• Magazine of the Korea Concrete Institute
• /
• v.8 no.2
• /
• pp.129-138
• /
• 1996

Localization of concrete is a phenomenon such that the deformation of concrete is localized in finite region with softening behavior and it governs ultimate load of concrete. In this Paper, concrete under strain localization was modeled with localization region and non-localization region and lc~calization behavior was formulated based on averaging concept of heterogeneous material. By using the formulation, the localization phenomena of concrete under uniaxial loadings were well predicted. The analytical results show that size of localization region of concrete under uniaxial compression is three times of maximum aggregate size and the size effect of concrete is well predicted. The use of tension-softening curve obtained from direct tension test is suitable for well prediction of localization of concrete under uniaxial tension.

• Restorative Dentistry and Endodontics
• /
• v.40 no.3
• /
• pp.209-215
• /
• 2015

Objectives: The aim of this study was to evaluate the fluoride release of conventional glass ionomer cements (GICs) and resin-modified GICs. Materials and Methods: The cements were grouped as follows: G1 (Vidrion R, SS White), G2 (Vitro Fil, DFL), G3 (Vitro Molar, DFL), G4 (Bioglass R, Biodinamica), and G5 (Ketac Fil, 3M ESPE), as conventional GICs, and G6 (Vitremer, 3M ESPE), G7 (Vitro Fil LC, DFL), and G8 (Resiglass, Biodinamica) as resin-modified GICs. Six specimens (8.60 mm in diameter; 1.65 mm in thickness) of each material were prepared using a stainless steel mold. The specimens were immersed in a demineralizing solution (pH 4.3) for 6 hr and a remineralizing solution (pH 7.0) for 18 hr a day. The fluoride ions were measured for 15 days. Analysis of variance (ANOVA) and Tukey's test with 5% significance were applied. Results: The highest amounts of fluoride release were found during the first 24 hr for all cements, decreasing abruptly on day 2, and reaching gradually decreasing levels on day 7. Based on these results, the decreasing scale of fluoride release was as follows: G2 > G3 > G8 = G4 = G7 > G6 = G1 > G5 (p < 0.05). Conclusions: There were wide variations among the materials in terms of the cumulative amount of fluoride ion released, and the amount of fluoride release could not be attributed to the category of cement, that is, conventional GICs or resin-modified GICs.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.6
• /
• pp.262-266
• /
• 2011

A simulation study of a current-mode direct current (DC)-DC boost converter is presented in this paper. This converter, with a fully-integrated power module, is implemented by using bipolar complementary metal-oxide semiconductor (BiCMOS) technology. The current-sensing circuit has an op-amp to achieve high accuracy. With the sense metal-oxide semiconductor field-effect transistor (MOSFET) in the current sensor, the sensed inductor current with the internal ramp signal can be used for feedback control. In addition, BiCMOS technology is applied to the converter, for accurate current sensing and low power consumption. The DC-DC converter is designed with a standard 0.35 ${\mu}m$ BiCMOS process. The off-chip inductor-capacitor (LC) filter is operated with an inductance of 1 mH and a capacitance of 12.5 nF. Simulation results show the high performance of the current-sensing circuit and the validity of the BiCMOS converter. The output voltage is found to be 4.1 V with a ripple ratio of 1.5% at the duty ratio of 0.3. The sensing current is measured to be within 1 mA and follows to fit the order of the aspect ratio, between sensing and power FET.

• Proceedings of the Plant Resources Society of Korea Conference
• /
• 2023.04a
• /
• pp.62-62
• /
• 2023

Zanthoxylum piperitum ("chopi" in Korean) has been used as traditional medicinal plants with high anti-inflammatory, antioxidant, and antifungal activities. The aims of the study were to identify marker compounds and to investigate metabolites variation of chopi according to different parts and harvest times. Every month from June to September, chopi were harvested with three different parts: leaves, leaf-twig mixtures, twigs. Using liquid chromatography-tandem mass spectrometry (LC-MS/MS), two main marker compounds (quercitrin and quercetin-3-O-glucoside) were characterized in 70% ethanol extracts of chopi. Quantification of the two marker compounds were subsequently conducted by high performance liquid chromatography (HPLC), representing that contents of these compounds were higher in leaves and leaf-twig mixtures rather than twigs. For the comprehensive analysis of metabolites associated with production of marker compounds, 35 primary metabolites were identified using gas chromatography-mass spectrometry (GC-MS). Multivariate analysis results represented that plant parts were main contributors to the separation of chopi. However, significant differences were not observed between leaves and leaf-twig mixtures samples. The partial least square (PLS) predictive model revealed that monosaccharides (fructose, galactose, glucose, mannose, xylose) and branched-chain amino acids (isoleucine, valine, leucine) were important determinants for the production of marker compounds together with alanine, inositol, GABA, and theronic acid. This study could be extended to stabilize and utilize chopi as an industrial material, as well as to find good candidates with various nutritional traits.

