• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.12 no.2
• /
• pp.49-54
• /
• 2013

Recently welding of aluminum material is actively carried out to make lightweight in the fields of LNG vessels, aircraft, chemical plants, etc. To obtain high strength, hardness and elongation, elements such as manganese, zinc, silicon, etc should be added in aluminum alloy, which has been improved on the mechanical properties like precipitation hardening, age hardening, loosening, corrosion resistance acid resistance. Ar gas is used as a shielding gas of MIG welding for aluminum, also $N_2$, $O_2$, $CO_2$, $H_2$ etc can be added depending on the composition of the alloy. In this study, Ar + $O_2$, Ar, and He were used for welding, hardness, penetration status and changes in composition of penetrated parts were compared and analyzed. This made it possible to know the status and changes of the process in the penetrated parts depending on used gas throughout this study.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.525-531
• /
• 1996

(Ti1-xAlx)N films were deposited on high speed steel and silicon substrates by reactive sputtering in mixed $Ar-N_2$ discharges. Crystalline phases and microhardness of ($Ti_1_xAl_x$)N films were investigated with variation of the film composition and substrate RF bias voltage. With Al content x of about 0.6, crystalline phase of ( $Ti_1_xAl_x$N films was changed from single-phase NaCl structure to two phase mixture of NaCl and wurtzite structures: Microhardness of ($Ti_1_xAl_x$)N films was largely improved by applying RF bias voltage above 50 V during deposition. Hardness of ($Ti_1_xAl_x$)N films reached a maximum value for Al content x of about 0.4, and 1900 kg/$mm^2$ was obtained for 1$\mu m$-thick ($Ti_{0.6}Al_{0.4}$)N films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.9
• /
• pp.808-811
• /
• 2008

Optical and mechanical properties of diamond-like carbon (DLC) films synthesized by RF plasma enhanced chemical vapor deposition were investigated as a function the C/H ratio in gas mixture. The C/H ratio was varied from 6 to 10 %, adjusting the amount of $CH_4$ and $H_2$ as the source gas. The optical and mechanical properties of DLC films were characterized by UV spectrometer, Ellipsometer and Nano-indenter. The change of the C/H ratio during synthesis of DLC films had many effects on the growth rate, transmittance, refractive index and hardness. The growth rate of the films increased exponentially with the increase in C/H ratio. The hardness of the films showed the tendency to improve with increasing C/H ratio, whereas the transmittance decreased. The refractive index was varied from 2.03 to 2.17, and these refractive indexes close to 2.0 indicates that it can be applied to Si-based solar cell.

• Transactions of Materials Processing
• /
• v.23 no.5
• /
• pp.303-310
• /
• 2014

Functionally graded properties are characterized by the gradual variation in composition and structure through the volume of the material, resulting in corresponding gradation in properties of the material. Direct laser melting (DLM) is a prototyping process whereby a 3-D part is built layer-wise by melting metal powder with laser scanning. Studies have been performed on the functionally graded properties induced by direct laser melting of compositionally selected metallic powders. For the current study, quadrangle structures were fabricated by DLM using Fe-Ni-Cr powders having variable compositions. Hardness and EDX analysis were conducted on cross-sections of the fabricated structure to characterize the properties. From the analysis, it is shown that functionally graded properties can be successfully obtained by DLM of selected metallic powders with varying compositions.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.2
• /
• pp.83-89
• /
• 2006

The surface phase changes, the hardness variations, the nitrogen contents and the corrosion resistances of 17-4 PH stainless steel have been investigated after nitrogen permeation(solution nitriding) at a temperature ranges from $1050^{\circ}C$ to $1150^{\circ}C$ The phases appeared at the nitrogen-permeated surface layer were shown to martensite plus austenite and austenite, depending on the variation of nitrogen and chromium contents. And the surface hardness was also depended on the phases appeared at the surface layer from 370 Hv to 220 Hv. The precipitates exhibited at the nitrogen-permeated surface layer were niobium nitride, niobium chromium nitride and carbo-nitride in the austenite and martensite matrices. The surface nitrogen contents were followed by the Cr contents of the surface layers, representing 0.55% at the temperatures of $1050^{\circ}C$ and $1150^{\circ}C$ respectively, and 0.96% at $1100^{\circ}C$ at the distances of $60{\mu}m$ from the outmost surface. From the comparison of the corrosion resistances between nitrogen-permeated and solution-annealed steels, nitrogen permeation remarkably improved the corrosion resistance in the solution of 1 N $H_2SO_4$ due to the increase of nitrogen content in the surface austenite phase.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.5
• /
• pp.215-220
• /
• 2014

