• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.309-312
• /
• 2004

The hydraulic structure of the hydroelectric power plant such as aqueduct tunnels and the drainage canal became old. Therefore, because the concrete surface of the aqueduct tunnel has received severe damage by wear-out and the crack etc the repair is demanded. This research examined the applicability of the repair mortar which mixed the fly ash and an artificial aggregate by using the very high early strength cement. As a result, good Quality repair mortar which satisfied the demand performance more than self-flow 270mm and compressive strength $50N/mm^2$ (age of 28days) adjusting of water cement ratio by using the MTX cement be able to be manufactured.

• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.438-443
• /
• 2000

This dissertation is focused on the study over the improvement for the early strength of belite-rich cement(BRC). For this purpose, the initial hydration behaviors according to addition of different calcium sulfate types were evaluated. From the observations by XRD, DSC and SEM, the BRC II and III with the addition of natural anhydrate and flue gas desulphurization(FGD) gypsum, respectively, formed much ettringite after 7 days more than the BRC I with the addition of chemical gypsum. The compressive strength of the BRC II and III developed outstandingly due to the formation of calcium aluminate hydrate within pores of hardened BRC paste. Especially, in the case of BRC III adding FGD with low impurities, the early as well as long term compressive strengths were shown very high, compared with other specimens.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.129-130
• /
• 2021

In order to solve the problem of low early-age compressive strength of high volume fly ash concrete. This paper studies the effect of 2% sodium sulfate (Na₂SO₄) as a chemical activator on the paste with 40% fly ash content and a water-binder ratio of 0.30. The results indicate that the addition of Na₂SO₄ can effectively improve the early-age compressive strength of the fly ash-cement system, and the strength improvement rate on the first day reached nearly 70%. In addition, calorimetric analysis reveals that the incorporation of Na₂SO₄ promotes the early hydration of cement and fly ash, increases the cumulative hydration heat and delays the heat peak of the aluminum phase.

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.130-135
• /
• 1999

고로슬래그 시멘트의 저온 조기 강도를 증진키 위하여 고로슬래그의 분말도를 높이고 낮은 물:시멘트 비(W/C)의 혼합수량을 사용하였다. 분쇄조제를 사용하여 6,280$\textrm{cm}^2$/g(Blaine)로 미분쇄한 고로슬래그를 일반 포틀랜드 시멘트와 혼합하여 고로슬래그 40%의 고로슬래그 시멘트를 만들었다. 그리고 시판의 naphthalene계 고성능감수제를 사용하여 혼합수량을 W/C=0.50(KS L 5105)에서 W/C=0.33으로 저하시킬 수 있었다. 상술한 방법을 통하여 고로슬래그 시멘트의 저온 조기 강도를 포트랜드 시멘트 강도보다 오히려 더 높게 향상시킬 수 있었으며, 기공구조 및 임피던스 분석의 방법으로 본 시멘트의 미세구조를 조사하였다.

• 한국세라믹학회지
• /
• 제47권5호
• /
• pp.387-393
• /
• 2010

To improve concrete quality one of the most widely used chemical admixtures is polycarboxylate type superplasticizer. Unlike lignosulfonate and naphthalene-sulfonate, it has high dispersion property and excellent sustainable dispersion property for cement and concrete. Thus, polycarboxylate type superplasticizer has been widely used as a high-performance water reducing admixture together with silica fume in high-performance concrete and other applications for the dispersion of high-strength concrete over 100 MPa. However, even though there have been many studied on the dispersion of concrete by the structure of polycarboxylate type superplasticizer, there have a few studied that clarified the relationships between its rheological properties and microstructure properties in the early hydration behavior of ordinary portland cement. To investigate the correlations between the rheological properties and microstructure of cementitious materials with polycarboxylate type superplasticizer, this study experimented on the rheology, pore structure, heat evolution, and consistency in early hydration as well as on the compressive strength by early dispersion characteristics.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2008년도 춘계 학술논문 발표대회
• /
• pp.117-121
• /
• 2008

This study investigates practical application of high early strength type concrete using fine particle classifying cement, and the results are summarized as following. The replacement use of FC 30% did not great influence on concrete mix, therefore mixing without additional SP and AE was available using equal mix with OPC. The ratio of increasing temperature by heat of hydration was similar with OPC, and the compressive strength was over then 5MPa at -28℃ outside temperature on 2nd day. Therefore, it is considering that the first purpose, the effect of shortening terms of work by early demolding, will be available. The rebound rate of type "P" schumidt hammer was relative with compressive strength, and the rebound rate for verifying 5MPa of compressive strength was estimated about 55 considering rate of safety. Therefore, assuming demolding date is available efficiently.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.601-604
• /
• 2008

