• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.159-160
• /
• 2006

$AgGaSe_2$ single crystal thin films grown by using hot wall epitaxy (HWE) system. The single crystal thin films were investigated by photoluminescence and double crystal X-ray diffraction(DCXD) measurement. From the photoluminescence measurement of $AgGaSe_2$ single crystal thin film, we observed free excition ($E_x$) observable only in high quality crystal and neutral bound exciton ($D^{\circ}$,X) having very strong peak intensity. And, the full width at hall maximum and binding energy of neutral donor bound excition were 8 meV and 14.1 meV, respectively. By Haynes rule, an activation energy of impurity was 141 meV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.136-137
• /
• 2006

The stochiometric mix of evaporating materials for the $ZnGa_2Se_4$ single crystal thin films were prepared from horizental furnace. To obtains the single crystal thin films, $ZnGa_2Se_4$ mixed crystal were deposited on throughly etched Si(100) by the Hot Wall Epitaxy (HWE) system. The temperates of the source and the substrate were $590^{\circ}C$ and $450^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the double crystal X-ray diffraction(DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility dependence on temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.182-183
• /
• 2006

$CuInSe_2$ single crystal thin films was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The temperature dependence of the energy band gap of the $CuInSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;1.1851\;eV\;-\;(8.99\;{\times}\;10^{-4}\;eV/K)T^2/(T\;+\;153K)$. After the as-grown $CuInSe_2$ single crystal thin films was annealed in Cu-, Se-, and In-atmospheres, the origin of point defects of $CuInSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K.

• Journal of Korean Vacuum Science & Technology
• /
• v.3 no.2
• /
• pp.112-115
• /
• 1999

The real ($\varepsilon$1) and imaginary ($\varepsilon$2) parts of the dielectric function of ZnS have been measured by spectroscopic ellipsometry (SE) in the 3.7-6.0 eV photon-energy range at room temperature. The obtained dielectric function spectra reveal distinct structures at energies E0/(E0+$\Delta$0) and E1 critical points. The spectrum after chemical treatment to remove surface oxide overlayer showed that these data seem to be the best representation of the dielectric function of ZnS, having the largest $\varepsilon$2 value at E1 peak region reported so far by SE. Dielectric-related optical constants of ZnS, such as the complex refractive indices (n+n=ik), absorption coefficient, and reflectance, are also presented.

• Journal of the Korean Vacuum Society
• /
• v.1 no.3
• /
• pp.360-370
• /
• 1992

HWE(Hot-Wall Epitaxy) 방법에 의하여 pyrex 유리기판 위에 CdS 다결정 박막을 성장하였다. X-선 회절실험 결과 CdS 박막은 육방정이었는데 (0002)면보다 91013)면이 강 하게 성장됨을 알 수 있었다. 전자현미경으로 표면을 분석한 결과 입자의 크기는 기판의 온 도가 48$0^{\circ}C$, 증발원의 온도가 $610^{\circ}C$일 때 1~1.5$mu extrm{m}$로서 가장 컸다. 박막의 표면저항은 4-point probe로서 측정한 결과 10-8$\Omega$/\ulcorner이상이었다. 성장된 CdS 다결정 박막의 photoluminesence을 20K에서 측정하였는데 bound exciton, donor acceptor pair에 의한 발광이 관측되었다. Spectral response의 peak는 505nm이었다. CdS 다결정 박막의 표면 저항을 줄이기 위하여 여러 가지 온도에서 Indium을 확산시켰다. 그 결과 표면저항은 ~ $\times$ 101에서 ~ $\times$ 103$\Omega$/\ulcorner 정도 감소되었다. 50$0^{\circ}C$에 In을 1시간 확산시켰을 때 표면저항은 1300$\Omega$/\ulcorner이었다. 이 때 CdS : In의 운반자 농도는 1.2 $\times$ 1018cm-3, 이동도는 1.8cm-2/V-sec, 비저항은 1.3 $\times$ 10-2$\Omega$-cm이었다. CdS : In의 photoluminescence는 20K 에서 Gaussian curve를 보여 주었으며 peak의 위치는 510nm이었다. CdS : In 박막의 spectral response의 peak는 상온에서 500nm이다. CdS : In 광전도 cell의 sensitivity ${\gamma}$ =0.77이고, 최대 허용소비전력은 p=120mW, 100lux에서 rise time은 8 msec, decay time 은 6 msec이다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.2
• /
• pp.197-206
• /
• 1999

