• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 봄 학술발표회 논문집(I)
• /
• pp.64-69
• /
• 1999

Slags are by-products of the metallurgical industry. The most important slag from the standpoint of the quantity used as building material is iron blastfurnace slag. Slags are either crystalline stable solid used as aggregates or glassy material used as hydraulic binder. Slag cements are low heat of hydration cements. Slags react more slowly with than portland cement but they can be activated chemically. Activatiors can be either alkaline activators such as soda, lime, sodium carbonate, sodium silicate or sulphate activators such as calcium sulphate or phosphogypsum. So, in this study slaked lime was used as an activator that the compressive strength of this modified cement(M1 type) is high range in early age. And initial setting time of M1 type cement was shorter than conventional cements.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2011년도 춘계 학술논문 발표대회 1부
• /
• pp.93-95
• /
• 2011

This study is to investigate experimentally the engineering characteristics of cement mortar incorporating both recycled aggregate powder (RP) below 0.08 mm and cement kiln dust(CKD). RP is substituted for fine aggregate ranged from 5~15% and CKD is also substituted for RP from 10~30%. The use of RP resulted in a decrease in flow value at fresh mortar, while an increase in CKD did not affect the flow value significantly. The combination of RP and CKD provided slight increase in compressive strength at early and 28 days and in the high curing temperature at early age showed an increasing Strength value.

• 콘크리트학회논문집
• /
• 제12권6호
• /
• pp.23-34
• /
• 2000

This paper reports the effects of curing temperature and aging on the strength and the modulus of elasticity. In oder to determine the strength and the modulus of elasticity with curing temperature and aging, experimental and analytical methods are adopted. The tests of 480 cylinders are carried out for type I, V and V with 15 percent replacement of fly ash cement concretes, which are cured at isothermal conditions of 10, 23, 35 and 5$0^{\circ}C$. and the concrete cylinders are tested at the ages of 1, 3, 7 and 28 days. According to the experimental results, the concrete subjected to high temperature at early ages attaines higher early-age compressive and splitting tensile strength but eventually attaines lower later-age compressive and splitting tensile strength. Even if modulus of elasticity has the same tendency, the variation of modulus of elasticity with curing temperature is smaller than that of compressive strength. Based on these experimental results, the relationships among compressive strength, modulus of elasticity and splitting tensile strength are proposed considering the effects of curing temperature, aging and cement type.

• 한국도로학회논문집
• /
• 제11권2호
• /
• pp.185-194
• /
• 2009

초속경 라텍스개질 콘크리트(VES-LMC)를 포함한 고성능 콘크리트는 낮은 물-시멘트비, 높은 결합재량 및 고성능감수제의 사용 등으로 인해 자기수축(Autogenous Shrinkage)이 1종 콘크리트(OPC)보다 크게 나타난다. 초속경 라텍스개질 콘크리트의 배합특성은 낮은 물-시멘트비(0.38), 높은 단위시멘트량($390kg/m^3$) 및 라텍스첨가(단위시멘트량 대비 15%)로 구성되므로, 자기수축이 크게 발생할 수 있고, 또한 콘크리트 타설 후 3시간 이내에 발생하는 급격한 수분소산(Water Dissipation)과 수분증발은 자기수축을 증가시킬 수 있다. 본 논문의 목적은 현장에서 작업시간 확보를 목적으로 사용되는 지연제 첨가량 변화에 따른 초기수축, 온도변형 및 자기수축을 평가하는 것이다. 실험결과 지연제의 첨가는 콘크리트의 최대 수화열에 영향을 미치지 않는 것으로 나타났으며, 초속경 라텍스개질 콘크리트의 초기 팽창은 일부 자기팽창의 영향이 있기는 하지만 대부분이 열팽창에 기인하는 것으로 나타났다. 지연제 첨가량이 증가함에 따라 자기수축이 감소하는 것으로 나타났지만, 지연제의 과도한 사용은 과도한 초기 팽창을 일으킬 수 있으므로 현장조건을 고려하여 신중하게 결정되어야 한다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.225-231
• /
• 1996

