• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.8-9
• /
• 2006

Hafnium oxide ($HfO_2$) thin films were deposited on p-type (100) silicon wafers by atomic layer deposition (ALD) using TEMAHf and $O_3$. Prior to the deposition of $HfO_2$ films, a thin Hf ($10\;{\AA}$) metal layer was deposited. Deposition temperature of $HfO_2$ thin film was $350^{\circ}C$ and its thickness was $150\;{\AA}$. Samples were then annealed using furnace heating to temperature ranges from 500 to $900^{\circ}C$. The MOS capacitor of round-type was fabricated on Si substrates. Thermally evaporated $3000\;{\AA}$-thick AI was used as top electrode. In this work, We study the interface characterization of $HfO_2$/Hf/Si MOS capacitor depending on annealing temperature. Through AES(Auger Electron Spectroscopy), capacitance-voltage (C-V) and current-voltage (I-V) analysis, the role of Hf layer for the better $HfO_2$/Si interface property was investigated. We found that Hf meta1 layer in our structure effective1y suppressed the generation of interfacial $SiO_2$ layer between $HfO_2$ film and silicon substrate.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.322-327
• /
• 2019

Hole carrier selective MoOx film is obtained by atomic layer deposition(ALD) using molybdenum hexacarbonyl[$Mo(CO)_6$] as precursor and ozone($O_3$) oxidant. The growth rate is about 0.036 nm/cycle at 200 g/Nm of ozone concentration and the thickness of interfacial oxide is about 2 nm. The measured band gap and work function of the MoOx film grown by ALD are 3.25 eV and 8 eV, respectively. X-ray photoelectron spectroscopy(XPS) result shows that the $Mo^{6+}$ state is dominant in the MoOx thin film. In the case of ALD-MoOx grown on Si wafer, the ozone concentration does not affect the passivation performance in the as-deposited state. But, the implied open-circuit voltage increases from $576^{\circ}C$ to $620^{\circ}C$ at 250 g/Nm after post-deposition annealing at $350^{\circ}C$ in a forming gas ambient. Instead of using a p-type amorphous silicon layer, high work function MoOx films as hole selective contact are applied for heterojunction silicon solar cells and the best efficiency yet recorded (21 %) is obtained.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.246-246
• /
• 2012

Smart catalyst design though novel catalyst preparation methods can improve catalytic activity of transition metals on reducible oxide supports such as titania by enhancement of metal oxide interface effects. In this work, we investigated Pt nanoparticles/titania catalysts under CO oxidation reaction by using novel preparation methods in order to enhance its catalytic activity by optimizing metal oxide interface. Arc plasma deposition (APD) and metal impregnation techniques are employed to achieve Pt metal deposition on titania supports which are prepared by multi-target sputtering and Sol-gel techniques. In order to tailor metal-support interface for catalytic CO oxidation reaction, Pt nanoparticles and thin films are deposited in varying surface coverages on sputtered titania films using APD. To assess the role of oxide support at the interface, APD-Pt is deposited on sputtered and Sol-gel prepared titania films. Lastly, characteristics of APD-Pt process are compared with Pt impregnation technique. Our results show that activity of Pt nanoparticles is improved when supported over Sol-Gel prepared titania than sputtered titania film. It is suggested that this enhanced activity can be partly ascribed to a very rough titania surface with the higher free metal surface area and higher number of sites at the interface between the metal and the support. Also, APD-Pt shows superior catalytic activity under CO oxidation as compared to Pt impregnation on sputtered titania support. XPS results show that bulk oxide is formed on Pt when deposited through impregnation and has higher proportion of oxidized Pt in the form of $Pt^{2+/4+}$ oxidation states than Pt metal. APD-Pt shows, however, mild oxidation with large proportion of active Pt metal. APD-Pt also shows trend of increasing CO oxidation activity with number of shots. The activity continues to increase with surface coverage beyond 100%, thus suggesting a very rough and porous Pt films with higher active surface metal sites due to an increased surface area available for the reactant CO and $O_2$ molecules. The results suggest a novel approach for systematic investigation into metal oxide interface by rational catalysts design which can be extended to other metal-support systems in the future.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.169-169
• /
• 2012