• Applied Chemistry for Engineering
• /
• v.28 no.4
• /
• pp.479-484
• /
• 2017

In this study, antioxidative activities and cellular protective effects of 70% ethanol extracts and fractions from lavender were evaluated. The scavenging activity ($FSC_{50}$) of free radical (1,1-phenyl-2-picrylhydrazyl, DPPH) was 46.6, 45.5 and $477.5{\mu}g/mL$ in the 70% ethanol extract, ethyl acetate fraction and aglycone fraction, respectively. The reactive oxygen species scavenging activities (${OSC_{50}$) of 70% ethanol extract, ethyl acetate fraction and aglycone fraction were 8.1, 3.3 and $17.6{\mu}g/mL$, respectively, and they showed lower antioxidative activity than that of using L-ascorbic acid ($1.5{\mu}g/mL$). However, the aglycone fraction showed higher photohemolysis protective effect than that of using the 70% ethanol extract and ethyl acetate fraction. At $50{\mu}M$ concentration, the cellular protective effect (${\tau}_{50}$) of 70% ethanol extract, ethyl acetate fraction and aglycone fraction from lavender was 70.6, 87.2 and 165.2 min, respectively. In particular, the lavender aglycone fraction showed 3.8 times higher cellular protective effect than that of (+)-${\alpha}$-tocopherol. The lavender fractional components including luteolin 7-O-glucuronide, vitextin, rosmarinic acid, luteolin, and apigenin were identified using TLC and LC-MS. However, the lavender aglycone fraction did not show any significant increase in flavonoids (luteolin and apigenin) compared to that of the ethyl acetate fraction. In conclusion, it is suggested that lavender may be applied as an antioxidant material in cosmetic industries.

• Culinary science and hospitality research
• /
• v.20 no.3
• /
• pp.37-49
• /
• 2014

In order to elucidate the usefulness of Lycopene, a cherry tomato variety, as a food material, the compositions of free amino acids, amino acid metabolites and polyphenol compounds were analyzed using HPLC and LC-MS/MS method. Lycopene contained eighteen free amino acids except for L-Cys and L-Try. L-Glu was the most abundant free amino acid, followed by L-Gln and L-Asp. The percentages of L-Glu, L-Gln and L-Asp of total free amino acid were 55.5%, 15.9% and 9.9% respectively. Lycopene contained essential amino acids with the exception of tryptophan. The following amino acid metabolites were found : ${\gamma}$-aminobutyric acid(GABA), carnitine(L-Car), o-phosphoethanolamine(o-Pea), hydroxylysine(Hyl) phosphoserine (p-Ser), N-methyl-histidine(Me-His), ethanolamine($EtNH_2$). Especially, GABA known as a neurotransmitter was present at a high level(305.99 mg/100 g dry weight). We identified the following polyphenol compounds in the cherry tomatoes : caffeic acid-hexose isomer I (CH I), caffeic acid-hexose isomer II (CH II), 3-caffeoylquinic acid(3-CQA), 5-caffeoylquinic acid(5-CQA), caffeoylquinic acid isomer(CQAI), quercetin-hexose-deoxyhexose-pentose(QTS), quercetin-3-rutinoside(Q-3-R), di-caffeoylquinic acid(di-CQA), tri-caffeoylquinic acid(tri-CQA), naringenin chalcone(NGC). Large quantities of Q-3-R and NGC known as bioactive compounds were found. These results revealed that Lycopene variety contained various nutritional and bioactive compounds and would be a potent functional food material.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.269-270
• /
• 2009

