• 한국염색가공학회지
• /
• 제31권3호
• /
• pp.177-186
• /
• 2019

In this study, we investigated for synthetic hydrotalcite in chloroprene rubber foam. Experiments were carried out to find the optimum content ratio by controlling the contents of MgO and Hydrotalcite. Swelling test in toluene immersion was made to measure the crosslinking density of CR foams, and the cure properties were investigated with flat die rheometer and Mooney viscosity. The difference of hardness, tensile strength and elongation at break were observed after immersing in 7% NaCl or 21% NaCl solutions for a day and four days. In addition, the volume change and water content remaining in CR foam were measured after immersing NaCl solution. As content of MgO increased, the value of the cure torque tended to increase, but it was almost constant above 2phr of MgO. However, the Mooney viscosity decreased with increasing MgO content. The crosslinking density, determined by the swelling ratio, showed that the CR compound without MgO showed a higher degree of swelling. When the content of hydrotalcite/MgO was 3:2, it was the lowest volume change of CR form. Also, As the content of hydrotalcite decreased, the difference of mechanical properties before and after immersion NaCl solution increased.

• 한국멀티미디어학회논문지
• /
• 제25권11호
• /
• pp.1591-1600
• /
• 2022

With the prosperity of Internet, the game industry is occuping an important position in the national economic system. The study on the game industry which has been drawing eyes from researchers is of great significance. Many scholars have done researches on game motivations, but the elements of intrinsic motivation are still in the exploratory stage. This study determines the dimensions of the influencing factors of players 'intrinsic game motivation and their game experience by adopting the method of literature research. A theoretical model is established to explore the influence of intrinsic game motivation on players' game experience. Questionnaires from players of "The Honor of Kings" are collected through the Internet. SPSS 21.0 is utilized to test the model and hypotheses, and finally the results of the data are analysed. It verifies that intrinsic motivation mainly consists of four components: achievement, social interaction, immersion and escapism. By exploring the influence of the four elements on players' experience, it is concluded that the players' immersion and social interaction have a greater positive impact on their game experience. It is indicated that a better game design highlights the storyline of the game and the interaction system is of importance to enable players to gain a better game experience.

• 한국조리학회지
• /
• 제22권3호
• /
• pp.66-78
• /
• 2016

본 연구는 호텔베이커리 종사원의 셀프리더십, 자기효능감, 조직몰입도 간의 관계와 연관성을 실증적으로 규명하여 호텔베이커리조직에 유익한 인적자원관리 정보제공에 목적을 두고 있다. 자료 수집은 2015년 6월 20일부터 7월 10일까지 총 500부를 배포하고, 이중 377부가 회수된 설문지 중 분석에 부적합한 설문지 23부를 제외하고, 354부에 대하여 SPSS 18.0과 AMOS 18.0을 이용하여 요인분석, 신뢰성 검증 및 가설을 검증하기 위해서 공변량 구조분석을 실시하였다. 분석결과를 요약하면, 첫째, 행위중심전략, 자연보상, 건설적 사고전략은 자기효능감에 정(+)의 유의한 영향을 미치는 것으로 분석되었다. 둘째, 자기효능감이 조직몰입에 미치는 영향관계에서 정서적 몰입에 유의한 것으로 나타났으나, 규범적 몰입에는 정(+)의 유의한 영향을 미치지 못하는 것으로 분석되었다. 셋째, 셀프리더십과 조직몰입의 관계를 살펴보면, 행위중심전략, 자연보상은 정서적 몰입에 유의적인 영향을 미치지 못하는 것으로 분석되었다. 그러나 건설적 사고전략은 유의한 영향을 미치는 것으로 분석되었다. 분석결과를 바탕으로 연구에 대한 시사점을 제시하면 다음과 같다. 첫째, 본 연구는 호텔베이커리 종사자의 셀프리더십의 하위차원으로 행위중심전략, 자연보상, 건설적 사고전략을 선행요인으로 설정하여 자기효능감과 조직몰입의 하위차원으로 정서적 몰입과 규범적 몰입을 종속요인으로 각 요인간의 인과관계를 분석하였다는 점에서 호텔베이커리 종사자의 정서적 몰입과 규범적 몰입에 의한 셀프리더십과 자기효능감이 호텔베이커리조직에 대한 안정적인 향상의 가능성을 보여줌으로써 자기효능감 변수들에 대한 앞으로의 연구가능성을 시사한다.

