• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.39 no.4
• /
• pp.523-530
• /
• 2019

Pavement distress and traffic accidents are caused by pot-hole. In addition, direct and indirect damages of road users are increasing, such as loss of life due to personal injury and damage to vehicles. Generally, the asphalt concrete pavements are continuously aging from the production process to the terminal performance period. Aging causes stripping due to cracks and moisture penetration and weakening the pavement structure to induce pot-hole. In this study, adhesion performance and moisture sensitivity were evaluated according to aging degree in order to investigate the effect of aging on asphalt pavement. As a result of the study, the viscosity of the asphalt binder was increased with aging and the bond strength of the aged was increased 2~3 times than that of the unaged. The results of accelerated aging test showed an increases in indirect tensile strength and the increase in the TSR (Tensile Strength Ratio) by 4.2~8.9 %. As a result, it is noted that the anti-stripping and adhesion performances of the aged asphalt concrete are improved compared to the unaged one under the aging conditions of asphalt binder coated on aggregates.

• Korean Chemical Engineering Research
• /
• v.55 no.3
• /
• pp.395-400
• /
• 2017

Coke strength was increased by adding ash-free coal (AFC) binder. In this study, the effect of the AFC binder on the physical and chemical properties of coke was experimentally investigated to understand the molecular mechanism for the improved coke strength. For reduced $CO_2$ emission in steelmaking industry, torrefied biomass fuel mixed with coal binder is also considered. The interface between the base coal and AFC was thus examined using Scanning Electron Microscope (SEM). The coke strength was commonly measured by performing the indirect tensile test and Nuclear Magnetic Resonance (NMR) spectroscopy in $^1H$ and $^{13}C$ modes. For comprehensive mechanism study of the enhanced coke strength thus obtained, ordinary coal for thermal power plant use was carbonized with AFC for subsequent SEM examination. The NMR spectroscopy results of coke samples positively revealed that the tensile strength was proportional to the average number of aromatic rings.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.665-674
• /
• 2007

Purpose: The purpose of this study was to investigate the effect of sire and shape of retention element on the bond strength of indirect composite resin and metal. Material and method: The metal disk specimens, each 6mm in diameter, were cast from CrCo alloy. They were divided into 8 groups by applied retention element. retention bead group $B2\;({\phi}\;0.2mm),\;B4\;({\phi}\;0.4mm),\;B6\;({\phi}\;0.6mm),\;B8\;({\phi}\;0.8mm)$, retention crystal group C2 (0.2mm), C5 (0.5mm), C8 (0.8mm) and sandblasting group SB ($110{\mu}m\;Al_2O_3$ blasting) as control. Eighty-eight metal specimens were veneered with $TESCERA^{(R)}$ Indirect resin system. One specimen of each group was sectioned and the resin-metal bonding pattern at the interface was observed under measuring microscope. Other specimens were then tested for tensile bond strength on an Instron universal testing machine at a crosshead speed of 2mm/min. Results: 1. Compared to sandblasting, beads or crystals increased the resin-metal bond strength (P<.05). 2. 0.2mm retention crystals were most effective in improving the resin-metal bond strength (P>.05). 3. 0.2mm beads showed the highest bond strength among retention bead groups, but there was no statistically significant difference (P>.05). 4. Retention crystals tend to be higher in bond strength than retention beads due to wider surface area. 5. The larger retention element, the larger the undercut for the mechanical retention, but the gap at resin-metal interface was also increased. Conclusion: Within the limitations of this study, 0.2mm retention crystals were most effective in improving the resin-metal bond strength.

