• 상하수도학회지
• /
• 제25권2호
• /
• pp.193-199
• /
• 2011

A method to improve internal corrosion control efficiency by adding lime and carbon dioxide, which, in turn increases the Langelier Index (LI) for filtered water at a conventional drinking water treatment plant (WTP) was investigated. The SJ WTP (Q=100,000 $m^{3}$/d) has been operating an internal corrosion control system since 2006. The system has achieved stable operation through technical development and trial and error over a period of several years. As a result of the operation, the LI of treated water has increased up to 29% by adjusting pH of filtered water to 7.8 with the addition of lime and carbon dioxide. Coupon tests in the distribution system indicated that the corrosion rate has been delayed by 24% when the internal corrosion method was implemented. The increase of LI by lime and carbon dioxide has been proven to be a practical method for controlling corrosion.

• 한국표면공학회지
• /
• 제48권4호
• /
• pp.142-148
• /
• 2015

The effect of equal channel angular pressing (ECAP) on the pitting corrosion resistance of hard anodized Al5052 alloy was investigated. The degree of internal stress generated in anodic oxide films during hard anodization was also evaluated with a strain gauge method. The pitting corrosion resistance of hard anodized Al5052 alloy was greatly decreased by ECAP. Cracks occurred in the anodic oxide film during hard anodization and these cracks were larger and deeper in the alloy with ECAP than without. The pitting corrosion was accelerated by cracks. The internal stress present in the anodic oxide films was compressive and the stress was higher in the alloys with ECAP than without, resulting in an increased likelihood of cracks. The pitting corrosion resistance of hard anodized Al5052 alloy was improved by annealing at the range of 473-573K after ECAP processed at room temperature for four passes. The compressive internal stress gradually decreased with increasing annealing temperature. It is assumed that the improvement in the pitting corrosion resistance of hard anodized Al5052 alloy by annealing may be attributed to a decrease in the likelihood of cracks due to the decreased internal stresses in anodic oxide films.

• Structural Monitoring and Maintenance
• /
• 제3권3호
• /
• pp.297-314
• /
• 2016

As the study of internal corrosion of pipeline need a large number of experiments as well as long time, so there is a need for new computational technique to expand the spectrum of the results and to save time. The present work represents a new non-destructive evaluation (NDE) technique for detecting the internal corrosion inside pipeline by evaluating the dielectric properties of steel pipe at room temperature by using electrical capacitance sensor (ECS), then predict the effect of pipeline environment temperature (${\theta}$) on the corrosion rates by designing an efficient artificial neural network (ANN) architecture. ECS consists of number of electrodes mounted on the outer surface of pipeline, the sensor shape, electrode configuration, and the number of electrodes that comprise three key elements of two dimensional capacitance sensors are illustrated. The variation in the dielectric signatures was employed to design electrical capacitance sensor (ECS) with high sensitivity to detect such defects. The rules of 24-electrode sensor parameters such as capacitance, capacitance change, and change rate of capacitance are discussed by ANSYS and MATLAB, which are combined to simulate sensor characteristic. A feed-forward neural network (FFNN) structure are applied, trained and tested to predict the finite element (FE) results of corrosion rates under room temperature, and then used the trained FFNN to predict corrosion rates at different temperature using MATLAB neural network toolbox. The FE results are in excellent agreement with an FFNN results, thus validating the accuracy and reliability of the proposed technique and leads to better understanding of the corrosion mechanism under different pipeline environmental temperature.

• 콘크리트학회논문집
• /
• 제11권3호
• /
• pp.193-203
• /
• 1999

The corrosion of steel reinforcements in concrete is of great concern in recent years. This study is focused on the corrosion behavior of steel bars induced by internal chlorides in concrete at early ages. The main objective of this study is to determine the chloride thresholds causing depassivation and active corrosion of steel reinforcement in concrete. To examine the threshold concentration of chloride ion, the half-cell potential, chemical composition of expressed pore solutions of concrete and the rate of corosion area of the specimens were measured. Major variables include the added amount of chlorides in concrete, types of binders, and water-to-binder ration. From the present comprehensive experimental results, the factors influencing chloride-induced corrosion are investigated, and the chloride thresholds causing active corrosion of steel bars are proposed. The present study will enable to specify the realistic chloride limit in concrete which can be used in the future technical specification.

