• Journal of the Korean Ceramic Society
• /
• v.33 no.4
• /
• pp.405-410
• /
• 1996

The partial substitution of LiTaO3 with Al2O3 caused the variation of dielectric properties and a lower melting temperature yielding an easier growth of single crystal. The lattice constants and Raman band broadening were measured for the LiTaO3 solid solution in which the cations of Li+ and Ta5+ were partially substituted by Al3+ cation. The LiTaO3 type limit phases were obtained. ; Li1.15Al0.45Ta0.7O3 for cationic excess Li1.15Al0.45Ta0.7O3 for stoichiometry Li0.85Al0.05TaO3 for cationic deficit. The second phase was formed beyond the solubility limit. The limit phase (Li0.85Al0.05TaO3) in the region of cationic deficit showed the lowest Cuire temperature of 61$0^{\circ}C$ and melting point of 152$0^{\circ}C$ compared to the solid solutions in other regions (TMp=1$650^{\circ}C$, Tc=69$0^{\circ}C$ for LiTaO3)

• Analytical Science and Technology
• /
• v.5 no.1
• /
• pp.115-120
• /
• 1992

The upper limit of solid solution of $Al_2O_3$ in $LiTaO_3$ was investigated using X-ray diffraction and Raman spectroscopy. By substituting cations in $LiTaO_3$ with $Al^{3+}$, the melting temperature was lowed and the ferroelectric properties can be improved. It is easier at lower temperature to fabricate the single crystal used for SAW filters and IR sensors. From the measured lattice constants and Raman band broadening, the solubility limit was X=0.25mol in $Li_{1-X}Al_{2X}Ta{1-X}O_3$, above which $Al_2O_3$ was obsered as a second phase. The Raman band of sintered $LiTaO_3$ was compared with that of the single crystal to see the effect of grain size on the band broadening.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.327-327
• /
• 2007

$LiTaO_3$ single crystal has been studied for surface acoustic wave(SAW) applications. There are two kinds of $LiTaO_3$ single crystals, stoichiometric $LiTaO_3$ (SLT) and congruent $LiTaO_3$ (CLT). These two crystals show quite different dielectrical properties, which might be related with defects in crystals. In this study, we observed the domain boundary of SLT and CLT with scanning nonlinear dielectric microscopy and discussed the stress distribution in $LiTaO_3$ single crystals.

• Proceedings of the KIEE Conference
• /
• 2008.05a
• /
• pp.175-176
• /
• 2008

In this study, the sintering properties and structural properties of the $Mg_5Ta_4O_{15}$cation-deficient perovskite ceramics with $Li_2CO_3$ additions are investigated. The cation-deficient perovskite ceramics are prepared through the solid-state route. According to the XRD pattern, $Mg_4Ta_2O_9$, $MgTa_2O_6$ and $Mg_5Ta_4O_{15}$ phase existed in sintered pure $Mg_5Ta_4O_{15}$ ceramics. With $Li_2CO_3$, additions, the peak intensities of $Mg_4Ta_2O_9$ and $MgTa_2O_6$ phase were reduced. Also, diffraction intensity of the $Mg_5Ta_4O_{15}$ phase was increased with increments of $Li_2CO_3$ additions. The bulk densities were increased with increasing of $Li_2CO_3$ amount and approach the theoretical density of the $Mg_5Ta_4O_{15}$ ceramics, more and more. Microstructure of the $Mg_5Ta_4O_{15}$ ceramics were densified more and more by additions of $Li_2CO_3$. The bulk density of $Mg_5Ta_4O_{15}$+5wt% $Li_2CO_3$ ceramics sintered at $1500^{\circ}C$ for 10 hours was $5.88g/cm^3$.

• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.177-180
• /
• 2005

Ferroelectric $LiTaO_3$ single crystals, grown by the Czochralski method, were thermally treated at temperature $1000^{\circ}C\;and\;1100^{\circ}C$. Electron paramagnetic resonance (EPR) study of stoichiometric $LiTaO_3$ and thermally treated $LiTaO_3$ crystals has been investigated by employing an X-band spectrometer. From the $Fe^{3+}$ EPR spectra, it turned out that there is no change of site location and local site symmetry around $Fe^{3+}$ impurity ion between stoichiometric and thermally treated $LiTaO_3$ single crystals. We confirmed that the ionic state of $Fe^{3+}$ ion changed after thermal treatment. The EPR parameters of $Fe^{3+}$ ion in $LiTaO_3$ single crystals are determined with effective spin Hamiltonian.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06a
• /
• pp.526-526
• /
• 1996

