• Journal of the Korean Geotechnical Society
• /
• v.31 no.3
• /
• pp.5-16
• /
• 2015

The characteristics of tensile strength of fiber-reinforced grouting (cement paste) injected into rocks or soils were studied. A tensile strength of such materials utilized in civil engineering has been commonly tested by an indirect splitting tensile test (Brazilian test). In this study, a direct tensile testing method was developed with built-in cylinder inside a cylindrical specimen with 15 cm in diameter and 30 cm in height. The testing specimen was prepared with 0%, 0.5%, or 1% (by weight) of a PVA or steel fiber reinforced mortar. A specimen with 5 cm in diameter and 10 cm in height was also prepared and tested for the splitting tensile test. Each specimen was air cured for 7 days or 28 days before testing. The tensile strength of built-in cylinder test showed 96%-290% higher than that of splitting tensile test. The 3D finite element analyses on these tensile tests showed that the tensile strength from built-in cylinder test had was 3 times higher than that of splitting tensile test. It is similar to experimental result. As an amount of fiber increased from 0% to 1%, its tensile strength increased by 119%-190% or 23%-131% for 7 days or 28 days-cured specimens, respectively. As a curing period increased from 7 days to 28 days, its strength decreased. Most specimens reinforced with PVA fiber showed tensile strength 14%-38% higher than that of steel fiber reinforced specimens.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.9 no.4
• /
• pp.83-92
• /
• 1989

For many of the rigid pavements the observations of significantly different performances were explained to relate distress mechanisms to distress manifestation and to develope better prediction of performance. This paper summarizes the result of an investigation of the resilient elastic and fatigue behavior of inservice cement concrete pavements. Static indirect tensile tests were. conducted in order to estimate the average tensile strength of each of the projects Repeat-load indirect tensile tests were conducted to determine the fatigue and resilient elastic characteristics and the relationship between fatigue life and stress/strength ratio. Deformation measurements were taken during fatigue testing in order to determine the resilient elastic properties of the material and the changes in these properties during the test period.

• Geomechanics and Engineering
• /
• v.13 no.6
• /
• pp.1045-1055
• /
• 2017

Tensile strength is considered key properties for characterizing rock material in engineering project. It is determined by direct and indirect methods. Point load test is a useful testing method to estimate the tensile strengths of rocks. In this paper, the effects of rock shape on the point load index of gypsum are investigated by PFC2D simulation. For PFC simulating, initially calibration of PFC was performed with respect to the Brazilian experimental data to ensure the conformity of the simulated numerical models response. In second step, nineteen models with different shape were prepared and tested under point load test. According to the obtained results, as the size of the models increases, the point load strength index increases. It is also found that the shape of particles has no major effect on its tensile strength. Our findings show that the dominant failure pattern for numerical models is breaking the model into two pieces. Also a criterion was rendered numerically for determination of tensile strength of gypsum. The proposed criteria were cross checked with the results of experimental point load test.

• International Journal of Highway Engineering
• /
• v.12 no.4
• /
• pp.203-209
• /
• 2010

The base asphalt mixtures that used the waste recycle asphalt correcting from the four different overlay construction sites in Seoul city were made using the foamed asphalt method. The sample mixtures were made in different ratio of the recycle asphalt and new asphalt material and the performance of the mixtures of the different ratio was investigated in the laboratory. The laboratory tests includes the Marshall test, the indirect tensile test, the resilient modulus test, the creep test and the wheel tracking test. The test of the recycle foamed asphalt mixtures(RFA) were compared with the those of the recycle hot mix asphalt(RHA) mixtures. The performance of the RFA is comparable to that of the RHA. On the other hand, the indirect tensile strength of the RFA in dry condition is lower than that of RHA and the indirect tensile strength of the RFA in wet condition is much lower than that of the RHA.

• International Journal of Highway Engineering
• /
• v.20 no.1
• /
• pp.47-58
• /
• 2018

PURPOSES : The purpose of this study is to evaluate the mechanical properties of a cold-recycling asphalt mixture used as a base layer and to determine the optimum emulsified-asphalt content for ensuring the mixture's performance. METHODS : The physical properties (storage stability, mixability, and workability) of three types of asphalt emulsion (CMS-1h, CSS-1h, and CSS-1hp) were evaluated using the rotational viscosity test. Asphalt emulsion residues, prepared according to the ASTM D 7497-09 standard, were evaluated for their rheological properties, including the $G*/sin{\delta}$and the dynamic shear modulus (${\mid}G*{\mid}$). In addition, the Marshall stability, indirect tensile strength, and tensile-strength ratio (TSR) were evaluated for the cold-recycling asphalt mixtures fabricated according to the type and contents of the emulsified asphalt. RESULTS : The CSS-1hp was found to be superior to the other two types in terms of storage stability, mixability, and workability, and its $G*/sin{\delta}$ value at high temperatures was higher than that of the other two types. From the dynamic shear modulus test, the CSS-1hp was also found to be superior to the other two types, with respect to low-temperature cracking and rutting resistance. The mixture test indicated that the indirect tensile strength and TSR increased with the increasing emulsified-asphalt content. However, the mixtures with one-percent emulsified-asphalt content did not meet the national specification in terms of the aggregate coverage (over 50%) and the indirect tensile strength (more than 0.4 MPa). CONCLUSIONS : The emulsified-asphalt performance varied greatly, depending on the type of base material and modifying additives; therefore, it is considered that this will have a great effect on the performance of the cold-recycling asphalt pavement. As the emulsified-asphalt content increased, the strength change was significant. Therefore, it is desirable to apply the strength properties as a factor for determining the optimum emulsified-asphalt content in the mix design. The 1% emulsified-asphalt content did not satisfy the strength and aggregate coverage criteria suggested by national standards. Therefore, the minimum emulsified-asphalt content should be specified to secure the performance.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.11
• /
• pp.1010-1015
• /
• 2008

