• 한국레이저가공학회지
• /
• 제11권2호
• /
• pp.15-19
• /
• 2008

Electron beam (EB) weldability of pure grade Nb sheet was studied. One of Nb sheets was as-annealed and the other was cold rolled. Microstructures, Vickers hardness, and transverse weld tensile test were carried out for the base metal, the heat affected zone (HAZ) and weld metal. In the case of the EB welds made using the annealed Nb sheeet, fine equiaxed grains and coarse grains were dominant at the base metal and the HAZ, respectively, and columnar grains were observed at the weld metal. For the EB welds made using the cold rolled Nb sheet, elongated grains in the rolling direction at the base metal, and the microstructures of the weld metal and the HAZ are similar to those of the EB welds made using the annealed Nb sheet, respectively. For both annealed and cold rolled Nb sheet, the width of the HAZs are unusually wide in spite of using high density heat source, i.e. electron beam, and the grain sizes of both HAZs are similar. When tensile test was carried out using the transverse weld specimens, the failure occurred at the HAZ for both EB welds made using Nb sheets annealed and cold rolled, respectively and the tensile strengths of both specimens were 161MPa. Vickers hardness of EB welds made using annealed Nb was 56-57 Hv at both base metal and weld metal, 52-53 Hv at the HAZ. On the other hand, Vickers hardness of EB welds made using cold rolled Nb was 97-99 Hv at the base metal, but the hardness values of weld metal were similar to those obtained at the weld metal of annealed Nb.

• 한국재료학회지
• /
• 제29권8호
• /
• pp.497-504
• /
• 2019

In this study, the correlation between microstructure and Charpy impact properties of FCAW(Flux cored arc welding) HAZ(Heat affected zone) of thick steel plates for offshore platforms was investigated. The 1/4 thickness(1/4t) location HAZ specimen had a higher volume fraction of bainite and finer grain size of acicular ferrite than those of the 1/2 thickness (1/2t) location HAZ specimen because of the post heat effect during the continuous FCAW process. The Charpy impact energy at $-20^{\circ}C$ of the 1/4t location HAZ specimen was lower than that of the 1/2t location HAZ specimen because of the high volume fraction of coarse bainite. The Charpy impact energy at -40 and $-60^{\circ}C$ of the 1/2t location HAZ specimen were higher than those of the 1/2t location HAZ specimen because the ductile fracture occurred in the fine acicular ferrite and martensite regions. In the ductile fracture mode, the deformed regions were observed in fine acicular ferrite and martensite regions. In the brittle fracture mode, long crack propagation path was observed in bainite regions.

• 한국지리정보학회지
• /
• 제23권3호
• /
• pp.220-235
• /
• 2020

도시에서의 폭염발생은 기본적으로 지구온난화에 영향을 받으나, 도시에서 발생하는 인공열 배출과 열축적이 큰 토지피복의 영향으로 더욱 가중된다. 특히 도시폭염의 영향은 야간 열대야 발생에도 직접적 영향을 준다. 그러나 기본적으로 주간의 폭염대응에 비해 열대야 대응수단 선택은 매우 제한적이다. 본 연구에서는 대구시를 대상으로 열대야 대응 방안으로 야간 찬공기 유동 특성을 분석하고 이의 공간적 활용가능성을 제시하고자 하였다. 연구방법은 찬공기 유동 분석 프로그램인 KLAM_21을 활용하여 대구시의 찬공기 유동의 공간적 특성인 찬공기 높이 및 유동범위와 유속 및 유동방향을 정량적으로 분석하였다. 분석결과 대구시 주변산지에서의 찬공기 생성, 유동은 매우 활발하나 열대야 발생지역인 도심지역으로 유입이 제한적인 것으로 나타났다. 그러나 일부 시가지에서는 주변산지로부터 유입되는 찬공기 유동성이 매우 활발하여 열대야 대응에 매우 효과적인 공간적 조건을 가지고 있는 것으로 나타났다. 이러한 공간적 조건을 도시계획적 차원에서 활용하면 열대야 대응방안 개발에 매우 유용할 것으로 판단된다.