Electrodeposition behaviors of Pd-Ni alloys were investigated from the polarization curves in a solution containing ethylenediamine as complexing agent. The microstructure and hardness of electrodeposited Pd-Ni alloys were also characterized. Codeposition of Pd-Ni alloys was successfully performed in the wide current density ranging from 2 to $5000A{\cdot}m^{-2}$ because the deposition potential of Pd became close to that of Ni in the ethylenediamine-contained solution. It was also found from X-ray diffraction patterns that the solid solution between Pd and Ni was formed with variation of the composition of alloys. The measured hardness of Pd-Ni alloys increased with increasing the contents of Ni due to solid solution strengthening and grain refinement. The electrodeposited Pd-Ni alloys also exhibited a crack free smooth surface morphology from the SEM observation.

• Journal of Ocean Engineering and Technology
• /
• v.22 no.2
• /
• pp.99-105
• /
• 2008

Ultrasonic nanocrystal surface modification (UNSM) is a method to induce severe plastic deformation to a material surface, so that the structure of the material surface becomes a nanocrystal structure from the surface to a certain depth. It improves the mechanical properties, namely hardness, compressive residual stress, and fatigue characteristics. Specimens of SKD61 were tested to verify the effects of the variation of UNSM static load level on fatigue characteristics. The results were as follows: the grain size of SKD61 treated with UNSM became very fine from the material surface to a $100{\mu}m$ depth. The surface hardness of SKD61 was increased up to 37% after UNSM. And fatigue strength at $10^7$ cycles was increased by 8.3, 11.2, and 17.9% respectively, when the static load levels of UNSM were 4, 6, 8 kgf.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.2 no.1
• /
• pp.67-77
• /
• 1998

Homogeneous liquids of Ni-21.5Nb-2.5Al and Ni-23.3Nb eutectic superalloys were solidified into Ni/$Ni_3$Al-$Ni_3$Nb(${\gamma}$/${\gamma}$'-${\delta}$)and Ni-Ni/$Ni_3$Nb(${\gamma}$-${\delta}$) phase by directional solidification and the effect of interlamellar spacing on microsturctural stability at high temperatures, hardness variation with growth rate was studied. The interlamellar spacing(${\lambda}$) in the eutectics was varied with the growth rate(R), corresponding to "${\lambda}^2$R ＝Constant" relationship. Isothermal heat treatments of the eutectics used in this study, provided the microstructural stability improvement at hight temperature as the interlamellar spacing increases. It was also seen that the hardness improvement is made with the growth raterowth rate

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.1
• /
• pp.51-65
• /
• 2019

A wood-plastic composite (WPC) paver block was manufactured using wood chips waste through an extrusion process, and it was intended to be used for paving in basic rest areas. The first stage in this study covered preliminary tests in terms of flexural strength and dimensional swelling to determine the optimal WPC compounding mix condition, by variation of the WPC ingredients. Next, three different paver blocks including the WPC block, a non-porous cement block, and a porous cement block were tested in terms of various material properties in the laboratory. Finally, two outdoor test sections of the proposed paver blocks were prepared to simulate a basic rest area. Test results indicated that the flexural strength of the WPC paver blocks was about 1.6 times greater than that of the tested cement paver blocks. The WPC block pavement was unaffected by water buoyance as well as volume expansion due to swelling. Results from the impact absorbance test and light falling weight deflectometer (LFWD) test clearly showed that the WPC block paving system marginally satisfied the comfortable and safe hardness range from the pedestrians' perspective, while the results demonstrated that it is structurally sound for application as a road paving block.

• Korean journal of food and cookery science
• /
• v.30 no.1
• /
• pp.64-75
• /
• 2014

Freeze-drying process was used for 10 major protein foods referred by the Korea Health Statistics 2011 as follows; chicken, pork, beef, eggs, tofu, squid, soybean, mackerel, anchovy, and pollack/frozen pollack. Boiled samples and re-hydrated samples after freeze-drying were prepared for analysis. The weight variation, the chromaticity, the mechanical texture and sensory properties by eight trained panelists were measured. In the ratio of re-hydration, the anchovy showed the highest value(89.40%), followed by eggs, and squid showed the lowest value(35.51%). Changes of Hunter color value were observed among all samples. For rates on changes of hardness, every sample was increased except for eggs(p<.05). Among the 9 samples, except for eggs, chicken showed the lowest rate of increase in hardness(125.44%) while squid showed the highest rate of increase in hardness(1335.1%). Except for eggs and pork, eight samples represented differences in sensory properties, especially in juiciness and tenderness(p<.05). As a result, we found that egg is the most suitable for freeze-drying among 10 protein sources followed by pork and chicken.