• 한국진공학회지
• /
• 제12권S1호
• /
• pp.21-27
• /
• 2003

Micro-arc discharge oxidation (MDO) is a cost-effective plasma electrolytic process which can be used to improve the wear and corrosion resistance of Al-alloy parts by forming a alumina coating on the component surface. However, the MDO coated Al-alloy components often exhibit relatively high friction coefficients and low wear resistance fitted with many counterface materials, additionally, the pitting corrosion for the MDO coated AI-alloy components, especially for a thinner alumina coating, often occurs in atmosphere circumstance due to the porous alumina coats. Therefore, a duplex treatment, combining a MDO coated ahumina thin layer with a TiN coating, prepared by magnetron sputtering (MS), has been investigated. The Vicker's microhardness, pin-on-disc, electrochemical measurement, salt spray, XRD and SEM tests were used to characterize and analyze the treated samples. The work demonstrates that the MDO/MS coated samples have a combination of a very low friction coefficient and good wear resistance as well as corrosion since the micro-holes on alumina coating are partly or fully covered by TiN material.

• 한국해양공학회지
• /
• 제8권2호
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2003년도 하계학술대회 논문집 B
• /
• pp.1081-1083
• /
• 2003

In this paper, a new speed sensorless induction motor scheme which can work at any speed including the zero speed is presented. The proposed method is robust to secondary resistance variations. Simultaneous estimation of speed and secondary resistance are realized based on a feedforward type torque control scheme. The secondary flux with a low frequency sinusoidal waveform is used to help the estimation. Simulations results supported by experiments are given to show the effectiveness of this method.

• Transactions on Electrical and Electronic Materials
• /
• 제18권4호
• /
• pp.195-198
• /
• 2017

This research analyzed the electrical characteristics of an 80 V optimal trench power MOSFET (metal oxide field effect transistor) for mobile applications. The power MOSFET is a fast switching device in fields with low voltage(<100 V) such as mobile application. Moreover, the power MOSFET is a major carrier device that is not minor carrier accumulation when the device is turned off. We performed process and device simulation using TCAD tools such as MEDICI and TSUPREM. The electrical characteristics of the proposed trench gate power MOSFET such as breakdown voltage and on resistance were compared with those of the conventional power MOSFET. Consequently, we obtained breakdown voltage of 100 V and low on resistance of $130m{\Omega}$. The proposed power MOSFET will be used as a switch in batteries of mobile phones and note books.

• 한국전기전자재료학회논문지
• /
• 제20권4호
• /
• pp.352-356
• /
• 2007

The Ni/Cr/Al/Cu (51/41/4/4 wt%) thin films were deposited by using DC magnetron sputtering method for the application of the resistors having low TCR (temperature coefficients of resistance) and high resistivity from the former printed-results[3]. The TCR values measured on the as-deposited thin film resistors were less than ${\pm}10\;ppm/^{\circ}C$ and $-6{\sim}+1\;ppm/^{\circ}C$ after annealing and packaging process. The TCR values were $-3{\sim}1\;ppm/^{\circ}C$ (ratio of variation : about 0.02 %) and $-30{\sim}20\;ppm/^{\circ}C$ (ratio of variation : about $0.5{\sim}1\;%$) for the thermal cycling and PCT (pressure cooker test), respectively. It was confirmed that the reliability properties of the thin film resistor were good for electronic components.

• Journal of Welding and Joining
• /
• 제16권1호
• /
• pp.125-133
• /
• 1998

The effect of volume fraction of Cr carbide phase (Cr CVF) on the low stress abrasion resistance in the chromium-carbide-type high Cr white iron hardfacing weld deposits has been investigated. In order to examine Cr CVF, a series of alloys with varying Cr CVF by changing chromium and carbon contents and the ratio of Cr/C were employed. The alloys were deposited once or twice on a mild steel plate using the self-shielding flux cored arc welding process. The low stress abrasion resistance of the alloys against sands was measured by the Dry Sand/Rubber Wheel Abrasion Test (RWAT). It was shown that hardness and abrasion resistance increased with increasing Cr CVF within the whole test range (Cr CVF : 0.23-0.64). Both primary Cr carbide and eutectic Cr carbide were particularly effective in resisting wear due to their high hardness.