• 대한토목학회논문집
• /
• 제7권1호
• /
• pp.93-101
• /
• 1987

용접부(鎔接部)에서 잔류응력(殘留應力)은 용접열(鎔接熱)에 의한 국부(局部) 가열(加熱)과 불규칙적(不規則的)이고 비교적(比較的) 급속(急速)한 냉각(冷却)으로 유발(誘發)되는 열응력(熱應力)과 구조물(構造物)의 강성(剛性) 및 재료(材料) 등에 의하여 발생(發生)되며, 잔류응력(殘留應力)의 존재(存在)는 취성파괴강도(脆性破壞强度), 피로강도(疲勞强度), 좌굴강도(挫屈强度), 진동특성(振動特性), 부식저항(腐蝕抵抗) 등에 영향(影響)을 미치는 궁극적(窮極的) 요인(要因)으로 간주(看做)됨으로 본(本) 연구(硏究)는 구조물(構造物)의 강도(强度)를 저하(低下)시키고 기능(機能)에 악영향(惡影響)을 끼치는 잔류응력(殘留應力)의 기구학적(機構學的) 특성(特性)을 파악(把握)하기 위하여 SWS 58 강판(鋼板)을 X홈 용접(鎔接)하여 이것을 4단계(段階) 즉 $350^{\circ}C$, $500^{\circ}C$, $650^{\circ}C$, $800^{\circ}C$로 열처리(熱處理)하여 hole drilling method를 사용(使用)하여 잔류응력(殘留應力)을 측정(測定)한 결과(結果), 다음과 같은 결론(結論)을 얻었다. 잔류응력(殘留應力)을 제거(除去)시키는 가장 효과적(效果的)인 온도(溫度)는 $650^{\circ}C$ 정도(程度)이었고, 구멍의 직경(直經)이 구멍의 깊이와 일치할 때 구멍바로 근처(近處)의 소성변형(塑性變形)은 완전(完全)히 해방(解放)되었으며, 경도시험(硬度試驗)을 통(通)해 열처리(熱處理) 후(後) 열영향부(熱影響部)의 높은 경도(硬度)가 모두 삭감(削減)되는 것을 알 수 있었으며 또한 잔류응력(殘留應力)에 끼치는 용접입열(鎔接入熱)의 영향(影響)은 입열량(入熱量)의 표준(標準)보다 1/4 이상(以上), 이하(以下)인 경우 잔류응력(殘留應力)은 용접입열(鎔接入熱)에 큰 영향(影響)이 없음을 알았다.

• 플랜트 저널
• /
• 제10권2호
• /
• pp.48-59
• /
• 2014

본 연구에서는 고온 고압 배관용 단조밸브 용접부의 품질확보를 위하여 단조밸브 제작현장에서 활용할 용접후열처리의 유지시간 및 유지온도를 연구했다. ASTM A182 F92 재료를 단조밸브의 용접부에 해당되는 밸브 끝단부 및 누설방지용접부와 동일한 형상의 두께 1 inch 쿠폰으로 가공하고, 쿠폰을 가스 텅스텐 아크용접(GTAW: Gas Tungsten Arc Welding) 방법으로 완전용입 용접하여 시편을 제작했다. 용접부 호칭두께가 1 inch인 시편을 $705^{\circ}C$, $735^{\circ}C$, $750^{\circ}C$, $765^{\circ}C$, $795^{\circ}C$ 및 $825^{\circ}C$에서 1시간 유지하여 용접후열처리를 실시(Group 1)하였다. 그리고 용접부 호칭두께가 1 inch인 시편 3개를 $735^{\circ}C$에서 30분, 1시간 및 2시간으로 달리 유지(Group 2)하여 용접후열처리를 실시하였다. 다른 유지시간과 유지온도에 따른 경도의 변화를 관찰하기 위하여 모재부, 열영향부 및 용착금속부에서 경도를 측정하였다. 본 실험의 결과에 따라, 1 inch당 1시간 온도를 유지할 경우는 용접후열처리가 $750^{\circ}C{\sim}765^{\circ}C$에서 수행되어야 바람직한 것으로 확인되었다. 단조밸브 제작규격에서 요구하는 최소 유지온도 보다 $5^{\circ}C$가 높은 $735^{\circ}C$에서 1 inch당 1시간 유지할 경우에 요구된 경도 값을 만족하지 못하여, 요건보다 긴 시간인 1 inch당 2시간 용접후열처리 시 경도 값을 만족하는 것으로 확인되었다. 또한 용착금속부의 조직은 템퍼드-마르텐사이트 조직으로 확인되었다.

• Journal of Welding and Joining
• /
• 제30권1호
• /
• pp.64-71
• /
• 2012

The characteristics of high heat input (342kJ/cm) EG (Electro Gas Arc) welded joint of EH36-TM steel has been investigated. The weld metal microstructure consisted of fine acicular ferrite (AF), a little volume of polygonal ferrite (PF) and grain boundary ferrite (GBF). Charpy impact test results of the weld metal and heat affected zone (HAZ) met the requirement of classification rule (Min. 34J at $-20^{\circ}C$). In order to evaluate the relationship between the impact toughness property and the grain size of HAZ, the austenite grain size of HAZ was measured. The prior austenite grain size in Fusion line (F.L+0.1 mm) was about $350{\mu}m$. The grain size in F.L+1.5 mm was measured to be less than $30{\mu}m$ and this region was identified as being included in FGHAZ(Fine Grain HAZ). It is seen that as the austenite grain size decreases, the size of GBF, FSP (Ferrite Side Plate) become smaller and the impact toughness of HAZ increases. Therefore, the CGHAZ was considered to be area up to 1.3mm away from the fusion line. Results of TEM replica analysis for a welded joint implied that very small size ($0.8\sim1.2{\mu}m$) oxygen inclusions played a role of forming fine acicular ferrite in the weld metal. A large amount of (Ti, Mn, Al)xOy oxygen inclusions dispersed, and oxides density was measured to be 4,600-5,300 (ea/mm2). During the welding thermal cycle, the area near a fusion line was reheated to temperature exceeding $1400^{\circ}C$. However, the nitrides and carbides were not completely dissolved near the fusion line because of rapid heating and cooling rate. Instead, they might grow during the cooling process. TiC precipitates of about 50 ~ 100nm size dispersed near the fusion line.

