477-480
• /
• 2019

Magnetic 0-D Nd₂Fe₁₄B powders are successfully fabricated using 1-D Nd₂Fe₁₄B nanowire formed by an efficient and facile electrospinning process approach. The synthesized Nd-Fe-B fibers and powders are investigated for their microstructural, crystallographic, and magnetic properties according to a series of subsequent heat treatments. Each heat-treatment process leads to the removal of organic impurities and the formation of the respective oxides/composites of Nd, Fe, and B, resulting in the formation of Nd₂Fe₁₄B powders. Nd-Fe-B fibers exhibit the following magnetic properties: The coercivity (H_ci) of 3260 Oe, a maximum magnetization at 3T of 109.44 emu/g, and a magnetization remanence (M_r) of 44.11 emu/g. This process easily mass produces hard magnetic Nd₂Fe₁₄B powders using a 1-D synthesis process and can be extended to the experimental design of other magnetic materials.