The biased vertical alignment (BVA) liquid crystal (LC) mode shows a has a distinct advantage of lower manufacture cost due to the elimination of a lithographic process step to form either ITO-patterning or protrusions on the color-filter substrates. However, those devices have complex voltage conditions which is the respective induce voltage on common electrode, pixel electrode and bias electrode when positive and negative frame. In order to overcome the complex voltage condition, the pretilt angles is controlled by photo polymerization of the UV-curable reactive mesogen (RM). According to our studies, voltages to the cell are critical to achieve an optimized surface-modified quality BVA (Q-BVA) mode which provides the well defined reorientation of the LCs with respect to an electric field.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.1
• /
• pp.21-33
• /
• 2007

Statement of problem: The esthetic component of dental care has become increasingly more important, while new tooth-colored materials are continually marketed. Various new indirect composite materials have been developed with required advantages. The most recent development in the indirect composites has been the introduction of the second-generation laboratory composite or poly-glass materials. They are processed by different laboratory techniques based on combinations of heat, pressure, vacuum and light polymerization. Although, second generation products became available in 1995, their characteristics and clinical performance have not been adequately investigated. Purpose: The aim of this study was to measure the mechanical properties of the second generation indirect resin system and compare these with an existing universal direct composite resin. Material and method: In this study four indirect composite material (Adoro LC, BelleGlass HP, Tescera, Synfony) were tested for flexural strength, wear resistance, hardness and their degree of conversion against Z250, a light cure direct composite. Results: Within the limitations of this study, the following conclusions were drawn: 1. From the abrasion wear result, Adoro showed the least volume loss while Synfony showed the greatest volume loss. Z250 and BelleGlass HP didn't show significant difference (p>0.05), but they showed significant difference with other groups (p<0.05). From the attrition wear, BelleGlass HP showed the least volume loss and it didn’t show significant difference with Tescera (p>0.05). While Synfony showed the greatest volume loss that it showed significant difference with other groups (p>0.05). 2. Mean values of flexural strength by means of three point bending test was in the order of Z250, Adoro, Belleglass HP, Tescera and Synfony. Mean elastic modulus was in the order of Z250, BelleGlass HP, Tescera, Adoro and Synfony. 3. The result of Vicker‘s microhardness value showed that significantly higher value in Z250 (p<0.05), and is in the order of BelleGlass HP, Tescera, Adoro and Synfony. 4. The degree of conversion measured by FT-IR showed significantly higher value in BelleGlass HP (p<0.05), and is in the order of Adoro, Synfony, Tescera and Z250. Conclusion: Significant differences were found in the flexural strength, wear resistance, hardness and their degree of conversion.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.306-306
• /
• 2008