The high-temperature superconductor YBa2Cu3O7-x (YBCO) have attached attentions because of a high superconducting transition temperature, low surface resistance, high superconducting critical current density (Jc), and superior superconducting capability under magnetic field. Moreover, the Jc of YBCO superconductors can be enhanced by adding impurities to the YBCO films for vortex-pinning. Understanding and controlling pinning centers are key factors to realize high Jc superconductors. We synthesized vertically-aligned ZnO nanorods on SrTiO3 (STO) substrates by catalyst-free metal-organic chemical vapor deposition (MOCVD), and subsequently, deposited YBCO films on the ZnO nanorods/STO templates using pulsed laser deposition (PLD). The various techniques were used to analyze the structural and interfacial properties of the YBCO/ZnO nanorods/STO hybrid structures. SEM, TEM, and XRD measurements demonstrated that YBCO films on ZnO nanorods/STO were well crystallized with the (001) orientation. EXAFS measurements from YBCO/ZnO nanorods/STO at Cu K edge demonstrated that the local structural properties around Cu atoms in YBCO were quite similar to those of YBCO/STO.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.93-93
• /
• 2009

실리콘 태양전지의 효율 향상을 위한 노력의 일환으로 결정질 실리콘 웨이퍼 표면passivation 물질 중 Atomic Layer Deposition (ALD)을 이용하여 증착한 $Al_2O_3$ 박막에 대한 관심이 증가하고 있다. 본 연구에서는 $Al_2O_3$ 박막의 증착 전 실리콘 웨이퍼의 산화막 두께에 따른 passivation 효과에 대해서 연구하였다. 실리콘 산화막은 $HNO_3$ 용액을 사용하여 화학적으로 생성시켰으며 $HNO_3$ 용액과의 반응 시간을 조절하여 실리콘 산화막의 두께를 조절하였다. 실리콘 산화막 생성 후 ALD로 $Al_2O_3$ 박막을 증착하였으며 증착 후 $N_2$ 분위기에서 annealing 하였다. Annealing 후 passivation 효과는 Quasi-Steady-State Photo Conductance를 사용하여 minority carrier의 lifetime을 측정하였다. Capacitance-Voltage measurement, Transmission Electron Microscopy, Ellipsometry를 사용하여 실리콘 산화막의 두께에 따른 $Al_2O_3$ 박막의 passivation 효과를 분석하였다.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.3 no.1
• /
• pp.1-12
• /
• 2003

This paper describes a study on the abnormal behavior of the electrical characteristics of the (n)GaAs/Ti/Pt/Au Schottky contacts prepared by the two techniques of electron beam deposition and rf sputtering and after an annealing treatment. The samples were characterized by I-V and C-V measurements carried out over the temperature range of 150 - 350 K both in the as prepared state and after a 300 C, 30 min. anneal step. The variation of ideality factor with forward bias, the variation of ideality factor and barrier height with temperature and the difference between the capacitance barrier and current barrier show the presence of a thin interfacial oxide layer along with barrier height inhomogenieties at the metal/semiconductor interface. This barrier height inhomogeneity model also explains the lower barrier height for the sputtered samples to be due to the presence of low barrier height patches produced because of high plasma energy. After the annealing step the contacts prepared by electron beam have the highest typical current barrier height of 0.85 eV and capacitance barrier height of 0.86 eV whereas those prepared by sputtering (at the highest power studied) have the lowest typical current barrier height of 0.67 eV and capacitance barrier height of 0.78 eV.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.42-51
• /
• 1994

