• Korean Journal of Materials Research
• /
• v.31 no.5
• /
• pp.301-311
• /
• 2021

The conversion of all carbon preforms to dense SiC by liquid infiltration can become a low-cost and reliable method to form SiC-Si composites of complex shape and high density. Reactive sintered silicon carbide (RBSC) is prepared by covering Si powder on top of 0.5-5.0 wt% Y₂O₃-added carbon preforms at 1,450 and 1,500℃ for 2 hours; samples are analyzed to determine densification. Reactive sintering from the Y₂O₃-free carbon preform causes Si to be pushed to one side and cracking defects occur. However, when prepared from the Y₂O₃-added carbon preform, an SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C = SiC reaction, 3C and 6H of SiC, crystalline Si, and Y₂O₃ phases are detected by XRD analysis without the appearance of graphite. As the content of Y₂O₃ in the carbon preform increases, the prepared RBSC accelerates the SiC conversion reaction, increasing the density and decreasing the pores, resulting in densification. The dense RBSC obtained by reaction sintering at 1,500 ℃ for 2 hours from a carbon preform with 2.0 wt% Y₂O₃ added has 0.20 % apparent porosity and 96.9 % relative density.

• Composites Research
• /
• v.30 no.2
• /
• pp.77-83
• /
• 2017

Liquid silicon infiltration, which is one of the methods of producing fiber reinforced ceramic composites, has several advantages such as low fabrication cost and good shape formability. In order to confirm LSI process feasibility of SiC fiber, $SiC_f/SiC$ composites were fabricated using three types of SiC fibers (Tyranno SA, LoxM, Tyranno S) which have different crystallinity and oxygen content. Composites that were fabricated with LSI process were well densified by less than 2% of porosity, but showed an obvious difference in 3-point bending strength according to crystallinity and oxygen content. When composites in LSI process was exposed to a high temperature, crystallization and micro structural changes were occurred in amorphous SiOC phase in SiC fiber. Fiber shrinkage also observed during LSI process that caused from reaction in fiber and between fiber and matrix. These were confirmed with changes of process temperature by SEM, XRD and TEM analysis.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.399-406
• /
• 1994

The SiC/MoSi2 composite material was prepared by infiltration with the mixture of metal Si and MoSi2 into the preform of $\alpha$-SiC and graphite under the vacuum atmosphere of 10-1 torr. The mechanical properties, phases and microstructural characteristics have been investigated by employing an universal testing machine, scanning electron microscope and X-ray diffractometer. With the increase of MoSi2/Si mixing content, the quantity of the residual silicon phase was decreased and the hardness and fracture toughness of composite materials were increased. Also, as the infiltration temperature increased, a lot of fine-grained $\beta$-SiC phases, which were produced from the reaction of graphite and liquid silicon melt, were transformed to $\alpha$-SiC phases.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.710-718
• /
• 1995

The new forming method, Pressureless Powder Packing Forming Method was applied to the manufacturing of reaction sintered SiC. After the experiments of vibratory powder packing and binder infiltration, the abrasive SiC powder of which mean size is 45${\mu}{\textrm}{m}$ was selected to this forming method. Uniform green bodies with porosity of 45% and narrow pore size distribution could be formed by this new forming method. Also, complex or varied cross-sectional shapes could be easily manufactured through the silicone rubber mould used in this forming method. Maximum 15 wt% amorphous carbon was penetrated into green body by multi impregnation-carbonization cycles. And reaction-bonded SiC was manufactured by infiltration of SiC-carbon shaped bodies with liquid silicon.

• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.51-58
• /
• 2021

The conversion of carbon preforms to dense SiC by liquid infiltration is a prospectively low-cost and reliable method of forming SiC-Si composites with complex shapes and high densities. Si powder was coated on top of a 2.0wt.% Y2O3-added carbon preform, and reaction bonded silicon carbide (RBSC) was prepared by infiltrating molten Si at 1,450℃ for 1-8 h. Reactive sintering of the Y2O3-free carbon preform caused Si to be pushed to one side, thereby forming cracking defects. However, when prepared from the Y2O3-added carbon preform, a SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C → SiC reaction at 1,450℃, 3C and 6H SiC phases, crystalline Si, and Y2O3 were generated based on XRD analysis, without the appearance of graphite. The RBSC prepared from the Y2O3-added carbon preform was densified by increasing the density and decreasing the porosity as the holding time increased at 1,450℃. Dense RBSC, which was reaction sintered at 1,450℃ for 4 h from the 2.0wt.% Y2O3-added carbon preform, had an apparent porosity of 0.11% and a relative density of 96.8%.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.485-490
• /
• 2010