• 대한조선학회 특별논문집
• /
• 대한조선학회 2005년도 특별논문집
• /
• pp.144-150
• /
• 2005

The size of ship is being larger than the past in the shipping industry thanks to the increased quantity of goods transported by ship. Therefore, HHIC (Hanjin Heavy industries & Construction co., LTD) invented innovative construction method, so called 'DAM', to build a ship which is longer than the length of the HHIC's dry dock. On Erection at the sea by the application of DAM Method, Squeezing & Detachment of A/F film may occur as a result of the wave and the constriction between A/F film pre-applied on the side shell and DAM's Rubber Packing. Thus, the test for finding the minimum curing time of A/F film was performed to protect Squeezing & Detachment of A/F film on the hull. To verify the soundness of paint and to find the optimum condition during the erection period of the DAM, laboratory test was carried out under no immersion condition through the application of various coatings on the Rubber Packing. And two methods were selected from the results of laboratory test for actual MOCK-UP Test. In addition, the test for the film profile per temperature of silicone A/F coat and the film Squeezing was performed.

• 대한금속재료학회지
• /
• 제46권2호
• /
• pp.80-87
• /
• 2008

Many researches related to the reliability of Pb-free solder joints with PCB (printed circuit board) surface finish under thermal or vibration stresses are in progress, because the electronics is operating in hash environment. Therefore, it is necessary to assess Pb-free solder joints life with PCB surface finish under thermal and mechanical stresses. We have investigated 4-points bending fatigue lifetime of Pb-free solder joints with OSP (organic solderability preservative) and ENIG (electroless nickel and immersion gold) surface finish. To predict the bending fatigue life of Sn-3.0Ag-0.5Cu solder joints, we use the test coupons mounted 192 BGA (ball grid array) package to be added the thermal stress by conducting thermal shock test, 500, 1,000, 1,500 and 2,000 cycles, respectively. An 4-point bending test is performed in force controlling mode. It is considered that as a failure when the resistance of daisy-chain circuit of test coupons reaches more than $1,000{\Omega}$. Finally, we obtained the solder joints fatigue life with OSP and ENIG surface finish using by Weibull probability distribution.

• Corrosion Science and Technology
• /
• 제5권4호
• /
• pp.129-136
• /
• 2006

High temperature corrosion behavior of AISI-type 316L stainless steel for the MCFC(molten carbonate fuel cell) bipolar application was studied by immersion test and penetration attack method in anode environment ($650^{\circ}C$, $Li_2CO_3/K_2CO_3=62/38$ mol%, $H_2/CO_2=80/20$ vol%) without or with different $CaCO_3$ content. Not only immersion test method but also morphological observation of samples in the carbonate melts are adopted as experimental methods. With aid of the morphological observation of cross section of samples immersed in a carbonate melt was possible to obtain penetration attack. The concentration effect of $CaCO_3$ inhibitor was investigated in order to verify the optimum concentration for practical application in MCFC stack operation. The corrosion rate in the presence of $CaCO_3$ was proven to be decreased as a function of $CaCO_3$ concentration. The corrosion rate in the presence of $CaCO_3$ was measured with a value of 6.9 mpy which is 2.4 times lower than that of inhibitor-free electrolyte. The cross section microscopy revealed that the internal penetration by oxidation in molten carbonate is very severe. In this case, the attack was occurred not only dissolution loss in the electrolyte by corrosion reaction but also weight gain through oxide layer by internal penetration.