The single crystal of LiTaO3 is well known eletro-optic material as well as the piezoelectric one applied to SAW filter. LiTaO3 has large electro-optic effects, so applied to optical switch, acosto-optic deflector, and optical memory device using photorefractive effects. The crystal growth of SAW-grade LiTaO3 has been studied many aspects, but there is no detail research about optic-grade crystal growth. The conditions of optic-grade LiTaO3 single crystal are as below. The optical transmittance must be over 75%, and axial and radial concentratiom uniformity below 1%. The variation of Curie temperature depending on Li/Ta ratio must be also below 2$^{\circ}C$ and no internal no internal cracks and defects. Because of the limitation of crystal quality, the growing of optic-grade LiTaO3 single crystal is very difficult compared with the growing of SAW-grade. In this research, upper conditions of optic-grade single crystal was investigated after growing of 1 inch diameter and 1.5 inch length LiTaO3 single crystal having no internal cracks and defects using Czochralski method. Curie temperature was determined with DSC and measuring capacitance and lattice parameter was calculated about the grown crystal and ceramic powder samples of various Li/Ta ratio. The result of Tc variation was below 1.2$^{\circ}C$ all over the grown crystal, so it is confirmed that LiTaO3 was grown under congruent melting composition having optical homogeniety. Also, the optical transmittance was about 78%, which was sufficient for optical device.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.193-204
• /
• 1998

The single crystal of the $LiTaO_3$has large electro-optic effects, so it is applied to optical switch, acousto-optic deflector, and optical memory device as hologram using photorefractive effect. In this study, optic-grade undoped $LiTaO_3$and Fe:LiTaO$LiTaO_3$single crystals were grown by the Czochralski method and optical transmission and absorption spectrums were measured in the wavelength of UV-VIS range. The curie temperature was determined with DSC and by measuring capacitance for the grown undoped crystal and ceramic powder samples of various Li/Ta ratio. In case of having a 48.6 mol% $Li_2O$ as a starting Li/Ta ratio, the results of concentration variations were below 0.01 mol% $Li_2O$ all over the crystal, so it was confirmed that $LiTaO_3$single crystals were grown under congruent melting composition having optical homogeneity. The curie temperature of the Fe:$LiTaO_3$crystal was increased with increased with increased doped Fe concentrations;by the ratio of $7.5^{\circ}C$ increase per Fe 0.1 wt%. Also, the optical transmittance was about 78 %, which was sufficient for optical device.

• Journal of the Korean Ceramic Society
• /
• v.39 no.8
• /
• pp.711-714
• /
• 2002

The Ce, Mn: $LiTaO_3$ crystals were grown by Czochralski method in congruent ${\varphi}$3＂ $LiTaO_3$ single crystal growing conditions. Concentrations of Ce and Mn in melt were respectively 0.1 mole%. As-grown crystals were red, transparent and the grown crystals were tested with oxidation/reduction treatment for clor and other properties. Influence of Ce and Mn dopants on $LiTaO_3$ crystal properties was discussed. And the nonlinear optical properties of the Ce, Mn: $LiTaO_3$ crystal are being studied.

• Journal of Magnetics
• /
• v.6 no.3
• /
• pp.77-79
• /
• 2001

The semi-empirical superposition model has been applied to calculate the zero field splitting parameters of $Mn^{2+}$ion in $LiTaO_3$ single crystal, assuming that $Mn^{2+}$ion occupies one of two possible sites: $Li^{l+} \;or\; Ta^{5+}$ site, respectively. The 2nd-order axial zero field splitting parameters are $958\times10^{-4}cm^{-1}\; at\; Li^{1+}$ site and $193\times 10^{-4}cm^{-1} \;at\; Ta^{5+}$ site for $Mn^{2+}$ions. The 4th-order zero field splitting parameters at $Li^{l+} \;and\; Ta^{5+}$ sites are also determined. These calculated zero field splitting parameters are very important to determine the substitutional sites of doped impurity ions in $LiTaO_3$ crystal.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.3 no.2
• /
• pp.99-106
• /
• 1993

A relationship $(T_c = -17.869C^2+1840.2C-46623)$ between Curie Temperature$(T_c)$ and (C), $Li_2O$ mole percent(%) was established from the measurement results of Curie temperature $(T_c)$) analysed by DTA(Differential Thermal Analysis) in the range from 48.50 to 49.00 $Li_2O$ mole %. Congruent melt composition of $LiTaO_3$ single crystal was to be 48.65 $Li_2O$ mole % and its Curie temperature was also determined to be $610{\pm}1^{\circ}C$ from the results of Curie temperature difference, ${\Delta}T (T_{c(Top)}-T{_c(Tail)})$ of Czochralski grown $LiTaO_3$ crystals and the distribution coefficient(k). The k was calculated from $LiO_2$ mole ratio of initial melt to final melt and initial crystal to final crystal in the range from 48.60 to 48.70 $Li_2O$ mole %.