In our previous studies, continuous SiC fiber-reinforced SiC-matrix composites ($SiC_f$/SiC) had been fabricated by two different slurry infiltration methods: vacuum infiltration and electrophoretic deposition (EPD). 12 wt% of $Al_2O_3-Y_2O_3$-MgO with respect to SiC powder was used as additives for liquid-phase assisted sintering. After hot pressing at $1750^{\circ}C$ under 20 MPa for 2 h in Ar atmosphere, a high composite density could be achieved for both cases, whereas the problems such as large grain size and non-uniform distribution of liquid phase were observed, which was resulted in the relatively poor mechanical properties of composites. Therefore, efforts have been made to reduce the grain growth during the sintering, including the optimization for hot pressing condition and utilization of spark plasma sintering using a SiC monolith. Based on the results, spark plasma sintering was found to be effective method in decreasing the amount of sintering additive, time and grain growth, which will be explained in comparison to the results of hot pressing in this paper.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.11a
• /
• pp.433-438
• /
• 2009

The main objective of this research effort is to develop the performance of C/SiC composites manufactured by LSI (Liquid Silicon Infiltration) method for solid and liquid rocket propulsion system and ensure the performance analysis technique. The high performance and reliability of C/SiC composite are proved for solid and liquid rocket propulsion system. And the performance analysis technique related to mathematical ablation model is originated.

• Journal of the Korean Ceramic Society
• /
• v.48 no.4
• /
• pp.288-292
• /
• 2011

In this study, we investigated the mechanical behavior of carbon fiber reinforced silicon carbide composites by indentation stress. Relatively porous and dense fiber reinforced ceramic composites were fabricated by liquid silicon infiltration (LSI) process. Densification of fiber composite was controlled by hardening temperature of preform and consecutive LSI process. Load-displacement curves were obtained during indentation of WC sphere on the carbon fiber reinforced silicon carbide composites. The indentation damages at various loads were observed, and the elastic modulus were predicted from unloading curve of load-displacement curve.

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.825-831
• /
• 1995

Reaction-bonded SiC-Si material was fabricated by infiltration of Si melt into a mixture of $\alpha$-SiC and carbon at 175$0^{\circ}C$ under the vacuum atmosphere. Wear properties were analyzed by ball-on-plate wear tester, changing loading weight, sliding speed, sliding time and atmosphere, Results showed that the friction coefficient was decreased with increasing load and sliding velocity. The lowest friction coefficient of 0.05 was obtained under an oil atmosphere. The analysis of the wear surface indicated that the areas wehre particles were pulled out and where free silicon particles worn out preferentially serve as liquid reservoirs to decrease the wear resistance.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1307-1314
• /
• 1994

The aim of this work is to show the way of manufacturing the SiC mechanical seal at the low temperature of 130$0^{\circ}C$ using clay and frit as source of secondary phase. $\alpha$-SiC and $\beta$-SiC powder which showed different distribution of particle were used as starting materials, i.e. average particle size of $\alpha$-SiC was larger than that of $\beta$-SiC. The mechanical and tribological properties of two groups of specimen, i.e. one contained mainly larger $\alpha$-SiC powder and the other mainly fine particle $\beta$-SiC, were measured. The specimen consisted of larger $\alpha$-SiC exhibited lower density flexural strength and wear resistance is comparison with these of sample containning mainly $\beta$-SiC . This difference could be originated from the dependence of capillary force on the particle size. For the larger SiC particle, the liquid phase may not fill the whole pores during sintering, due to low capillary force, whereas the liquid phase can infiltrate into the small ores surrounded small $\beta$-SiC particle. Thus, the course of high flexural strength and high wear resistance of specimen prepared using small particles can be explaced from the easy infiltration of liquid phase.