• Corrosion Science and Technology
• /
• 제6권6호
• /
• pp.275-281
• /
• 2007

The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of $AlCl_3$ and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at $100-400A/m^2$ at 293 K in a solution containing 1.53 mol/L of $H_2SO_4$ and 0.0185 mol/L of $Al_2(SO_4)_3$. The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. However, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasingthe likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films

• Corrosion Science and Technology
• /
• 제6권6호
• /
• pp.316-321
• /
• 2007

The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of $AlCl_3$ and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at $100-400A/m^2$ at 293 K in a solution containing 1.53 mol/L of $H_2SO_4$ and 0.0185 mol/L of $Al_2(SO_4)_3$. The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. However, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasingthe likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표회 논문집(I)
• /
• pp.197-202
• /
• 1998

The corrosion of steel reinforcements in concrete is of much concern in recent years. The mechanism of corrosion, however, is not clear yet. This study is focused on the corrosion of steel induced by internal chlorides in concrete at early ages. To examine the critical concentration of steel, half-cell potential, chemical composition of expressed pore solutions of mortars and rate of corrosion area were observed with respect to additions of chlorides, types of binders, water-binders ratio.

• 한국환경과학회지
• /
• 제22권11호
• /
• pp.1383-1388
• /
• 2013

The pilot plant experiment was performed to investigate phosphorus and nitrogen removal from domestic wastewater by MLE process combined with aluminum corrosion reactor. When operating 0.5Q and 1Q to internal recycle and sludge recycle in the MLE process, the effluent $COD_{Mn}$ concentration of internal recycle 0.5Q were higher than internal recycle 1Q, the removal efficiency rates of $NH_3$-N in the internal recycle 0.5Q were was higher than internal recycle 1Q. Denitrification rates were about 86.8% in internal recycle and sludge recycle 0.5Q. When operating 0.5Q to internal recycle and sludge recycle in the MLE process, the removal efficiency rates of total nitrogen was the highest. The removal efficiency rates of total phosphorus was about 91.5% in the aluminum corrosion reactor.

• 상하수도학회지
• /
• 제20권2호
• /
• pp.215-223
• /
• 2006

The internal corrosion of water distribution systems is the main cause for the problem of the public health threat as well as water leakage in the damaged pipeline, red water, and odor and taste of the tap water. This study was examined the effect of chemicals used for pH and alkalinity control and corrosion inhibitors for producing the optimal corrosion control method. Corrosion study at different pH and alkalinity indicated that these control using alkaline chemicals was effective in corrosion rate, Fe release reduction, but examined to be increased in turbidity and corrosion-by-products(TTHMs) problems. The turbidity was slightly increased, requiring caution in controlling corrosion with $Ca(OH)_2$. At pH 9.0, TTHMs concentration is increased two times corn pared with non-control of pH. Using the pipe which had experienced 28 years of exposure, iron release was decreased with the corrosion inhibitor. Consequently, pH, Alkalinity control method using alkaline chemicals must be complemented by corrosion inhibitor application for efficient corrosion control.

• 한국지반환경공학회 논문집
• /
• 제9권1호
• /
• pp.17-25
• /
• 2008

본 연구에서는 상수도 금속관의 관 내 외면 부식상태를 평가하고, 내 외면 부식깊이(속도)와 매설년수의 관계를 통하여 내 외면 공식성장속도, 그리고 국내의 토양특성 인자들이 관 외면부식에 미치는 영향을 평가하여 관 외면의 노후상태를 예측할 수 있는 부식속도 모델을 제안하였다. 수집된 관체의 외면 부식깊이는 평균적으로 1.38 mm, 내면은 2.13 mm이었고, 이는 수질 등 내면부식영향 인자가 토양 등 외면부식영향 인자보다 부식에 미치는 영향이 크기 때문이며, 평균 공식성장 속도도 내면이 외면보다 두 배정도 빠른 것으로 나타났다. 외면부식에 영향을 주는 각 토양과 외면부식속도와의 상관성은 높지 않았으나, 모든 토양항목을 포함하여 회귀분석을 통하여 수립된 외면부식속도 예측모델은 기존 모델과 비교하여 더 높은 상관성을 보였다.