• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.189-195
• /
• 2001

We prepared TMR junctions of NiFe(170 )/CoFe(48 )/Al(13 )-O/CoFe(500 )/Ta(50 ) structure on 2.5$\times$2.5 $\textrm{cm}^2$ area Si/SiO$_2$ substrates in order to investigate the uniformity of magnetoresistance(MR) value using a ICP magnetron sputter. Each layer was deposited by the ICP magnetron sputter and tunnel barrier was formed by the plasma oxidation method. We measured MR ratio and resistance of TMR devices with four-terminal probe system by applying external magnetic field. Although we used ICP sputter which is known as superior to make uniform films, the standard variation of MR ratio was 2.72. The variation was not dependent on the TMR devices location of a substrate. We found that MR ratio and spin-flip field (H's) increased as the resistance increased, which may be caused by local interface irregularity of the insulating layer. The variation of resistance value was 64.19 and MR ratio was 2.72, respectively. Our results imply that to improve the insulating layer fabrication process including annealing process to lessen interface modulation in order to mass produce the TMR devices.

• Journal of the Korean Magnetics Society
• /
• v.13 no.5
• /
• pp.187-192
• /
• 2003

The magnetic and thermal properties of NiFe/[IrMn-Mn]/CoFe with Mn additions have been studied. As-deposited CoFe pinned layers with [IrMn-Mn]layer had dominantly larger exchange biasing field ( $H_{ex}$) and blocking temperature ( $T_{b}$) than those with pure I $r_{22}$M $n_{78}$ used. The $H_{ex}$ and $T_{b}$ improved with 76.8-78.1 vol% Mn, but those of the NiFe/IrMn/CoFe dropped considerably with more addition of 0.6 vol % Mn. The average x-ray diffraction peak ratios of fcc [(111)CoFe, NiFe]/(111)IrM $n_3$ textures for the Mn inserted total vol of 75.5, 77.5, and 79.3% were about 1.4, 0.8, and 0.6, respectively. For the sample without Mn inserted layer, the $H_{ex}$ between IrMn and CoFe layers was almost zero, but it increased to 100 Oe after annealing of 250 $^{\circ}C$. For as-grown two multilayers samples with ultra-thin Mn layers of 77.5 and 78.7 vol %, the $H_{ex}$s were 259 and 150 Oe, respectively. In case of IrMn with 77.5 vol% Mn, the $H_{ex}$ was increased up to 475 Oe at 350 $^{\circ}C$ but decreased to 200 Oe at 450 $^{\circ}C$, respectively. The magnetic properties and thermal stabilities of NiFe/[IrMn-Mn]/CoFe multilayer were enhanced with Mn additions. In applications where higher $H_{ex}$ and $T_{b}$ are required, proper contents of Mn can be used. be used. used.

• Journal of the Korean Magnetics Society
• /
• v.27 no.4
• /
• pp.123-128
• /
• 2017

The magnetic isotropy property from the magnetoresistance (MR) curve and magnetization (MH) loop for the PtMn based spin valve (SV) multilayer films fabricated with different the bottom structure after post-annealing treatment was investigated. The exchange biased coupling field ($H_{ex}$), coercivity ($H_c$), and MR ratio of Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/Ta(4 nm) SV multilayer film without antiferromagnetic PtMn layer are 0 Oe, 25 Oe, and 3.3 %, respectively. MR curve for the Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/PtMn(6 nm)/Ta(4 nm) SV multilayer film showed $H_{ex}=2Oe$, $H_c=316Oe$, and MR (%) = 4.4 % with one butterfly MR curve having by the effect of antiferromagnetic PtMn layer. MR curve for the dualtype Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/PtMn(6 nm)/CoFe(3 nm)/Cu(2.5 nm)/CoFe(6 nm)/Ta(4 nm) SV multilayer film showed $H_c=37.5Oe$ and 386 Oe, MR = 3.5 % and 6.5 % with two butterfly MR curves and square-like hysteresis MH loops. The anisotropy property in CoFe spin valve-PtMn multilayer is neglected by the effects of a very small value of $H_{ex}$ and a very slightly shape magnetic anisotropy. This result is possible to explain the effect of magnetization configuration spin array of the bottom SV film and the top SV film of PtMn layer.

• Resources Recycling
• /
• v.16 no.3 s.77
• /
• pp.19-26
• /
• 2007

The bottom ash of municipal solid waste incineration generated during incineration of municipal solid waste in metropolitan area consists of ceramics, glasses, ferrous materials, combustible materials and food waste and so on. Although the ferrous material was separated by the magnetic separation before the incineration process, of which content accounts for about $3{\sim}11%$ in bottom ash. The formation of a $Fe_3O_4-Fe_2O_3$ double layer(similar to pure Fe) on the iron surface was found during air-annealing in the incinerator at $1000^{\circ}C$. A strong thermal shock, such as that takes place during water-cooling of bottom ash, leads to the breakdown of this oxidation layer, facilitating the degradation of ferrous metals and the formation of corrosion products and it existed as $Fe_2O_3,\;Fe_3O_4\;and\;FeS_2$. So, many problems could occur in the use of bottom ash as an aggregate substitutes in construction field. Therefore, in this study, the separation of ferrous materials from municipal solid waste incineration bottom ash was investigated. In the result, the ferrous product(such as $Fe_2O_3,\;Fe_3O_4,\;FeS_2$ and iron) by magnetic separator at 3800 gauss per total bottom ash(w/w.%) accounted for about 18.7%, and 87.7% of the ferrous product was in the size over 1.18 mm. Also the iron per total bottom ash accounted for about 3.8% and the majority of it was in the size over 1.18 mm.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.437-444
• /
• 2000

We investigated the effect of substrate temperature, chemical composition and post-deposition heat-treatment on the crystal structure and electrical transport of $La_{1-x}Sr_xMnO_{3-{\delta}}$(0.19${\leq}x{\leq}$0.31) thin films. As-prepared $La_{1-x}Sr_xMnO_{3-{\delta}}$ films grown at $500^{\circ}C$ by sputter techniques were found to have the pseudo-tetragonal system(a/c=0.97) and a highly preferential <001> orientation. The films were changed to be of the cubic system by post-deposition annealing at around $900^{\circ}C$. A main target of $La_{0.67}Sr_{0.33}MnO_3$ as well as auxliary targets of $La_{0.3}Sr_{0.7}MnO_3$ ceramics were co-sputtered to control the chemical composition of the film. The Sr content(x) of the film ranged from 0.19 to 0.31, depending on the number of the auxiliary target. When x increased from 0.19 to 0.31, the electrical resistivity of the film decreased and the transition temperature between metal and semiconductor shifted to higher temperature. With a magnetic field of 0.18 T, the magneto-resistance ratio (MR(%) = (${\rho}_o-{\rho}_H/{\rho}_H$) of the $La_{0.69}Sr_{0.31}MnO_3$ thin film was about 390%.