• Journal of the Semiconductor & Display Technology
• /
• v.8 no.2
• /
• pp.49-53
• /
• 2009

The oxygen barrier films were formed on poly(ethylene terephthalate) (PET) substrate by a sol-gel process using 3-aminoproprytrimethoxysilane (APTMOS). The effects of solvent type, coating times and incorporation of fumed silica on oxygen permeability coefficient were investigated. The APTMOS coating film prepared from methanol as a solvent exhibited higher oxygen barrier properties than that using THF. The oxygen permeability coefficient of coated film with APTMOS/methanol by coating 7 times was measured to be $2.28{\times}10^{-6}$, while that of PET film was $1.16{\times}10^{-4}$ GPU. The addition of fumed silica does not affect the oxygen barrier properties. It may be explained that silica particles disrupt chain packing, which leads to an increase in free volume for permeation.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.9
• /
• pp.3822-3826
• /
• 2012

We have studied the effect of temperature and exposure time on the UV curing rate of Urethane Acrylate. UV dose has been modulated by changing the electric power, and temperature has been controled by coating rate and water temperature of the coating roll. Curing rate was evaluated by measuring gel fraction of the cured film. It has been found that effect of coating velocity on the gel fraction of the final film is predominant, but role of temperature of the UV chamber is negligible. These observations imply that exposure time of UV light is critical to have a fully cured film. To better understand the effect of design and operating condition of UV coater on the behavior of UV curing of Urethane Acrylate, we have also conducted heat-flux analysis of UV chamber.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.5
• /
• pp.617-627
• /
• 2006

Statement of problem: HA has been used as a coating material on Ti implants to improve osteoconductivity. However. it is difficult to form uniform HA coatings on implants with complex surface geometries using a plasma spraying technique. Purpose : To determine if Ti6Al4V sintered porous-surfaced implants coated with HA sol-gel coated and hydrothermal treated would accelerate osseointegration. Materials and Methods : Porous implants which were made by electric discharge were used in this study. Implants were anodized and hydrothermal treatment or HA sol-gel coating was performed. Hydrothermal treatment was conducted by high pressure steam at $300^{\circ}C$ for 2 hours using a autoclave. To make a HA sol, triethyl phosphite and calcium nitrate were diluted and dissolved in anhydrous ethanol and mixed. Then anodized implant were spin-coated with the prepared HA sols and heat treated. Samples were soaked in the Hanks solution with pH 7.4 at $37^{\circ}C$ for 6 weeks. The microstructure of the specimens was observed with a scanning electron microscope (SEM), and the composition of the surface layer was analyzed with an energy dispersive spectroscope (EDS). Results : The scanning electron micrographs of HA sol-gel coated and hydrothermal treated surface did not show any significant change in the size or shape of the pores. After immersion in Hanks' solution the precipitated HA crystals covered macro- and micro-pores The precipitated Ca and P increased in Hanks' solution that surface treatment caused increased activity. Conclusion : This study shows that sol-gel coated HA and hydrothermal treatment significantly enhance the rate of HA formation due to the altered surface chemistry.

• Korean Journal of Optics and Photonics
• /
• v.11 no.4
• /
• pp.255-260
• /
• 2000

We report that the crack-free organic-inorganic hybrid silica thin films were fabricated by sol-gel process using organometallic compounds as a precursor and that we have established very reproducible fabrication condition with systematic investigation of thickness and refractive index variations for various control parameters, such as, coating type, coating speed, chemical composition, prebake and postbake temperature. Additionally, we measured and compared the change of optical property with the UV exposure dose for three different kinds of photoinitiators. Furthermore, the fabrication of Ix4 MMI optical power splitter using the sol-gel thin film provides the possibility of various applications to the optical waveguide devices. vices.

• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.859-864
• /
• 1991

High quality lead titanate thin films were fabricated by spin coating on a silicon substrate. The resulting dried gel layers were uniform in thickness through 2$\times$2 $\textrm{cm}^2$ area, and polycrystalline perovskite structures developed almost crack free with a heat treatment above 50$0^{\circ}C$ in films with thickness above 360 nm. Metastable pyrochlore structures were observed in films with thickness of 160 nm when heat treated at 500 and $600^{\circ}C$, but these structure did not appear in films with thickness of 360 nm. The thickness dependence in crystal structure of films was studied. by varying the substrate condition and analyzing the interface between the film and substrate. In native oxide films on silicon stbstrates, amorphous dried gel layers were heterogeneously nucleated. Metastable cubic pyrochlore structure could be crystallized in amorphous native oxide.

• Journal of Electrical Engineering and Technology
• /
• v.8 no.1
• /
• pp.163-167
• /
• 2013

Aluminum doped zinc oxide (AZO) thin films have been prepared on the glass substrates (Corning 1737) by sol-gel dip-coating method employing zinc acetate and aluminum chloride hexahydrate for the transparent conducting oxide (TCO) applications. 1 at% Al was doped to the ZnO thin films. The effects of post-heating temperature on the crystallization, optical and electrical properties of the AZO films have been investigated. Experimental results showed that post-heating temperature affected the microstructure, electrical resistance, and optical transmittance of the AZO films. From the X-ray diffraction analysis, all films have hexagonal wurtzite crystal structure. Optical transmittance spectra of the AZO films exhibited transmittance higher than about 80% within the visible wavelength region and the optical direct band gap ($E_g$) of these films was increased with increasing post-heating temperature. A minimum resistivity of $2.5{\times}10^{-3}{\Omega}cm$ was observed at $650^{\circ}C$.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.255-256
• /
• 2018

In this study, to confirm the performance of gel type urethane (hereinafter referred to as urethane gel) developed for the purpose of securing waterproof stability after application by increasing compatibility with asphalt mastic film material, general urethane coating material and adhesion. As a result, gel type urethane showed "all right" in fatigue resistance test.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.83-86
• /
• 1998

Ferroelectric PZT(40/67)/PZT(60/40)heterolayered thin films were Prepared by the alkoxide-based Sol-Gel method. PZT(40/60) and PZT(60/40) stock solutions were made and spin-coated on the P7Ti/Si02/Si substrate alternately. These PZT(40/60) and PZT(60/40) films were dried at 300$^{\circ}C$ for 30min to remove organic materials and were sintered at 650$^{\circ}C$ for 1 hour to crystalize into a perovskite structure. The coating and heating procedure were repeated 6 times to form heterolayered films. Increasing the number of coating, coercive field was decreased. The relative dielectric constant, loss, remanent polarization and coercive field of the 4-coated PZT heterolayered were 1200, 4.1[%], 30.794[${\mu}$C/㎡] and 147.22[kV/cm], respectively.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.338-344
• /
• 2000

Grain boundary chemistry and electrical characteristics of polycrystalline BaTiO3 ceramics, which were prepared with sol-gel surface-coated semiconducting powders, were investigated. Mn ions were coated on the powder surface by sol-gel coating-techniques. The additives coated on the surface of the powders were observed to be present near the grain boundaries of the ceramics. The ceramics exhibit the PTCR characteristics with a resistivity jump ratio(Pmax/Pmin) of about 2$\times$103. With raising the temperature from room temprature to 20$0^{\circ}C$, the oxidation state of the Mn ions varied from Mn3+ to Mn2+ in the coating layers. Near the grain boundaries an excessive negative charge layer of about 20nm was formed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.192-195
• /
• 2000

Antimony doped tin oxyde thin films have been deposited by sol-gel method using non-alkoxide precursor SnCl$_2$$.$2H$_2$O as host and SbC1$_3$ as dopant material. Using spin coating method, thin films of thickness up to 200nm have been uniformly deposited on Corning 1737F non-alkali glass substrates. Effect of Sb doping concentration and heat treatment on electrical and optical properties was investigated. Heat treatment was performed at the temperature from 350$^{\circ}C$ to 650$^{\circ}C$ in flowing O$_2$. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition and firing condition.