• Macromolecular Research
• /
• 제14권1호
• /
• pp.38-44
• /
• 2006

Vacuum deposited copper phthalocyanine (CuPc) was placed as a thin interlayer between indium tin oxide (ITO) electrode and a hole transporting layer (HTL) in a multi-layered, organic, light-emitting diode (OLEOs). The well-stacked CuPc layer increased the stability and efficiency of the devices. Thermal annealing after CuPc deposition and magnetic field treatment during CuPc deposition were performed to obtain a stacked-CuPc layer; the former increased the stacking density of the CuPc molecules and the alignment of the CuPc film. Thermal annealing at about 100$^{circ}C$ increased the current flow through the CuPc layer by over 25$\%$. Surface roughness decreased from 4.12 to 3.65 nm and spikes were lowered at the film surface as well. However, magnetic field treatment during deposition was less effective than thermal treatment. Eventually, a higher luminescence at a given voltage was obtained when a thermally-annealed CuPc layer was placed in the present, multi-layered, ITO/CuPc/NPD/Alq3/LiF/AI devices. Thermal annealing at about 100$^{circ}C$ for 3 h produced the most efficient, multi-layered EL devices in the present study.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2006년도 전기학술대회논문집
• /
• pp.23-24
• /
• 2006

The International Maritime Organization announced that the regulation of nitrogen oxide put into force for vessels constructed after 2000 from May, 2005 as agenda is satisfied on May, 2004. A honeycomb-typed Pillared Inter-Layered Clay(PILC) catalyst was developed for do-NOx SCR system in 2004. This catalyst has been applied to 9H25/33 engine that is one of the main diesel engines in Engine Machinery Division of the Hyundai Heavy Industries CO., LTD. In addition, we have tried to develop better catalysts in the aspects of easy synthetic method and performance.

• 전자공학회논문지A
• /
• 제30A권1호
• /
• pp.44-50
• /
• 1993

In an attempt to improve the electrical characteristics of tantalum pentoxide dielectric film, silicon substrate was reacted with a nitrogen plasma to form a silicon nitride of 50.angs. and then tantalum pentoxide thin films were formed by reactive sputtering in the same chamber. Breakdown field and leakage current density were measured to be 2.9 MV/cm and 9${\times}10^{8}\;A/cm^{2}$ respectively in these films whose thickness was about 180.angs.. With annealing at rectangular waveguides with a slant grid are investigated here. In particular, 900.deg. C in oxygen ambient for 100 minutes, breakdown field and leakage current density were improved to be 4.8 MV/cm and 1.61.6${\times}10^{8}\;A/cm^{2}$ respectively. It turned out that the electrical characteristics could also be improved by oxygen plasma post-treatment and the conduction mechanism at high electric field proved to be Schottky emission in these double-layered films.

• 대한화학회지
• /
• 제49권6호
• /
• pp.623-627
• /
• 2005

• Bulletin of the Korean Chemical Society
• /
• 제17권8호
• /
• pp.730-735
• /
• 1996

The layered perovskite oxide, KSr2Nb3O10, was synthesized. The interlayer potassium cations were readily exchanged by protons in hydrochloric acid solution to give the protonation compound, HSr2Nb3O10·0.5H2O. The intercalation compounds, [NH3(CH2)nNH3]xSr2Nb3O10, were also obtained by acid-base reactions between the protonation compound and organic bases, 1,n-alkyldiamines. The interlayer distances in the intercalation compounds were linearly increased with the increase of the number of carbon (Δc/Δn=1.05 Å) in 1,n-alkyldiamines. The intercalated alkyldiammonium ions formed a paraffin-like monolayer with average tilting angle (θ) of ca. 56°. The intercalation reactions occurred stoichiometrically. The thermal decomposition process of the intercalation compounds showed distinct three steps due to the desorption of hydrated water, the decomposition of organic moiety, and the decomposition of Sr-related compounds.

• 한국전기전자재료학회논문지
• /
• 제31권2호
• /
• pp.85-89
• /
• 2018

In this study, functional transparent conducting layers were investigated for Si-based photoelectric applications. Double transparent conductive oxide (TCO) films were deposited on a Si substrate in the sequence of indium tin oxide (ITO) followed by aluminum-doped zinc oxide (AZO). First, we observed that the conductivity and transparency of AZO dominate the overall performance of the double TCO layers. Secondly, the double layered TCO film (consisting of AZO/ITO) deposited by sputtering was compared to a AZO-only film in terms of their optical and electrical properties. We prepared three different AZO films: ITO:3min/AZO:10min, ITO:5min/AZO:7min, and ITO:7min/AZO:4min. The results show that the optical properties (transmittance, absorbance, and reflection) can be controlled by the film composition. This may provide a significant pathway for the manipulation of the optical and electrical properties of photoelectric devices.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 추계학술대회 초록집
• /
• pp.84.1-84.1
• /
• 2011