• 대한기계학회논문집A
• /
• 제34권1호
• /
• pp.85-90
• /
• 2010

자동차 후진기어용 축재는 단조재로서 그 형상은 복잡하고 열처리 및 가공공정이 어려울 뿐 아니라, 제품수명 저하 등의 문제점으로 인한 경제적 손실이 크다. 따라서 종전의 일체형 단조품을 캠 형상 부분만을 기존의 단조품(SF 45)으로 사용하고, 나머지 축 부분은 일반 기계구조용 탄소강재(SM 45C)로 대체를 위한 이종마찰용접을 적용하였다. 마찰용접 변수인 회전수, 마찰압력, 업셋압력, 가열시간, 업셋시간 등의 상호작용에 의한 용접품질과의 상관관계를 고찰하였으며, 최적조건에서 마찰용접을 한 후 용접재(as-welded)와 고주파 열처리를 시행한 후열처리재(PWHT)의 접합부 특성을 비교 고찰하였다. 이는 종전의 일체형 단조품에 비해 단조비용 절감, 피로수명향상, 기계가공에 따른 공정수 및 재료절감 등의 경제적 파급효과가 클 것으로 기대된다.

• 대한금속재료학회지
• /
• 제49권8호
• /
• pp.628-634
• /
• 2011

SA508 Gr.4N Ni-Cr-Mo low alloy steel, in which Ni and Cr contents are higher than in commercial SA508 Gr.3 Mn-Mo-Ni low alloy steels, may be a candidate reactor pressure vessel (RPV) material with higher strength and toughness from its tempered martensitic microstructure. The inner surface of the RPV is weld-cladded with stainless steels to prevent corrosion. The goal of this study is to evaluate the microstructural properties of the clad interface between Ni-Cr-Mo low alloy steel and stainless weldment, and the effects of post weld heat treatment (PWHT) on the properties. The properties of the clad interface were compared with those of commercial Mn-Mo-Ni low alloy steel. Multi-layer welding of model alloys with ER308L and ER309L stainless steel by the SAW method was performed, and then PWHT was conducted at $610^{\circ}C$ for 30 h. The microstructural changes of the clad interface were analyzed using OM, SEM and TEM, and micro-Vickers hardness tests were performed. Before PWHT, the heat affected zone (HAZ) showed higher hardness than base and weld metals due to formation of martensite after welding in both steels. In addition, the hardness of the HAZ in Ni-Cr-Mo low alloy steel was higher than that in Mn-Mo-Ni low alloy steel due to a comparatively high martensite fraction. The hardness of the HAZ decreased after PWHT in both steels, but the dark region was formed near the fusion line in which the hardness was locally high. In the case of Mn-Mo-Ni low alloy steel, formation of fine Cr-carbides in the weld region near the fusion line by diffusion of C from the base metal resulted in locally high hardness in the dark region. However, the precipitates of the region in the Ni-Cr-Mo low alloy steel were similar to that in the base metal, and the hardness in the region was not greatly different from that in the base metal.

• 한국해양공학회지
• /
• 제22권5호
• /
• pp.87-93
• /
• 2008

The objective of this paper is the investigation of the statistical properties of Vickers hardness (HV) of friction welded parts in nickel based super resisting steel, alloy 718 steel. First, we examine the statistical properties on the case of as-welded parts. Several Virkers indentations were made under same nominal conditions. This was repeated for three different applied loads, 100, 200 and 300g with a duration time, 10 second. The arithmetic mean of Vickers hardness in base metal (BM) materials is larger than that of HAZ in all applied loads. The measure of dispersion, that is, the coefficient of variation (COV) for BM and HAZ is decreased by increasing with the applied load. The distribution of Vickers hardness was not found to be symmetric type. The probability distribution of Vickers hardness was well followed Weibull distribution. The shape parameter and the scale parameter (characteristic hardness) are increased by increasing with the applied load, as both BM and HAZ.

• 대한기계학회논문집A
• /
• 제34권1호
• /
• pp.67-72
• /
• 2010

원전 배관의 LBB 해석을 위한 파괴인성(J-R곡선)은 일반적으로 ASTM E1820에 따라 시험을 수행하여 획득한다. 그러나 ASTM E1820에 제시되어 있는 파괴인성에 관한 식은 균질재의 물성 평가를 위한 것 이며, 협개선 용접부에 적용할 경우 실제와는 다른 파괴인성을 나타낼 수 있다. 따라서 본 연구에서는 ASTM에 제시되어 있는 균질재의 파괴인성식에 의한 결과와 협개선 용접재의 특성을 고려하여 제안된 소성 $\eta$계수 식에 의한 파괴인성의 차이를 비교 검토하기 위하여 협개선 용접이 적용된 배관에서 CT 시험편을 채취한 후 파괴인성 시험을 수행하였다.