• 한국수소및신에너지학회논문집
• /
• 제13권4호
• /
• pp.259-269
• /
• 2002

A battery based on the lithium/elemental sulfur redox couple has the advantage of high theoretical specific capacity of 1,675 mAh/g-sulfur. However, Li/S battery has bad cyclic durability at room temperature due to sulfur active material loss resulting from lithium polysulfide dissolution. To improve the cycle life of Li/S battery, PEGDME (Poly(ethylene glycol) dimethyl ether) 500 containing 1M LiTFSI salt which has high viscosity was used as electrolyte to retard the polysulfide dissolution and nano-sized $Mg_{0.6}Ni_{0.4}O$ was added to sulfur cathode as additive to adsorb soluble polysulfide within sulfur cathode. From experimental results, the improvement of the capacity and cycle life of Li/S battery was observed( maximum discharge capacity : 1,185 mAh/g-sulfur, C50/C1 = 85 % ). Through the charge-discharge test, we knew that PEGDME 500 played a role of preventing incomplete charge-discharge $behavior^{1,2)$. And then, in sulfur dissolution analysis and rate capability test, we first confirmed that nano-sized $Mg_{0.6}Ni_{0.4}O$ had polysulfide adsorbing effect and catalytic effect of promoting the Li/S redox reaction. In addition, from BET surface area analysis, we also verified that it played the part of increasing the porosity of sulfur cathode.

• 멤브레인
• /
• 제20권3호
• /
• pp.259-266
• /
• 2010

다공성 Poly(propylene) 분리막의 지지 하에 전해질 용액 (EC/DEC 1 : 1 혼합물 내의 $LiPF_6$ 1 M 용액) 내에서 DEGDMA [Di(ethylene glycol) dimethacrylate]의 $70^{\circ}C$ 열중합을 통하여 겔 고분자 전해질(GPE)막이 합성 되었다. 합성된 겔 고분자 전해질막의 이온전도도 및 전기화학적 안정성은 AC 임피던스법 및 CV (cyclic voltametry)법에 의하여 측정 평가하였다. 겔 고분자를 전해질로, 그리고 양극 및 음극으로는 각각 $LiMi_{0.8}Co_{0.2}O_2$ 및 graphite로 이용하여 리튬이온전지(LIB)도 제작하였다. 열중합을 통하여 리튬 이온전지에 적합한 이온전도도($10^{-3}\;S/cm$ 이상) 및 전기화학적 안정성을 보이면서 자체적인 성상을 유지하는 겔 고분자 전해질막을 얻을 수 있었다. 단량체 함량 5%의 전구체로 제작한 겔 고분자 전지는 단량체 함량이 7.0% 및 10.0%인 경우에 비하여 우수한 고율 및 충-방전 효율을 보였다.

• 대한금속재료학회지
• /
• 제48권3호
• /
• pp.262-267
• /
• 2010

$LiNi_{1-x}Mg_xO_2$(x=0, 0.025, 0.05, 0.075, 0.1) samples were synthesized by the solid-state reaction method. The crystal structure was analyzed by X-ray powder diffraction and Rietveld refinement. $LiNi_{1-x}Mg_xO_2$samples give single phases of hexagonal layered structures with a space group of R-3m. The calculated cation-anion distances and angles from the Rietveld refinement were changed with Mg contents in $LiNi_{1-x}Mg_xO_2$. The thicknesses of $NiO_2$ slabs were increased and the distances between the $NiO_2$ slabs were decreased with the increase in Mg contents in the samples. The electrical conductivities of sintered $LiNi_{1-x}Mg_xO_2$ samples were around $10^{-2}$ S/cm at room temperature. The electrochemical performances of $LiNi_{1-x}Mg_xO_2$were evaluated by coin cell test. Compared to $LiNiO_2$, $LiNi_{0.95}Mg_{0.05}O_2$ exhibited improved high-rate capability and cyclability due to the well-ordered layered structure by doping of Mg ion.