• The Journal of Advanced Prosthodontics
• /
• 제8권5호
• /
• pp.333-338
• /
• 2016

PURPOSE. The aim of this study was to compare the effects of different denture cleansers on the surface roughness and microhardness of various types of posterior denture teeth. MATERIALS AND METHODS. 168 artificial tooth specimens were divided into the following four subgroups (n=42): SR Orthotyp PE (polymethylmethacrylate); SR Orthosit PE (Isosit); SR Postaris DCL (double cross-linked); and SR Phonares II (nanohybrid composite). The specimens were further divided according to the type of the denture cleanser (Corega Tabs (sodium perborate), sodium hypochlorite (NaOCl), and distilled water (control) (n=14)) and immersed in the cleanser to simulate a 180-day immersion period, after which the surface roughness and microhardness were tested. The data were analyzed using the Kruskal-Wallis test, Conover's nonparametric multiple comparison test, and Spearman's rank correlation analysis (P<.05). RESULTS. A comparison among the denture cleanser groups showed that NaOCl caused significantly higher roughness values on SR Orthotyp PE specimens when compared with the other artificial teeth (P<.001). Furthermore, Corega Tabs resulted in higher microhardness values in SR Orthotyp PE specimens than distilled water and NaOCl (P<.005). The microhardness values decreased significantly from distilled water, NaOCl, to Corega Tabs for SR Orthosit PE specimens (P<.001). SR Postaris DLC specimens showed increased microhardness when immersed in distilled water or NaOCl when compared with immersion in Corega Tabs (P<.003). No correlation was found between surface roughness and microhardness (r=0.104, P=.178). CONCLUSION. NaOCl and Corega Tabs affected the surface roughness and microhardness of all artificial denture teeth except for the new generation nanohybrid composite teeth.

• 한국산학기술학회논문지
• /
• 제15권2호
• /
• pp.1188-1194
• /
• 2014

본 연구의 목적은 플라이 애시, 고로슬래그 미분말, 실리카흄을 사용하여 4성분계 콘크리트의 염해 저항성능을 평가하기 위한 것이다. 본 연구에서는 압축강도, 탄성계수, 염수침지 시험, 염화물 확산계수 및 침투계수를 실시하였다. 4성분계 콘크리트의 염화물 확산계수와 침투계수는 재령 17주에 $0.032{\times}10^{-12}m^2/sec$와 650 coulomb으로 측정되었다. 또한 침지시험 결과 염화물 이온 침투깊이와 염화물량은 3.7 mm and $10.211kg/m^3$로 측정 되었다. 이러한 결과로부터 플라이 애시, 고로슬래그 미분말, 실리카흄을 사용하여 제조한 4성분계 콘크리트는 염해 저항성능과 역학적 특성이 매우 높을 것을 알 수 있었다.

• 한국가스학회지
• /
• 제3권3호
• /
• pp.39-44
• /
• 1999

일반강구조물로 많이 사용되고 있는 SM20C, BsC3 및 STC4H에 대하여, 여러 가지 부식환경(지하수($6,000{\Omega}{\cdot}cm$), $0.5\%\;H_2SO_4$ 및 $0.5\%HNO_3$)침지하에서의 부식특성 및 건조상태에서의 찰과마멸특성실험에 의한 이종금속간의 찰과마멸특성을 고찰하였다. 침지시험의 경우, 이들 금속의 전위값은 $HNO_3$, 지하수, $H_2SO_4$ 순으로 크게 나타났으며, BsC3을 제외한 동재금속보다 이종금속의 전위가 높았다. 동종재인 SM20C의 마멸은 회전측의 경우가 이동측보다 약 1.9배 증가하였으며, 이는 마찰력에 의한 표면경화가 그 원인인 것으로 추측된다.

• Journal of the Korean Wood Science and Technology
• /
• 제47권4호
• /
• pp.418-424
• /
• 2019

Densification is a process for improving the strength properties of wood from the felling of young trees, which is a common harvest practice in community forests. A series of experiments was conducted to refine the process with particular regard to the determination of suitable pretreatment and treatment conditions. Samples of pine and gmelina measuring $23cm(L){\times}20cm(W){\times}2cm(T)$ underwent pretreatment through immersion in a 1:1 $CH_3COOH-H_2O_2$ solution at concentrations of 15%, 20%, and 30%. Samples pretreated with the 20% solution showed the greatest improvement in strength; further experiments were conducted to determine the optimum treatment conditions in terms of temperature and duration following immersion. Test samples with the same dimensions as those in the pretreatment experiment were soaked in a 1:1 20% $CH_3COOH-H_2O_2$ solution and warmed in a water bath. The test samples were then individually hot pressed to the target thickness, which was 30% less than the original thickness and held at $150^{\circ}C$ or $170^{\circ}C$ for 15 or 30 minutes. The treated samples were cut for an analysis of their density, recovery of set, and bending strength. Pine and gmelina exhibited the best characteristics after treatment at $150^{\circ}C$ for 30 and 15 minutes, respectively. The results suggest that the modified densification process had increased the bending strength of the wood, but the temperature and duration of treatment must be carefully considered for different wood species.