In this study, the characteristics of aluminum tube hydroformed products at different extrusion type and heat treatment conditions were investigated. For the investigation, as-extruded, full annealed and T6-treated Al 6061 tubes at different extrusion type were prepared. To evaluate the hydroformability, free bulge test was performed at room temperature to $300^{\circ}C$. Also mechanical properties of hydroformed products at various pre- and post-heat treatments were estimated by hexagonal prototype hydroforming test at $250^{\circ}C$. And the tensile test specimens were obtained from hexagonal prototype hydroformed tube. As a results, hydroformability of full annealed tube is $5{\sim}8%$ higher than that of extruded and T6-treated tube. The tensile strength and elongation of T6-post heat treated indirect extrusion tube were more than 330MPa and 12%, respectively. However, T6 pre treated hydroformed product represents high strength, 330MPa and low elongation, 8%. Therefore, Hydroformability of Al6061 tube showed similar value for both extrusion types. However flow stress of direct tube showed $20{\sim}50MPa$ lower value than indirect tube.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.305-312
• /
• 2017

This paper presents a laboratory investigation into the effects of fillers using industrial by-product such as coal ash, IGCC slag on properties of hot-mixed asphalt concrete variation with filler content. For comparison, existing mixture with lime and dust have also been considered. Marshall and flow test has been considered for the purpose of mix design as well as evaluation of mixture. Other performance tests such as indirect tensile strength test, tensile strength ratio(moisture susceptibility), dynamic stability have also been carried out variation with filler content. It is observed that the mixes with industrial by-product exhibit conform with quality standard. Therefore, it has been recommended to utilize industrial by-product based on fly ash wherever available, not only reducing the produce cost but also partly solve the industrial by-product utilization and disposal problem.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.279-286
• /
• 2019

In this study, an experimental study on the tensile properties of steel fiber-reinforced ultra high strength concrete(UHSC) with a standard compressive strength of 180MPa was performed. Steel fibers with a volume ratio of 1% were mixed to prepare direct tensile strength specimens and prism specimens for the three-point bending test. The fabricated specimens were set up in the middle section of the specimen to induce cracks, and the test was carried out according to each evaluation method. First, the stress-strain curves were analyzed by performing direct tensile strength tests to investigate the behavior characteristics of concrete after cracking. In addition, the load-CMOD curve was obtained through the three-point bending test, and the inverse analysis was performed to evaluate the stress-strain curve. Tensile behavior characteristics of the direct tensile test and the three-point bending test of the indirect test were similar. In addition, the tensile stress-strain curve modeling presented in the SC structural design guidelines was performed, and the comparative analysis of the measured and predicted values was performed. When the material reduction factor of 1.0 was applied, the predicted value was similar to the measured value up to the strain of 0.02, but when the material reduction factor of 0.8 was applied, the predicted value was close to the lower limit of the measured value. In addition, when the strain was greater than 0.02, the predicted value by SC structural design guideline to underestimated the measured value.

• Tunnel and Underground Space
• /
• v.26 no.4
• /
• pp.316-326
• /
• 2016

The purpose of this study is to investigate the influence of cleavages on indirect tensile strength (ITS) of the granite. Brazilian disc tests and ring tests with three different hole sizes were performed. 2D DEM (Discrete Element Method) simulation was employed to further understand the failure process during the tests and the mechanism behind. Results show that ITS decreases across hardway, grain and rift cleavage. Measured average ITS from ring tests is about 2.5 ~ 6.4 times of those measured from Brazilian disc tests, and it decreases with increasing ratio of diameters of inner hole and specimen. Failure pattern in ring tests is influenced by both hole size and relative positions of cleavages parallel and perpendicular to the loading direction.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.4
• /
• pp.489-495
• /
• 2016

In this study, the Warm-Mix Asphalt was prepared using a modified Sulfur Binder mixed with an additive of a polymer component in sulfur, which is an industrial by-product generated in the crude oil refining process. The dynamic stability and durability characteristics of the prepared Warm-Mix Asphalt was evaluated by the indirect tensile strength, the tensile strength ratio before and after water immersion and freezing-thawing, and the dynamic stability by wheel tracking test. The Warm-Mix Asphalt Mixtures using Modified Sulfur Binder has a tensile strength ratio before and after water immersion of 0.88, which is about 1.13 times that of the Warm-Mix formed modified Asphalt, and the tensile strength ration before and after freezing-thawing is also 0.82, thus, all tensile strength ratios satisfied the KS quality standard value of 0.75 or more. The indirect tensile strength was 1.6MPa which was twice the KS quality standard value of 0.8MPa, and about 1.24 times higher than that of normal heated asphalt 1.29MPa. In addition, the dynamic stability by the wheel tracking test was 14,075 times/mm, which was about 15 times higher than that of normal heated asphalt and about 3 times higher than that of the Warm-Mix formed modified Asphalt, showing excellent resistance to plastic deformation such as fatigue cracks.