• 한국진공학회지
• /
• 제7권s1호
• /
• pp.30-36
• /
• 1998

The plasma-spray technique is currently the most frequently used method to produce calcium phosphate coatings. Hydroxyapatite(HAp), one form of calcium phosphate, is preferred by its ability to form a direct bond with living bone, resulting in improvements of implant fixation and faster bone healing. Recently, concerns have been raised regarding the viable use and long-term stability of plasma-spray HAp coatings due to its nature of comparatively thick, porous, and poor bonding strength to metal implants. Thin layers (maximum of few microns) of calcium phosphate were formed by an e-beam evaporation with and without ion bombardments. The Ca/P ration of film was controlled by either using the evaporants having the different ration of Ca/P with addition of CaO, or adjusting the ion beam assist current. The Ca/P ration had great effects on the structure formation after heat treatment and the dissolution bahavior. The calcium phosphate films produced by IBAD exhibited high adhesion strength.

• International Journal of Oral Biology
• /
• 제43권2호
• /
• pp.83-91
• /
• 2018

Nonthermal atmospheric plasma has been studied for its many biomedical effects, such as tooth bleaching, wound healing, and coagulation. In this study, the effects of dentinal tubules occlusion were investigated using fluoride-carboxymethyl cellulose (F-CMC) gel, nano-sized hydroxyapatite (n-HA), and nonthermal atmospheric plasma. Human dentin specimens were divided to 5 groups (group C, HA, HAF, HAP, and HAFP). Group HA was treated with n-HA, group HAF was treated with n-HA after a F-CMC gel application, group HAP was treated with n-HA after a plasma treatment and group HAFP was treated with n-HA after a plasma and F-CMC gel treatment. The occlusion of dentinal tubules was investigated using scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS), which shows Ca/P ratio. In the EDS results, a higher Ca/P ratio was shown in the groups including n-HA than in the control group. The specimens of group HAP and HAFP had a higher Ca/P ratio in retentivity. In the SEM results, there was not a significant difference in the amount of times applied. Therefore, this study suggests F-CMC gel and n-HA treatment using nonthermal atmospheric plasma will be a new treatment method for decreasing hypersensitivity.

• Bulletin of the Korean Chemical Society
• /
• 제34권1호
• /
• pp.221-224
• /
• 2013

Three different kinds of hydroxyapatites (HAPs) having different sizes and compositions are prepared by hydrothermal and molten salt syntheses. Using the ion exchange reactions, ruthenium ions are incorporated on the surface of HAPs. The crystallinity, morphology and ruthenium contents are investigated by XRD, SEM, TEM and ICP. We found that smaller size of HAP having large amounts of ruthenium under ion exchange reaction shows higher catalytic activity for aerobic oxidation of alcohols.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2007년도 추계학술발표대회 및
• /
• pp.146.2-146.2
• /
• 2007

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2007년도 추계학술발표대회 및
• /
• pp.147.1-147.1
• /
• 2007

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 추계학술대회 논문집
• /
• pp.141-141
• /
• 2015

In this study, a series of hydroxyaptite (HAp) are produced on Ti dental implant using electrochemical deposition. Based on the preliminary analysis of the coating structure, composition and morphology. In vitro studies were performed with MC3T3-E1 cell to investigate the effect of biological change on different surface conditions.

• 생명과학회지
• /
• 제24권6호
• /
• pp.642-647
• /
• 2014

치아과민증은 치아의 병적인 증세는 아니지만 치아뿌리가 잇몸밖으로 노출되어 외부의 자극에 대한 민감한 반응으로 환자가 통증을 느끼는 것을 말한다. 칫솔질이나 잇몸질환 등의 다양한 원인이 있으며 치료를 위해서는 자극을 줄여 주는 방법으로 치아과민치료활성이 있는 물질을 이용하거나 레진으로 들어난 치주를 도포하는 방법이 있다. 본 연구에서 수산화인회석과 인산삼칼슘을 혼합하여 만든 치약과 시중에 판매하고 있는 불소함유치약을 4주간 사용하면서 치주과민성 치료효과를 비교 조사하였다. 첨가한 수산화인회석과 인산삼칼슘의 순도는 XRD분석결과 99% 이상으로 나타났으며, 제조한 치약(Hap-TCP)에는 각각 10%와 19%(W/W) 되게 첨가하였다. 치아과민성 치료효과를 VRS값으로 조사한 결과 사용직후에는 대조군과 차이가 없었으나, 1주후에는 대조군에 비해 8% 통증감소효과가 나타났고, 2주와 4주 후에는 각각 30%와 60%정도 통증감소효과가 나타났다. 그리고 냉자극에 대한 지각과민증을 VAS값으로 조사한 결과도 초기에는 차이가 없었으나, 1주, 2주, 4주 후에 측정한 결과 기간에 따라 유의적으로 감소하였다. 4주후에는 VAS값이 3배이상 차이를 보였다. 이 결과는 현미경관찰에서도 확인이 되어진 것과 같이 수산화인회석이 확장된 상아세관들을 메우고, 구강내의 칼슘, 인 등 이온평형을 인산삼칼슘이 조절하여 메워진 상아세관을 안정적으로 자리를 잡도록 도와주는 재석회화현상으로 치아과민증상을 완화하는 것으로 확인되었다.