• 한국레이저가공학회지
• /
• 제3권1호
• /
• pp.38-45
• /
• 2000

A 4㎾ RS840 CO2 laser with a powder auto-feeding apparatus has been used to deposit multiple overlapping tracks of Ni-base superalloy on to low carbon steel. It was found that the surface roughness(turbulence) of an overlapped cladding layer decreased with the increase of the overlapping ratio in an oscillating manner. When the overlapping ratio had values of 0.62, the surface turbulence was lowest. Overlapping ratio offer significant potential for improvement of materials surface properties such as corrosion performance and wear resistance. This paper reports that the overlapping ratio shows best corrosion resistance. The tensile residual stresses generated at the higher overlapping ratio( ＞ 0.45) and the element concentration of Fe increased in the surface layer at the lower overlapping ratio( ＜ 0.45) may lead to worse corrosion resistance.

• 한국육종학회지
• /
• 제41권2호
• /
• pp.73-83
• /
• 2009

To investigate genes related to vernalization and cold- resistance in barley (Hordeum vulgare L. cv. Nagaoka), differentially expressed genes were identified from cold-resistant barley leaves with suppression subtractive hybridization (SSH) and Northern blot analyses. The nucleotide and the deduced amino acid sequences of the putative gene products were compared. The bvrn-7 showed high homology(84%) with gene related to vernalization, and the bvrn-3, bvrn-12, bvrn-28, bvrn-29 and bvrn-36 related to cold-resistant genes had high identity of 88~98% with low temperature-induced genes. The results indicate that the 6 genes were closely related to vernalization and cold-resistance during low temperature treatment.

• Computers and Concrete
• /
• 제33권5호
• /
• pp.605-619
• /
• 2024

The increase of reclaimed asphalt pavement (RAP) content in recycled asphalt concrete (RAC) is accompanied by the degradation of low-temperature cracking resistance, which has become an obstacle to the development of RAC. This paper aims to reveal the meso-scale mechanisms of the low-temperature fracture behavior of RAC and provide a theoretical basis for the economical recycling of RAP. For this purpose, micromechanical heterogeneous peridynamic model of RAC was established and validated by comparing three-point bending (TPB) test results against corresponding numerical simulation results of RAC with 50% RAP content. Furthermore, the models with different aggregate shapes (i.e., average aggregates circularity (${\bar{C_r}}=1.00$, 0.75, and 0.50) and RAP content (i.e., 0%, 15%, 30%, 50%, 75%, and 100%) were constructed to investigate the effect of aggregate shape and RAP content on the low-temperature cracking resistance. The results show that peridynamic models can accurately simulate the low-temperature fracture behavior of RAC, with only 2.9% and 13.9% differences from the TPB test in flexural strength and failure strain, respectively. On the meso-scale, the damage in the RAC is mainly controlled by horizontal tensile stress and the stress concentration appears in the interface transition zone (ITZ). Aggregate shape has a significant effect on the low-temperature fracture resistance, i.e., higher aggregate circularity leads to better low-temperature performance. The large number of microcracks generated during the damage evolution process for the peridynamic model with circular aggregates contributes to slowing down the fracture, whereas the severe stress concentration at the corners leads to the fracture of the aggregates with low circularity under lower stress levels. The effect of RAP content below 30% or above 50% is not significant, but a substantial reduction (16.9% in flexural strength and 16.4% in failure strain) is observed between the RAP content of 30% and 50%. This reduction is mainly attributed to the fact that the damage in the ITZ region transfers significantly to the aggregates, especially the RAP aggregates, when the RAP content ranges from 30% to 50%.

• Corrosion Science and Technology
• /
• 제3권1호
• /
• pp.1-5
• /
• 2004

A polarization resistance is generally used to estimate the corrosion rate in the corrosion monitoring by an electrochemical impedance method. When the Faradaic impedance has a time constant due to the reaction intermediate, the electrochemical impedance describes more than one loop on the complex plane. For example, the electrochemical impedance of iron in acidic solution shows capacitive and inductive loops on the complex plane. In this case, the charge transfer resistance and the polarization resistance are determined at middle and low frequency ranges, respectively. Which should be selected for corrosion resistance in corrosion monitoring, the charge transfer resistance or the polarization resistance'? In the present paper, the above-mentioned question is examined theoretically and experimentally.