기계적 에너지를 전기적 에너지로 변환하는 에너지 변환소자인 압전 세라믹스는 액추에이터, 변압기, 초음파모터, 초음파 소자 및 각종 센서로 응용되고 있으며, 그 응용분야는 크게 증가하고 있다. 최근에는 이러한 압전 소자를 앞으로 도래하는 ubiquitous, 무선 모바일 시대의 휴대용 전자제품, robotics, MEMS 분야 등의 대체 에너지원으로 응용하기 위한 연구가 진행되고 있다. 특히 인간의 걷기 운동 등과 같은 일상적인 동작으로 필요한 전력을 얻을 수 있고, 세라믹 소자를 이용하기 때문에 전자노이즈가 발생되지 않을 뿐 아니라 반영구적으로 사용할 수 가 있어서, 기존 이차전지를 대체 또는 보완 할 수 있는 방안도 검토되고 있다. PZT계 세라믹스는 높은 유전상수와 우수한 압전특성으로 전자세라믹스 분야에서 가장 널리 사용되어지고 있지만 $1200^{\circ}C$ 이상의 높은 소결온도 때문에 $1000^{\circ}C$ 부근에서 급격히 휘발되는 PbO로 인한 환경오염과 기본조성의 변화로 인한 압전 특성의 저하가 문제시 되고 있다. 또한 적층 세라믹스의 제작 시 구조적 특성상 내부전극이 도포된 상태에서 동시 소결이 필요한데, 융점이 낮은 Ag전극 대신 값비싼 Pd나 Pt가 다량 함유된 Ag/Pd, Ag/Pt 전극이 사용되고 있어 경제성이 떨어지는 단점을 갖게 된다. 순수 Ag 전극을 사용하거나 Ag의 비율이 높은 내부전극을 사용하기 위해서는 $900^{\circ}C$ 이하에서 소결되고 우수한 전기적 특성을 보이는 압전 세라믹스를 개발 하는 것이 필요하다. 따라서 본 연구에서는 압전특성이 우수한 $(Pb_{1-x}Cd_x)(Ni_{1/3}/Nb_{2/3})_{0.25}(Zr_{0.35}/Ti_{0.4})O_3$ 계의 조성을 설계하고, 소걸온도를 낮추기 위해서 2 단계 하소법을 이용하였다. 또한 $MnCO_3$, $SiO_2$, $Pb_3O_4$ 등을 소량 첨가하여 액상 소결 특성을 부여하여 소결 온도를 감소시키려는 시도도 하였다. 분말을 볼 밀링 (ball milling)을 통해 24시간 동안 혼합하고, 혼합된 분말은 $800^{\circ}C$에서 2시간 동안 하소하였다. 하소한 분말을 다시 72시간 동안 볼 밀링 하여 최종 분말을 얻었다. 최종 분말에 PVB를 첨가하여 직경 15mm의 디스크 형태로 성형한 후, 850~$975^{\circ}C$ 범위에서 온도를 변화시키면서 소결을 하였다. 최종 분말 및 소결된 시편을 XRD분석을 통하여 상을 확인하였고, SEM을 이용하여 미세조직을 관찰 하였다. 전기적 특성을 평가하기 위하여 두께를 1mm로 연마한 시편에 Ag 전극을 도포하여 $650^{\circ}C$에서 열처리한 후, 분극처리 하였다. 압전특성은 $d_{33}$-meter로 측정하였고, impedance analyzer를 이용하여 압전 특성 (전기기계결합계수 및 기계적품질계수)을 측정 하였다. 또한 강유전체 특성 평가 장치 (Precision-LC)를 이용하여 분극-전계 특성을 평가하였다. 이상의 연구를 통하여 소결 온도가 $900^{\circ}C$인 경우에서도 양호한 압전 특성을 확보 할 수 있었다.

• Restorative Dentistry and Endodontics
• /
• v.25 no.1
• /
• pp.123-132
• /
• 2000

To overcome problems of conventional glass ionomers, resin components have been added to glass ionomers. On a continuum between glass ionomers and composites are a variety of blends, employing different proportions of acid-base and free radical reactions to bring about cure. Popular groups defined between the ends are resin-modified glass-ionomers(RMGIs), polyacid-modified composite resins(Compomers) and ionomer modified resins. These groups show different clinical properties, and in selecting these materials for a restoration, one should sufficiently understand these different setting properties. In this study, some difference in the setting characteristics of different groups of hybrid ionomers were examined. Two RMGIs (Fuji2 LC,GC / Vitremer, 3M), three Compomers (Dyract AP, Dentsply / F2000, 3M / Elan, Kerr) were involved in this study. The identification of the setting characteristics of different groups was achieved by a two-stage study. First, thermal analysis was performed by a differential scanning calorimeter, and then the hardness of each group at different depth and time were measured by a micro-hardness tester. Thermal analysis was performed to identify the inorganic filler content and to record the heat change during setting process. The setting process was progressed for each material by chemical set mode and light-cured mode. In the hardness test, samples of materials were prepared with a 6mm-diameter metal ring, and the hardness was measured at the top, and 1mm, 2.5mm, 4mm below at just after a 40 second-cure, and after 10 minutes, 24 hours, and 7 days. Statistical analysis was performed by Mann-Whitney rank sum test to assess significant differences between set modes and types of materials, and by ANOVA and T-test to evaluate the statistical meanings of data at different times and depths of each materials. Followings are findings and conclusions derived from this study. Thermal analysis; 1. Compomers show no evidence of chemical setting while RMGIs exhibit heat output during the process of chemical setting. 2. Heat of cure of RMGIs exceed Compomers. 3. The net heat output of RMGIs through light-cured mode is higher than through chemically set mode. Hardness test; 1. Initial hardness of RMGIs immediately after light cure is relatively low, but the hardness increases as time goes by. On the contrary, Comomers do not show evident increase of the hardness following time. 2. Compomers show a marked decrease of setting degree as the depth of the material increases. In RMGIs, the setting degree at different depths does not significantly differ.