• Clean Technology
• /
• v.21 no.4
• /
• pp.209-216
• /
• 2015

Indium-Tin-Oxide (ITO) is a material that is widely used for transparent conductive electrodes (TCEs). Indium (In), chief element of the ITO, is expected to be depleted in the near future owing to its high cost and limited reserves. To overcome the issue, ITO has to be retained by recycling redundant ITO targets after manufacturing processes. In this article, we proposed an efficient recycling way of the redundant ITO targets with investigation of the current recycling tendencies in domestic and foreign countries. As a result, it was revealed that only In is recycled from the redundant targets in domestic and Japan. As well, fabrication of TCEs is being researched with ITO nanoparticles solutions. However, since the TCEs fabricated with ITO target is superior to those with other materials, it is thought that establishment of regeneration technology of ITO itself is demanded for an efficient recycling and fabrication of ITO target.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.221-221
• /
• 2012

Small-molecule organic photovoltaic cells have recently attracted growing attention due to their potential for the low-cost fabrication of flexible and lightweight solar modules. The PVP/Ag nanoparticles were synthesized by the reaction of poly vinylpyrrolidone (PVP) and silver nitrate at $150^{\circ}C$. In the reaction, the size of the nanoparticles was controlled by relative mole fractions between PVP and Ag. The PVP/Ag nanoparticles with various sizes were then spin coated on the patterned ITO glass prior to the deposition of the PEDOT:PSS hole transport layer. The scattering of the incident light caused by these incorporated nanoparticles resulted in an increase in the path length of the light through the active layer and hence the enhancement of the light absorption. This scattering effect increased as the size of the nanoparticles increased, but it was offset by the decrease in total transmittance caused by the non-transparent nanoparticles. As a result, the maximum power conversion efficiency, 0.96% which was the value enhanced by 14% compared to the cell without incorporation of nanoparticles, was obtained when the mole fraction of PVP:Ag was 24:1 and the size of the nanoparticles was 20~40 nm.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.9
• /
• pp.1827-1830
• /
• 2008

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.390.2-390.2
• /
• 2016

Single crystalline indium-tin-oxide (ITO) nanowires (NWs) were grown by sputtering method. A thin Ni film of 5 nm was coated before ITO sputtering. Thermal treatment forms Ni nanoparticles, which act as templates to diffuse Ni into the sputtered ITO layer to grow single crystalline ITO NWs. Highly optical transparent photoelectric devices were realized by using a transparent metal-oxide semiconductor heterojunction by combining of p-type NiO and n-type ZnO. A functional template of ITO nanowires was applied to this transparent heterojunction device to enlarge the light-reactive surface. The ITO NWs/n-ZnO/p-NiO heterojunction device provided a significant high rectification ratio of 275 with a considerably low reverse saturation current of 0.2 nA. The optical transparency was about 80% for visible wavelengths, however showed an excellent blocking UV light. The nanostructured transparent heterojunction devices were applied for UV photodetectors to show ultra fast photoresponses with a rise time of 8.3 mS and a fall time of 20 ms, respectively. We suggest this transparent and super-performing UV responser can practically applied in transparent electronics and smart window applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.321-321
• /
• 2010

The PEDOT:PSS layer is usually used as hole transporting layer for the polymer bulk heterojunction solar cells. However, the interface between ITO and PEDOT:PSS is not stable and the chemical reaction between ITO and PEDOT can result in degraded device performance. We used the tungsten oxides as a hole transport layer by spin-coating. The $WO_3$ nanoparticles were well dispersed in ammonium hydroxide and deionized water and formed thin layer on the ITO anode. We found that $WO_3$ surface is more hydrophobic than the bare ITO or PEDOT:PSS-coated surfaces. The hydrophobic surfaces promote an ordered growth of P3HT films. A higher degree of P3HT ordering is expected to improve the hole mobility and the lifetime of the device using the tungsten oxide showed better stability compared to the device using the PEDOT:PSS.

