• Bulletin of the Korean Chemical Society
• /
• v.27 no.9
• /
• pp.1341-1345
• /
• 2006

An electrostatic interaction is responsible for the attachment of gold seeds of 1-3 nm onto APTMS (3-aminopropyl trimethoxysilane)-coated silica cores in the formation of gold clusters. A surface plasmon resonance and morphology of gold clusters were significantly affected by the pH of gold colloids prepared by THPC reducing agent. Gold colloids of alkaline pH induced the heterogeneous deposition of gold seeds onto the silica nanoparticles, probably due to the continuous reduction of residual gold ions during the attachment process. Gold colloids of acidic pH induced the monodisperse deposition of gold seeds, consequently leading to the formation of smooth gold layer on the silica nanoparticles surface. The gold nanoshells (core radius = 80 nm) prepared by gold colloids of pH 3.1 exhibited the more red-shift and relatively stronger intensity of plasmon absorption bands, compared with gold nanoshells prepared by alkaline gold colloids of pH 9.7.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.11
• /
• pp.3735-3739
• /
• 2012

We have developed magnetically controllable gold nanoparticles by synthesizing superparamagnetic $Fe_3O_4$ core/gold shell nanoparticles. The core/shell particles have the capability of forming gold 1D chains in the presence of an external magnetic field. Here we demonstrate dynamic and reversible self-assembly of the gold 1D chain structures in an aqueous solution without any templates or physical or chemical attachment. The spatial configuration of gold chains can be arbitrarily manipulated by controlling the direction of a magnetic field. This technique can provide arbitrary manipulation of gold 1D chains for fabrication purpose. To demonstrate this capability, we present a technique for immobilization of the gold particle chains on a glass substrate.

• Economic and Environmental Geology
• /
• v.46 no.1
• /
• pp.21-28
• /
• 2013

In order to optimize gold leaching from refractory sulfide concentrate, a HCl-NaClO-$FeCl_3$ solution with varying attributes was applied to the roasted concentrate from Uil mine. The gold from Uil mine occurs in the form of invisible gold that is difficult to leach. The results of the gold leaching experiments showed that the best gold leaching parameters were $550^{\circ}C$ of roasting temperature, 2.0 M of concentration, 1.0% of pulp density, and $70^{\circ}C$ of leaching temperature. It is confirmed that the HCl-NaClO-$FeCl_3$ solution was an environmentally friendly method to leach gold and silver from the refractory sulfide concentrate as an alternative lixiviant to cyanide.

• Journal of the Mineralogical Society of Korea
• /
• v.25 no.3
• /
• pp.123-130
• /
• 2012

Leaching experiments of gold and silver from roasted concentrate were carried out using a chlorine-hypochlorite solution. The leaching rate of gold was 75% at 1.5:1 ratio of chlorine and hypochlorite and increased to 81% with adding 1 M NaCl. However, at 1% pulp density and at $65^{\circ}C$, the leaching rates of Au were close to 100%. XRD analysis identified quartz in the solid residues after digestion of roasted concentrate with aqua regia or chlorine-hypochloride leaching solution. This suggests that the gold may not be leached out of the quartz in aqua regia or chlorine-hypochlorite solution. In order to leach the gold from the quartz, the concentrate will have to be pre-treated through ultra-fine grinding or treated with stronger oxidative agents.

• Journal of Radiopharmaceuticals and Molecular Probes
• /
• v.1 no.1
• /
• pp.46-52
• /
• 2015

Herein we present the synthesis of $^{68}Ga$-labeled gold nanoparticles for in vivo PET imaging. A novel chelator DTPA-Cys was easily prepared from diethylenetriaminepentaacetic dianhydride in high yield. The ${\alpha}_v{\beta}_3$ integrin receptor targeted gold nanoparticle probe was synthesized by using DTPA-Cys, polyethylene glycol and cRGD peptide. $^{68}Ga$ labeling of cRGD conjugated gold nanoparticle was carried out at $40^{\circ}C$ for 30 min. Observed radiochemical yield was more than 75% as determined by radio-TLC and the probe was purified by centrifugation. In vitro stability test showed that 90% of $^{68}Ga$-labeled gold nanoparticle probe was stable in FBS for 1 h. Those results demonstrated that $^{68}Ga$-labeled gold nanoparticle could be used as a potentially useful probe for specific tumor imaging.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.1
• /
• pp.237-242
• /
• 2013

This experiment was conducted for the purpose of developing such a sensor that can quickly sense dopamine concentration by using chitosan-gold nanoshell. Chitosan nano particles were reacted with gold nano particles so as to synthesize chitosan-gold nanoshell, and the size of the synthesized product was about 150 nm. When dopamine was reacted with chitosan-gold nanoshell, the size of it was not definitely changed, but dopamine was well reacted with chitosan-gold nanoshell, and it generated SERS (surface-enhanced Raman scattering), which led to a clear difference in the intensity of Raman scattering within the range of dopamine concentration (1 mM-10 mM). When Raman scattering was intensity marked on chitosan-gold nanoshell by employing a calibration curve according to dopamine concentration, a straight line whose margin of error was narrow was earned.

