• Korean Journal of Materials Research
• /
• v.15 no.2
• /
• pp.134-138
• /
• 2005

This study was performed to investigate the surface properties of electrochemically oxidized pure niobium by anodic oxide and hydrothermal treatment technique. Niobium specimens of $10mm\times10mm\times1.0mm$ in dimension were polished sequentially from $\#600,\;\#800,\;\#1000$ emery paper. The surface of pure niobium sperimens was anodized in an electrolytic solution that was dissolved calcium and phosphate in water. The electrolytic voltage was set in the range of 250 V and the current density was $10mA/cm^2$. The specimen was hydrothermal treated in high-pressure steam at $300^{\circ}C$ for 2 hours using an autoclave. And all specimens were immersed in the in the Hanks' solution nth pH 7.4 at $37^{\circ}C$ for 30 days. The surface of specimen was characterized by surface roughness, scanning electron microscope(SEM), energy dispersion X-ray analysis(EDX), X-ray photoemission spectroscopy(XPS) test. The value of surface roughness was the highest in the anodized sample and $0.41{\pm}0.04\;{\mu}m$. The results of the SEM observation show that oxide layers of the multi porosity in the anodized sample were piled up on another, and hydroxyapatite crystal was precipitate from the surface of the hydrothermal treated sample. In the XPS analysis, O, Nb, C peak and small amounts of N peak were found in the polished specimens while Ca and P peak in addition to O, Nb, C and peak were observed in the hydrothermal treated sample.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.5
• /
• pp.617-627
• /
• 2006

Statement of problem: HA has been used as a coating material on Ti implants to improve osteoconductivity. However. it is difficult to form uniform HA coatings on implants with complex surface geometries using a plasma spraying technique. Purpose : To determine if Ti6Al4V sintered porous-surfaced implants coated with HA sol-gel coated and hydrothermal treated would accelerate osseointegration. Materials and Methods : Porous implants which were made by electric discharge were used in this study. Implants were anodized and hydrothermal treatment or HA sol-gel coating was performed. Hydrothermal treatment was conducted by high pressure steam at $300^{\circ}C$ for 2 hours using a autoclave. To make a HA sol, triethyl phosphite and calcium nitrate were diluted and dissolved in anhydrous ethanol and mixed. Then anodized implant were spin-coated with the prepared HA sols and heat treated. Samples were soaked in the Hanks solution with pH 7.4 at $37^{\circ}C$ for 6 weeks. The microstructure of the specimens was observed with a scanning electron microscope (SEM), and the composition of the surface layer was analyzed with an energy dispersive spectroscope (EDS). Results : The scanning electron micrographs of HA sol-gel coated and hydrothermal treated surface did not show any significant change in the size or shape of the pores. After immersion in Hanks' solution the precipitated HA crystals covered macro- and micro-pores The precipitated Ca and P increased in Hanks' solution that surface treatment caused increased activity. Conclusion : This study shows that sol-gel coated HA and hydrothermal treatment significantly enhance the rate of HA formation due to the altered surface chemistry.

• Journal of the Society of Disaster Information
• /
• v.16 no.2
• /
• pp.383-391
• /
• 2020

Purpose: To identify internal self ignition and ignition caused by external flames in energy storage rooms, and to analyze the difference between ignition due to overheating and ignition caused by external heat sources. Method: membrane melting point measurement, battery external hydrothermal experiment, battery overcharge experiment, comparative analysis of electrode plate during combustion by overcharge and external heat, overcharge combustion characteristics, external hydrothermal fire combustion characteristics, 3.4 (electrode plate comparison) / 3.5 (overcharge) /3.6 (external sequence) analysis experiment. Result: Since the temperature difference was very different depending on the position of the sensor until the fire occurred, it is judged that two temperature sensors per module are not enough to prevent the fire through temperature control in advance. Conclusion: The short circuit acts as an ignition source and ignites the mixed gas, causing a gas explosion. The electrode breaks finely due to the explosion pressure, and the powder-like lithium oxide is sparked like a firecracker by the flame reaction.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.12
• /
• pp.822-827
• /
• 2017

Mg/Al layered double hydroxide with two-dimensional (2D) nanostructures was synthesized by a hydrothermal technique. The morphology and aspect ratio of $Mg_4Al_2(OH)_{14}3H_2O$ were controlled by the concentration and kinds of the hydrolysis agent, and temperature. The aspect ratio of $Mg_4Al_2(OH)_{14}3H_2O$ layered double hydroxides with the 2D hexagonal crystal structure was tailored from about 12.6 to about 45.7. The intercalated $CO{_3}^{2-}$ anions of the synthesized 2D $Mg_4Al_2(OH)_{14}3H_2O$ layered double hydroxides were exchanged to $NO_3{^-}$ anions. The bulk 2D $Mg_4Al_2(OH)_{14}3H_2O$ layered double hydroxides with the increased space between two layers due to the anion exchange were exfoliated in a formamide solution. The aspect ratio of the exfoliated 2D $Mg_4Al_2(OH)_{14}3H_2O$ layered double hydroxides increased to 570.3.

• Journal of Hydrogen and New Energy
• /
• v.28 no.4
• /
• pp.426-432
• /
• 2017

Hydrothermal carbonization (HTC) is an effective and environment friendly technique; it possesses extensive potential towards producing high-energy density solid fuels. it is a carbonization method of thermochemical process at a relatively low temperature ($180-250^{\circ}C$). It is reacted by water containing raw material. However, the production and quality of solid fuels from HTC depends upon several parameters; temperature, residence time, and pressure. This study investigates the influence of operating parameters on solid fuel production during HTC. Especially, when food waste was reacted for 2 hours, 4 hours, and 8 hours at $200^{\circ}C$ and 2.0-2.5 MPa, Data including heating value, proximate analysis and water content was consequently collected and analyzed. It was found that reaction temperature, residence time are the primary factors that influence the HTC process.

