• Journal of the Korean Wood Science and Technology
• /
• v.15 no.4
• /
• pp.12-17
• /
• 1987

To extract arabinogalactan from larch (Larix Leptolepis), chips immersed with water(20-$90^{\circ}C$) for 1hr, were defiberized by refiner. The liquors were recovered and purified to pure arabinogalactan by ion exchange resin(IRC-50 a. IR-45) or MgO. Additionally the optimal condition in purification with MgO was also investigated. 1. The amounts of solids(crude sugars) and pure arabinogalctan in solids are 8.6-11.3% and 7.3-8.5%(raw material = 100), respectively. 2. Phenolic materials in crude sugars are removed up to 96-89% by ion exchange resin and 94-88% by MgO, while recovery yields of pure arabinogalactan are 81-75% on purification with ion exchange resin and 91-87% on purification with MgO. 3. The optimal conditions of purification with MgO are the addition of 35mg MgO/0.5g of crude sugars, 45 minutes at $70^{\circ}C$, or 25 mg MgO, 30 minutes at $85^{\circ}C$.

• Journal of the Korean Society of Safety
• /
• v.12 no.3
• /
• pp.90-96
• /
• 1997

This paper was concerned with temperature aspect in the smoldering time of the accumulated each saw-dust sample of larch, oregon, aromatic trees which was formed with heaped cone-shape. The smoldering time and temperature of each sample was measured under the wind velocity of 0.10~0.15 m/s and circumstance relative humidity of 60%. As a result, the very lowest heat beginning temperature was detected in aromatic. The effective smoldering phenomena in the sample were detected when the larch saw-dust of [-20+40mesh] and the aromatic saw-dust of [-40+50mesh, -50+60mesh]. Finally the larger a particle size of saw-dust was the better a smoldering time was short. Also, it showed more increasing temperature above $70^{\circ}C$in the smoldering reaction.

• Journal of Plant Biotechnology
• /
• v.42 no.3
• /
• pp.223-227
• /
• 2015

Embryogenic callus (EC) was created from mature embryos of Larix kaempferi. With the mature embryos, keeping the culture in dark conditions throughout the experiment (38.2%) seemed to give better results than exposing them to 16 h light ($25{\mu}Em^{-2}s^{-1}$) for the first week (21.9%). EC was obtained most frequently from Quoirin and Lepoivre (LP) mediums with 1.0 mg/L 4-amino-3,5,6-trichloropicolinic acid (Picloram), plus 1.0 mg/L benzyladenine (BA) (62.8%) or Litvay's medium (LM) containing 1.0 mg/L p-chlorophenoxyacetic acid (pCPA) plus 1.0 mg/L BA (62.8%) treatment. In both cases, best results were obtained when zygotic embryos were cultured in darkness. As for the effective sucrose concentration on initiation of EC, 29.2 mM sucrose (38.6%) gave the best results.

• Journal of Korea Foresty Energy
• /
• v.22 no.1
• /
• pp.44-48
• /
• 2003

Flexural properties were investigated on clear specimens made from small diameter thinned trees of pitch pine (Pinus rigida Mill.), Japanese red pine (Pinus densiflora Sieb. et Zucc), Japanese larch (Larix kaempferi Carr.), and sawtooth oak (Quercus acutissima Carr.). MOR and MOE values of small clear specimen were depended on the species. The highest density of sawtooth oak shows the highest values of MOR and MOE. However, the lowest density of Japanese larch shows the lowest values of MOR. It was also shown that flexural properties could be predicted by stress wave MOE, since the correlations between stress wave MOE and flexural properties were relatively good.

