Local two-phase flow parameters of subcooled flow boiling in inclined annulus were measured to investigate the effect of inclination on the internal flow structure. Two-conductivity probe technique was applied to measure local gas phasic parameters, including void fraction, vapor bubble frequency, chord length, vapor bubble velocity and interfacial area concentration. Local liquid velocity was measured by Pilot tube. Experiments were conducted for three angles of inclination; 0$^{\circ}$(vertical), 30$^{\circ}$, 60$^{\circ}$. The system pressure was maintained at atmospheric pressure. The range of average void fraction was up to 10% and the average liquid superficial velocities were less than 1.3 m/sec. The results of experiments showed that the distributions of two-phase How parameters were influenced by the angle of channel inclination. Especially, the void fraction and chord length distributions were strongly affected by the increase of inclination angle, and flow pattern transition to slug flow was observed depending on the How conditions. The profiles of vapor velocity, liquid velocity and interfacial area concentration were found to be affected by the non-symmetric bubble size distribution in inclined channel. Using the measured distributions of local phasic parameters, an analysis for predicting average void fraction was performed based on the drift flux model and flowing volumetric concentration. And it was demonstrated that the average void fraction can be more appropriately presented in terms of flowing volumetric concentration.

• 대한금속재료학회지
• /
• 제46권12호
• /
• pp.817-822
• /
• 2008

Metal matrix composite (MMC) materials having low electrical contact resistance based on 316L stainless steel (STS) matrix alloy with $ZrB_2$ particles were fabricated for PEMFC (Polymer Electrolyte Membrane Fuel Cell) separator by powder metallurgy (PM). The effects of the boride particle addition into the matrix alloy on microstructure, surface morphology, and interfacial contact resistance (ICR) between the samples and gas diffusion layer (GDL) were investigated. Both conventional and PM 316L STS samples showed high ICR due to the existence of non-conductive passive film on the alloy surface. The addition of the boride particles, however, remarkably reduced ICR of the samples. SEM observation revealed that the boride particles were protruded out of the matrix surface and particle density existing on the surface increased with increasing the boride content, causing increase of the total contact area between the conductive particles and GDL. ICR of the samples also decreased with increasing the boride content resulted from the increased contact area.

• 폴리머
• /
• 제26권4호
• /
• pp.445-451
• /
• 2002

본 연구에서는 실리카의 표면처리를 위해 실란 커플링제인, ${\gamma}$-methacryloxy propyl trimethoxy silane (MPS), ${\gamma}$-glycidoxy propyl trimethoxy silane (GPS), and ${\gamma}$-mercapto propyl trimethoxy silane (MCPS) 등을 사용하여 실리카 흡착특성과 기계적 계면물성에 대하여 고착하였다. 실란처리에 따른 실리카의 평형 확산압력, 표면 자유에너지, 비표면적을 BET법을 이용한 $N_2$/77 K 기체 흡착을 통하여 알아보았다. 본 실험결과 신란처리에 의해 실리카 표면에 도입된 비극성 관능기로 인해 실리카의 비표면적, 평형 확산압력, 표면 자유에너지의 비극성 요소가 증가하였으며 결과적으로 실리카/고무 복합재료의 기계적 계면 물성인 tearing energy ($G_{mc}$)가 향상되었음을 확인할 수 있었다. 그리고 MPS로 표면처리한 경우가 GPS, MCPS에 비해서 우수한 기계적 계면물성을 나타남을 관찰할 수 있었다.

• KCI Concrete Journal
• /
• 제13권2호
• /
• pp.19-25
• /
• 2001

A simple expression to predict bond strength of reinforcing bars with rib deformation to the surrounding is derived for the case of splitting bond failure. Finite element analysis is used to model the confining behavior of concrete cover. The roles of the interfacial properties, specifically, the friction coefficient, cohesion, the relative rib area and the rib face angle are examined. Values of bond strength obtained using the analytical model are in good agreement with the bond test results from the previous studies. The analytical model provides insight into interfacial bond mechanisms and the effects of the key variables on the bond strength of deformed bars to concrete. Based on the comparison between the analytical results and the test results, the values of cohesion, coefficient of friction, and the effective rib face angle are proposed.

• Nuclear Engineering and Technology
• /
• 제24권2호
• /
• pp.130-140
• /
• 1992

동방향 성층이상유동에서의 직접적촉 응축현상을 일차원 모델인 RELAP5/MOD2와 /MOD3를 이용하여 해석하였으며, 해석결과를 Northwestern의 실험결과와 비교·검토하였다. 해석결과 RELAP5의 공유열전달 모델은 동방향 성층이상유동에서 응축율을 비교적 잘 예측하고 있다. 그러나 공유접촉면에 파형이 생기는 경우는 물경계두께 및 국부 열전달계수는 유사한 범위로 일치할분 현상을 예측하는데 상당한 차이가 있다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.3-6
• /
• 2003

In this work, poly(ethylene oxide) nanofibers were fabricated by electrospinning to prepare nanofibers-reinforced composites. And the PEO powders-impregnated composites were also prepared to compare with physicochemical properties of nanofibers-reinforced composites. Morphology and fiber diameter of PEO nanofibers were determined by SEM observation. Mechanical interfacial properties of the composites were investigated in fracture toughness tests and interlaminar shear strength (ILSS) test. As a result, the fiber diameter decreased in increasing applied voltage. However the optimum condition for the fiber formation was 15 ㎸, resulting from increasing of jet instability at high voltage and the prepared PEO nanofibers were useful in fiber reinforced composites. The PEO-based nanofibers-reinforced composites showed an improvement of fracture toughness factors ($K_{IC} and G_{ IC}$) and ILSS, compared to the composites impregnated with PEO powders. These results were noted that the nanofibers had higher specific surface area and larger aspect ratio than those of the powder, which played an important role in improving the mechanical interfacial properties of the composites.