The stochiometric mixture of evaporating materials for the $AgInSe_2$single crystal thin films were prepared from horizontal furnace. Using extrapolation method of X-ray diffraction patterns for the $AgInSe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0$ and $C_0$ were 6.092 $\AA$ and 11.688 $\AA$, respectively. To obtain the single crystal thin films of AgInSe$_2$, the mixed crystal was deposited on thoroughly etched semi-insulator GaAs(100) substrate by HWE system. The source and substrate temperature were fixed to $610^{\circ}C$ and $450^{\circ}C$ respectively, and the thickness of the single thin films was obtained to 3.8 $\mu\textrm{m}$. The crystallization of single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray dirrfaction (DCXD). The Hall effect was measured by the method of van der Pauw and carrier density and mobility dependence on temperature were studied. The carrier density and mobility of $AgInSe_2$single crystal thin films deduced from Hall data are $9.58{\times}10^{22} electron/m^3,\; 3.42{\times}10^{-2}m^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $AgInSe_2$single crystal thin film, the spin orbit coupling $\Delta$So and the crystal field splitting $\Delta$Cr were obtained to 0.29 eV and 0.12 eV at 20 K respectively. From PL peaks measured at 20 K, 881.1 nm (1.4071 eV) and 882.4 nm (1.4051 eV) mean $E_x^U$ the upper polariton and $E_x^L$ the lower polariton of the free exciton $(E_x)$, also 884.1 nm (1.402 eV) express $I_2 peak of donor-bound exciton emission and 885.9 nm (1.3995 Ev) emerges $I_1$ peak of acceptor-bound exciton emission. In addition, the peak observed at 887.5 nm (1.3970 eV) was analyzed to be PL peak due to DAP.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.425-433
• /
• 2000

The stochiometric mix of evaporating materials for the $CuGaTe_2$single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuGaTe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0 and c_0$ were 6.025 $\AA$ and 11.931 $\AA$, respectively. To obtain the single crystal thin films, $CuGaTe_2$mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $670^{\circ}C$ and $410^{\circ}C$ respectively, and the thickness of the single crystal thin films is 2.1$\mu\textrm{m}$. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility dependence on temperature. The carrier density and mobility of $CuGaTe_2$single crystal thin films deduced from Hall data are $8.72{\times}10{23}$개 $\textrm m^3$, $3.42{\times}10^{-2}$ $\textrm m^2$/V.s at 293K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuGaTe_2$single crystal thin film, we have found that the values of spin orbit coupling $\Delta$s.o and the crystal field splitting $\Delta$cr were 0.0791 eV and 0.2463 eV at 10 K, respectively. From the PL spectra at 10 K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be 0.0470 eV and the dissipation energy of the donor-bound exciton and acceptor-bound exciton to be 0.0490 eV, 0.0558 eV, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.366-376
• /
• 1997

$CdGa_2Se_4$, epilayer of tetragonal type are grown on Si(100) substrate by hot wall epitaxy method. The source and substrate temperature is $580^{\circ}C$ and $420^{\circ}C$ respectively, and the thickness of the film is 3 $\mu \textrm{m}$. The crystallihe structure of epilayers were investigated by double crystal X-ray diffraction(DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility depending on temperature. From Hall data, the mobility was likely to be decreased by pizoelectric scattering in the temperature range 30 K to 200 K and by polar optical scattering in the temperature range 200 K to 293 K. In order to explore of photocurrent to darkcurrent (pc/dc), maximum allowable power dissipation (MAPD), spectral response and response time. The results indicated that for the samples annealed in Se vapor the photoconductive characteristics are best. Then we obtained the sensitivity of 0.98, the value of pc/dc of $9.62{\times}10^6$, the MAPD of 321 ㎽ and the rise and decay time of 9 ㎳ and 9.5 ㎳, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.6
• /
• pp.252-259
• /
• 2005

Single crystal $CuGaSe_2$ layers were grown on thoroughly etched semi-insulating CaAs(100) substrate at $450^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuGaSe_2$ source at $610^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $CuGaSe_2$ thin films measured with Hall effect by Van der Pauw method are $4.87{\times}10^{17}cm^{-3}$ and $129cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=1.7998eV-(8.7489{\times}10^{-4}eV/K)T^2/(T+335K)$. The voltage, current density of maxiumun power, fill factor, and conversion, efficiency of $n-CdS/p-CuGaSe_2$, heterojunction solar cells under $80mW/cm^2$ illumination were found to be 0.41 V, $21.8mA/cm^2$, 0.75 and 11.17%, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.211-220
• /
• 1998

The stochiometric composition of $AgGaS_2$polycrystal source materials for the single crystal thin films were prepared from horizontal furnace. From the extrapolation method of X-ray diffraction patterns, it was found that the polycrystal $AgGaS_2$has tetragonal structure of which lattice constant $a_0\;and \;c_0$ were 5.756 $\AA$ and 10.305 $\AA$, respectively. $AgGaS_2$single crystal thin film was deposited on throughly etched GaAs(100) substrate from mixed crystal $AgGaS_2$by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $590^{\circ}C$ and $440^{\circ}C$ respectively, and the growth rate of the single crystal thin films was about 0.5 $mu \textrm{m}$/h. The crystallinity of the grown single crystal thin films was investigated by the DCRC (double crystal X-ray diffraction rocking curve). The optical energy gaps were found to be 2.61 eV for $AgGaS_2$single crystal thin films at room temperature. The temperature dependence of the photocurrent peak energy is well explained by the Varshni equation, then the constants in the Varshni equation are given by${\Alpha};=;8.695{\times}10^{-4};eV/K,and;{\beta};=;332;K$. from the photocurrent spectra by illumination of polarized light of the $AgGaS_2$single crystal thin film, we have found that crystal field splitting $\Delta$Cr was 0.28 eV at 20 K. From the PL spectra at 20 K, the peaks corresponding to free and bound excitons and a broad emission band due to D-A pairs are identified. The binding energy of the free excitons are determined to be 0.2676 eV and 0.2430 eV and the dissociation energy of the bound excitons to be 0.4695 eV.