본 연구에서는 FA의 치환율을 20 % 까지 증가시킨 콘크리트의 초기강도 증진 등 품질향상을 목적으로 새롭게 개발한 혼화제(이하 개발혼화제: 기호 G), 조강제, 수산화칼슘｛Ca(OH)$_2$｝및 미분시멘트 등을 사용하여 그 다량활용 가능성을 검토하였는데, 그 결과를 요약하면 다음과 같다. 혼합재료 종류별 슬럼프 로스는 Plain보다 조강제및 Ca(OH)2가 감소폭이 작게 나타나 개선된 결과치를 나타내었고, 미분시멘트와 G 혼화제는 슬럼프 로스가 크게나타났다. 공기량은 모든 혼합재료에서 모두 목표공기량을 만족하는 것으로 나타났다. 혼합재료 종류별 콘크리트의 압축강도는 조기 강도에서 G 혼화제가 재령 3일, 7일, 28일 모두 가장 크게 나타났고, 미분시멘트 및 조강제는 재령 3일 강도가 Plain보다 높은 강도증가율을 보였지만 재령이 증가하면 강도증가는 점차 둔화되는 것으로 나타났으며, Ca(OH)$_2$는 거의 효과가 없었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2006년도 춘계학술논문 발표대회 제6권1호
• /
• pp.159-162
• /
• 2006

This study generally compared and investigated cement type and quality of China and Korea. Cement in Korea is divided into five such as ordinary, high early strength, moderate heat, low heat and sulfate resistance portland cement. However cement in China is divided into portland cement($P{\cdot}I,\;P{\cdot}II$) and ordinary portland cement($P{\cdot}O$) with admixture displacement ratio and it is again divided into 6 level and 7 level with 28 days compressive strength. In addition China classified cement into several standards, such as Mgo, SO3,, igloss, blame, setting time, stability, strength, alkali and sampling test. Therefore it should be careful to conclude so quickly without right understanding whether quality of China cement is bad or good. The better way to evaluate China cement is synthetically understanding a value engineering and consumer awareness.

• 한국건설순환자원학회논문집
• /
• 제11권3호
• /
• pp.218-225
• /
• 2023

본 연구에서는 염소 성분의 시멘트 수화반응 촉진 효과를 이용하여 염소 함량을 증가시킨 클링커의 조강형 시멘트로서의 활용 가능성을 평가하였다. 실제 시멘트 제조설비를 이용해 염소 성분 200-1,000 ppm 수준의 클링커를 제조하고, 여기에 석고 및 혼합재를 첨가하여 46개의 시멘트 시료를 제조하여 이의 표준주도 및 응결, 압축강도를 측정해 통계 분석하였다. 시험 결과, 염소 함량 증가에 따라 응결이 단축되고, 1일 압축강도가 향상되었지만, 28일 압축강도는 하락하였다. 특히 염소 함량을 230에서 965 ppm으로 증가시킬 경우 1일 압축강도가 4.6 MPa 향상되어 3,400-3,970 cm²/g 범위에서 Blaine을 증가시키는 것보다 향상 효과가 뛰어난 것으로 분석되었다.

• 한국건축시공학회지
• /
• 제18권5호
• /
• pp.413-418
• /
• 2018

이 기초 연구는 시멘트 페이스트의 초기강도 향상 및 열전도율 향상을 위한 흄드 실리카의 첨가에 대한 적용성 및 문제점을 평가하기 위한 것이다. 주요 변수인 흄드 실리카 는 시멘트 질량 대비 0%에서 1.6%까지 0.4% 간격으로 첨가하였다. 실험결과, 흄드 실리카의 첨가는 시멘트 페이스트의 초기강도 발현에 효율적이었는데, 재령 1일 압축강도는 28일 강도의 약 45%이었다. 이 높은 초기강도 발현율은 증기 양생 시멘트 콘크리트의 경우와 비슷한 수준이다. 하지만 흄드 실리카의 첨가가 시멘트 페이스트의 열전도 저항성 향상에 미치는 영향은 무의미 하였다.