• International Journal of Highway Engineering
• /
• v.3 no.4 s.10
• /
• pp.105-116
• /
• 2001

This study was performed to evaluate the characteristics of waste foundry sand (WFS) and the asphalt mixture made of a foundry waste sand. To estimate the applicability of WFS, chemical and physical properties were measured by XRF(X-ray fluorescent), and SEM(Scanning electronic microfilm). To improve the stripping resistance of WFS asphalt mixture, anti-stripping agents (a hydrated lime and a liquid anti-stripping agent) were used. To improve tensile properties and durability of WFS asphalt concrete mixture, LDPE(low-density polyethylene) was used as an asphalt modifier Marshall mix design, indirect tensile strength, tensile strength ratio(TSR) after freezing and thawing, moisture susceptibility and wheel tracking tests were carried out to evaluate performance of WFS asphalt concrete. Comparing with conventional asphalt concrete, WFS asphalt concretes showed similar or the better qualify in mechanical properties, and satisfied all specification limits. Therefore, it Is concluded that waste foundry sand can be recycled as an asphalt pavement material.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 1998.10a
• /
• pp.180-185
• /
• 1998

The study was conducted to evaluate the fundamental properties of waste tire asphalt concretes using polymer modified hinder that were made by dry process. The specimens of four types of polymer modified asphalt concretes were prepared, then Marshall test and indirect tensile strength tests were performed on these samples. The results showed that polymer modified waste tire rubber asphalt concrete was acceptable for the material of asphalt pavement surface layer.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.2D
• /
• pp.243-248
• /
• 2008

Moisture damage of asphalt pavements can usually occur because of the loss of adhesion and cohesion between the asphalt binder and aggregate in the asphalt mixture due to presence of water. And this is one of the causes that is effect on the main distress of asphalt pavement. The objective of this study is to find out moisture damage characteristics of asphalt pavement. Effects of this study changes of the material properties and resistance characteristics of moisture damage on the asphalt mixtures under various temperatures and repeated immersion using indirect tensile test and modify Lottman test were evaluated during this study. The asphalt mixtures were produced using straight asphalt binder, SBS modified asphalt binder and aggregates. The material properties (resilient modulus, indirect tensile strength, failure energy and $DCSE_f$) of the asphalt mixtures were generally decreased with increasing to moisture damage caused by the number of repeated immersion. The decrease ratios of material properties by repeated immersion on SBS modified asphalt mixtures were lower than those of straight asphalt mixtures at all three test temperatures. As a conclusion, current criterion for evaluation moisture damage of asphalt mixtures is difficult for using distinction standard because of the limited evaluation criterion with one time immersion and single material property. Based on this research, to evaluate long term moisture damage on asphalt mixtures, material property tests of various kinds with repeated immersion test are considered.

• International Journal of Highway Engineering
• /
• v.18 no.3
• /
• pp.67-74
• /
• 2016

PURPOSES : This study evaluated the field applicability and laboratory performance of glass fiber-reinforced asphalt (GFRA) mixtures. METHODS : The general hot-mix asphalt (HMA) and GFRA mixtures were paved in five sites, including three national highways, one express highway, and an arterial road, to evaluate field applicability and durability. The plant mixing and construction method for the GFRA were similar to those for the general HMA. The lab performances of the field samples were relatively compared through the mechanical measures from the Marshall stability, indirect tensile strength, and dynamic stability. The field performance was surveyed after a year. RESULTS : The lab tests verified the superior lab performances of the GFRA compared to the general HMA. The Marshall stability of the GFRA increased for about 128% of the general HMA. The indirect tensile strength of the GFRA was 115% greater than that of the general HMA. The dynamic stability of the GFRA resulted in 16,180 reps/mm, which indicated that high rut resistance may be expected. No noticeable defects, such as cracks or deformation, were observed for the GFRA sections after a year. CONCLUSIONS : The lab tests and field survey for the five GFRA sites resulted in superior performances compared to the general HMA. The relatively low-cost GFRA, which required no pre-processing procedures, such as polymer modification, may be a promising alternative to the polymer-modified asphalt mixtures. The long-term performance will be verified by the superior field durability of the GFRA in the near future.