Prediction of the early-stage strength of concrete is useful for modernized concrete construction. An experiment was attempted on the high-strength of concrete produced by ordinary portland cement under the curing temperatures of 30, 20, $10^{\cire}C$ and the various mixing proportions such as water-binder ratio of 0.30, 0.35 and silica fume content of 10% by weight of cement. It is the aim of this study to investigare and compare the development of concrete strength with maturity and analyze the application of Maturity as a parameter to correlation estimate test results of concrete. They are statistically analyzed to infer the correlation coefficient between the Maturity and the compressive strength of high-strength concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 추계 학술논문 발표대회
• /
• pp.221-222
• /
• 2012

This study is to high early concrete development which reveals 14 MPa within 12 hours in order to reduce the mold time of dismantlement and not do the steam curing of the precast concrete product. About (40~50) min could shorten the final setting time if the coagulation test result cement amount 100 kg/m3 was increased. In the case of the compressive strength, it was exposed to be satisfied the target value with the cement amount 500 kg/m3 combination according to the hardening accelerator addition.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.254-255
• /
• 2014

This study is a part of development to improve early-age compressive strength of concrete by using industrial by-products. It tried to investigate the characteristics of early-age compressive strength according to curing temperature and industrial by-product replacement ratio 10, 20, and 30 %. As a result, regardless of industrial by-product replacement ratio and age, early-age compressive strength of concrete was found to be high compared to Plain using 100 % cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.573-576
• /
• 2003

We have developed and applied the super high early strength concrete overlay pavements for repairing asphalts pavements within 24hours. This pavements repairing method by the super high early strength concrete have already applied in U.S.A, japan, England, etc. The super high early strength concrete developed by Ssangyong cement co. for repairing pavements speedily have replaced at No. 2, 17 pavements in managing by Sunchoen national pavements management office. In the results, all of works have finished within 16~24hours after intercepting traffics and all of traffics was opened to be hamonious. In present, this pavements is sound and strong

• Computers and Concrete
• /
• 제7권1호
• /
• pp.17-38
• /
• 2010

This research aimed to investigate the influence of high-volume mineral admixtures (MAs), i.e., fly ash and slag, on the hydration characteristics and microstructures of cement pastes. Degree of cement hydration was quantified by the loss-on-ignition technique and degree of pozzolanic reaction was determined by a selective dissolution method. The influence of MAs on the pore structure of paste was measured by mercury intrusion porosimetry. The results showed that the hydration properties of the blended pastes were a function of water to binder ratio, cement replacement level by MAs, and curing age. Pastes containing fly ash exhibited strongly reduced early strength, especially for mix with 45% fly ash. Moreover, at a similar cement replacement level, slag incorporated cement paste showed higher degrees of cement hydration and pozzolanic reaction than that of fly ash incorporated cement paste. Thus, the present study demonstrates that high substitution rates of slag for cement result in better effects on the short- and long-term hydration properties of cement pastes.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.269-272
• /
• 2003

This study is intended to investigate the properties of concrete using AE Water Reducing Agent of Early-Strength Type. According to the results, as for the replacing method of mineral admixture, setting time is shortened faster in order of replacement for fine aggregate, combination and replacement for cement, and when AE Water Reducing Agent of Early-Strength Type is used, it is shortened by about 4 hours, compared with normal AE Water Reducing Agent Compressive strength is lower in the case of replacement for fine aggregate, but higher in the other case than that of plain concrete. And When AE Water Reducing Agent of Early-Strength Type is used, early compressive strength is very high in comparison to normal AE Water Reducing Agent. Early strength development is very favorable by the use of AE Water Reducing Agent of Early-Strength Type regardless of the replacing method of mineral admixture at $20^{\circ}C$, but at $l0^{\circ}C$, it is effective for Early strength development that W/B is lowered to below 45%, BS of 20% is replaced for fine aggregate, and AE Water Reducing Agent of Early-Strength Type is used.