• Journal of the Korean Chemical Society
• /
• v.50 no.1
• /
• pp.32-36
• /
• 2006

films of gold nanoparticles were formed on indium tin oxide (ITO) by an electrodeposition method from an aminosilicate stabilized gold colloid solution. The thin films were examined by cyclic voltammetry (CV), scanning electron microscopy (SEM), UV-visible, and energy dispersive X-ray spectroscopy (EDXS). The surface coverage of gold nanoparticles on the thin film was estimated to 1.2 nanomole/cm2. An anthraquinone-2, 6-disulfonic acid, disodium salt (AQDS) self-assembled layer was generated by immersing gold thin film into 1mM of AQDS in 0.1M HClO4 solution for over 20 hours. As a result, a new absorbance peak from the multi-layers (AQDS/thin film of gold /ITO) was obtained about at 690 nm. Also, the surface plasmon absorption of multi-layers was measured by UV-Visible spectrometer along with chronoamperometry by applying the various potentials from +0.5V to -0.5V. The maximum surface plasmon absorption band at 550 nm was decreased by applying negative potentials. The change of absorbance was correlated with the surface coverage of the AQDS indicating the pseudo-capacity surface state of the AQDS layer was coupled to the energy level of the plasmonband by applied negative potentials.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.37-40
• /
• 2004

CdTe nanoparticles were synthesized in aqueous solution by colloidal method. The absorption and photoluminescence(PL) spectrum of the synthesized CdTe nanoparticles revealed the strong exitonic peak in the visible region. Photocurrent of CdTe nanoparticles were observed in the structure of Al/CdTe/ITO that was fabricated by spin coating of CdTe nanoparticles. The wavelength dependence of photocurrent was very similar to the absorption spectrum, indicating the charges generated by the absorption of photons give direct contribution to photocurrent. This study suggests that CdTe nanoparticles are very prospective materials for optoelectronics.

• Korean Membrane Journal
• /
• v.5 no.1
• /
• pp.54-60
• /
• 2003

The rejection properties and flux rates of silica nanoparticles in ultrafiltration membranes has been investigated. Cross-flow permeation experiments were conducted using polycarbonate track-etch flat membranes with pore sizes of 30 and 50 nm, and a silica nanoparticle solute with particle sizes of 5 and 18 nm with narrow size distributions. The fluxes and rejection factors were investigated at various particle concentrations, cross-flow velocities, pH, and ionic strengths of solution. Even though the size of the silica nanoparticles was much smaller than that of the membrane pores, the observed rejection rates were very high compared with those for a similar-sized polymer (dextran). The observed rejection rate decreased with increasing ionic strength, which implies that the transport mechanism of the silica nanoparticles is significantly influenced by electrostatic repulsion between particles and membranes.

• Journal of the Korean Ceramic Society
• /
• v.48 no.1
• /
• pp.94-98
• /
• 2011

A Sn-doped $In_2O_3$ (ITO) nanowire photoelectrode was produced using a simple metal evaporation method at low synthesis temperature (< $540^{\circ}C$). The nanowire electrodes have large surface area compared with that of flat ITO thin film, and show low electrical resistivity of $5.6{\times}10^{-3}{\Omega}cm$ at room temperature. In order to apply ITO nanowires to the photoelectrodes of dye-sensitized solar cell (DSSC), those surfaces were modified by $TiO_2$ nanoparticles using a chemical bath deposition (CBD) method. The conversion efficiency of the fabricated $TiO_2$/ITO nanostructure-based DSSC was obtained at 1.4%, which was increased value by a factor of 6 than one without ITO nanowires photoelectrode. This result is attributed to the large surface area and superior electrical property of the ITO nanowires photoelectrode, as well as the structural advantages, including short diffusion length of photo-induced electrons, of the fabricated $TiO_2$/ITO nanostructure-based DSSC.

• Composites Research
• /
• v.24 no.5
• /
• pp.17-22
• /
• 2011

Recently transparent electrodes using carbon nanotube (CNT) have been studied actively to replace conventional ITO. In this work, CNT or ITO coated poly(ethylene terephthalate) (PET) were prepared by controlling the surfaces since the cohesion degree depends upon drying conditions. As transparent electrode application, 3 drying temperatures were set as 20, 80, and $120^{\circ}C$ to produce the change of surface properties. Interfacial durability and electrical properties of prepared transparent electrodes were evaluated by electrical resistance measurement. Surface change with changing drying temperature was observed by FE-SEM, whereas the transparency change was measured by UV-spectroscopy. The electronic properties of nanoparticle coated surface were evaluated using cyclic voltametry method upon the surface change with controlled drying temperature. Durability of CNT coated surfaces was better than ITO coated ease. As drying temperature increased, better coated surface was prepared due to improved cohesion among nanoparticles, which resulted in increased electrical properties.