• International Journal of Highway Engineering
• /
• v.19 no.5
• /
• pp.131-141
• /
• 2017

PURPOSES : The main distress of asphalt pavements in monsoon climate regions are caused by water damage and plastic deformation due to repeated rain season and increased heavy vehicle traffic volume. In this study, the mechanical properties of polymer-modified warm mix asphalt (PWMA) materials are evaluated to use in monsoon climate regions such as Indonesia. METHODS : Comprehensive laboratory tests are conducted to evaluate moisture resistance and permanent deformation resistance for three different asphalt mixtures such as the Indonesian conventional hot-mix asphalt (HMA) mixture, the polymer-modified asphalt mixture, and the polymer-modified warm mix asphalt (PWMA) mixture. Dynamic immersion test and indirect tensile strength ratio test are performed to evaluate moisture resistance. The wheel tracking test is performed to evaluate rutting resistance. Additionally, the Hamburg wheel tracking test is performed to evaluate rutting and moisture resistances simultaneously. RESULTS :The dynamic immersion test results indicate that the PWMA mixture shows the highest resistance to moisture. The indirect tensile strength ratio test indicates that TSR values of PWMA mixture, Indonesian PMA mixture, and Indonesian HMA mixture show 87.2%, 84.1%, and 67.9%, respectively. The wheel tracking test results indicate that the PWMA mixture is found to be more resistant to plastic deformation than the Indonesian PMA. The dynamic stability values are 2,739 times/mm and 3,150 times/mm, respectively. Moreover, the Hamburg wheel tracking test results indicate that PWMA mixture is more resistant to plastic deformation than Indonesian PMA and HMA mixtures. CONCLUSIONS :Based on limited laboratory test results, it is concluded that rutting resistance and moisture susceptibility of the PWMA mixture is superior to Indonesian HMA and Indonesian PMA mixtures. It is postulated that PWMA mixture would be suitable for climate and traffic conditions in Indonesia.

• International Journal of Highway Engineering
• /
• v.12 no.2
• /
• pp.17-23
• /
• 2010

Since the relatively stiff binder shows a higher tensile strength as well as higher rutting resistance, it is believed that the binder stiffness is an important factor for rutting and tensile strength of asphalt mixtures. The typical tensile property is measured by indirect tensile strength (ITS) test at $25^{\circ}C$ and the rutting resistance is most widely measured by wheel tracking (WT) test at $60^{\circ}C$. The deformation strength ($S_D$) is newly developed property to estimate rut resistance of asphalt concretes at $60^{\circ}C$. The ITS and $S_D$ are very simple to measure by static test techniques, but the WT is measured by repeated loading procedure which requires relatively longer time and more efforts. Since these three properties are highly dependent upon the binder stiffness, it may be possible to estimate one property from another. Therefore, this study investigate the possibility of estimating the rutting characteristics (measured by WT test) by ITS or $S_D$ test, and the ITS by $S_D$. Because of binder stiffness effect, in the WT estimation by ITS, a tendency was observed for the higher ITS mixture to have the lower rut depth, giving $R^2{\fallingdotseq}$0.6, on the average. The ITS estimation by $S_D$ showed $R^2{\fallingdotseq}$0.64, and the WT estimation by SD showed $R^2{\fallingdotseq}$0.84, which is highest correlation among the three. Therefore, it was concluded that there is relatively good possibility of estimating WT result by $S_D$, and even though $R^2$ is somewhat low, there is some correlation between WT and ITS.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1998.03a
• /
• pp.269-273
• /
• 1998

The failure of material structures or mechanical system is considered as a direct or indirect result of fatigue. In the design of mechanical structure for estimating of reliability, the prediction of failure life is the most important failure mode to be considered. However, because of a complicated behavior of fatigue in mechanical structure, the analysis of fatigue is in need of much researches on life prediction. This document presents a prediction of fatigue life of the SAPH45 steel, which is extensively for vehicle frame. The method using lethargy coefficient and stress distribution factor at pediction of fatigue life based on the consideration of the failure characteristics from the tensile test should be provided in this study.