• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.75-81
• /
• 2014

Usage of heavy metal element (Pb, Hg and Cd etc.) in electronic devices have been restricted due to the environmental banning of the European Union, such as WEEE and RoHS. Therefore, it is needed to develop the Pb-free solder plated ribbon in photovoltaic (PV) module. This study described that degradation characteristics of PV module under damp heat (DH, $85^{\circ}C$ and 85% R.H.) condition test for 1,000 h. Solar cell ribbons were utilized to hot dipping plate with Pb-free solder alloys. Two types of Pb-free solder plated ribbons, Sn-3.0Ag-0.5Cu (SAC305) and Sn-48Bi-2Ag, and an electroless Sn-40Pb solder hot dipping plated ribbon as a reference sample were prepared to evaluate degradation characteristics. To detect the degradation of PV module with the eutectic and Pb-free solder plated ribbons, I-V curve, electro-luminescence (EL) and cross-sectional SEM analysis were carried out. DH test results show that the reason of maximum power (Pm) drop was mainly due to the decrease fill factor (FF). It was attributed to the crack or oxidation of interface between the cell and the ribbon. Among PV modules with the eutectic and Pb-free solder plated ribbon, the PV module with SAC305 ribbon relatively showed higher stability after DH test than the case of PV module with Sn-40Pb and Sn-48Bi-2Ag solder plated ribbons.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.17-22
• /
• 2013

We investigated the optimum bonding conditions for thermo-compression bonding of electrodes between flexible printed circuit board(FPCB) and rigid printed circuit board(RPCB) with Sn-58Bi solder as interlayer. In order to figure out the optimum bonding conditions, peel test of FPCB/RPCB joint was conducted. The peel strength was affected by the bonding conditions, such as temperature and time. The fracture energies were calculated through F-x (Force-displacement) curve during peel test and the relationships between bonding conditions and fracture behaviors were investigated. The optimum condition for the thermo-compression bonding with Sn-58Bi solder was found to be temperature of $195^{\circ}C$ and time of 7 s.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.10a
• /
• pp.25-26
• /
• 2006

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.93-95
• /
• 2003

• Proceedings of the KWS Conference
• /
• 1998.05a
• /
• pp.157-158
• /
• 1998

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.45-45
• /
• 1999

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.156-158
• /
• 2001

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.211-220
• /
• 2011

To improve the low ductility and high strain-rate sensitivity in Sn-Bi based solder alloys, the influences of the minor additions of alloying elements (Ag, Mn, In) were investigated. The strain-stress curves of various Sn-40Bi(-X) alloys, including a pre-suggested Sn-40Bi-0.1Cu composition were measured using a tensile testing machine. As a result, the elongation and ultimate tensile strength (UTS) values were compared. The small addition (0.5 wt.%) of Ag significantly enhanced the ductility and high strain-rate sensitivity of the alloys at strain rates of $10^{-4}$ to $10^{-2}\;s^{-1}$ mainly due to the increase and refinement of eutectic lamellar structures. The microstructure change increased the area of grain boundaries, thus ameliorating the grain boundary sliding mode. It was also found that Mn is an effective element in enhancing the ductility, especially at the strain rates of $10^{-3}$ to $10^{-2}\;s^{-1}$ The enhancement is likely attributed to the fine and homogeneous microstructure in the alloys containing Mn.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.35-41
• /
• 2015

In this study, in order to improve the reliability of ACF interconnections, solder ACF joints were investigated interms of solder joint morphology and solder wetting areas, and evaluated the electrical properties of Flex-on-Board (FOB) interconncections. Solder ACF joints with the ultrasonic bonding method showed excellent solder wetting by broken solder oxide layers on solder surfaces compared with solder joints with remaining solder oxide layer bonded by the conventional thermo-compression (TC) bonding method. When higher target temperature was used, Sn58Bi solder joints showed concave shape due to lower degree of cure of resin at solder MP by higher heating rate. ACFs with epoxy resins and SAC305 solders showed lower degree of resin cure at solder MP due to the slow curing rate resulting in concave shaped solder joints. In terms of solder wetting area, solder ACFs with $25-32{\mu}m$ diameters and 30-40 wt% showed highest wetted solder areas. Solder ACF joints with the concave shape and the highest wetting area showed lower contact resistances and higher reliability in PCT results than conventional ACF joints. These results indicate that solder morphologies and wetting areas of solder ACF joints can be controlled by adjustment of bonding conditions and material properties of solder and polymer resin to improve reliability of ACF joints.

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.62-62
• /
• 2006