• Korean Journal of Materials Research
• /
• v.17 no.5
• /
• pp.273-277
• /
• 2007

Vertically aligned Zinc Oxide rod arrays were grown by the self-assembly hydrothermal process on the GaN epitaxial layer which has a same lattice structure with ZnO. Zinc nitrate and DETA solutions are used in the hydrothermal process. The $(HfO_2)$ thin film was deposited on GaN and the patterning was made by the photolithography technique. The selective growth of ZnO rod was achieved with the patterned GaN substrate. The fabricated ZnO rods are single crystal, and have grown along hexagonal c-axis direction of (002) which is the same growth orientation of GaN epitaxial layer. The density and the size of ZnO rod can be controlled by the pattern. The optical property of ordered array of vertical ZnO rods will be discussed in the present work.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.401-406
• /
• 2018

We investigated the effect of ZnO seed layer thickness on the density of ZnO nanorod arrays. ZnO has been deposited using two distinct processes consisting of the seed layer deposition using ALD and subsequent hydrothermal ZnO growth. Due to the coexistence of the growth and dissociation during ZnO hydrothermal growth process on the seed layer, the thickness of seed layer plays a critical role in determining the nanorod growth and morphology. The optimized thickness resulted in the regular ZnO nanorod growth. Moreover, the introduction of ALD to form the seed layer facilitates the growth of the nanorods on ultrathin seed layer and enables the densification of nanorods with a narrow change in the seed layer thickness. This study demonstrates that ALD technique can produce densely packed, virtually defect-free, and highly uniform seed layers and two distinctive processes may form ZnO as the final product via the initial nucleation step consisting of the reaction between $Zn^{2+}$ ions from respective zinc precursors and $OH^-$ ions from $H_2O$.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.401-406
• /
• 2018

We investigated the effect of ZnO seed layer thickness on the density of ZnO nanorod arrays. ZnO has been deposited using two distinct processes consisting of the seed layer deposition using ALD and subsequent hydrothermal ZnO growth. Due to the coexistence of the growth and dissociation during ZnO hydrothermal growth process on the seed layer, the thickness of seed layer plays a critical role in determining the nanorod growth and morphology. The optimized thickness resulted in the regular ZnO nanorod growth. Moreover, the introduction of ALD to form the seed layer facilitates the growth of the nanorods on ultrathin seed layer and enables the densification of nanorods with a narrow change in the seed layer thickness. This study demonstrates that ALD technique can produce densely packed, virtually defect-free, and highly uniform seed layers and two distinctive processes may form ZnO as the final product via the initial nucleation step consisting of the reaction between Zn²⁺ions from respective zinc precursors and OH^- ions from H₂O.

• Journal of the Optical Society of Korea
• /
• v.18 no.4
• /
• pp.307-316
• /
• 2014

Improved power conversion efficiency of hybrid solar cells with ITO/ZnO seed layer/ZnO NRs/ZnS QDs/P3HT/PCBM/Ag structure was obtained by optimizing the growth period of ZnO nanorods (NRs). ZnO NRs were grown using a hydrothermal method on ZnO seed layers, while ZnS quantum dots (QDs) (average thickness about 24 nm) were fabricated on the ZnO NRs by the successive ionic layer adsorption and reaction (SILAR) technique. Morphology, crystalline structure and optical absorption of layers were analyzed by a scanning electron microscope (SEM), X-ray diffraction (XRD) and UV-Visible absorption spectra, respectively. The XRD results implied that ZnS QDs were in the cubic phase (sphalerite). Other experimental results showed that the maximum power conversion efficiency of 4.09% was obtained for a device based on ZnO NR10 under an illumination of one Sun (AM 1.5G, $100mW/cm^2$).

• Membrane and Water Treatment
• /
• v.7 no.6
• /
• pp.495-505
• /
• 2016

Mesoporous MCM-41 was deposited on an inexpensive disk shaped ceramic support through hydrothermal technique for ultrafiltration of $Fe^{3+}$ from aqueous solution. The ceramic support was fabricated using uni-axial compaction technique followed by sintering at $950^{\circ}C$. The characteristics of MCM-41 powder as well as the composite membrane were examined by X-ray diffraction (XRD), thermogravimetric analysis (TGA), field emission scanning electron microscope (FESEM), porosity and pure water permeation test. The XRD result revealed the good crystallinity and well-resolved hexagonally arranged pore geometry of MCM-41. TGA profile of synthesized MCM-41 zeolite displayed the three different stepwise mechanisms for the removal of organic template. The formation of MCM-41 on the porous support was verified by FESEM analysis. The characterization results clearly indicated that the accumulation of MCM-41 by repeated coating on the ceramic disk directs to reduce the porosity and pore size from 47% to 23% and 1.0 to $0.173{\mu}m$, respectively. Moreover, the potential of the fabricated MCM-41 membrane was investigated by ultrafiltration of $Fe^{3+}$ from aqueous stream at various influencing parameters such as applied pressure, initial feed concentration and pH of solution. The maximum rejection 85% was obtained at applied pressure of 276 kPa and the initial feed concentration of 250 ppm at pH 2.