MCMB (mesocarbon microbeads) has been synthesized from coal tar pitch, petroleum pitch and polymer compound generally. But yield of MCMB was low about 20~40 wt% and was not above 50 wt%. Neither MCMB was replaced with natural graphite because of economic performance, refining MCMB, and control of the particle size distribution. This study was performed to elevate yield of MCMB and to develop technique of particle size distribution. As the result, yield of MCMB that was synthesized from coal tar pitch increased more than 60 wt% about raw material and particle size of MCMB was restrained according to control of QI (quinoline insoluble) ingredient in raw pitch, heat treatment temperature and time.

• Journal of the Korean Ceramic Society
• /
• v.38 no.8
• /
• pp.755-760
• /
• 2001

본 연구에서는 카본전극의 표면개질에 따른 리튬이온 전지의 전지특성 변화에 대해서 연구하였다. 즉, mesocarbon microbeads(MCMB) 카본에 에폭시 수지(resin)를 코팅시킴으로서 카본전극 표면에 개질시켰으며, 이에 따른 전극의 전기화학적 특성을 고찰하였다. 에폭시 수지에 의한 카본의 표면코팅은 30%의 H$_2$SO$_4$용액에서 2시간 동안 refluxing한 MCMB를 에폭시 수지를 용해시킨 THF(tetrahydrofuran) 용액에 넣어 혼합함으로써 MCMB 표면에 에폭시 수지가 코팅되도록 하였다. 이렇게 에폭시 수지가 코팅된 MCMB를 약 1000-130$0^{\circ}C$로 열처리하여 고분해능 투과전자현미경으로 관찰한 결과, 코팅층은 비정질 카본 구조를 갖게됨을 알 수 있었다. 또한, 에폭시 수지에 의하여 코팅된 MCMB는 코팅되지 않은 MCMB보다 더 높은 BET 비표면적을 나타내었다. Li/MCMB 전지 cell을 만들어 충방전시험을 수행한 결과, 에폭시 수지에 의하여 코팅된 MCMB로 만든 전극이 더 우수한 충방전 용량과 싸이클 특성을 나타내었다. 에폭시 수지 코팅으로 전극 표면을 개질시킴으로서 전지특성이 개선된 원인에 관하여 에폭시 코팅의 결정구조와 전극계면에서의 부동태 피막(passivation film) 형성과 연계하여 논의하였다.

• Carbon letters
• /
• v.5 no.3
• /
• pp.118-126
• /
• 2004

MCMB (Mesocarbon microbeads) is a kind of anode material for lithium-ion secondary battery. MCMB charge/discharge cycle stability is one of the important criterion at lithium-ion battery operation. In this study, the cycling stability of a lithium-ion secondary battery has been examined. MCMB was made by the direct solvent extraction method. After the MCMB was carbonized and graphitized, the measurement of charge/discharge capacity and efficiency were carried out. In the result, discharge capacity of MCMB in the initial cycle was above 290.0 mAh/g. After the second cycle, efficiency of charge/discharge MCMB was about 98%. These results were similar to the commercial MCMB product.

• Korean Chemical Engineering Research
• /
• v.52 no.1
• /
• pp.52-57
• /
• 2014

The MCMB-$Li_4Ti_5O_{12}$ with core-shell structure was prepared by sol-gel process to improve low cycle capability of MCMB in this study. The electrochemical characteristics were investigated for hybrid capacitor using MCMB-$Li_4Ti_5O_{12}$ as the negative electrode and $LiMn_2O_4$, Active carbon fiber as the positive electrode. The electrochemical behaviors of hybrid capacitor using organic electrolytes ($LiPF_6$, EC/DMC/EMC) were characterized by charge/discharge, cyclic voltammetry, cycle and impedance tests. The hybrid capacitor using MCMB-$Li_4Ti_5O_{12}/LiMn_2O_4$ electrodes had better capacitance than MCMB hybrid systems and was able to deliver a specific energy with 67 Wh/kg at a specific power of 781 W/kg.