• 전기화학회지
• /
• 제15권1호
• /
• pp.48-53
• /
• 2012

리튬 이차전지의 대표적인 분리막인 polyethylene(PE) 분리막은 열에 의한 수축 및 기계적 파열의 단점을 가지고 있다. 본 연구에서는 이러한 기존 PE 분리막을 개선하기 위해 $Si_3N_4$ 코팅 분리막 (SCS, Silicon-nitride Coated Separator)을 제작하였다. $Si_3N_4$ 코팅이 분리막의 열적/기계적 수치안정성, 이온전도도, 및 전지의 출력 특성에 미치는 영향을 알아보았다. $Si_3N_4$ 분말을 polyvinylidene fluoride(PVdF) 결착재를 이용하여 PE 분리막의 한 쪽 면에 10 ${\mu}m$ 두께로 코팅하여 SCS를 제작하였다. SCS는 PE 분리막보다 $100{\sim}150^{\circ}C$에서 우수한 열적안정성을 나타냈으며, 특히 $150^{\circ}C$에서의 수축률은 10~20% 감소를 보였다. 또한, SCS의 인장강도는 PE 분리막에 비해 증가를 보였다. SCS는 PE 분리막에 비해 다소 낮은 이온 전도도를 보였지만, $LiCoO_2$/Li 코인전지의 C-rate(0.2~3C) 특성 평가에서는 유사한 결과를 보였다.

• 한국수소및신에너지학회논문집
• /
• 제28권2호
• /
• pp.156-165
• /
• 2017

This study quantitatively assessed the environmental impacts of fuel cell (FC) systems by performing life cycle assessment (LCA) and analyzed their energy efficiencies based on energy return on investment (EROI) and electrical energy stored on investment (ESOI). Molten carbonate fuel cell (MCFC) system and polymer electrolyte membrane fuel cell (PEMFC) system were selected as the fuel cell systems. Five different paths to produce hydrogen ($H_2$) as fuel such as natural gas steam reforming (NGSR), centralized naptha SR (NSR(C)), NSR station (NSR(S)), liquified petroleum gas SR (LPGSR), water electrolysis (WE) were each applied to the FCs. The environmental impacts and the energy efficiencies of the FCs were compared with rechargeable batteries such as $LiFePO_4$ (LFP) and Nickel-metal hydride (Ni-MH). The LCA results show that MCFC_NSR(C) and PEMFC_NSR(C) have the lowest global warming potential (GWP) with 6.23E-02 kg $CO_2$ eq./MJ electricity and 6.84E-02 kg $CO_2$ eq./MJ electricity, respectively. For the impact category of abiotic resource depletion potential (ADP), MCFC_NGSR(S) and PEMFC_NGSR(S) show the lowest impacts of 7.42E-01 g Sb eq./MJ electricity and 7.19E-01 g Sb eq./MJ electricity, respectively. And, the energy efficiencies of the FCs are higher than those of the rechargeable batteries except for the case of hydrogen produced by WE.

• 전기화학회지
• /
• 제12권2호
• /
• pp.155-161
• /
• 2009

리튬 2차전지는 휴대용 전자기기의 전원으로 사용되어 왔다. 최근 하이브리드 자동차, 전기자동차의 에너지 저장매체로써 적용으로 인해 시장 확대가 기대되고 있다. 양극 활물질은 리튬2차전지의 성능, 수명, 용량을 결정하는 물질이며, 급증하는 시장의 수요에 따라 양극 활물질을 대량으로 생산할 수 있는 기술을 개발하는 것이 시급하다. 본 연구에서 실제 양극 활물질($LiCoO_2$) 생산라인에서 가동 중인 소성로를 3D 모델링하였고, 수치적 해석을 통해 소성로 내부의 온도와 유동의 방향, 화학적 거동을 밝혀내었다. 결과로써, 생산량 증가로 인해 소성로에서 생성되는 $CO_2$ 농도가 증가하며 정체되는 지점을 확인하였고, TGA-DSC 실험을 통해 $CO_2$가 몰분율 15%이상에선 $LiCoO_2$의 적절한 형성에 영향을 주는 현상을 확인하였다. 또한 소성로의 형상변화와 공정조건의 변화를 통해 문제되는 $CO_2$를 원활히 배출할 수 있는 해결책을 제안하였다.