• Journal of Welding and Joining
• /
• 제14권4호
• /
• pp.62-70
• /
• 1996

Al or Al-alloy have been known to be able to be claded on various materials by using explosive welding process, however, the intermetallic layer frequently formed along the interface have made this process very complicated. In this study, it was focussed to select the process variables, which can get rid of interfacial layer in the Al-claded steel plate. As a result, it was demonstrated that there was a certain range of explosive thickness which did not form the intermetallic phase as well as the non-bonded area. On the other hand, ultasonic tests performed for identifying the presence of interfacial layer nondestructively showed that it could be applied for the intended purpose but its result was weakly related with the microstructural quality of interface.

• Composites Research
• /
• 제28권1호
• /
• pp.22-27
• /
• 2015

복합재의 고강성을 얻기 위하여 매트릭스 및 섬유 각각의 물성도 중요하지만, 매트릭스와 섬유간 계면접착력이 매우 중요하다. 바닷물이 계면을 침투하게 되면 계면물성이 낮아지게 되고, 복합재의 균열이 일어나게 될 것이다. 이번 실험에서, 물리적/계면 시험법과 미세역학 시험법을 이용하여 유리섬유 노화일수에 따른 계면물성 변화를 연구하였다. 유리섬유의 기계적 물성변화는 단섬유 인장시험을 통해 조사했다. 유리섬유의 계면물성 변화는 비파괴 음향방출과 피로시험을 응용한 미세역학 시험을 통해 조사했다. 피로강도의 변화를 통하여 유리섬유와 에폭시간의 상대적인 계면물성을 평가하였다. 실험결과, 염수노화 일수에 따라 유리섬유의 직경이 감소하는 것을 관찰하였고, 미처리의 경우보다 기계적 및 계면 물성 감소를 나타내었다.

• 접착 및 계면
• /
• 제23권3호
• /
• pp.87-93
• /
• 2022

섬유와 기지 간 계면 특성을 분석하기 위해 일반적으로 접촉각을 활용하여 계산된 접착일을 활용한다. 접촉각 측정 방식으로 동적접촉각과 정적접촉각이 있으며, 본 논문에서는 보다 정확도가 높은 접촉각 측정 방법이 무엇인지 모색하였다. 각각 4가지 종류의 에폭시 수지와 유리섬유를 사용하였고, 유리섬유와 에폭시의 표면 에너지 결과를 기반으로 접착일, W_a을 계산하여 계면강도를 예측하였다. 접착일과 계면 전단강도는 이론상 비례관계이며, 이를 확인하기 위해 조성이 다른 에폭시와 유리섬유 간의 계면강도를 마이크로드롭렛 시험법을 이용하여 측정하였다. 정적접촉각 결과의 경우 접착일과 계면 전단강도 사이에는 일치하지 않는 경향을 보였다. 이는, 동적 접촉각 평가 방법은 정적접촉각에 비해, 드롭 크기에 따른 최소 표면적을 이루는 에러와 미니스커서에서 접선 측정에 따른 에러를 최소화할 수 있다는 점이다.

• 마이크로전자및패키징학회지
• /
• 제30권2호
• /
• pp.52-59
• /
• 2023

팬 아웃 웨이퍼 레벨 패키지의 Cu 재배선층 적용을 위해 Ti 확산방지층과 폴리벤즈옥사졸(polybenzoxazole, PBO) 절연층 사이의 계면 신뢰성을 평가하였다. PBO 경화 온도 및 고온/고습 시간에 따라 4점 굽힘 시험으로 정량적인 계면접착에너지를 평가하였고, 박리계면을 분석하였다. 175, 200, 및 225℃의 세 가지 PBO 경화 온도에 따른 계면접착에너지는 각각 16.63, 25.95, 16.58 J/m² 로 200℃의 경화 온도에서 가장 높은 값을 보였다. 박리표면에 대한 X-선 광전자 분광분석 결과, 200℃에서 PBO 표면의 C-O 결합의 분율이 가장 높으므로, M-O-C 결합이 Ti/PBO 계면접착 기구와 연관성이 높은 것으로 판단된다. 200℃에서 경화된 시편을 85℃/85% 상대 습도에서 500시간 동안 고온/고습 처리 하는 동안 계면접착에너지는 3 .99 J/m²까지 크게 감소하였다. 이는 고온/고습 처리동안 Ti/PBO 계면으로의 지속적인 수분 침투로 인해 계면 근처 PBO의 화학결합이 약해져서 weak boundary layer를 형성하기 때문으로 판단된다.