• Journal of the Korean Ceramic Society
• /
• v.40 no.11
• /
• pp.1085-1089
• /
• 2003

In the present study effects of SnO$_2$-impregnation on the cell performance of Mesocarbon Microbeads (MCMB) electrode in the Li-ion battery have been investigated. Sn element was impreganted into MCMB powders by the chemical titration, and then post annealed at 250$^{\circ}C$ for 1 h in ambient atmosphere to be transformed as tin-oxide. From the measurement for the cell performance with the half cell in which the SnO$_2$-impregnated MCMB was used as an anode, the SnO$_2$-impregnated MCMB showed higher charge/discharge capacities, higher reversible specific charge capacity and better cycleability than a raw MCMB. As the amount of impregnated SnO$_2$ increased, both reversible and irreversible capacities increased.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.2
• /
• pp.25-29
• /
• 2001

This study examined the effects of carbon surface modification by the epoxy resin coating on the electrochemical performance. The mesocarbon microbeads(MCMB) carbon was surface-modified by coating the epoxy resin and its electrochemical properties as an anode was examined. The surface coating of MCMB was carried out by refluxing the MCMB powders in a dilute H2SO4 solution, and mixing them with the epoxy resin-dissolved tetrahydrofuran(THF) solution. Under heat-treatment of the coated MCMB at the temperature over $1000^{\circ}C$, the epoxy-resin coating layer was converted into amorphous phase which was identified by a high resolution transmission electron microscope (HRTEM). The epoxy resin coated MCMB has higher Brunauer-Emmett-Teller (BET) surface area, higher charge/ discharge capacity and better cycleability than a raw MCMB without coating. The reason for the enhancement of cell performance by the epoxy resin coating were considered as the epoxy resin coating layer plays an important role to be a barrier for carbon reacting with electrolyte and to retard the formation of passivation layer.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.157-160
• /
• 2003

mesocarbon microbeads (MCMB) 카본 분말에 제2상 첨가물로서 소량의 주석산화물$(SnO_2)$을 균일하게 분산 첨가시킴으로서 리튬이차전지의 부극재료로 사용되는 카본 분말의 전지 성능을 개선하였다. 주석산화물 첨가 방법는 전하적정법을 사용하여 Sn을 MCMB 분말에 삽입시키고, 다시 삽입된 Sn이 산화되도록 대기 중에서 $250^{\circ}C$로 1시간동안 후열처리를 하였다. 주석산화물이 첨가된 MCMB 카본분말로 Li/MCMB 전지 cell을 만들어 충방전시험을 수행한 결과, raw MCMB로 만든 전극보다 더 우수한 충방전 용량과 싸이클 특성을 나타내었다. 즉, 주석산화물 삽입에 의해 표면개질된 MCMB 카본 분말은 기존의 MCMB에 비해 높은 초기 방전용량과 충전용량을 나타내었고, 또한 높은 가역 특성과 좋은 cycleability를 보였다. 삽입된 $SnO_2$의 양이 증가할수록 높은 가역용량을 나타내었고 비가역용량 역시 높은 값을 나타내었다.

• 한국전기화학회:학술대회논문집
• /
• 1998.10a
• /
• pp.83-83
• /
• 1998

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.513-516
• /
• 2001

In this study, the properties of MCMB anode Mixed with KCF were evaluated, KCF material was used as not only conducting agent but also active material, The Electirc conductivity of MCMB and KCF were 23.7S/cm and 45.8S/cm. Characteristics of anode with different KCF contents were the best effect at 2wt%. The 1st Ah efficiency of cells were increased with increment of KCF contents. The internal resistance and the rate capability were $1.59{\Omega}$ and 135mAh/g at 2C, The discharge capacity was gradually faded with the charge-discharge cycling to about 50th cycles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.513-516
• /
• 2001

In this study, the properties of MCMB anode Mixed with KCF were evaluated. KCF material was used as not only conducting agent but also active material. The Electric conductivity of MCMB and KCF were 23.7S/cm and 45.8S/cm. Characteristics of anode with different KCF contents were the best effect at 2wt%. The 1st Ah efficiency of cells were increased with increment of KCF contents. The internal resistance and the rate capability were 1.59Ω and 135mAh/g at 2C. The discharge capacity was gradually faded with the charge-discharge cycling to about 50th cycles.