• Magazine of the Korean Society of Agricultural Engineers
• /
• v.20 no.1
• /
• pp.4626-4630
• /
• 1978

The objective of this study is to investigate how the varieties of consistency of fresh concrete influence on the plastic shrinkage in dry condition. The test was conducted under the controlled chamber in which the temperature was kept at 25 ${\pm}$2$^{\circ}C$, the humidity 35 ${\pm}$3%, and the wind velocity 4.0 ${\pm}$0.5m/sec. The results obtained from the test are as follow. 1) The rate of evaporation was highest at 2-3 hour after casting, and decreased gradually. 2) The plastic shrinkage was increased as to the slump values. The shrinkage rate was very highest at 2-4 hour and hardly showed any changes after 6 hour. 3) The recommendation for good cloncrete is that slump value should be as low as possible in construction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.781-784
• /
• 2005

Concrete structures often present volumetrical changes particularly due to thermal and moisture related shrinkages. Volumetric instability is detrimental to the performance and durability of concrete structures because structural elements are usually restrained. These restrained shrinkages develope tensile stresses which often results in cracking in combination with the low fracture resistance of concrete. Early-age defects in high-performance concrete due to thermal and autogenous deformation shorten the life cycle of concrete structures. Thus, it is necessary to examine the behavior .of early-age concrete at the stages of design and construction. The purpose of this study was to propose a shrinkage models of VES-LMC (very-early strength latex-modified concrete) at early-age considering thermal deformation and autogenous shrinkage.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.789-792
• /
• 2005

Development of high-strength concrete and improved durability has brought new opportunities to the construction industry. However, some attention was given to characteristics of such concrete, in particular with respect to their cracking sensitivity. It has been argued and demonstrated experimentally that a low water/cement ratio concrete undergoes shrinkage due to self-desiccation. This so-called autogenous shrinkage cracking is a major concern for concrete durability. One possible method to reduce cracking due to autogenous shrinkage is the addition of expansive additive. Tests conducted by many researches have shown the beneficial effects of addition of expansive for reducing the risk of shrinkage-introduced cracking. This paper aimed at forecasting deformation of high strength cement paste with expansive additive for early age.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.401-402
• /
• 2009

This study prepared super high strength concrete, in which the water.binder ratio is very low, through experimental mixture, and conducted basic research on how super high strength concrete is affected by shrinkage reducing agent that is utilized to inhibit the shrinkage of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.1071-1076
• /
• 2003

Basic creep of concrete during very early ages is an important factor on the behavior of young concrete and a great deal of research has been executed. However, in recent studies, it was revealed that the basic creep measured by sealed concrete was inaccurate, especially for high strength concrete because of autogenous shrinkage at early age. This paper presents the results from experimental study that investigate to explore the effect of autogenous shrinkage in basic creep. More specifically, four different mix proportions were casted and the primary variables were water-cement ratios. Through this research, it was found that the differences between apparent specific creep and real specific creep were remarkable in low water-cement ratio at early age. Therefore, it is recommended to modify existing creep model by considering autogenous shrinkage

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.275-276
• /
• 2018

Ultra high performance concrete(UHPC) represents high early age autogenous shrinkage strain due to its low water-to-binder ratio(W/B) and high fineness admixture usage. It has been reported that fiber can control restrained tensile stress and crack. The purpose of the present study is, therefore, to investigate the autogenous shrinkage as well as mechanical properties including compressive strength, flexural strength and modulus of elasticity on the UHPC with fiber type and pre-mix of binder.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.11a
• /
• pp.1-4
• /
• 2007

Because reinforced concrete structures were being high more and more in recent year, concrete was being demanded high performance of high strength and high fluidity. But various characteristics must be confirmed besides guarantee of demand strength in ultra-high strength concrete. In ultra-high strength concrete, autogenous shrinkage and drying shrinkage grow big because of a low water cement ratio and much quantity of binder. So dangerousness of crack generation grow big in early ages. And ultra-high strength concrete is influenced by use materials more than ordinary strength concrete. In this study we were examined mix design, atuogenous shrinkage and pumpability of ultra-high strength concrete to apply on the ground.

• Structural Engineering and Mechanics
• /
• v.89 no.4
• /
• pp.335-347
• /
• 2024

This study pioneers the exploration of creep and shrinkage behavior in ambient-cured geopolymer concrete (GPC), a vital yet under-researched area in concrete technology. Focusing on the influence of sodium hydroxide (NaOH) solution concentration, the research utilizes low calcium fly ash (Class-F) and alkaline solutions to prepare two sets of GPC. The results show distinct patterns in compressive strength development and dry shrinkage reduction, with a 14 M NaOH solution demonstrating a 26.5% lower dry shrinkage than the 16 M solution. The creep behavior indicated a high initial strain within the first 7 days, significantly influenced by curing conditions and NaOH concentration. This study contributes to the existing knowledge by providing a deeper understanding of the time-dependent properties of GPC, which is crucial for optimizing its performance in structural applications.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.11 no.1
• /
• pp.79-85
• /
• 1987

The purpose of this study was to help the consumer about the care of nonwoven fabrics by investigation of the properties such as launderability. shrinkage, color fastness and strenth. Materials used were two types, soft and stiff, of commercial nonwoven fabrics. Deter-gents used were neutral detergents, synthetic detergents and dry cleaning solutions(perch-toro-ethylene) The results of this study were summerized as follows; 1. Laundering of nonwoven fabrics in low temperature is more ideal as morphological changes by laundering in high temperature were more prominent than that in low temperature. 2. Ironing of nonwoven fabrics wants more attention on environmental temperature as the rate of shrinkage in high temperature was higher than that in low temperature. Neutral detergents are more desirable as the rate of shrinkage of nonwoven fabrics by laundering with synthetic detergents was more prominent than that with neutral deter-gents. The rate of shringkage of nonwoven fabrics was not affected by dry cleanining. 3. Special care is wanted in order to prevent color transfer from non woven fabrics to polyester or wool during dry cleaning or laundering as the color fastness test show that color changes of nonwoven fabrics were not affected, but that color stain was increased on polyester or wool. 4. The strength was affected by composition of fibers and types of nonwoven fabrics, soft or stiff.

• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.295-301
• /
• 2011

Recently, the use of UHPC made of superplasticizers, silica fume, and steel fibers has been increasing worldwide. Although UHPC has a very high strength as well as an excellent durability performance due to its dense microstructures, earlyage cracks may occur due to the high heat of hydration and autogenous shrinkage caused by low W/B and high unit cement content. The early-age shrinkage cracking of UHPC can be controlled by using the shrinkage reducers and expansive admixtures having autogenous shrinkage compensation effect. In this paper, ultrasonic pulse velocity of UHPC containing shrinkage reducers and expansive agents was measured to predict its stiffness change. Also, the effect of shrinkage reducers and expansive agents on the autogenous shinkage of UHPC was investigated through the shrinkage test of UHPC specimens. Furthermore, the material coefficients of autogenous shrinkage prediction model were determined using the autogenous shrinkage values of UHPC with age. Consequently, the test results showed that, by adding shrinkage reducers and expansive agents, the stiffness of UHPC was rapidly developed at early-ages and the autogenous shrinkage was considerably reduced.