• Journal of the Korea Furniture Society
• /
• v.19 no.4
• /
• pp.229-234
• /
• 2008

In a previous study, it was revealed that three major softwoods, Japanese pine, Korean pine and Japanese larch, heat-treated at $220^{\circ}C$, could produce high quality dark-colored boards. It is known that heat treatment decreases the hygroscopicity of wood. The hygroscopicity of major domestic softwoods and hardwoods heat-treated at $220^{\circ}C$ was investigated by a saturated salt solution method and compared with that of black and white charcoals. Equilibrium moisture contents of wood decreased with the increase of heat treatment time. Isotherm shapes of wood species were different from those of charcoals. Heat treatment decreases the equilibrium moisture contents of black locust more than those of Korean pine and Japanese larch. It was found that surface hardness of wood is improved by heat treatment to a certain extent, but a longer heat treatment causes thermal degradation, resulting in the decrease of the surface hardness.

• Journal of the Korean Wood Science and Technology
• /
• v.9 no.2
• /
• pp.31-35
• /
• 1981

This study was carried out to investigate the properties of hardboard made from fire killed larch tree and also effects of standing period after killed by fire. The results are as follows; 1. There were no effects on hardboard properties among the standing period differences after killed by fire within about 2 years. 2. Specific gravities, moisture contents, water absorptions of the boards from dead trees have no differences compared with those of sound wood. 3. Bending strengths of the boards from dead trees we re decreased in the range of 24-28% of the boards from sound wood.

• Journal of the Korean Wood Science and Technology
• /
• v.21 no.2
• /
• pp.67-72
• /
• 1993

Hot water extractives of sawdust/particle from domestic and foreign wood species, which were composed of pitch pine, Korean pine, larch, Italy poplar, acacia and oak as Korean wood species, Malaysian oil palm and German spruce were quantitatively analyzed with thin layer chromatography. Sugar components of saccharose, galactose, glucose, fructose and arabinose were contained in these wood species. It was assumed that arabinose and glucose are major inhibitory components against cement hardening in larch and oil palm, respectively, since both species contain a large amount of each sugar. In contrast, fructose might not influence so badly on a cement hardening, when considering that fructose was contained much in Italy poplar with a good cement hardening character. Galactose was a minor component.

• Journal of the Korean Wood Science and Technology
• /
• v.51 no.1
• /
• pp.14-22
• /
• 2023

Economical use of larix (larch) boards (grade 3) in industries is lower than that of imported hardwood; thus, studies have been conducted toward performance improvement of larix boards. Herein, flexural modulus of larix board samples laminated with wood adhesives polyurethane resins, poly (vinyl acetate) resins, phenol-resorcinol-formaldehyde resins, melamine-formaldehyde resins, and urea-formaldehyde resins was compared with that of the samples bonded with adhesives reinforced with mesh-type basalt fibers. Moreover, the flexural moduli of the laminated samples bonded by mesh-type basalt fibers were compared with those of reinforced samples. The results showed that boards laminated with polyurethane and urea-formaldehyde resin adhesives had higher flexural modulus than those without the lamination. In particular, the increase in the flexural modulus was relatively significant for the 2- and 3-ply board structures laminated with polyurethane adhesives compared to those with reinforcement. The 3-ply board structure without reinforcement had the highest flexural modulus when the urea-formaldehyde resin adhesive was used.

• Proceedings of the Korea Forestry Energy Research Society Conference
• /
• 1999.04a
• /
• pp.41-42
• /
• 1999

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.1
• /
• pp.36-44
• /
• 2008

It is necessary to assess wood quality and strength of the clear specimens from used members in old wooden structures for the reuse of old members on the same structure or a new structure. Wood species classification by microscope observation of each wood member that was used in truss cord and temple, and several physical and strength tests by the specification of present KS standards were conducted to compare with some references. From the comparison of strengths with references, Korean larch gives relatively better wood quality and mechanical properties than other wood species. No significant deterioration of cell wall was found by microscopic observation for the sound wood part that was selected visually. Tensile specimens with 3 mm in thickness on the middle span showed greater strength than 5 mm thick specimens, which explains that dimension of tensile specimen should be examined for evaluating precise tensile strength properties. Other tests, compression, shear, and bending, are adoptable for each strength properties. Test methods for the evaluation of basic strengths and fastener connections for old wood species should be further examined.