6061Al-SiCP metal matrix composite materials(MMCs) were fabricated by injecting SiCP particles directly into the atomized spray. The main attraction of this technique is the rapid fabrication of semi-finished, composite products in a combined atomization, particulate injection(10 $\mu\textrm{m}$, 40 $\mu\textrm{m}$, SiCP) and deposition operation. Conclusions obtained are as follows; The microstructure of the unreinforced spray formed 6061Al alloy consisted of relatively fine(50 $\mu\textrm{m}$) equiaxed grains. By comparision, the microstructure of the I/M materials was segregated and consisted of relatively coarse(150 $\mu\textrm{m}$) grains. The probability of clustering of SiCP particles in co-sprayed metal matrix composites increased it ceramic particle size(SiCP) was reduced and the volume fraction was held constant. Analysis of overspray powders collected from the spray atomization and deposition experiments indicated that morphology of powders were nearly spherical and degree of powders sphercity was deviated due to composite with SiCp particles. Interfacial bonding between matrix and ceramics was improved by heat treatment and addition of alloying elements(Mg). Maximum hardness values [Hv: 165 kg/mm2 for Al-10 $\mu\textrm{m}$ SiCp Hv--159 kg/mm2 for Al-40 $\mu\textrm{m}$SiCp] were obtained through the solution heat treatment at $530^{\circ}C$ for 2 hrs and aging at $178^{\circ}C$, and there by the resistance were improved.

• Korean Journal of Materials Research
• /
• v.17 no.5
• /
• pp.263-267
• /
• 2007

Hafnium oxide $(HfO_2)$ films were deposited on Si(100) substrates by remote plasma-enhanced atomic layer deposition (PEALD) method at $250^{\circ}C$ using TEMAH [tetrakis(ethylmethylamino)hafnium] and $O_2$ plasma. $(HfO_2)$ films showed a relatively low carbon contamination of about 3 at %. As-deposited and annealed $(HfO_2)$ films showed amorphous and randomly oriented polycrystalline structure. respectively. The interfacial layer of $(HfO_2)$ films deposited using remote PEALD was Hf silicate and its thickness increased with increasing annealing temperature. The hysteresis of $(HfO_2)$ films became lower and the flat band voltages shifted towards the positive direction after annealing. Post-annealing process significantly changed the physical, chemical, and electrical properties of $(HfO_2)$ films. $(HfO_2)$ films deposited by remote PEALD using TEMAH and $O_2$ plasma showed generally improved film qualities compare to those of the films deposited by conventional ALD.

• Journal of Powder Materials
• /
• v.26 no.4
• /
• pp.319-326
• /
• 2019

Additive manufacturing (AM) is a highly innovative method for joining dissimilar materials for industrial applications. In the present work, AM of STS630 and Ti-6Al-4V powder alloys on medium entropy alloys (MEAs) NiCrCo and NiCrCoMn is studied. The STS630 and Ti64 powders are deposited on the MEAs. Joint delamination and cracks are observed after the deposition of Ti64 on the MEAs, whereas the deposition of STS630 on the MEAs is successful, without any cracks and joint delamination. The microstructure around the fusion zone interface is characterized by scanning electron microscopy and X-ray diffraction. Intermetallic compounds are formed at the interfacial regions of MEA-Ti64 samples. In addition, Vicker's hardness value increased dramatically at the joint interface between MEAs and Ti-6Al-4V compared to that between MEAs and STS630. This result is attributed to the brittle nature of the joint, which can lead to a decrease in the joint strength.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.2
• /
• pp.98-102
• /
• 2019

Direct plasma-enhanced atomic layer deposition (PEALD) are widely used for $SiO_2$ and SiON thin film process in current semiconductor industry. However, this exhibits poor step coverage for three-dimensional device structure due directionality of plasma species as well as plasma damage on the substrate. In this study, to overcome this issue, low temperature (< $300^{\circ}C$) $SiO_2$ and SiON thin film processes were studied using inductively coupled plasma (ICP) type remote PEALD with various reactant gases such as $O_2$, $H_2O$, $N_2$ and $NH_3$. It was confirmed that the interfacial properties such as fixed charge density and charge trapping behavior of thin films were considerably improved by hydrogen species in $H_2O$ and $NH_3$ plasma compared to the films grown with $O_2$ and $N_2$ plasma. Furthermore, the leakage current density of the thin films was suppressed for same reason.