• Conservation Science in Museum
• /
• v.17
• /
• pp.17-42
• /
• 2016

A scientific analysis was performed on the gold belt with eight dangling ornaments discovered in the large Silla period Seobongchong Tomb. The object's gold sheets, nails, curved ornaments and gold wire were analyzed separately. Results show that all the components are gold-silver alloy, each varying in overall alloy composition. Gold sheets of two different gold contents are used for the belt, 17-18K gold and 19-20K gold, this seemingly by design. Nails are 20K gold, while the curved ornaments and gold wire of the belt are mostly 18K gold. Gold sheets for the dangling ornaments are mainly of 17-19K gold. Connecting rings used in the dangling ornaments are 17-19K gold, nails 17-20K gold and the curved ornaments and wire 19K gold.

• Fibers and Polymers
• /
• v.5 no.1
• /
• pp.1-5
• /
• 2004

The ability of inherently conducting polymer (ICP) coated textiles to recover gold metal from aqueous solutions containing $[AuCl_4]^-$ was investigated. Nylon-lycra, nylon, acrylic, polyester and cotton were coated with a layer of polypyrrole (PPy) doped with 1,5-naphthalenedisulfonic acid (NDSA), 2-anthraquinonesulfonic acid (AQSA) or p-toluenesulfonic acid (pTS). Textiles coated with polyaniline (PAn) doped with chloride were also used. The highest gold capacity was displayed by PPy/NDSA/nylon-lycra, which exhibited a capacity of 115 mgAu/g coated textile, or 9700 mgAu/g polymer. Varying the underlying textile substrate or the ICP coating had a major effect on the gold capacity of the composites. Several ICP coated textiles recovered more than 90 % of the gold initially present in solutions containing 10 ppm $[AuCl_4]^-$ and 0.1 M HCl in less than 1 min. Both PPy/NDSA/nylon-lycra and PAn/Cl/nylon-lycra recovered approximately 60 % of the gold and none of the iron present in a solution containing 1 ppm $[AuCl_4]^-$, 1000 ppm $Fe^{3+}$ and 0.1 M HCl. The spontaneous and sustained recovery of gold metal from aqueous solutions containing $[AuCl_4]^-$ using ICP coated textiles has good prospects as a potential future technology.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.3
• /
• pp.303-309
• /
• 2007

Statement of problem. The effect of gold electroforming on gold alloy was not studied. Purpose. This in vitro study investigate the effect of gold electroforming on gold-silver-palladium alloy. Material and methods. Three pieces of gold strips had undergone the electroforming procedures on one side and then half of the side again electroformed. The set mode for this study was program 1 ($200{\mu}m$). And the processing time was 15min (1/20 time to form $200{\mu}m$ coping). The confocal laser scanning microscope (PASCAL 5, Carl Zeiss, Bernried, Germany) was used to measure the thickness of the pure gold layer electroformed on the gold strips. Half of the gold strip was coated two times with electroformed gold, and the other half one time. The data from the cone focal laser system was processed to get the vertical profile of the strips and the difference of the vertical height between the double coated and single coated layer was regarded as the thickness of the gold coating. The layer thickness value to built 3D image of the cone-focal laser was set $0.5{\mu}m$. Next to the measurement of the thickness of the coating, the Vicker's hardness test was done. It was performed on the double coated surface, single coated surface and non-coated surface (back side) three times each. Results. The mean thickness value gained from gold electroforming technique was measured to be $22{\mu}m$ for sample 1, $23{\mu}m$ for sample 2, $21{\mu}m$ for sample 3. In the same condition of time, power and the amount of electrolyte, the data showed no difference between samples. According to the results of variance analysis, the differences among the variations in number of coating were statistically insignificant (p>0.05), meaning that the two times of gold electroforming coating did not change the hardness of gold-silver-palladium alloy. Conclusion. The test of thickness of gold coating proved the coherency of the gold electroforming procedure, in other words, when the power, the exposed surface area, processing time and the amount of electrolytes were set same, the same thickness of gold would be coated on. The hardness test showed that the electroformed gold coating did not change the hardness of the gold-silver-palladium alloy when it is coated not more than $45{\mu}m$.

• International Commerce and Information Review
• /
• v.8 no.1
• /
• pp.371-398
• /
• 2006

Gold prices are rising around the world in all major currencies. This is a telltale sign of a Stage Two gold bull where gold decouples from the US dollar. In this study, We analysed a confluence of factors seem to be feeding gold's gains and the typical shape of a secular gold bull---gold bulls' three stages. Stages one, two, and three of a secular gold bull are defined by the major changes. Each stage, considered in turn, makes perfect sense when described in terms of global investor demand. Since Stage One is currency-devaluation driven, the young gold bull is most noticeable in terms of the dominant eroding currency. Now after three or four years of stage one, Stage Two arrives. Stage Two marks a momentous event when gold decouples from the local-currency devaluation. In the case of our gold bull today, Stage Two will be here when gold starts consistently rising faster than the dollar is able to fall. After five or so years of Stage Two gains, gold has a chance at going ballistic in stage three. Stage Three is only ignited if the general public around the world starts growing enamored with gold investing. In summary, the first stage being when insiders and professionals invest in the market. The second stage is when the general public and financial media recognizes that the bull market is real. The third stage is the mania stage when people feel that not only is the bull market real, but it is a must own situation. Through the study we found that gold is entering it now.