• Structural Engineering and Mechanics
• /
• 제86권4호
• /
• pp.487-501
• /
• 2023

Nanoparticles have lower size and larger specific surface area, good stability and less toxic and side effects. In recent years, with the development of nanotechnology, its application range has become wider and wider, especially in the field of biomedicine, which has received more and more attention. Bone defect repair materials with high strength, high elasticity and high tissue affinity can be prepared by nanotechnology. The purpose of this paper was to study how to analyze and study the composite materials for sports bone injury based on multifunctional nanomaterials, and described the electrospinning method. In this paper, nano-sized zirconia (ZrO₂) filled micro-sized hydroxyapatite (HAP) composites were prepared according to the mechanical properties of bone substitute materials in the process of human rehabilitation. Through material tensile and compression experiments, the performance parameters of ZrO₂/HAP composites with different mass fraction ratios were analyzed, the influence of filling ZrO₂ particles on the mechanical properties of HAP matrix materials was clarified, and the effect of ZrO₂ mass fraction on the mechanical properties of matrix materials was analyzed. From the analysis of the compressive elastic modulus, when the mass fraction of ZrO₂ was 15%, the compressive elastic modulus of the material was 1222 MPa, and when 45% was 1672 MPa. From the analysis of compression ratio stiffness, when the mass fraction of ZrO₂ was 15%, the compression ratio stiffness was 658.07 MPa·cm³/g, and when it was 45%, the compression ratio stiffness is 943.51MPa·cm³/g. It can be seen that by increasing the mass fraction of ZrO₂, the stiffness of the composite material can be effectively increased, and the ability of the material to resist deformation would be increased. Typically, the more stressed the bone substitute material, the greater the stiffness of the compression ratio. Different mass fractions of ZrO₂/HAP filling materials can be selected to meet the mechanical performance requirements of sports bone injury, and it can also provide a reference for the selection of bone substitute materials for different patients.

• 공업화학
• /
• 제29권6호
• /
• pp.740-745
• /
• 2018

본 연구에서는 비정질 칼슘 포스페이트(ACP) 나노 입자의 합성과 특성 분석을 진행하였다. 염화칼슘(calcium chloride ($CaCl_2$))과 아데노신 인산나트륨(disodium adenosine triphosphate ($Na_2ATP$)) 그리고 피트산 나트륨(sodium phytate) 첨가제를 열수 반응을 통해 상대적으로 단분산된 100 nm 크기 이하의 ACP 나노 입자를 성공적으로 합성하였고 나노 입자의 화학적 조성과 구조를 재료 분석을 통해 확인하였다. 피트산 나트륨 첨가제의 사용을 통해 얻은 ACP 나노 입자는 비정질성을 유지하고 결정성 하이드록시아파타이트(HAP)로의 전환을 방지하는 안정성이 향상되었음을 발견하였다. 본 연구를 통해 발견된 향상된 안정성을 가지는 ACP 나노 입자는 재생 의학 분야에서의 생체 적합 물질로의 응용에 중요한 잠재적 용도가 있을 것이라 사료된다.

• 치위생과학회지
• /
• 제14권2호
• /
• pp.191-197
• /
• 2014

본 연구는 전문가의 지도 없이 소비자가 쉽게 구매할 수 있는 일반적 치아 미백제에 대한 연구로 과산화수소의 함량제한이 있는 국내 사용 환경에서 보다 효과적인 미백 효능을 제공하고자 동일 과산화수소 함량에서 미백 효과를 증진시켜 줄 수 있는 금속 이온 등을 함유한 primer에 대해 착색시킨 수산화인회석 시편을 이용한 실험실적 방법으로 미백효과를 평가하였다. 평가원료들은 인체 안전성을 고려하여 식품 첨가물 공전에 수재된 원료에서 선별하였으며 금속 이온의 종류 및 염의 종류에 따른 효과를 평가한 결과 3가 철 이온을 방출하는 염화제이철을 함유한 primer를 적용 시 미백 효과가 가장 우수하였다. 여기에 제삼인산칼륨을 사용하여 pH를 알칼리조건으로 만든 pH 10.0 primer를 적용 시 더욱 미백 효과가 증가됨을 확인하였으며 primer를 사용하지 않은 대조군과 시간에 따른 미백 효과를 비교한 결과 30분 부착 시 1.75배의 명도 변화량을 나타내었다. 본 연구는 인공 재료와 인공적 실험 환경에서 이뤄진 실험실적 연구로서 실제 인체에 적용 시 안전성이나 부수적 효과에 대해서는 추후 추가적으로 평가해야 할 필요가 있으나 제한된 과산화수소 함량에서 primer의 사용으로 미백 효과를 극대화할 수 있다는 것을 확인하였다는 점에서 의미가 있다고 생각된다.