Typical solid oxide fuel cells (SOFCs) have limited applications because they operate at high temperature due to low ionic conductivity of electrolyte. Thin film solid oxide fuel cell with yttria stabilized zirconia (YSZ) electrolyte is developed to decrease operating temperature. Pt/YSZ/Pt thin film SOFC was fabricated on anodic aluminum oxide (AAO). The crystalline structure of YSZ electrolyte by sputter is heavily depends on the roughness of porous Pt layer, which results in pinholes. To deposit YSZ electrolyte without pinholes and electrical shortage, it is necessary to deposit smoother and denser layer between Pt anode layer and YSZ layer by sputter. Atomic Layer Deposition (ALD) technique is used to deposit pre-YSZ layer, and it improved electrolyte quality. 300nm thick Bi-layered YSZ electrolyte was successfully deposited without electrical shortage.

• 한국분말재료학회지
• /
• 제24권2호
• /
• pp.87-95
• /
• 2017

Lithium silicate, a lithium-ion conducting ceramic, is coated on a layer-structured lithium nickel manganese oxide ($LiNi_{0.7}Mn_{0.3}O_2$). Residual lithium compounds ($Li_2CO_3$ and LiOH) on the surface of the cathode material and $SiO_2$ derived from tetraethylorthosilicate are used as lithium and silicon sources, respectively. Powder X-ray diffraction and scanning electron microscopy with energy-dispersive spectroscopy analyses show that lithium silicate is coated uniformly on the cathode particles. Charge and discharge tests of the samples show that the coating can enhance the rate capability and cycle life performance. The improvements are attributed to the reduced interfacial resistance originating from suppression of solid-electrolyte interface (SEI) formation and dissolution of Ni and Mn due to the coating. An X-ray photoelectron spectroscopy study of the cycled electrodes shows that nickel oxide and manganese oxide particles are formed on the surface of the electrode and that greater decomposition of the electrolyte occurs for the bare sample, which confirms the assumption that SEI formation and Ni and Mn dissolution can be reduced using the coating process.

• 한국재료학회지
• /
• 제14권5호
• /
• pp.368-373
• /
• 2004

To improve the conventional cathode-supported tubular solid oxide fuel cell (SOFC) from the viewpoint of low cell power density, expensive fabrication process and high operation temperature, the anode-supported tubular solid oxide fuel cell was investigated. The anode tube of Ni-8mol% $Y_2$O$_3$-stabilized $ZrO_2$ (8YSZ) was manufactured by extrusion process, and, the electrolyte of 8YSZ and the multi-layered cathode of $LaSrMnO_3$(LSM)ILSM-YSZ composite/$LaSrCoFeO_3$ were coated on the surface of the anode tube by slurry dip coating process, subsequently. Their cell performances were examined under gases of humidified hydrogen with 3% water and air. In the thermal cycle condition of heating and cooling rates with $3.33^{\circ}C$/min, the anode-supported tubular cell showed an excellent resistance as compared with the electrolyte-supported planar cell. The optimum hydrogen flow rate was evaluated and the air preheating increased the cell performance due to the increased gas temperature inside the cell. In long-term stability test, the single cell indicated a stable performance of 300 mA/$\textrm{cm}^2$ at 0.85 V for 255 hr.

• 멤브레인
• /
• 제29권3호
• /
• pp.130-139
• /
• 2019

그래핀, 제올라이트, metal-organic frameworks (MOF)s 등 다양한 나노 소재를 이차원 나노쉬트 형태로 제조하고, 이를 이용한 초박막 고성능 분리막을 개발하고자 하는 연구가 활발히 진행되고 있다. 특히, 산화그래핀의 경우, 2000년대 초반에 관련 연구가 시작된 이후, 다양한 합성 및 박막 코팅 기술이 축적되어 있어 빠른 속도로 분리막 분야에 응용되고 있다. 다층으로 적층된 산화그래핀 박막은 층간 거리를 조절함에 따라 물리적 거름막으로 작용할 수 있으며, 또한 표면의 기능기 및 삽입된 물질과 거르는 물질 간의 상호작용을 제어함에 따라 다양한 물질의 선택적 분리가 가능하다. 본 총설에서는 산화그래핀의 나노여과막 응용분야에 관하여 중점적으로 다루고자 한다. 본고에서는, 다양한 용매 내에서 산화그래핀 박막의 분리 기작 및 성능에 영향을 미치는 핵심 요소들에 대해 요약하였으며, 그 외 산화그래핀 기반 분리막의 실질적인 상용화에 필요한 핵심 기술요소 및 개발 동향에 대하여 논하고자 한다.