• 한국산학기술학회논문지
• /
• 제22권2호
• /
• pp.789-793
• /
• 2021

리튬이차전지는 매우 우수한 차세대 에너지 저장장치이다. 하지만, 전해액 내에 존재하는 미량의 수분과 리튬염의 분해에 의해 충방전이 진행됨에 따라 용량이 감소하게 되고, 고온인 경우 이 현상은 더욱 악화된다. 많은 연구자들이 싸이클 성능향상을 위한 연구는 활발히 진행되고 있지만, 근본적인 문제인 수분 및 HF를 제거하는 연구는 많이 진행되고 있지 않다. 본 연구에서는 이를 해결하기위해, 수분 및 HF가 흡착이 가능한 실란계 물질을 분리막에 도입하였다. 우선 아미노실란(APTES, 3-Aminopropyltriethoxysilane)이 코팅된 실리카를 제조 후 에폭시 실란(GPTMS, (3-Glycidyloxypropyl)trimethoxysilane)과 반응을 시켜 표면에 실란이 위치한 실리카를 합성하였다. 실란이 코팅된 세라믹 코팅층을 다공성 폴리에틸렌에 코팅을 하여 세라믹 코팅된 분리막을 제조하였다. FT-IR, TEM을 이용하여 실란이 코팅된 세라믹층의 성분분석, 형상분석을 실시하였으며, 분리막의 세라믹층을 확인하기위해 SEM 분석을 실시하였다. 또한, 제조된 분리막의 60 ℃ 싸이클 성능을 평가하기위해 LMO 반쪽 전지를 제조하였다. GPTMS가 도입된 분리막은 안정적인 고온 싸이클 성능을 보였으며, 이러한 기술은 향후 고온 싸이클 성능을 개선하기 위한 하나의 방법이 될 수 있을 것이다.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권2호
• /
• pp.53-61
• /
• 2004

Characteristics of half cells of graphite/lithium and LiCoO$_2$/lithium, and full cells of graphite/LiCoO$_2$/ were analyzed by the use of GISOC(the gradual increasing of the state of charge). GISOC analyses generated IIE(the initial intercalation efficiency), which represents lithium intercalation property of the electrode material, and IIC$_{s}$(the initial irreversible capacity by the surface), which represents irreversible reaction between the electrode surface and electrolyte. Linear-fit range of graphite and LiCo/O$_2$electrodes were respectively 370 and 150 mAh/g based on material weight. IIE of graphite and LiCo/O$_2$electrodes were respectively 93∼94 % and 94∼95 %, and IICs of graphite and LiCo/O$_2$electrodes were 15∼17 mAH/g and 0.3∼1.7 mAh/g, respectively. IIE of graphite/LiCo/O$_2$full cell for GX25 and DJG311 as graphite showed 89∼90 %, which IIE value was lower than IIE of half cell of the cathode and the anode. Parameters of IIE and IIC$_{s}$ can also be used to represent not only half cell but also full cell. The characteristics of the full cell can be simulated through the correlative interpretation of potential profile, IIE, and IIC$_{s}$ of half cells.cells.

• 전기화학회지
• /
• 제3권4호
• /
• pp.219-223
• /
• 2000

구리-바나듐 산화물 양극을 이용하여 $(Cu_{0.5}V_2O_5)$으로 구성된 전 고상의 리튬이차박막전지를 제작하였다. 구리-바나듐 산화물 박막은 reactive DC magnetron sputtering을 이용하여 co-sputtering에 의해 제조하였고 Lipon고체전해질은 순수한 질소 분위기 하에서 RF 스퍼터링으로 제조하였다. XRD분석을 통해 구리-바나듐 산화물 박막이 비정질임을 확인하였고, EC:DMC(1:1 in IM $LiPF_5$)액체전해질을 사용한 반전지 구조에서 그 전기화학적 특성을 고찰하였다. Lipon고체전해질의 이온전도도는 $25^{\circ}C$에서 $1.02\times10^{-6}S/cm$를 나타내었고 전고상 박막전지는 $1.5V\~3.6V$의 전압구간, $50{\mu}A/cm^2$의 전류밀도에서 500싸이클까지 약 $50{\mu}Ah/cm^2{\mu}m$의 방전용량을 유지하였다

• 청정기술
• /
• 제29권2호
• /
• pp.87-94
• /
• 2023

폐리튬계 이차전지로부터 유가금속을 회수하는 것은 한정된 지구자원의 활용 측면에서 매우 중요하다. 최근 자동차의 전지로 많이 사용하고 있는 LiFePO₄ 전지 양극재 성분에는 리튬이 약 5.2% 함유되어 있으며, 사용 후 전지에서 리튬 재활용을 통하여 다시 전지의 원료로써 사용할 수 있다. 본 연구에서는 폐LiFePO₄ 양극재 분말에 함유된 리튬을 선택적으로 침출하기 위하여 일반적으로 많이 사용하고 있는 무기산의 일종인 저농도 황산을 이용하였다. 그리고 각 성분의 침출율 및 분리효율을 비교·분석을 위하여 침출 시 광액농도를 변수로 2 스텝 침출 공정을 적용하여 최적의 침출조건을 도출하고자 하였다. 광액농도를 변수로 침출 시 철 및 인 성분이 거의 침출되지 않는 200 g/L의 광액농도 조건에서는 타 조건과 분리 효율이 약 200배 이상 높은 것으로 확인되었다. 이에 리튬의 선택적 침출 및 회수에 있어서 침출조건을 최적화하였다.